CN106867141A - It is integrally formed blowing clothes PP Pipe Compound and the preparation method of the clothes - Google Patents
It is integrally formed blowing clothes PP Pipe Compound and the preparation method of the clothes Download PDFInfo
- Publication number
- CN106867141A CN106867141A CN201710067057.7A CN201710067057A CN106867141A CN 106867141 A CN106867141 A CN 106867141A CN 201710067057 A CN201710067057 A CN 201710067057A CN 106867141 A CN106867141 A CN 106867141A
- Authority
- CN
- China
- Prior art keywords
- clothes
- integrally formed
- pipe compound
- weight portions
- parison
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Blowing clothes PP Pipe Compound and the manufacture craft of the clothes are integrally formed the present invention relates to a kind of, the raw material components for being integrally formed blowing clothes PP Pipe Compound include thermoplastic resin, DOP, DBP, DOS, epoxidized soybean oil, tribasic lead sulfate, barium stearate and are suitably matched, so that the PP Pipe Compound can be applied to blow molding process, realize the disposal molding of clothes especially raincoat, rain cape, and the clothes such as the raincoat or rain cape of making are integrally formed using blow molding process, water resistance is good；It is cost-effective without cutting and suturing, it is to avoid the waste of raw material in manufacturing process, and the mechanical module of technique can be realized, it is ensured that the stability of clothing product quality.
Description
Technical field
The invention belongs to Garment Technology field, and in particular to one kind is integrally formed blowing clothes PP Pipe Compound and the clothes
Preparation method.
Background technology
Clothes (including raincoat or rain cape) in the market, are all to cut out sewing method using piece, and idiographic flow is：Face
Material is first decomposed by organization of human body and plane template is obtained, then it is cut-parts to be cut into fabric by plane template, finally passes through cut-parts
The modes such as sewing, heat seam are made into the clothes (including raincoat or rain cape) of required style.However, above-mentioned use piece cuts out sewing method
Obtained clothes (comprising raincoat or rain cape), water resistance is simultaneously bad, and suture of the rainwater easily between cut-parts and cut-parts oozes
Enter, drench underwear and body；Additionally, sheet above has a large amount of former materials during cutting out sewing method, production fabric, cutting fabric
The loss of material, wastes serious, and all manual operationss, inefficiency, high cost.
The content of the invention
In order to solve the above mentioned problem of prior art presence, blowing clothes PP Pipe Compound is integrally formed the invention provides one kind
And the preparation method of the clothes；Using blow molding process, with the PP Pipe Compound as raw material, raincoat or rain cape of making etc. are integrally formed
Clothes, water resistance is good；It is cost-effective without cutting and suturing, it is to avoid the waste of raw material in manufacturing process, and can realize
The mechanical module of technique, it is ensured that the stability of quality of finished.
The technical solution adopted in the present invention is：
Blowing clothes PP Pipe Compound is integrally formed, raw material components include：
Thermoplastic resin 50-75 weight portions, DOP (o-phthalic acid dibutyl ester) 10-30 weight portions, DBP (phthalic acids
Dibutylester) 3-10 weight portions, DOS (dioctyl sebacate) 1-10 weight portions, epoxidized soybean oil 1-10 weight portions, three alkali formula sulfuric acid
Lead 0.8-1.5 weight portions, barium stearate 0.8-1.5 weight portions.
The thermoplastic resin is PVC (polyvinyl chloride), PA (polyamide), PBT (polybutylene terephthalate (PBT)), PC
(makrolon), PE (polyethylene), PET (polyethylene terephthalate), PMMA (polymethyl methacrylate), POM are (poly-
Formaldehyde), PP (polypropylene), one or more mixtures constituted with arbitrary proportion in PS (polystyrene).
Being integrally formed described in further preferably also adds 0.1-4 weight portions in being blow molded the raw material components of clothes PP Pipe Compound
Filler, described filler is one or more mixtures constituted with arbitrary proportion in stabilizer, smoothing preparation, anti-wear agent, pigment.
The stabilizer is organic tin stabilizer, and the smoothing preparation is paraffin, and the anti-wear agent is calcium carbonate.
Being integrally formed described in further preferably also adds 0.1-30 weight portions in being blow molded the raw material components of clothes PP Pipe Compound
Fiber powder.
The fiber powder is constituted for one or more in wood fiber powder, bamboo fibre powder, flaxen fiber powder with arbitrary proportion
Mixture, selects the fiber of different attribute, adjusts the proportioning of fiber, adjustable to allot different functional clothing fabrics, such as rain-proof,
The functions such as windproof, moisture absorbing and sweat releasing, antistatic, sun-proof antiultraviolet.
The wood fiber powder, bamboo fibre powder, the particle diameter of flaxen fiber powder are 100-200 mesh.
A kind of method of the shaping blowing clothes that are made into one based on the PP Pipe Compound, is comprised the following steps：
(1) each raw material components are weighed and be sufficiently mixed uniformly, obtain final product the PP Pipe Compound；
(2) PP Pipe Compound is carried out into heating melting, obtains melted material；
(3) step (2) described melted material is made tubular parison, the tubular parison is first heated and softened, then will be soft
Parison after change is placed in the blow mold of clothes to be processed and seals；
(4) parison in the blow mold is carried out into inflation using compressed air, until the parison after inflation is close to mould
Tool inwall, through cooling and demolding, obtains final product and described is integrally formed blowing clothes.
In step (2), the temperature for carrying out the heating melting is 195-298 DEG C；It should be noted that：The heating melting
Temperature depend on using each raw material average condensing temperature point (Tf), i.e., it is described heating melting temperature be slightly larger than Tf.
In step (3), the extruded shaping of tubular parison or injection moulding are obtained；The temperature for being heated and softened is
172-255℃；It should be noted that：The temperature of the heating and softening is depended on using the average condensing temperature point (Tf) of each raw material
With average softening temperature point (Tg), i.e., the temperature of described heating and softening is located between Tg and Tf, is slightly less than Tf.
Thickness after the preform blowup is 0.06-1.2mm.
Beneficial effects of the present invention are：
It is of the present invention be integrally formed blowing clothes PP Pipe Compound, raw material components include thermoplastic resin, DOP, DBP,
DOS, epoxidized soybean oil, tribasic lead sulfate, barium stearate are simultaneously suitably matched, so that the PP Pipe Compound can be applicable
In blow molding process, the disposal molding of clothes especially raincoat, rain cape is realized, and making is integrally formed using blow molding process
Raincoat or the clothes such as rain cape, water resistance is good；In manufacturing process, without cutting and suturing, it is to avoid the waste of raw material, save
Cost, and the mechanical module of technique can be realized, it is ensured that the stability of clothing product quality.
Specific embodiment
To make the object, technical solutions and advantages of the present invention clearer, technical scheme will be carried out below
Detailed description.Obviously, described embodiment is only a part of embodiment of the utility model, rather than whole implementation
Example.Based on the embodiment in the present invention, those of ordinary skill in the art are resulting on the premise of creative work is not made
All other implementation method, belong to the scope protected of the present invention.
1g is represented with 1 weight portion in example below.
Embodiment 1
The present embodiment provides one kind and is integrally formed blowing clothes PP Pipe Compound, and raw material components include：
Thermoplastic resin PVC is 50 weight portions, DOP is 30 weight portions, DBP is 3 weight portions, DOS is 10 weight portions, epoxy
The weight portion of soybean oil 1, the weight portion of tribasic lead sulfate 1.5, the weight portion of barium stearate 0.8.
A kind of method of the shaping blowing clothes that are made into one based on the PP Pipe Compound, is comprised the following steps：
(1) each raw material components are weighed according to above-mentioned weight and be sufficiently mixed uniformly, obtain final product the PP Pipe Compound；
(2) PP Pipe Compound is carried out into heating melting at 200 DEG C, obtains melted material；
(3) the extruded shaping of step (2) described melted material or injection moulding are made tubular parison, by the tubular-type
Base is first in 190 DEG C of heating and softenings, then the parison after softening is placed in into sealing in the blow mold of clothes to be processed；
(4) parison in the blow mold is carried out into inflation using compressed air, until the parison after inflation is close to mould
Tool inwall, thickness after the preform blowup is 0.06mm, through cooling and demolding, obtains final product and described is integrally formed blowing clothes.
Embodiment 2
The present embodiment provides one kind and is integrally formed blowing clothes PP Pipe Compound, and raw material components include：
Thermoplastics PA 6 is 75 weight portions, DOP is 10 weight portions, DBP is 10 weight portions, DOS is 1 weight portion, epoxy
The weight portion of soybean oil 10, the weight portion of tribasic lead sulfate 0.8, the weight portion of barium stearate 1.5, the weight of organic tin stabilizer 0.025
Part, the weight portion of paraffin 0.1, the weight portion of calcium carbonate 0.025, the weight portion of pigment 0.1.
A kind of method of the shaping blowing clothes that are made into one based on the PP Pipe Compound, is comprised the following steps：
(1) each raw material components are weighed according to above-mentioned weight and be sufficiently mixed uniformly, obtain final product the PP Pipe Compound；
(2) PP Pipe Compound is carried out into heating melting at 250 DEG C, obtains melted material；
(3) the extruded shaping of step (2) described melted material or injection moulding are made tubular parison, by the tubular-type
Base is first in 215 DEG C of heating and softenings, then the parison after softening is placed in into sealing in the blow mold of clothes to be processed；
(4) parison in the blow mold is carried out into inflation using compressed air, until the parison after inflation is close to mould
Tool inwall, thickness after the preform blowup is 1.2mm, through cooling and demolding, obtains final product and described is integrally formed blowing clothes.
Embodiment 3
The present embodiment provides one kind and is integrally formed blowing clothes PP Pipe Compound, and raw material components include：
Thermoplastic resin PBT60 weight portions, DOP20 weight portions, DBP6 weight portions, DOS6 weight portions, the weight of epoxidized soybean oil 6
Amount part, the weight portion of tribasic lead sulfate 1.2, the weight portion of barium stearate 1.2, the weight portion of organic tin stabilizer 0.075, paraffin
0.075 weight portion, the weight portion of calcium carbonate 0.075, the weight portion of pigment 0.075, the weight portion of wood fiber powder 15 that particle diameter is 150 mesh.
A kind of method of the shaping blowing clothes that are made into one based on the PP Pipe Compound, is comprised the following steps：
(1) each raw material components are weighed according to above-mentioned weight and be sufficiently mixed uniformly, obtain final product the PP Pipe Compound；
(2) PP Pipe Compound is carried out into heating melting at 283 DEG C, obtains melted material；
(3) the extruded shaping of step (2) described melted material or injection moulding are made tubular parison, by the tubular-type
Base is first in 251 DEG C of heating and softenings, then the parison after softening is placed in into sealing in the blow mold of clothes to be processed；
(4) parison in the blow mold is carried out into inflation using compressed air, until the parison after inflation is close to mould
Tool inwall, thickness after the preform blowup is 0.09mm, through cooling and demolding, obtains final product and described is integrally formed blowing clothes.
Embodiment 4
The present embodiment provides one kind and is integrally formed blowing clothes PP Pipe Compound, and raw material components include：
Thermoplastic resin PC65 weight portions, DOP20 weight portions, DBP8 weight portions, DOS7.5 weight portions, epoxidized soybean oil
7.5 weight portions, the weight portion of tribasic lead sulfate 1.2, the weight portion of barium stearate 1.2, the weight portion of organic tin stabilizer 0.06, paraffin
0.06 weight portion, the weight portion of calcium carbonate 0.06, the weight portion of pigment 0.06, particle diameter are the wood fiber powder of 150 mesh, bamboo fibre powder, fiber crops
Fiber powder is according to mass ratio 1:1:The weight portion of mixture 20 of 1 composition.
A kind of method of the shaping blowing clothes that are made into one based on the PP Pipe Compound, is comprised the following steps：
(1) each raw material components are weighed according to above-mentioned weight and be sufficiently mixed uniformly, obtain final product the PP Pipe Compound；
(2) PP Pipe Compound is carried out into heating melting at 298 DEG C, obtains melted material；
(3) the extruded shaping of step (2) described melted material or injection moulding are made tubular parison, by the tubular-type
Base is first in 255 DEG C of heating and softenings, then the parison after softening is placed in into sealing in the blow mold of clothes to be processed；
(4) parison in the blow mold is carried out into inflation using compressed air, until the parison after inflation is close to mould
Tool inwall, thickness after the preform blowup is 1.1mm, through cooling and demolding, obtains final product and described is integrally formed blowing clothes.
Embodiment 5
The present embodiment provides one kind and is integrally formed blowing clothes PP Pipe Compound, and raw material components include：
Thermoplastic resin PE and PET is according to mass ratio 1:The weight portion of mixture 65 of 1 composition, DOP20 weight portions, DBP8 weights
Amount part, DOS6 weight portions, the weight portion of epoxidized soybean oil 6, the weight portion of tribasic lead sulfate 1.2, the weight portion of barium stearate 1.0, have
The weight portion of machine tin stabilizer 0.05, the weight portion of paraffin 0.05, the weight portion of calcium carbonate 0.05, the weight portion of pigment 0.05, particle diameter are 150
Purpose wood fiber powder, bamboo fibre powder, flaxen fiber powder are according to mass ratio 1:1:The weight portion of mixture 15 of 1 composition.
A kind of method of the shaping blowing clothes that are made into one based on the PP Pipe Compound, is comprised the following steps：
(1) each raw material components are weighed according to above-mentioned weight and be sufficiently mixed uniformly, obtain final product the PP Pipe Compound；
(2) PP Pipe Compound is carried out into heating melting at 265 DEG C, obtains melted material；
(3) the extruded shaping of step (2) described melted material or injection moulding are made tubular parison, by the tubular-type
Base is first in 252 DEG C of heating and softenings, then the parison after softening is placed in into sealing in the blow mold of clothes to be processed；
(4) parison in the blow mold is carried out into inflation using compressed air, until the parison after inflation is close to mould
Tool inwall, thickness after the preform blowup is 0.08mm, through cooling and demolding, obtains final product and described is integrally formed blowing clothes.
Embodiment 6
The present embodiment provides one kind and is integrally formed blowing clothes PP Pipe Compound, and raw material components include：
Thermoplastic resin PMMA and POM is according to mass ratio 1:1 composition the weight portion of mixture 60, DOP20 weight portions,
DBP3-10 weight portions, DOS8 weight portions, the weight portion of epoxidized soybean oil 8, the weight portion of tribasic lead sulfate 1.2, barium stearate 1.2
Weight portion, the weight portion of organic tin stabilizer 0.05, the weight portion of paraffin 0.05, the weight portion of calcium carbonate 0.05, the weight portion of pigment 0.05,
Particle diameter is the wood fiber powder of 150 mesh, bamboo fibre powder, flaxen fiber powder according to mass ratio 1:1:The weight portion of mixture 18 of 1 composition.
A kind of method of the shaping blowing clothes that are made into one based on the PP Pipe Compound, is comprised the following steps：
(1) each raw material components are weighed according to above-mentioned weight and be sufficiently mixed uniformly, obtain final product the PP Pipe Compound；
(2) PP Pipe Compound is carried out into heating melting at 228 DEG C, obtains melted material；
(3) the extruded shaping of step (2) described melted material or injection moulding are made tubular parison, by the tubular-type
Base is first in 196 DEG C of heating and softenings, then the parison after softening is placed in into sealing in the blow mold of clothes to be processed；
(4) parison in the blow mold is carried out into inflation using compressed air, until the parison after inflation is close to mould
Tool inwall, thickness after the preform blowup is 1.0mm, through cooling and demolding, obtains final product and described is integrally formed blowing clothes.
Embodiment 7
The present embodiment provides one kind and is integrally formed blowing clothes PP Pipe Compound, and raw material components include：
Thermoplastic resin PP and PS is according to mass ratio 1:The weight portion of mixture 60 of 1 composition, DOP20 weight portions, DBP8 weights
Amount part, DOS6 weight portions, the weight portion of epoxidized soybean oil 6, the weight portion of tribasic lead sulfate 1.2, the weight portion of barium stearate 1.2, have
The weight portion of machine tin stabilizer 0.05, the weight portion of paraffin 0.05, the weight portion of calcium carbonate 0.05, the weight portion of pigment 0.05, particle diameter are 150
The weight portion of purpose bamboo fibre powder 18.
A kind of method of the shaping blowing clothes that are made into one based on the PP Pipe Compound, is comprised the following steps：
(1) each raw material components are weighed according to above-mentioned weight and be sufficiently mixed uniformly, obtain final product the PP Pipe Compound；
(2) PP Pipe Compound is carried out into heating melting at 195 DEG C, obtains melted material；
(3) the extruded shaping of step (2) described melted material or injection moulding are made tubular parison, by the tubular-type
Base is first in 172 DEG C of heating and softenings, then the parison after softening is placed in into sealing in the blow mold of clothes to be processed；
(4) parison in the blow mold is carried out into inflation using compressed air, until the parison after inflation is close to mould
Tool inwall, thickness after the preform blowup is 1.1mm, through cooling and demolding, obtains final product and described is integrally formed blowing clothes.
Appurtenances such as decoration, bag, cap etc. on clothes, can be obtained using Shooting Technique, will be molded shape again afterwards
Into appurtenances directly install additional or be heat sealed to it is described be integrally formed on blowing clothes, complete the making of whole clothing.
The above, specific embodiment only of the invention, but protection scope of the present invention is not limited thereto, and it is any
Those familiar with the art the invention discloses technical scope in, change or replacement can be readily occurred in, should all contain
Cover within protection scope of the present invention.Therefore, protection scope of the present invention should be based on the protection scope of the described claims.
Claims (10)
1. blowing clothes PP Pipe Compound is integrally formed, it is characterised in that raw material components include：
Thermoplastic resin 50-75 weight portions, DOP10-30 weight portions, DBP3-10 weight portions, DOS1-10 weight portions, epoxy soybean
Oily 1-10 weight portions, tribasic lead sulfate 0.8-1.5 weight portions, barium stearate 0.8-1.5 weight portions.
2. it is according to claim 1 to be integrally formed blowing clothes PP Pipe Compound, it is characterised in that the thermoplastic resin is
One or more mixtures constituted with arbitrary proportion in PVC, PA, PBT, PC, PE, PET, PMMA, POM, PP, PS.
3. it is according to claim 1 to be integrally formed blowing clothes PP Pipe Compound, it is characterised in that also to be added in raw material components
The filler of 0.1-4 weight portions, described filler is one or more in stabilizer, smoothing preparation, anti-wear agent, pigment with arbitrary proportion
The mixture of composition.
4. it is according to claim 3 to be integrally formed blowing clothes PP Pipe Compound, it is characterised in that the stabilizer is organotin
Stabilizer, the smoothing preparation is paraffin, and the anti-wear agent is calcium carbonate.
It is 5. according to claim 1 to be integrally formed blowing clothes PP Pipe Compound, it is characterised in that
The fiber powder of 0.1-30 weight portions is also added in raw material components.
6. it is according to claim 5 to be integrally formed blowing clothes PP Pipe Compound, it is characterised in that the fiber powder is wood-fibred
One or more mixtures constituted with arbitrary proportion in powder, bamboo fibre powder, flaxen fiber powder.
7. it is according to claim 6 to be integrally formed blowing clothes PP Pipe Compound, it is characterised in that the wood fiber powder, bamboo are fine
Dimension powder, the particle diameter of flaxen fiber powder are 100-200 mesh.
8. a kind of method of the shaping blowing clothes that are made into one based on PP Pipe Compound described in claim any one of 1-7, its feature exists
In comprising the following steps：
(1) each raw material components are weighed and be sufficiently mixed uniformly, obtain final product the PP Pipe Compound；
(2) PP Pipe Compound is carried out into heating melting, obtains melted material；
(3) step (2) described melted material is made tubular parison, the tubular parison is first heated and softened, then by after softening
Parison be placed in the blow mold of clothes to be processed seal；
(4) parison in the blow mold is carried out into inflation using compressed air, until the parison after inflation is close in mould
Wall, through cooling and demolding, obtains final product and described is integrally formed blowing clothes.
9. it is according to claim 8 to be integrally formed the preparation method for being blow molded clothes, it is characterised in that in step (2), to carry out
The temperature of the heating melting is 195-298 DEG C.
10. it is according to claim 8 to be integrally formed the preparation method for being blow molded clothes, it is characterised in that in step (3), institute
State the extruded shaping of tubular parison or injection moulding is obtained；The temperature for being heated and softened is 172-255 DEG C.
Thickness after the preform blowup is 0.06-1.2mm.