CN106835425A - Terylene harness cord thread and preparation method thereof - Google Patents
Terylene harness cord thread and preparation method thereof Download PDFInfo
- Publication number
- CN106835425A CN106835425A CN201611209762.8A CN201611209762A CN106835425A CN 106835425 A CN106835425 A CN 106835425A CN 201611209762 A CN201611209762 A CN 201611209762A CN 106835425 A CN106835425 A CN 106835425A
- Authority
- CN
- China
- Prior art keywords
- terylene
- cable
- harness cord
- cord thread
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of terylene harness cord thread, treated shaping is made after twisting into cable through Split Down as raw material with pure Polyester Yarns, and its surface dip-coating has one layer of paraffin.The preparation method of above-mentioned terylene harness cord thread, including make terylene strand, make terylene cable, be wound into terylene cylinder line and by terylene cylinder line introduce special equipment through drawing-off, soaking paste carding, again drawing-off solidification, waxdip, polish, be wound into the step process such as cylinder, skeining and be fabricated to terylene harness cord thread product.Terylene harness cord thread product quality stabilization of the invention, single-wire strong is high, and rub resistance, weather resistance is good, flexible to have obtained effective control.The preparation method production technology of terylene harness cord thread of the present invention is advanced, and slurry raffinate and waste discharge are not produced, and energy consumption is low.
Description
Technical field
The present invention relates to a kind of textile raw material, more particularly to a kind of terylene harness cord thread for making jacquard fabric or fabric
And preparation method thereof.
Background technology
The figured pattern of jacquard fabric or fabric, must rely on the fortune up and down of jacquard loom shedding mechanism in weaving process
It is dynamic to adjust the frequency that every warp thread moves up and down so that weft yarn is when shuttle is gone here and there, when and pass crosswise, when and tripping is circumvented,
Fabric or intersecting according to certain requirement through weft yarn for fabric surface is set to produce regular density and concavo-convex figured pattern.Harness cord
It is the jacquard loom shedding mechanism control indispensable material of movement of the warp.
Traditional harness cord is generally with ramie, polyvinyl etc. for raw material makes.Ramie valency is high, and ramie harness cord must also used before
HTHP adds the stifling arrangement of beeswax, and work loaded down with trivial details complexity, is the noble in harness cord, and general user dare not make inquiries easily;
Although polyvinyl harness cord can be used directly, but it is afraid of dry, especially be afraid of wet, fearness temperature Change, and single-wire strong is low, not wear-resisting, easily disconnected
Split, often produce irregular elongating or shortening to cause cracked ends, directly affect the quality and yield of textile fabrics.Further, since dimension
Synthetic fibre can produce a large amount of wastewater and waste materials in process of production, and power consumption is high, tends to superseded, and its resource is gradually reduced.Polyvinyl resource subtracts
Major general causes the shortage of harness cord raw material, the development of influence jacquard fabric or fabric.
The content of the invention
The purpose of the present invention, is to solve the above mentioned problem that prior art is present, there is provided one kind is with pure Polyester Yarns as raw material
Terylene harness cord thread of making and preparation method thereof.
The object of the present invention is achieved like this:A kind of terylene harness cord thread, is twisted into as raw material with pure Polyester Yarns through Split Down
Treated shaping is made after cable, and its surface dip-coating has one layer of paraffin.
Described pure Polyester Yarns includes the pure Polyester Yarns of 15 spy~53 spies.
The preparation method of above-mentioned terylene harness cord thread, comprises the following steps:
A, making terylene strand
Terylene strand is obtained through twisting after the pure Polyester Yarns of 15 spy~53 spies is merged with 2 strands~6 strands;
B, making terylene cable
Terylene cable is obtained through retwist after terylene strand obtained in step A is merged with 2~6 strands again;
C, be wound into terylene cylinder line
By terylene cable wrap obtained in step B into terylene cylinder line;
D, by step C gained terylene cylinder line introduce special equipment be fabricated to terylene harness cord thread product through steps of processing:
D1, drawing-off
Terylene cable is set to obtain first drawing-off through the roller traction on special equipment on step C gained terylene cylinder lines;
D2, soaking paste carding
The terylene cable after first drawing-off will be obtained and import dip tank, soaked 8~15 seconds by special slurries, comb is passed through after going out groove
Hair device carries out carding and removes impurity to the terylene cable for being impregnated with slurries, makes terylene cable surface bright and clean;
D3, again drawing-off solidification
Terylene cable after soaking paste carding is imported in special baking oven, terylene cable is led for the second time after being heated to soften
Stretch and allow slurries to solidify rapidly, consolidate terylene cable elongation;
D4, waxdip
Will drawing-off again solidify after terylene cable import in special wax pan, make terylene cable in the paraffin of fusing immersion 5~
10 seconds;
D5, polishing
After terylene cable after waxdip is removed into unnecessary wax liquor, terylene harness cord thread is polished to;
D6, it is wound into cylinder
Terylene harness cord thread after polishing is wound into cylinder;
D7, skeining
The terylene harness cord thread of cylinder will be wound into skeining shape is wound in skeining equipment according to required length, obtain terylene harness cord thread product
Product.
The twist of terylene strand obtained in step A is 200~850 twists/m.
The twist of terylene cable obtained in step B is 100~425 twists/m.
The elongation of the first drawing-off described in step D1 is controlled in 8%-12%.
Special slurries described in step D2 are by the epoxy resin of 35%-40% weight, the propylene of 35%-40% weight
Sour fat, the water of the algae starch, the curing agent of 5%-10% weight and 4%-6% weight of 10%-15% weight are formulated.
Described curing agent is selected from phenol aldehyde modified amine or low molecular polyamides.
The temperature control in baking oven described in step D3 at 60~220 DEG C, the elongation control of the terylene cable after solidification
Within 0.4 ‰, the rate of sizing of the terylene cable after solidification is controlled 6~11% system.
Waxing rate after terylene cable waxdip described in step D4 is controlled 7~19%.
The present invention makes it compared with prior art as a result of above technical scheme, has the following advantages that and feature:
1st, production technology is advanced, using special equipment drawing-off, soaking paste carding, again drawing-off solidification, waxdip, polish, be wound into cylinder, machine
Tool at the uniform velocity, tension force it is always consistent, be heat-treated in addition it is qualitative make product quality stabilization, change in the past craft sizing, wax
The heavy labors such as light, vary with each individual cause product quality difference and product quality it is unstable the problems such as.
2nd, the slurry produced using suitable terylene harness cord thread, it is grout curing after, the terylene harness cord thread weatherability has been obtained greatly
The enhancing of amplitude, resistance to drying, humidity, chance is wet indeformable, flexible to have obtained effective control.
3rd, the indices of harness cord thread texture material are better than polyvinyl, and especially single-wire strong is high, abrasion-resistant, weather resistance
Good, its raw material relatively enriches and moderate, and its price is not over Matong silk after being made terylene harness cord thread.
4th, traditional harness cord production, is all realized, therefore produce substantial amounts of slurry raffinate in process of production by making by hand
And waste discharge, environment is polluted, energy consumption is also high, and the present invention uses special equipment, and slurry raffinate and waste discharge, energy are not produced
Consumption is low, is energy-saving novel environment friendly product.
Specific embodiment
Terylene harness cord thread of the present invention, is that treated shaping makes after twisting into cable through Split Down as raw material with pure Polyester Yarns
, its surface dip-coating has one layer of paraffin.
The preparation method that terylene harness cord thread of the present invention is illustrated below by several embodiments.
Embodiment 1
Twisted after being merged with the white yarn of 5 capital stocks with 1 strand of dyed yarn with the pure Polyester Yarns of 20 spies, control the twist for 700 twists/m, be obtained and wash
Synthetic fibre strand;Above-mentioned terylene strand is merged with 5 strands is again twisted, control the twist for 300 twists/m, folder flower terylene cable is obtained.Then
Above-mentioned terylene cable is wound into a line on winding apparatus, special equipment is introduced, makes to wash through the roller traction on special equipment
Synthetic fibre cable is drawn and is extended (it is 10% or so to control its elongation) for the first time, and terylene cable then is imported into dip tank,
The slurries being tailored during by dip tank (by 37 kg ethylene resins, 37 kilograms of acrylates, 13 kilograms of algae starched by the slurries
Powder, 8 kilograms of phenol aldehyde modified amine and 5 kg of water are formulated) immersion 8~15 seconds is covered, unnecessary slurries are removed when going out dip tank, then
Carding to the terylene cable for being impregnated with slurries is carried out by carding device and impurity is removed, makes terylene cable surface bright and clean.Then will
Terylene cable after soaking paste carding is imported in special baking oven, controls the temperature in baking oven for 60~220 DEG C, is made in importing baking oven
Terylene cable be softened after obtain second drawing-off and allow slurries to solidify rapidly, reach product qualitatively purpose, consolidate terylene
Cable elongation, the elongation of the terylene cable after solidification is controlled within 0.4 ‰.The rate of sizing of the terylene cable after solidification is
6~11%.Then the terylene cable after solidification is imported in special wax pan, it is soaked 5~10 seconds in the paraffin of fusing
Clock, makes one layer of paraffin of terylene cable surface dip-coating (the waxing rate of the terylene cable after waxdip is controlled 7~19%).Then will leaching
Terylene cable after wax removes unnecessary wax liquor and is sufficiently polished, it is polished after terylene cable just turn into smooth clean bright
It is wear-resisting to resist flexible terylene harness cord thread.The terylene harness cord thread after polishing is finally wound into cylinder, according to length needed for customer order
Skeining shape is wound in skeining equipment, a kind of terylene harness cord thread product of the invention is become, is available for enlacement packaging to dispatch from the factory.
Embodiment 2
Basic step is same as Example 1, unlike, its terylene cable is first with the pure Polyester Yarns of 30 spies with 2 strands of dyed yarns and 2
The white yarn of capital stock is twisted after merging, and controls the twist for 600 twists/m, and terylene strand is obtained;Again by above-mentioned terylene strand with 6 bursts of merging
Twisting, controls the twist for 400 twists/m, and folder flower terylene cable is obtained.Slurries in dip tank are by 38 kg ethylene resins, 36 public affairs
Jin acrylate, 10 kilograms of algae starches, 10 kilograms of low molecular polyamides and 6 kg of water are formulated.
Embodiment 3
Basic step is same as Example 1, unlike, its terylene cable is first with the pure Polyester Yarns of 40 spies with 3 strands of dyed yarns and 2
The white yarn of capital stock is twisted after merging, and controls the twist for 500 twists/m, and terylene strand is obtained;Again by above-mentioned terylene strand with 4 bursts of merging
Twisting, controls the twist for 200 twists/m, and folder flower terylene cable is obtained.Slurries in dip tank are by 35 kg ethylene resins, 40 public affairs
Jin acrylate, 15 kilograms of algae starches, 6 kilograms of phenol aldehyde modified amine and 4 kg of water are formulated.
Embodiment 4
Basic step is same as Example 1, unlike, its terylene cable is first with the pure Polyester Yarns of 50 spies with 1 strand of dyed yarn and 2
The white yarn of capital stock is twisted after merging, and controls the twist for 400 twists/m, and terylene strand is obtained;Again by above-mentioned terylene strand with 3 bursts of merging
Twisting, controls the twist for 150 twists/m, and folder flower terylene cable is obtained.Slurries in dip tank are by 40 kg ethylene resins, 35 public affairs
Jin acrylate, 12 kilograms of algae starches, 7 kilograms of low molecular polyamides and 6 kg of water are formulated.
Embodiment 5
Basic step is same as Example 1, unlike, its terylene cable is 2 bursts of merging of pure terylene raw white yarn first with 53 spies
After twist, control the twist for 300 twists/m, terylene strand is obtained;Above-mentioned terylene strand is merged with 2 strands is again twisted, control the twist
It is 100 twists/m, white polyester cable is obtained.Slurries in dip tank are by 36 kg ethylene resins, 38 kilograms of acrylates, 14
Kilogram algae starch, 8 kilograms of phenol aldehyde modified amine and 4 kg of water are formulated.
Claims (10)
1. a kind of terylene harness cord thread, it is characterised in that:After twisting into cable through Split Down as raw material with pure Polyester Yarns it is treated into
Type is made, and its surface dip-coating has one layer of paraffin.
2. terylene harness cord thread as claimed in claim 1, it is characterised in that:Described pure Polyester Yarns includes that 15 spy~53 spies' is pure
Polyester Yarns.
3. the preparation method of terylene harness cord thread as claimed in claim 1, it is characterised in that:Comprise the following steps:A, making are washed
Synthetic fibre strand is obtained terylene strand after the pure Polyester Yarns of 15 spy~53 spies is merged with 2 strands~6 strands through twisting;B, making terylene cable
Line is obtained terylene cable after terylene strand obtained in step A is merged with 2~6 strands again through retwist;C, be wound into terylene cylinder line
By terylene cable wrap obtained in step B into terylene cylinder line;D, by step C gained terylene cylinder line introduce special equipment through following
Step process is fabricated to terylene harness cord thread product:Step C gained terylene cylinder lines are drawn in D1, drawing-off through the roller on special equipment
Terylene cable is set to obtain first drawing-off;D2, soaking paste carding will obtain the terylene cable after first drawing-off and import dip tank, by spy
The slurries of system soak 8~15 seconds, carry out carding to the terylene cable for being impregnated with slurries and remove impurity by carding device after going out groove,
Make terylene cable surface bright and clean;D3, again drawing-off solidification import in special baking oven the terylene cable after soaking paste carding, make terylene
Cable obtains second drawing-off and allows slurries to solidify rapidly after being heated to soften, consolidate terylene cable elongation;D4:Waxdip will
The terylene cable after drawing-off solidification is imported in special wax pan again, terylene cable is soaked 5~10 seconds in the paraffin of fusing;
D5:Polish after the terylene cable after waxdip is removed into unnecessary wax liquor, be polished to terylene harness cord thread; D6:Being wound into cylinder will
Terylene harness cord thread after polishing is wound into cylinder;D7:The terylene harness cord thread that skeining will be wound into cylinder sets according to required length in skeining
Standby upper winding skeining shape, obtains terylene harness cord thread product.
4. the preparation method of terylene harness cord thread as claimed in claim 3, it is characterised in that:Terylene strand obtained in step A
The twist is 200~850 twists/m.
5. the preparation method of terylene harness cord thread as claimed in claim 3, it is characterised in that:Terylene cable obtained in step B
The twist is 100~425 twists/m.
6. the preparation method of terylene harness cord thread as claimed in claim 3, it is characterised in that:Leading for the first time described in step D1
The elongation stretched is controlled in 8%-12%.
7. the preparation method of terylene harness cord thread as claimed in claim 3, it is characterised in that:It is special described in step D2
Slurries are starched by the algae of the epoxy resin of 35%-40% weight, the acrylate of 35%-40% weight, 10%-15% weight
The water of powder, the curing agent of 5%-10% weight and 4%-6% weight is formulated.
8. the preparation method of terylene harness cord thread as claimed in claim 7, it is characterised in that:Described curing agent is selected from phenolic aldehyde
Modified amine or low molecular polyamides.
9. the preparation method of terylene harness cord thread as claimed in claim 3, it is characterised in that:In baking oven described in step D3
Temperature control at 60~220 DEG C, the elongation of the terylene cable after solidification is controlled within 0.4 ‰, the terylene cable after solidification
The rate of sizing of line is controlled 6~11%.
10. the preparation method of terylene harness cord thread as claimed in claim 3, it is characterised in that:Terylene cable described in step D4
Waxing rate after line waxdip is controlled 7~19%.