CN106867401A - Water paint with high temperature resistant property - Google Patents
Water paint with high temperature resistant property Download PDFInfo
- Publication number
- CN106867401A CN106867401A CN201710251505.9A CN201710251505A CN106867401A CN 106867401 A CN106867401 A CN 106867401A CN 201710251505 A CN201710251505 A CN 201710251505A CN 106867401 A CN106867401 A CN 106867401A
- Authority
- CN
- China
- Prior art keywords
- parts
- high temperature
- coating
- temperature resistant
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the water paint with high temperature resistant property, including following components：Water, epoxy modified silicone resin, bisphenol A epoxide resin, aqueous acroleic acid resin, oxidized starch, organic phospho acid, zinc oxide, Boratex, sepiolite, borax, silica sand, dimethyl silicone polymer, calcium carbonate, propandiol butyl ether.Present invention employs a large amount of components with resistance to elevated temperatures, at high temperature, the performance of each component will not change, and coating has good heat resistance, and, the maximum problem that coating faces at high temperature is exactly fast paint solidification, viscosity is low, poor fluidity, and the thickness of the film of formation is big, fragility is high, and the service life of coating is low；Therefore, present invention employs high temperature retarder, the hardening time of coating can be postponed, improve the decentralization of coating, it is to avoid coating at high temperature rapid curing and film forming is uneven.
Description
Technical field
The present invention relates to a kind of coating, and in particular to the water paint with high temperature resistant property.
Background technology
Ancient building has high history science, artistic value, if be destroyed, it is then not possible to exist again；And ancient building
It is of the remote past, inevitably by nature or it is artificial destroy, it would therefore be desirable to be repaired to ancient building and tieed up
Shield.To ancient building room, Men Qiang, inner and outer eaves are bulky, can often use coating in the reparative processes of helping bulky, ground, metope.Due to repairing
Process of copying is numerous and diverse, and the duration is more long, so repair work preferably once completing, this requires that coating has good high temperature resistant
Property, corrosion resistance, caking property, water resistance and mechanical performance, it is to avoid coating color-changing is destroyed.
At present, water paint can be widely applied to the industries such as electrical equipment, metallurgy, oil, aviation field, chemical industry, medicine, food
In various, but the resistance to elevated temperatures of the coating of equipment surface is poor, especially for exposed to outdoor equipment, is exposed to the sun for a long time
With drench with rain, cause coating to drop, damage equipment surface, reduce service life of equipment, increase cost.
The content of the invention
The technical problems to be solved by the invention are that water paint resistance to elevated temperatures is poor, it is therefore intended that providing has high temperature resistance
The water paint of performance, solves the resistant to elevated temperatures problem of water paint.
The present invention is achieved through the following technical solutions：
Water paint with high temperature resistant property, including following components：
Water, epoxy modified silicone resin, bisphenol A epoxide resin, aqueous acroleic acid resin, oxidized starch, organic phospho acid,
Zinc oxide, Boratex, sepiolite, borax, silica sand, dimethyl silicone polymer, calcium carbonate, propandiol butyl ether.
Epoxy modified silicone resin, bisphenol A epoxide resin, aqueous acroleic acid resin are film forming matters, and organosilicon is high poly-
Thing is heat-resist with Si-O keys as main chain；There are the excellent properties of many protrusions after epoxy resin is cured, it is such as special to various materials
It is not very strong to the adhesion of metal, has very strong chemical resistance, mechanical strength are very high, electrical insulating property is good, corrosion-resistant etc..
Additionally, epoxy resin can solidify within the scope of comparatively wide temperature, and volume contraction is small during solidification, bisphenol type epoxy tree
Fat is condensed in the basic conditions by bisphenol-A, epoxychloropropane, through washing, the macromolecular compound that desolventizing is refined；Water
Property acrylic resin include emulsion acrylic resin, aqueous acrylic resin dispersion and acrylic resin aqueous solution, it is and traditional
Solvent based coating is compared, and water paint has that price is low, use safety；Oxidized starch be starch in acid, alkali, neutral medium with
Oxidant is acted on, and a kind of converted starch obtained from starch oxidation, oxidized starch is reduced starch gelatinization temperature, heat paste viscosity
Diminish and heat endurance increase, product colour is pure white, paste transparent, good film-forming property, freeze-thaw resistance is good, is the increasing of low viscosity high concentration
Thick dose；Oxidized starch, organic phospho acid, zinc oxide, Boratex, sepiolite, borax synergy can effectively slow down at high temperature
Hardening time is applied, there is high temperature deferred action to coating solution；And oxidized starch, organic phospho acid, zinc oxide, Boratex, sea
Afrodite, borax asepsis environment-protecting, high temperature resistant property are good；It is good that silica sand has the performances such as the small, high-insulation of high temperature resistant, thermal coefficient of expansion
Good high-temperature stabilizer；The chemical state of dimethyl siloxane is dimethicone, colourless or light yellow liquid, tasteless, transparency
Height, varies with temperature small, water proofing property, surface tension small with heat resistance, cold resistance, viscosity；Calcium carbonate is used to strengthen paint film
Intensity, organic phospho acid is prevented from calcium carbonate sedimentation；Propandiol butyl ether is coalescents, promotes film forming of the present invention.The present invention is adopted
With a large amount of components with resistance to elevated temperatures, at high temperature, the performance of each component will not change, and coating has good
Heat resistance, also, the maximum problem that coating faces at high temperature is exactly fast paint solidification, and viscosity is low, poor fluidity, is formed
Film thickness it is big, fragility is high, and the service life of coating is low；Therefore, present invention employs by oxidized starch, organic phospho acid, oxygen
Change zinc, Boratex, sepiolite, the high temperature retarder of borax composition, the hardening time of coating can be postponed, improve dividing for coating
Divergence, it is to avoid coating at high temperature rapid curing and film forming is uneven.
The described water paint with high temperature resistant property, also including following components：Tristerin, defoamer, profit
Humectant, thickener, mould inhibitor, propyl trimethoxy silicane.Tristerin, dimethyl silicone polymer, defoamer, wetting
Agent, thickener, mould inhibitor cooperate, and increase dispersiveness of the invention, stability and resistance to going mouldy property；Propyl trimethoxy silicane
Increase the caking property of the present invention and coated article；Each material cooperates so that of the invention with good heat-resisting quantity and suitable
Viscosity, coating has good hardness, toughness.
The described water paint with high temperature resistant property, also including following components：Pearl essence, titanium dioxide, kaolin.Pearl
The nonhazardous of light powder, high temperature resistant, light shine, acid and alkali-resistance, not spontaneous combustion, it is not combustion-supporting, non-conductive, do not migrate, suitable color can be obtained
Light；The deflocculation of titanium dioxide, anti-decolourization are good；Kaolin is in pure white fine and smooth, soft earthy, with good plasticity
With the physics and chemistry such as fire resistance.
The described water paint with high temperature resistant property, including following parts by weight component：60-80 parts of water, 80-90
Part epoxy modified silicone resin, 40-50 parts of bisphenol A epoxide resin, 10-15 parts of aqueous acroleic acid resin, 30-40 parts of oxidation are formed sediment
Powder, 10-15 part organic phospho acid, 5-10 parts of zinc oxide, 1-5 parts of Boratex, 1-3 parts of sepiolite, 1-3 parts of borax, 10-15 parts of silicon
Sand, 10-15 part dimethyl silicone polymer, 5-8 parts of calcium carbonate, 5-10 parts of propandiol butyl ether.The present invention is based on existing aqueous painting
The consumption of material, Binding experiment result and production cost, have selected the amount of the excellent each component of coating property；Invention increases resistance to
The amount of the good component of high-temperature behavior, increased the component of raising coating resistance to elevated temperatures, but not influence the combination property of coating,
Coating film strength, stability and corrosion resistance etc. can be improved on the contrary.
The described water paint with high temperature resistant property, including following parts by weight component：70 parts of water, 90 parts of epoxies
Modified organic silicone resin, 40 parts of bisphenol A epoxide resins, 13 parts of aqueous acroleic acid resins, 35 parts of oxidized starch, 10 parts of organic phosphines
Acid, 8 parts of zinc oxide, 3 parts of Boratexes, 2 parts of sepiolites, 1 part of borax, 13 parts of silica sands, 12 parts of dimethyl silicone polymers, 6 parts of carbonic acid
Calcium, 8 parts of propandiol butyl ethers.The preferred amount of component of the present invention.
The present invention compared with prior art, has the following advantages and advantages：
1st, water paint of the present invention with high temperature resistant property employs a large amount of components with resistance to elevated temperatures, in high temperature
Under, the performance of each component will not change, and coating has good temperature tolerance；
2nd, water paint of the present invention with high temperature resistant property is employed by oxidized starch, organic phospho acid, zinc oxide, boric acid
Sodium, sepiolite, the high temperature retarder of borax composition, can postpone the hardening time of coating, improve the decentralization of coating, it is to avoid
Coating at high temperature rapid curing and film forming is uneven；
3rd, the good combination property such as water paint stability, resistance to going mouldy property, corrosion resistance with high temperature resistant property of the present invention
And asepsis environment-protecting.
Specific embodiment
To make the object, technical solutions and advantages of the present invention become more apparent, with reference to embodiment, the present invention is made
Further to describe in detail, exemplary embodiment of the invention and its explanation are only used for explaining the present invention, are not intended as to this
The restriction of invention.
Embodiment 1
Water paint of the present invention with high temperature resistant property, including following components：
Water, epoxy modified silicone resin, bisphenol A epoxide resin, aqueous acroleic acid resin, oxidized starch, organic phospho acid,
Zinc oxide, Boratex, sepiolite, borax, silica sand, dimethyl silicone polymer, calcium carbonate, propandiol butyl ether.
Epoxy modified silicone resin, bisphenol A epoxide resin, aqueous acroleic acid resin are film forming matters, and organosilicon is high poly-
Thing is heat-resist with Si-O keys as main chain；There are the excellent properties of many protrusions after epoxy resin is cured, it is such as special to various materials
It is not very strong to the adhesion of metal, has very strong chemical resistance, mechanical strength are very high, electrical insulating property is good, corrosion-resistant etc..
Additionally, epoxy resin can solidify within the scope of comparatively wide temperature, and volume contraction is small during solidification, bisphenol type epoxy tree
Fat is condensed in the basic conditions by bisphenol-A, epoxychloropropane, through washing, the macromolecular compound that desolventizing is refined；Water
Property acrylic resin include emulsion acrylic resin, aqueous acrylic resin dispersion and acrylic resin aqueous solution, it is and traditional
Solvent based coating is compared, and water paint has that price is low, use safety；Oxidized starch be starch in acid, alkali, neutral medium with
Oxidant is acted on, and a kind of converted starch obtained from starch oxidation, oxidized starch is reduced starch gelatinization temperature, heat paste viscosity
Diminish and heat endurance increase, product colour is pure white, paste transparent, good film-forming property, freeze-thaw resistance is good, is the increasing of low viscosity high concentration
Thick dose；Oxidized starch, organic phospho acid, zinc oxide, Boratex, sepiolite, borax synergy can effectively slow down at high temperature
Hardening time is applied, there is high temperature deferred action to coating solution；And oxidized starch, organic phospho acid, zinc oxide, Boratex, sea
Afrodite, borax asepsis environment-protecting, high temperature resistant property are good；It is good that silica sand has the performances such as the small, high-insulation of high temperature resistant, thermal coefficient of expansion
Good high-temperature stabilizer；The chemical state of dimethyl siloxane is dimethicone, colourless or light yellow liquid, tasteless, transparency
Height, varies with temperature small, water proofing property, surface tension small with heat resistance, cold resistance, viscosity；Calcium carbonate is used to strengthen paint film
Intensity, organic phospho acid is prevented from calcium carbonate sedimentation；Propandiol butyl ether is coalescents, promotes film forming of the present invention.The present invention is adopted
With a large amount of components with resistance to elevated temperatures, at high temperature, the performance of each component will not change, and coating has good
Heat resistance, also, the maximum problem that coating faces at high temperature is exactly fast paint solidification, and viscosity is low, poor fluidity, is formed
Film thickness it is big, fragility is high, and the service life of coating is low；Therefore, present invention employs by oxidized starch, organic phospho acid, oxygen
Change zinc, Boratex, sepiolite, the high temperature retarder of borax composition, the hardening time of coating can be postponed, improve dividing for coating
Divergence, it is to avoid coating at high temperature rapid curing and film forming is uneven.
The described water paint with high temperature resistant property, also including following components：Tristerin, defoamer, profit
Humectant, thickener, mould inhibitor, propyl trimethoxy silicane.Tristerin, dimethyl silicone polymer, defoamer, wetting
Agent, thickener, mould inhibitor cooperate, and increase dispersiveness of the invention, stability and resistance to going mouldy property；Propyl trimethoxy silicane
Increase the caking property of the present invention and coated article；Each material cooperates so that of the invention with good heat-resisting quantity and suitable
Viscosity, coating has good hardness, toughness.
Embodiment 2
Based on embodiment 1, the described water paint with high temperature resistant property, also including following components：Pearl essence, titanium white
Powder, kaolin.Pearl essence nonhazardous, high temperature resistant, light shine, acid and alkali-resistance, not spontaneous combustion, it is not combustion-supporting, non-conductive, do not migrate, can be with
Obtain suitable coloured light；Titanium dioxide deflocculation, anti-decolourization are good；Kaolin is in pure white fine and smooth, soft earthy, with good
The physics and chemistry such as good plasticity and fire resistance.
Embodiment 3
Based on above-described embodiment, the component of the described water paint with high temperature resistant property, including following parts by weight：
60-80 parts of water, 80-90 parts of epoxy modified silicone resin, 40-50 parts of bisphenol A epoxide resin, 10-15 parts of water soluble acrylic acid tree
Ester, 30-40 part oxidized starch, 10-15 parts of organic phospho acid, 5-10 parts of zinc oxide, 1-5 parts of Boratex, 1-3 parts of sepiolite, 1-3 parts
Borax, 10-15 part silica sand, 10-15 parts of dimethyl silicone polymer, 5-8 parts of calcium carbonate, 5-10 parts of propandiol butyl ether.Base of the present invention
In the consumption of existing water paint, Binding experiment result and production cost have selected the amount of the excellent each component of coating property；
Invention increases the amount of the good component of resistance to elevated temperatures, the component for improving coating resistance to elevated temperatures is increased, but do not influence
The combination property of coating, can improve coating film strength, stability and corrosion resistance etc. on the contrary.
Embodiment 4
Based on above-described embodiment, the component of the described water paint with high temperature resistant property, including following parts by weight：
70 parts of water, 90 parts of epoxy modified silicone resins, 40 parts of bisphenol A epoxide resins, 13 parts of aqueous acroleic acid resins, 35 parts of oxidations are formed sediment
Powder, 10 parts of organic phospho acids, 8 parts of zinc oxide, 3 parts of Boratexes, 2 parts of sepiolites, 1 part of borax, 13 parts of silica sands, 12 parts of poly dimethyl silicon
Oxygen alkane, 6 parts of calcium carbonate, 8 parts of propandiol butyl ethers.The preferred amount of component of the present invention.
Above-described specific embodiment, has been carried out further to the purpose of the present invention, technical scheme and beneficial effect
Describe in detail, should be understood that and the foregoing is only specific embodiment of the invention, be not intended to limit the present invention
Protection domain, all any modification, equivalent substitution and improvements within the spirit and principles in the present invention, done etc. all should include
Within protection scope of the present invention.
Claims (5)
1. there is the water paint of high temperature resistant property, it is characterised in that including following components：Water, epoxy modified silicone resin,
Bisphenol A epoxide resin, aqueous acroleic acid resin, oxidized starch, organic phospho acid, zinc oxide, Boratex, sepiolite, borax, silicon
Sand, dimethyl silicone polymer, calcium carbonate, propandiol butyl ether.
2. the water paint with high temperature resistant property according to claim 1, it is characterised in that also including following components：
Tristerin, defoamer, wetting agent, thickener, mould inhibitor, propyl trimethoxy silicane.
3. the water paint with high temperature resistant property according to claim 2, it is characterised in that also including following components：
Pearl essence, titanium dioxide, kaolin.
4. the water paint with high temperature resistant property according to claim 1, it is characterised in that including following parts by weight
Component：60-80 parts of water, 80-90 parts of epoxy modified silicone resin, 40-50 parts of bisphenol A epoxide resin, 10-15 parts aqueous third
Olefin(e) acid resin, 30-40 part oxidized starch, 10-15 parts of organic phospho acid, 5-10 parts of zinc oxide, 1-5 parts of Boratex, 1-3 parts of Hai Pao
Stone, 1-3 part borax, 10-15 parts of silica sand, 10-15 parts of dimethyl silicone polymer, 5-8 parts of calcium carbonate, 5-10 parts of propandiol butyl ether.
5. the water paint with high temperature resistant property according to claim 4, it is characterised in that including following parts by weight
Component：70 parts of water, 90 parts of epoxy modified silicone resins, 40 parts of bisphenol A epoxide resins, 13 parts of aqueous acroleic acid resins, 35
Part oxidized starch, 10 parts of organic phospho acids, 8 parts of zinc oxide, 3 parts of Boratexes, 2 parts of sepiolites, 1 part of borax, 13 parts of silica sands, 12 parts gather
Dimethyl siloxane, 6 parts of calcium carbonate, 8 parts of propandiol butyl ethers.