CN1068774A - Highly damped aluminium alloy laminated composite plate - Google Patents
Highly damped aluminium alloy laminated composite plate Download PDFInfo
- Publication number
- CN1068774A CN1068774A CN 91106755 CN91106755A CN1068774A CN 1068774 A CN1068774 A CN 1068774A CN 91106755 CN91106755 CN 91106755 CN 91106755 A CN91106755 A CN 91106755A CN 1068774 A CN1068774 A CN 1068774A
- Authority
- CN
- China
- Prior art keywords
- aluminium alloy
- layer
- aluminium
- high damping
- reinforced aluminum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of highly damped aluminium alloy laminated composite plate is characterized in that: it is made up of with the high damping aluminium alloy layer that is compounded in both sides the middle layer of reinforced aluminum alloy.Interlayer can add transition layer, and the outside can add corrosion resistant aluminium surrounding layer.Plate property is: Q
-1〉=2.0 * 10
-2(1Hz, 18 ℃), σ
b〉=250MPa, δ
5〉=8%, ρ=3.0～3.8 were not split in clod wash for 90 ° when interior curved radius equaled thickness of slab.Have good welding, cold deformation cycling processability, solidity to corrosion and LY12CZ are suitable.Be particularly suitable for doing naval vessel, aeronautical material use.
Description
The present invention relates to a kind of aluminium alloy high damping material and preparation method thereof.
At present, the more high damping aluminium alloy of research is Al-Zn and Al-Si system.Al-Zn system is that damping capacity is best in the alloyed aluminium-alloy, Q
-1Can reach 0.05, its main drawback is that solidity to corrosion is poor than great (ρ 〉=5), and intensity is low, and damping capacity and mechanical property are difficult to take into account.In addition, Japanese Patent (clear 63-209832, openly speciallyyed permit communique on August 31st, 1988) introduced a kind of combined vibration-damping sheet material, be that folder one deck macromolecule resin forms through Compound Machining as damping layer between double layer of metal plate (for example steel plate, aluminium sheet), its damping capacity is greatly improved, but because its interfacial bonding strength is poor, the resin in middle layer is thermo-labile, poorly conductive, thereby be unsuitable for welding, processing such as cold deformation reprocessing.
At above-mentioned the deficiencies in the prior art, the objective of the invention is, provide a kind of damping and mechanical property good, can weld, be convenient to reprocessing, corrosion resistant high damping aluminium alloy matrix material.
The solution of the present invention is, is the middle layer with the reinforced aluminum alloy, makes the lamination composition board with the high damping aluminium alloy that is added in both sides.The compound again one deck rot-resistant of outermost layer metal surrounding layer in case of necessity.
For improving the bonding strength of interlayer, between high damping aluminium alloy and reinforced aluminum alloy, add the compatible intermediate metal in an interface.
Consisting of of high damping aluminium alloy:
Al20-40%; Zn55-80%; 0-5% is one or more that select among Zr, Ce, Ti, the Ni, and the adding of these several elements is favourable to improving mechanical property and damping capacity.
Consisting of of reinforced aluminum alloy:
Al89-98%; Mg2-6%; 0-5% is one or more that select among Mn, Cu, Cr, Ti, the B, and the adding of these several elements is favourable to improving mechanical property.
Surrounding layer is a fine aluminium, be to improve corrosion resisting property, can contain one or more that select among Zn, Mg, Mn, Cr, the Ti of 0-5%, and the thickness of surrounding layer is 0.01-0.1mm.
Transition layer can be used fine aluminium, or the aluminum base alloy of each component content between high damping aluminium alloy and the used component content of reinforced aluminum alloy; Its thickness is 0.01-0.1mm.
In the sheet material, the ratio a/b of the thickness of one deck high damping aluminium alloy and the thickness of one deck reinforced aluminum alloy is in the 0.05-0.5 scope.With the increase of a/b value, in-fighting value Q
-1, proportion ρ and elongation δ
5All increase, but tensile strength sigma
bReduce, thickness compared greater than 0.3 o'clock, Q
-1Increase slack-off, the a/b value of best over-all properties is between 0.2-0.35.
The working method of composition board is:
1. hot rolling is compound, and rolling temperature is 200-400 ℃, and it is compound to carry out hot rolling under the condition of control total deformation 〉=60%;
2. insulation 10 minutes to 20 hours under 300-420 ℃ of condition, then with 〉=10 ℃/second speed be cooled to≤50 ℃, speed of cooling is low excessively, Q
-1Variation;
20-150 ℃ rolling once more, the control total deformation is 20-90%;
4. stabilizing annealing, annealing temperature is 50-200 ℃, the residence time is 5 minutes to 100 hours.
Highly damped aluminium alloy laminated composite plate of the present invention, its salient features is as follows:
Damping capacity: Q
-1〉=2.0 * 10
-2(1Hz, 18 ℃)
Mechanical property: σ
b〉=250MPa, δ
5〉=8%
Cold-bending property: clod wash was not split for 90 ° when interior curved radius equaled thickness of slab
Proportion: ρ=3.0～3.8
Can weld, solidity to corrosion and LY12CZ are suitable, are particularly suitable for doing naval vessel, aeronautical material use.
Fig. 1 is the high damping lamination composite sheet structural representation that seven layers of aluminium alloy are formed;
Fig. 2 is the recombining process schema of high damping lamination composition board.
Embodiment 1:
As shown in Figure 1, highly damped aluminium alloy laminated composite plate is made of seven layers of aluminium alloy, and the finished product sheet metal thickness is 2mm, and wherein 1 is reinforced aluminum alloy, and its material is formed (weight) and is: Al92%, Mg4.5%, 3.5% Mn, Cu, Cr, Ti, B; Two sides are high damping aluminium alloy layer 2, and its material is formed (weight) and is: Al24%, Zn74%, 2% Cu, Zr, Ce, Ni, Ti; Surrounding layer 3 is an aluminium alloy, and its material is formed (weight) and is: Al99%, Zn1%; Thickness is 0.05mm.Transition layer 4 is the thick commercial-purity aluminium of 0.05mm.
The recombining process flow process as shown in Figure 2.Wherein, hot rolling recombining process: rolling temperature is 360 ℃, total deformation 80%; Quenching technology: 360 ℃ of quenching temperatures, be incubated 3 hours, be cooled to 50 ℃ with 40 ℃ of/second speed then; Rolling technology again: 150 ℃ of rolling temperatures, total deformation are 50%; Stabilizing annealing technology: 100 ℃ are incubated 24 hours.
The high damping aluminium alloy layer is more as shown in table 1 than the relation of a/b and material property with the reinforced aluminum alloy layer thickness.
Table 1: the relation of material property and a/b ratio
a/b 0.05 0.1 0.15 0.2 0.25 0.3 0.35 0.4 0.45 0.5
Q
-10.9 1.3 1.6 1.9 2.1 2.25 2.35 2.4 2.45 2.45
σ
b(Mpa) 330 316 283 263 251 243 240 233 228 221
δ
56.2 7.1 8.4 8.9 10.1 11.1 11.9 12.5 12.9 13.3
ρ 2.91 3.08 3.22 3.35 3.44 3.53?3.60?3.68?3.75?3.81
Embodiment 2:
The high damping aluminium alloy composition board is made of five layers of aluminium alloy, and the finished product sheet metal thickness is 1mm, and the material of reinforced aluminum alloy is formed (weight) and is: Al97%, Mg2%, 1% Mn, Cu, Cr, B; The material of high damping aluminium alloy layer is formed (weight): Al40%, Zn55%, 5% Zr, Ce, Ti, Ni; A/b=0.35; Surrounding layer is the fine aluminium that contains Al99.99%, and its thickness is 0.01mm.
The hot rolling recombining process: rolling temperature is 200 ℃, total deformation 90%; Quenching technology: 420 ℃ of quenching temperatures, be incubated 10 minutes, be cooled to 0 ℃ with 100 ℃ of/second speed then; Rolling technology again: 80 ℃ of rolling temperatures, total deformation are 20%; Stabilizing annealing technology: 200 ℃ are incubated 5 minutes.Its salient features is as follows:
Damping capacity: Q
-1=2.1 * 10
-2(1Hz, 18 ℃)
Mechanical property: σ
b=265MPa, δ
5=9%
Cold-bending property: clod wash was not split for 90 ° when interior curved radius equaled thickness of slab
Proportion: ρ=3.4
Can weld, solidity to corrosion and LY12CZ are suitable
Embodiment 3:
The high damping aluminium alloy composition board is made of seven layers of aluminium alloy, and the finished product sheet metal thickness is 5mm, and the material of reinforced aluminum alloy is formed (weight) and is: Al94%, Mg5%, Ti1%; The material of high damping aluminium alloy layer is formed (weight): Al20%, Zn80%; A/b=0.25; The material of outer aluminium coating is formed (weight): Al95%, 5% Zn, Mg, Cr, Ti; Its thickness is 0.1mm.The material of transition layer is formed (weight): Al98%, and Zn1%, Mg1%, thickness are 0.05mm.
Hot rolling technology: rolling temperature is 400 ℃, total deformation 60%; Quenching technology: 300 ℃ of quenching temperatures, be incubated 20 hours, be cooled to 20 ℃ with 10 ℃ of/second speed then; Rolling technology again: 20 ℃ of rolling temperatures, total deformation are 20%; Stabilizing annealing technology: 50 ℃ are incubated 100 hours.Its salient features is as follows:
Damping capacity: Q
-1=2.5 * 10
-2(1Hz, 18 ℃)
Mechanical property: σ
b=295MPa, δ
5=8%
Cold-bending property: clod wash was not split for 90 ° when interior curved radius equaled thickness of slab
Proportion: ρ=3.5
Can weld, solidity to corrosion and LY12CZ are suitable
Claims (8)
1, a kind of highly damped aluminium alloy laminated composite plate is characterized in that: it is made up of with the high damping aluminium alloy layer that is compounded in both sides the middle layer of reinforced aluminum alloy.
2, composition board according to claim 1 is characterized in that, it has rot-resistant aluminium surrounding layer.
3, composition board according to claim 1 is characterized in that, accompanies the compatible intermediate metal in interface between high damping aluminium alloy layer and the reinforced aluminum alloy layer.
4, according to claim 1 or 2 or 3 described composition boards, it is characterized in that, consist of seven layers, its middle layer is a reinforced aluminum alloy, adjacent both sides are the high damping aluminium alloy layer, accompany intermediate metal between high damping aluminium alloy layer and reinforced aluminum alloy layer, and the outside is the aluminium surrounding layer.
5, composition board according to claim 1 is characterized in that, the composition of described high damping aluminium alloy (weight) is: Al20-40%; Zn55-80%; 0-5% is one or more that select among Zr, Ce, Ti, the Ni; The composition of reinforced aluminum alloy (weight) is: Al89-98%; Mg2-6%; 0-5% is one or more that select among Mn, Cu, Cr, Ti, the B; The thickness of high damping aluminium alloy and reinforced aluminum alloy than a/b in the 0.05-0.5 scope.
6, composition board according to claim 2 is characterized in that, described aluminium surrounding layer is the aluminium alloy of one or more elements of selecting among fine aluminium or Zn, the Mg that contains (weight) 0-5%, Mn, Cr, the Ti, and its thickness is 0.01-0.1mm.
7, composition board according to claim 3, it is characterized in that, the intermediate metal that described interface is compatible, its material are aluminium or the aluminum base alloy of each component content between described high damping aluminium alloy and reinforced aluminum alloy each component content, and its thickness is 0.01-0.1mm.
8, a kind of making method as claim 1 or 2 or 3 or 4 described composition boards is characterized in that following steps and condition:
1) be 200-400 ℃ in rolling temperature, the control total deformation is compound for carrying out hot rolling under 〉=60% the condition;
2) insulation 10 minutes to 20 hours under 250-420 ℃ of condition, then with 〉=10 ℃/second speed be cooled to≤50 ℃;
3) 20-150 ℃ rolling once more, the control total deformation is 20-90%;
4), be incubated 5 minutes to 100 hours at 50-200 ℃.