CN106835687A - A kind of method for preparing polycarbonate conductive material of aluminizing - Google Patents
A kind of method for preparing polycarbonate conductive material of aluminizing Download PDFInfo
- Publication number
- CN106835687A CN106835687A CN201710067403.1A CN201710067403A CN106835687A CN 106835687 A CN106835687 A CN 106835687A CN 201710067403 A CN201710067403 A CN 201710067403A CN 106835687 A CN106835687 A CN 106835687A
- Authority
- CN
- China
- Prior art keywords
- polycarbonate
- conductive material
- ito
- sensitized treatment
- aluminizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of method for preparing polycarbonate conductive material of aluminizing, it is characterised in that comprise the following steps:(1)Polycarbonate is washed(2)ITO colloidal sols soak(3)Sensitized treatment(4)Washing;The present invention introduces ITO sol layers, the binding strength for introducing the compatibility that on the one hand can solve the problem that between metal simple-substance and fibre-forming polymer, lifting silver layer and fiber of ITO layer between aluminium lamination and polycarbonate;On the other hand, the introducing of this layer is realized and builds ITO Al composite constructions in fiber surface, is remarkably improved the electric conductivity of Conductive Silver-Coated PET Fibers using the structure while reducing thickness of coating.In addition, sensitized treatment, so that fiber surface has the relatively low slaine of SnCl2 and PdCl2 activity, preferable environment is provided with for sequential reduction aluminium using being carried out in the mixed solution of SnCl2 and PdCl2.
Description
Technical field
The present invention relates to conductive material field, more particularly to a kind of side for preparing polycarbonate conductive material of aluminizing
Method.
Background technology
Composite polymer conductive material, by general macromolecular material and various conductive materials by filled composite,
The mode such as surface recombination or lamination be compound and be obtained.Principal item has conductive plastics, conductive rubber, conductive fibers, conduction
Coating, conductive adhesive and transparent conductive film etc..
Conductive fiber prepared by the market, is embedded in fibrous material by the material using high conductivity such as silver-colored monomers,
Make it have good conductive effect.But due to higher using silver-colored production cost so that the preparation cost of material rises, and does not apply to
In the growth requirement of modern industry.
The content of the invention
The technical problem to be solved in the present invention is:For above-mentioned the deficiencies in the prior art, there is provided one kind prepares poly- carbon of aluminizing
The method of acid esters fibrous conductive material.
The present invention solve its technical problem solution be:A kind of side for preparing polycarbonate conductive material of aluminizing
Method, it is characterised in that it is comprised the following steps:
(1)Polycarbonate is washed:Polycarbonate is immersed acetone, organic solvent soluble in water successively carries out ultrasound
Cleaning 10-30 minutes, is then cleaned with deionized water, is dried;
(2)ITO colloidal sols soak:Polycarbonate after treatment is soaked into 5-20min in ITO colloidal sols, through 50-60 after taking-up
Slowly dried at a temperature of DEG C;
(3)Sensitized treatment:By step(2)In polycarbonate through sensitized treatment after, be soaked on aluminum plating liquid, and be added dropwise also
Former agent, in carrying out insulation 20-60min at 40-60 DEG C;
(4)Washing:By step(3)In polycarbonate, through distilled water flushing, final products are obtained after drying.
As one of preferred technical scheme, it is characterised in that described polycarbonate is aromatic copolycarbonate
Fiber.
As one of preferred technical scheme, it is characterised in that described step(3)Sensitized treatment specific steps
For:Impregnated in mixed solution by polycarbonate using SnCl2 and PdCl2;
As one of preferred technical scheme, it is characterised in that described step(3)In reducing agent be organic reducing agent.
The beneficial effects of the invention are as follows:
(1)ITO sol layers are introduced between aluminium lamination and polycarbonate with the present invention, on the one hand the introducing of ITO layer can solve
Certainly the compatibility between metal simple-substance and fibre-forming polymer, lifts the binding strength of silver layer and fiber;On the other hand, this layer draws
Enter to realize and build ITO-Al composite constructions in fiber surface, the electric conductivity of Conductive Silver-Coated PET Fibers is remarkably improved using the structure
Thickness of coating can simultaneously be reduced.
(2)Sensitized treatment using being carried out in the mixed solution of SnCl2 and PdCl2 so that fiber surface has SnCl2
The slaine relatively low with PdCl2 activity, preferable environment is provided with for sequential reduction aluminium.
Specific embodiment
The technique effect of design of the invention, concrete thought and generation is carried out below with reference to embodiment clear, complete
Ground description, to be completely understood by the purpose of the present invention, feature and effect.Obviously, described embodiment is of the invention one
Section Example, rather than whole embodiments, based on embodiments of the invention, those skilled in the art is not paying creativeness
The other embodiment obtained on the premise of work, belongs to the scope of protection of the invention.
Embodiment:
A kind of method for preparing polycarbonate conductive material of aluminizing, it is characterised in that it is comprised the following steps:
(1)Polycarbonate is washed:Polycarbonate is immersed acetone, organic solvent soluble in water successively carries out ultrasound
Cleaning 20 minutes, is then cleaned with deionized water, is dried;
(2)ITO colloidal sols soak:Polycarbonate after treatment is soaked into 20min in ITO colloidal sols, through 50 DEG C after taking-up
At a temperature of slowly dry;
(3)Sensitized treatment:By step(2)In polycarbonate through sensitized treatment after, be soaked on aluminum plating liquid, and be added dropwise also
Former agent, in carrying out insulation 30min at 50 DEG C;
(4)Washing:By step(3)In polycarbonate, through distilled water flushing, final products are obtained after drying.
As one of preferred embodiment, it is characterised in that described polycarbonate is aromatic copolycarbonate
Fiber.
As one of preferred embodiment, it is characterised in that described step(3)Sensitized treatment specific steps
For:Impregnated in mixed solution by polycarbonate using SnCl2 and PdCl2.
As one of preferred embodiment, it is characterised in that described step(3)In reducing agent be organic reduction
Agent.
Better embodiment of the invention is illustrated above, but the invention is not limited to the implementation
Example, those of ordinary skill in the art can also make a variety of equivalent modifications or replace on the premise of without prejudice to spirit of the invention
Change, these equivalent modifications or replacement are all contained in the application claim limited range.
Claims (4)
1. a kind of method for preparing polycarbonate conductive material of aluminizing, it is characterised in that it is comprised the following steps:
(1)Polycarbonate is washed:Polycarbonate is immersed acetone, organic solvent soluble in water successively carries out ultrasound
Cleaning 10-30 minutes, is then cleaned with deionized water, is dried;
(2)ITO colloidal sols soak:Polycarbonate after treatment is soaked into 5-20min in ITO colloidal sols, through 50-60 after taking-up
Slowly dried at a temperature of DEG C;
(3)Sensitized treatment:By step(2)In polycarbonate through sensitized treatment after, be soaked on aluminum plating liquid, and be added dropwise also
Former agent, in carrying out insulation 20-60min at 40-60 DEG C;
(4)Washing:By step(3)In polycarbonate, through distilled water flushing, final products are obtained after drying.
2. preparation according to claim 1 is aluminized the method for polycarbonate conductive material, it is characterised in that described
Polycarbonate is aromatic copolycarbonate fiber.
3. preparation according to claim 1 is aluminized the method for polycarbonate conductive material, it is characterised in that described
Step(3)Sensitized treatment concretely comprise the following steps:Impregnated in mixed solution by polycarbonate using SnCl2 and PdCl2.
4. the preparation according to claim 1,2 or 3 any one claims is aluminized polycarbonate conductive material
Method, it is characterised in that described step(3)In reducing agent be organic reducing agent.