CN106854418A - A kind of emulsified paint and preparation method - Google Patents
A kind of emulsified paint and preparation method Download PDFInfo
- Publication number
- CN106854418A CN106854418A CN201611179042.1A CN201611179042A CN106854418A CN 106854418 A CN106854418 A CN 106854418A CN 201611179042 A CN201611179042 A CN 201611179042A CN 106854418 A CN106854418 A CN 106854418A
- Authority
- CN
- China
- Prior art keywords
- parts
- red
- intermediate blend
- aerosil
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of emulsified paint and preparation method, it is made up of following mass fraction formula components：40~45 parts of bisphenol A type epoxy resin breast, 35~40 parts of nanometer rutile, 10~15 parts of ether formaldehyde condensation products, 10~15 parts of phenol formaldehyde condensate, 10~15 parts of sulfonate sodium, 5~8 parts of iron oxide red, red 5~8 parts of key, soft black 5~8 parts, 3~5 parts of dispersant, 3~5 parts of defoamer, 3~5 parts of anti-flash rusting agent, 3~5 parts of thickener, 1~3 part of boron-moisten soil, 1~3 part of aerosil, 1~3 part of polyether modified silicon oil, 5~10 parts of water, coating of the invention and metal tool is well bonded.
Description
Technical field
The present invention relates to technical field of chemical paint, in particular to a kind of emulsified paint and preparation method.
Background technology
Seamless steel pipe easy oxidation and rusting in its natural state, there is many influences on its outward appearance and quality, particularly seamless
Steel pipe is many times contributed in the equipment and pipeline of HTHP, and the corrosion on surface has very big to the compressive resistance of its own
Influence, has phosphatization, passivation, application etc. to the preservative treatment of seamless steel pipe, and wherein application account for very big ratio.At present, big portion
Divide all carries out application using solvent based coating, and solvent organic solvent of the plough coating containing someone's amount is polluted, to operation to environment
The healthy of workman has serious influence, and well and product go out when saying has environmental issue, causes the product return of goods or fine etc. to be lost
Stay problem.At present, because environmental issue, part producer has been forced to reduce out to be said order or not to go out a day product, part is seamless steel
The water-based anticorrosive paint that pipe manufacturer have to use import instead is produced..
The content of the invention
Regarding to the issue above, the invention provides a kind of emulsified paint and preparation method.
To achieve the above object, the present invention provides following technical scheme：
A kind of emulsified paint, is made up of following mass fraction formula components：
40~45 parts of bisphenol A type epoxy resin breast, 35~40 parts of nanometer rutile, 10~15 parts of ether formaldehyde condensation products, phenol
10~15 parts of formaldehyde condensation products, 10~15 parts of sulfonate sodium, 5~8 parts of iron oxide red, red 5~8 parts of key, soft black 5~8 parts, dispersant 3
~5 parts, 3~5 parts of defoamer, 3~5 parts of anti-flash rusting agent, 3~5 parts of thickener, 1~3 part of boron-moisten soil, aerosil 1~3
Part, 1~3 part of polyether modified silicon oil, 5~10 parts of water.
Further, it is made up of following mass fraction formula components：
40 parts of bisphenol A type epoxy resin breast, 35 parts of nanometer rutile, 10 parts of ether formaldehyde condensation products, phenol formaldehyde condensate 10
Part, 10 parts of sulfonate sodium, 5 parts of iron oxide red, red 5 parts of key, soft black 5 parts, 3 parts of dispersant, 3 parts of defoamer, 3 parts of anti-flash rusting agent, thickening
3 parts of agent, 1 part of boron-moisten soil, 1 part of aerosil, 1 part of polyether modified silicon oil, 5 parts of water.
Further, it is made up of following mass fraction formula components：
45 parts of bisphenol A type epoxy resin breast, 40 parts of nanometer rutile, 15 parts of ether formaldehyde condensation products, phenol formaldehyde condensate 15
Part, 15 parts of sulfonate sodium, 8 parts of iron oxide red, red 8 parts of key, soft black 8 parts, 5 parts of dispersant, 5 parts of defoamer, 5 parts of anti-flash rusting agent, thickening
5 parts of agent, 3 parts of boron-moisten soil, 3 parts of aerosil, 3 parts of polyether modified silicon oil, 10 parts of water.
Further, it is made up of following mass fraction formula components：
43 parts of bisphenol A type epoxy resin breast, 37 parts of nanometer rutile, 12 parts of ether formaldehyde condensation products, phenol formaldehyde condensate 13
Part, 11 parts of sulfonate sodium, 7 parts of iron oxide red, red 7 parts of key, soft black 6 parts, 4 parts of dispersant, 4 parts of defoamer, 4 parts of anti-flash rusting agent, thickening
4 parts of agent, 2 parts of boron-moisten soil, 2 parts of aerosil, 2 parts of polyether modified silicon oil, 8 parts of water.
Further：Preparation method of the present invention has following steps：
Step one：Heated more than 24 hours after bisphenol A type epoxy resin breast and nanometer rutile are mixed, for drying,
Then continuation is heated until thawing, is subsequently adding ether formaldehyde condensation products, phenol formaldehyde condensate and sulfonic acid in putting it into reactor
Sodium salt is sufficiently stirred for, and is made intermediate blend 1；
Step 2：By iron oxide red, key be red, during soft black drop adds intermediate blend 1, and constantly heating, heating-up temperature is 100~
120 DEG C, heating 1 hour is kept after being added dropwise to complete, be made intermediate blend 2；
Step 3：By dispersant, defoamer, anti-flash rusting agent, thickener, boron-moisten soil, aerosil, polyether-modified silicon
Oil is stirred continuously in sequentially adding intermediate blend 2, and mixing time is 1~1.2 hour, is made intermediate blend 3；
Step 4：Add water in intermediate blend 3, adjust concentration, be made intermediate blend 4.
Step 5：Intermediate blend 4 is tested, is filtered and packaging operation, be made finished product.
The beneficial effects of the invention are as follows：
1st, coating of the invention and metal tool are well bonded；
2nd, coating high temperature resistant of the invention, low temperature.
3rd, coating hydrophobicity of the invention is good.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment one：
A kind of emulsified paint, is made up of following mass fraction formula components：40~45 parts of bisphenol A type epoxy resin breast, receive
Rice 35~40 parts of rutile, 10~15 parts of ether formaldehyde condensation products, 10~15 parts of phenol formaldehyde condensate, 10~15 parts of sulfonate sodium,
Red 5~8 parts of 5~8 parts of iron oxide red, key, soft black 5~8 parts, 3~5 parts of dispersant, 3~5 parts of defoamer, 3~5 parts of anti-flash rusting agent, increase
Thick dose 3~5 parts, 1~3 part of boron-moisten soil, 1~3 part of aerosil, 1~3 part of polyether modified silicon oil, 5~10 parts of water.
Embodiment two：
A kind of emulsified paint, is made up of following mass fraction formula components：Bisphenol A type epoxy resin breast 40 parts, nm of gold
35 parts of red stone, 10 parts of ether formaldehyde condensation products, 10 parts of phenol formaldehyde condensate, 10 parts of sulfonate sodium, 5 parts of iron oxide red, red 5 parts of key, soft black 5
Part, 3 parts of dispersant, 3 parts of defoamer, 3 parts of anti-flash rusting agent, 3 parts of thickener, 1 part of boron-moisten soil, 1 part of aerosil, polyethers change
1 part of silicone oil of property, 5 parts of water.
Embodiment three：
A kind of emulsified paint, is made up of following mass fraction formula components：Bisphenol A type epoxy resin breast 45 parts, nm of gold
40 parts of red stone, 15 parts of ether formaldehyde condensation products, 15 parts of phenol formaldehyde condensate, 15 parts of sulfonate sodium, 8 parts of iron oxide red, red 8 parts of key, soft black 8
Part, 5 parts of dispersant, 5 parts of defoamer, 5 parts of anti-flash rusting agent, 5 parts of thickener, 3 parts of boron-moisten soil, 3 parts of aerosil, polyethers change
3 parts of silicone oil of property, 10 parts of water.
Example IV：
A kind of emulsified paint, is made up of following mass fraction formula components：Bisphenol A type epoxy resin breast 43 parts, nm of gold
37 parts of red stone, 12 parts of ether formaldehyde condensation products, 13 parts of phenol formaldehyde condensate, 11 parts of sulfonate sodium, 7 parts of iron oxide red, red 7 parts of key, soft black 6
Part, 4 parts of dispersant, 4 parts of defoamer, 4 parts of anti-flash rusting agent, 4 parts of thickener, 2 parts of boron-moisten soil, 2 parts of aerosil, polyethers change
2 parts of silicone oil of property, 8 parts of water.
Embodiment five：
A kind of emulsified paint its preparation method comprises the following steps：
Step one：Heated more than 24 hours after bisphenol A type epoxy resin breast and nanometer rutile are mixed, for drying,
Then continuation is heated until thawing, is subsequently adding ether formaldehyde condensation products, phenol formaldehyde condensate and sulfonic acid in putting it into reactor
Sodium salt is sufficiently stirred for, and is made intermediate blend 1；
Step 2：By iron oxide red, key be red, during soft black drop adds intermediate blend 1, and constantly heating, heating-up temperature is 100~
120 DEG C, heating 1 hour is kept after being added dropwise to complete, be made intermediate blend 2；
Step 3：By dispersant, defoamer, anti-flash rusting agent, thickener, boron-moisten soil, aerosil, polyether-modified silicon
Oil is stirred continuously in sequentially adding intermediate blend 2, and mixing time is 1~1.2 hour, is made intermediate blend 3；
Step 4：Add water in intermediate blend 3, adjust concentration, be made intermediate blend 4.
Step 5：Intermediate blend 4 is tested, is filtered and packaging operation, be made finished product.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each implementation method is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity, those skilled in the art should
Specification an as entirety, the technical scheme in each embodiment can also be formed into those skilled in the art through appropriately combined
May be appreciated other embodiment.
Claims (5)
1. a kind of emulsified paint, it is characterised in that：It is made up of following mass fraction formula components：
40~45 parts of bisphenol A type epoxy resin breast, 35~40 parts of nanometer rutile, 10~15 parts of ether formaldehyde condensation products, phenol formaldehyde
10~15 parts of condensation product, 10~15 parts of sulfonate sodium, 5~8 parts of iron oxide red, red 5~8 parts of key, soft black 5~8 parts, dispersant 3~5
Part, 3~5 parts of defoamer, 3~5 parts of anti-flash rusting agent, 3~5 parts of thickener, 1~3 part of boron-moisten soil, 1~3 part of aerosil,
1~3 part of polyether modified silicon oil, 5~10 parts of water.
2. a kind of emulsified paint according to claim 1, it is characterised in that：It is made up of following mass fraction formula components：
40 parts of bisphenol A type epoxy resin breast, 35 parts of nanometer rutile, 10 parts of ether formaldehyde condensation products, 10 parts of phenol formaldehyde condensate, sulphur
10 parts of acid sodium-salt, 5 parts of iron oxide red, red 5 parts of key, soft black 5 parts, 3 parts of dispersant, 3 parts of defoamer, 3 parts of anti-flash rusting agent, 3 parts of thickener,
1 part of boron-moisten soil, 1 part of aerosil, 1 part of polyether modified silicon oil, 5 parts of water.
3. a kind of emulsified paint according to claim 1, it is characterised in that：It is made up of following mass fraction formula components：
45 parts of bisphenol A type epoxy resin breast, 40 parts of nanometer rutile, 15 parts of ether formaldehyde condensation products, 15 parts of phenol formaldehyde condensate, sulphur
15 parts of acid sodium-salt, 8 parts of iron oxide red, red 8 parts of key, soft black 8 parts, 5 parts of dispersant, 5 parts of defoamer, 5 parts of anti-flash rusting agent, 5 parts of thickener,
3 parts of boron-moisten soil, 3 parts of aerosil, 3 parts of polyether modified silicon oil, 10 parts of water.
4. a kind of emulsified paint according to claim 1, it is characterised in that：It is made up of following mass fraction formula components：
43 parts of bisphenol A type epoxy resin breast, 37 parts of nanometer rutile, 12 parts of ether formaldehyde condensation products, 13 parts of phenol formaldehyde condensate, sulphur
11 parts of acid sodium-salt, 7 parts of iron oxide red, red 7 parts of key, soft black 6 parts, 4 parts of dispersant, 4 parts of defoamer, 4 parts of anti-flash rusting agent, 4 parts of thickener,
2 parts of boron-moisten soil, 2 parts of aerosil, 2 parts of polyether modified silicon oil, 8 parts of water.
5. the preparation method of a kind of emulsified paint according to claim 1, it is characterised in that：Comprise the following steps：
Step one：Heating more than 24 hours after bisphenol A type epoxy resin breast and nanometer rutile are mixed, for drying, then
Continuation is heated until thawing, is subsequently adding ether formaldehyde condensation products, phenol formaldehyde condensate and sulfonate sodium in putting it into reactor
It is sufficiently stirred for, is made intermediate blend 1；
Step 2：By iron oxide red, key be red, during soft black drop adds intermediate blend 1, and constantly heat, heating-up temperature is 100~120
DEG C, heating 1 hour is kept after being added dropwise to complete, it is made intermediate blend 2；
Step 3：By dispersant, defoamer, anti-flash rusting agent, thickener, boron-moisten soil, aerosil, polyether modified silicon oil according to
It is stirred continuously in secondary addition intermediate blend 2, mixing time is 1~1.2 hour, is made intermediate blend 3；
Step 4：Add water in intermediate blend 3, adjust concentration, be made intermediate blend 4.
Step 5：Intermediate blend 4 is tested, is filtered and packaging operation, be made finished product.