CN106867269A - A kind of composite building material - Google Patents
A kind of composite building material Download PDFInfo
- Publication number
- CN106867269A CN106867269A CN201510925017.2A CN201510925017A CN106867269A CN 106867269 A CN106867269 A CN 106867269A CN 201510925017 A CN201510925017 A CN 201510925017A CN 106867269 A CN106867269 A CN 106867269A
- Authority
- CN
- China
- Prior art keywords
- parts
- building material
- reed
- composite building
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of composite building material, is made up of the raw material of following portions by weight：Reed 40-60 parts, calcium carbonate 20-30 parts, polyvinyl chloride 10-20 parts, stabilizer 5-10 parts.The preparation method of the composite building material, comprises the following steps：(1) reed is beaten；(2) other raw materials are crushed；(3) each raw material is mixed, is heated to 120 DEG C, be cooled to 25 DEG C, poured into mould and go out building materials.It is an advantage of the invention that：By the use of reed as building material, twice laid, energy saving.
Description
Technical field
The present invention relates to building material technical field, especially a kind of composite building material.
Background technology
Composite building material is the conventional construction material of building field.It is easy to use, low cost.Usual composite is made of wood chip,
The application a large amount of timber of consumption of wood chip, are unfavorable for environmental protection.
The current environmental pollution of China is serious, and trees are particularly important for purify air, country's also strict control, forbids arbitrarily felling.
Therefore need to find a kind of material that can substitute wood chip.For the production of composite.
The content of the invention
To realize above-mentioned goal of the invention, the implementation method that the present invention takes is as follows：
A kind of composite building material, is made up of the raw material of following portions by weight：Reed 40-60 parts, calcium carbonate 20-30 parts, polychlorostyrene second
Alkene 10-20 parts, stabilizer 5-10 parts.
Further, it is made up of the raw material of following portions by weight：50 parts of reed, 25 parts of calcium carbonate, 15 parts of polyvinyl chloride, stabilization
8 parts of agent.
The preparation method of composite building material, comprises the following steps：
(1) reed is beaten；
(2) other raw materials are crushed；
(3) each raw material is mixed, is heated to 120 DEG C, be cooled to 25 DEG C, poured into mould and go out building materials.
It is an advantage of the invention that：By the use of reed as building material, twice laid, energy saving.
Specific embodiment
With reference to embodiments, to the specific embodiment according to present invention offer, details are as follows：
Embodiment 1
A kind of composite building material, is made up of the raw material of following portions by weight：40 parts of reed, 30 parts of calcium carbonate, 10 parts of polyvinyl chloride,
10 parts of stabilizer.
The preparation method of composite building material, comprises the following steps：
(1) reed is beaten；
(2) other raw materials are crushed；
(3) each raw material is mixed, is heated to 120 DEG C, be cooled to 25 DEG C, poured into mould and go out building materials.
Embodiment 2
A kind of composite building material, is made up of the raw material of following portions by weight：50 parts of reed, 25 parts of calcium carbonate, 15 parts of polyvinyl chloride,
8 parts of stabilizer.
The preparation method of composite building material, comprises the following steps：
(1) reed is beaten；
(2) other raw materials are crushed；
(3) each raw material is mixed, is heated to 120 DEG C, be cooled to 25 DEG C, poured into mould and go out building materials.
Claims (3)
1. a kind of composite building material, it is characterised in that be made up of the raw material of following portions by weight：Reed 40-60 parts, calcium carbonate 20-30
Part, polyvinyl chloride 10-20 parts, stabilizer 5-10 parts.
2. a kind of composite building material according to claim 1, it is characterised in that be made up of the raw material of following portions by weight：Reed
50 parts, 25 parts of calcium carbonate, 15 parts of polyvinyl chloride, 8 parts of stabilizer.
3. the preparation method of composite building material described in a kind of claim 1, it is characterised in that comprise the following steps：
(1) reed is beaten；
(2) other raw materials are crushed；
(3) each raw material is mixed, is heated to 120 DEG C, be cooled to 25 DEG C, poured into mould and go out building materials.