CN106867113A - A kind of computer mouse composite and preparation method thereof - Google Patents
A kind of computer mouse composite and preparation method thereof Download PDFInfo
- Publication number
- CN106867113A CN106867113A CN201710205613.2A CN201710205613A CN106867113A CN 106867113 A CN106867113 A CN 106867113A CN 201710205613 A CN201710205613 A CN 201710205613A CN 106867113 A CN106867113 A CN 106867113A
- Authority
- CN
- China
- Prior art keywords
- parts
- computer mouse
- toughener
- mouse composite
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of computer mouse composite, belong to computer field of material technology, including following weight portion raw material：20 50 parts of acrylic resin, 10 35 parts of polycarbonate, 5 28 parts of epoxy resin, 48 parts of carbon fiber, 2.5 5 parts of EP rubbers, 5 10 parts of toughener, 4 12 parts of fire retardant；0.2 0.5 parts of toner, 23 parts of carbon black, 12 20 parts of lubricant, 48 parts of toughener, 37 parts of plasticizer, 12 parts of coupling agent, 45 parts of Tissuemat E, 45 parts of ethanol, 26 parts of fluorescent material, the invention also discloses a kind of preparation method of computer mouse composite；The present invention has preferably combination property, and with preferably smoothness and brightness.
Description
Technical field
The present invention relates to computer technology field, and in particular to a kind of computer mouse composite and preparation method thereof.
Background technology
Computer is a kind of modern electronic computer device for supercomputing, can carry out numerical computations, can be carried out again
Logical calculated, also with store-memory function.It is that can be run according to program, the automatic, modernization of high speed processing mass data
Intelligent electronic device.It is made up of hardware system and software systems, is fitted without the computer referred to as bare machine of any software.Can divide
It is supercomputer, industrial control computer, network computer, personal computer, the class of embedded computer five, more advanced meter
Calculation machine has biocomputer, photonic computer, quantum computer etc..
Mouse is a kind of input equipment of computer, is also the indicator of calculator display organization coordinate setting in length and breadth, because
Likeness in form mouse and gain the name " mouse ", during due to using mouse, mouse need it is often mobile, hand to the friction of mouse, touch compared with
Many, so the requirement very high of the performance need of the material to making mouse, this is also the problem urgently studied and improve at present.
The content of the invention
It is an object of the invention to overcome above-mentioned the deficiencies in the prior art, there is provided a kind of computer mouse composite,
Raw material including following weight portion：Acrylic resin 20-50 parts, polycarbonate 10-35 parts, epoxy resin 5-28 parts, carbon fiber
4-8 parts, EP rubbers 2.5-5 parts, toughener 5-10 parts, fire retardant 4-12 parts, toner 0.2-0.5 parts, carbon black 2-3 parts, lubrication
Agent 12-20 parts, toughener 4-8 parts, plasticizer 3-7 parts, coupling agent 1-2 parts, Tissuemat E 4-5 parts, ethanol 4-5 parts, fluorescent material
2-6 parts.
Preferably, fire retardant is microencapsulated powder oil fire retardant.
Preferably, lubricant is tristerin, butyl stearate, oleamide, one kind of ethylene bis stearamide
Or it is various.
Preferably, toughener is styrene butadiene thermoplasticelastomer SBS, haloflex CPE and ethene-vinegar
One or more of vinyl acetate copolymer EVA.
Preferably, plasticizer is ditridecyl phthalate and dioctyl phthalate, both mass ratioes are 1:1.
Preferably, coupling agent is epoxy silane class coupling agent.
Present invention also offers a kind of preparation method of computer mouse composite, comprise the following steps：
First, various raw materials are weighed according to above-mentioned weight portion respectively；
2nd, acrylic resin, polycarbonate, epoxy resin, carbon fiber, EP rubbers, Tissuemat E are put into reactor and are melted
Melt, control temperature for 130-150 DEG C, time 2-3min obtains melt；
3rd, remaining clout is continuously added in the reactor in step 2, is warming up to 160-170 DEG C, at the uniform velocity stir 5-10min,
Obtain mixture；
4th, will be extruded in the mixture input double screw extruder in step 3, barrel temperature is 190-200 DEG C；
5th, cooled down after injection moulding.
Wherein,
Step 2 mixing speed is 600-700r/min.
The computer mouse composite that the present invention is provided has good performance, due to the addition of a certain proportion of poly- third
Olefine resin, polycarbonate, epoxy resin, carbon fiber, EP rubbers, add a certain proportion of additive so that computer mouse
There is preferably tensile strength, bending strength and impact strength with composite；Due to the addition of fire retardant, fire retardant is micro- glue
Encapsulated red phosphorus combustion inhibitor so that this composite has preferably fire resistance, and environment-protecting asepsis；A certain proportion of lubricant
With the addition of Tissuemat E so that this composite has preferably smoothness, make hand hold mouse feel it is preferable；Ethanol
Addition can tart up, and the addition of fluorescent material can improve the brightness of mouse composite, be easy to find mouse in night.
A kind of preparation method of counter body composite that the present invention is provided is simple to operate, makes the electricity for preparing
Brain mouse is with composite quality is good, good stability.
Specific embodiment
Invention is described in further detail below in conjunction with specific embodiment.
Embodiment 1
A kind of computer mouse composite of the present embodiment, including following weight portion raw material：20 parts of acrylic resin, poly- carbon
10 parts of sour fat, 5 parts of epoxy resin, 4 parts of carbon fiber, 2.5 parts of EP rubbers, 5 parts of toughener, 4 parts of fire retardant, 0.2 part of toner, charcoal
Black 2 parts, 12 parts of lubricant, 4 parts of toughener, 3 parts of plasticizer, 1 part of coupling agent, 4 parts of Tissuemat E, 4 parts of ethanol, 2 parts of fluorescent material.
Wherein,
Fire retardant is microencapsulated powder oil fire retardant.
Lubricant is tristerin.
Toughener is styrene butadiene thermoplasticelastomer SBS.
Plasticizer is ditridecyl phthalate and dioctyl phthalate, and both mass ratioes are 1:1.
Coupling agent is epoxy silane class coupling agent.
A kind of preparation method of computer mouse composite of the present embodiment, comprises the following steps：
First, various raw materials are weighed according to above-mentioned weight portion respectively；
2nd, acrylic resin, polycarbonate, epoxy resin, carbon fiber, EP rubbers, Tissuemat E are put into reactor and are melted
Melt, control temperature for 130 DEG C, time 2min obtains melt；
3rd, remaining clout is continuously added in the reactor in step 2, is warming up to 160 DEG C, at the uniform velocity stir 5min, mixed
Thing；
4th, will be extruded in the mixture input double screw extruder in step 3, barrel temperature is 190 DEG C；
5th, cooled down after injection moulding.
Wherein,
Step 2 mixing speed is 600r/min.
Embodiment 2
A kind of computer mouse composite of the present embodiment, including following weight portion raw material：35 parts of acrylic resin, poly- carbon
20 parts of sour fat, 18 parts of epoxy resin, 6 parts of carbon fiber, 4 parts of EP rubbers, 8 parts of toughener, 8 parts of fire retardant, 0.4 part of toner, charcoal
Black 2.5 parts, it is 16 parts of lubricant, 6 parts of toughener, 5 parts of plasticizer, 1.5 parts of coupling agent, 4.5 parts of Tissuemat E, 4.5 parts of ethanol, glimmering
4 parts of light powder.
Wherein,
Fire retardant is microencapsulated powder oil fire retardant.
Lubricant is tristerin and butyl stearate, and both ratios are 2:1.
Toughener is haloflex CPE and ethylene-vinyl acetate copolymer EVA, and both ratios are 1:1.
Plasticizer is ditridecyl phthalate and dioctyl phthalate, and both mass ratioes are 1:1.
Coupling agent is epoxy silane class coupling agent.
A kind of preparation method of computer mouse composite of the present embodiment, comprises the following steps：
First, various raw materials are weighed according to above-mentioned weight portion respectively；
2nd, acrylic resin, polycarbonate, epoxy resin, carbon fiber, EP rubbers, Tissuemat E are put into reactor and are melted
Melt, control temperature for 140 DEG C, time 2.5min obtains melt；
3rd, remaining clout is continuously added in the reactor in step 2, is warming up to 165 DEG C, at the uniform velocity stir 8min, mixed
Thing；
4th, will be extruded in the mixture input double screw extruder in step 3, barrel temperature is 195 DEG C；
5th, cooled down after injection moulding.
Wherein,
Step 2 mixing speed is 650r/min.
Embodiment 3
A kind of computer mouse composite of the present embodiment, including following weight portion raw material：50 parts of acrylic resin, poly- carbon
35 parts of sour fat, 28 parts of epoxy resin, 8 parts of carbon fiber, 5 parts of EP rubbers, 10 parts of toughener, 12 parts of fire retardant, 0.5 part of toner,
3 parts of carbon black, 20 parts of lubricant, 8 parts of toughener, 7 parts of plasticizer, 2 parts of coupling agent, 5 parts of Tissuemat E, 5 parts of ethanol, fluorescent material 6
Part.
Wherein,
Fire retardant is microencapsulated powder oil fire retardant.
Lubricant is tristerin and butyl stearate, and both ratios are 2:1.
Toughener is common for styrene butadiene thermoplasticelastomer SBS, haloflex CPE and ethylene-vinyl acetate
One or more of polymers EVA.
Plasticizer is ditridecyl phthalate and dioctyl phthalate, and both mass ratioes are 1:1.
Coupling agent is epoxy silane class coupling agent.
A kind of preparation method of computer mouse composite of the present embodiment, comprises the following steps：
First, various raw materials are weighed according to above-mentioned weight portion respectively；
2nd, acrylic resin, polycarbonate, epoxy resin, carbon fiber, EP rubbers, Tissuemat E are put into reactor and are melted
Melt, control temperature for 150 DEG C, time 3min obtains melt；
3rd, remaining clout is continuously added in the reactor in step 2, is warming up to 170 DEG C, at the uniform velocity stir 10min, mixed
Compound；
4th, will be extruded in the mixture input double screw extruder in step 3, barrel temperature is 200 DEG C；
5th, cooled down after injection moulding.
Wherein,
Step 2 mixing speed is 700r/min.
According to related performance test methods, the performance test results of embodiment 1-3 and ABS reference examples are as follows：
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Reference examples（ABS） | |
| Tensile strength/MPa | 78.7 | 79.3 | 80.4 | 62 |
| Bending modulus/MPa | 4289.8 | 4312.3 | 4312.8 | 2500 |
| Bending strength/MPa | 121 | 119 | 124 | 100 |
| 79.4 | 80.1 | 79.8 | 60 | |
| 62.2 | 59.4 | 60.4 | 20 | |
| Heat distortion temperature/DEG C | 160.4 | 162.4 | 162.2 | 90 |
| Anti-flammability/level | V-0 | V-0 | V-0 | V-0 |
| 1.14 | 1.13 | 1.13 | 1.14 | |
| Surface roughness/μm | 0.19 | 0.17 | 0.12 | 0.36 |
It follows that the computer mouse in embodiment 1-3 has preferably combination property with composite, surface has preferably
Smoothness.
The above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical schemes belonged under thinking of the present invention belong to protection scope of the present invention.It should be pointed out that for the art
Those of ordinary skill for, some improvements and modifications without departing from the principles of the present invention, these improvements and modifications
Should be regarded as protection scope of the present invention.
Claims (8)
1. a kind of computer mouse composite, it is characterised in that：Raw material including following weight portion：Acrylic resin 20-50
Part, polycarbonate 10-35 parts, epoxy resin 5-28 parts, carbon fiber 4-8 parts, EP rubbers 2.5-5 parts, toughener 5-10 parts, resistance
4-12 parts of agent of combustion, toner 0.2-0.5 parts, carbon black 2-3 parts, lubricant 12-20 parts, toughener 4-8 parts, plasticizer 3-7 parts, coupling
Agent 1-2 parts, Tissuemat E 4-5 parts, ethanol 4-5 parts, fluorescent material 2-6 parts.
2. computer mouse composite according to claim 1, it is characterised in that：Fire retardant hinders for microencapsulated powder oil
Combustion agent.
3. computer mouse composite according to claim 1, it is characterised in that：Lubricant be tristerin,
Butyl stearate, oleamide, one or more of ethylene bis stearamide.
4. computer mouse composite according to claim 1, it is characterised in that：Toughener is styrene-butadiene
One or more of thermoplastic elastomer SBS, haloflex CPE and ethylene-vinyl acetate copolymer EVA.
5. computer mouse composite according to claim 1, it is characterised in that：Plasticizer is ditridecyl phthalate
And dioctyl phthalate, both mass ratioes are 1:1.
6. computer mouse composite according to claim 1, it is characterised in that：Coupling agent is coupled for epoxy silane class
Agent.
7. the preparation method of the computer mouse composite described in a kind of claim 1 ~ 6 any one, it is characterised in that：Bag
Include following steps：
First, various raw materials are weighed according to above-mentioned weight portion respectively；
2nd, acrylic resin, polycarbonate, epoxy resin, carbon fiber, EP rubbers, Tissuemat E are put into reactor and are melted
Melt, control temperature for 130-150 DEG C, time 2-3min obtains melt；
3rd, remaining clout is continuously added in the reactor in step 2, is warming up to 160-170 DEG C, at the uniform velocity stir 5-10min,
Obtain mixture；
4th, will be extruded in the mixture input double screw extruder in step 3, barrel temperature is 190-200 DEG C；
5th, cooled down after injection moulding.
8. the preparation method of building materials water-repellent paint according to claim 7, it is characterised in that：Step 2 mixing speed is
600-700r/min。