CN106832602A - Corrosion-and high-temp-resistant diaphragm - Google Patents
Corrosion-and high-temp-resistant diaphragm Download PDFInfo
- Publication number
- CN106832602A CN106832602A CN201710099217.6A CN201710099217A CN106832602A CN 106832602 A CN106832602 A CN 106832602A CN 201710099217 A CN201710099217 A CN 201710099217A CN 106832602 A CN106832602 A CN 106832602A
- Authority
- CN
- China
- Prior art keywords
- parts
- diaphragm
- resistant
- corrosion
- temp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses corrosion-and high-temp-resistant diaphragm, by weight by 55.8 75.8 parts of atactic copolymerized polypropene, 10 30 parts of high temperature resistant composite toughing agent, 0.1 0.3 parts of heat stabilizer, 28 parts of nucleator, 0.5 1.5 parts of antioxidant, 3 13 parts of compatilizer, through double screw extruder in blending and modifying at 200 240 DEG C after obtain diaphragm special raw material, diaphragm is prepared from by diaphragm special raw material.With advantages below:High temperature resistant, it is corrosion-resistant;The service life under high temperature, strong acid, basic conditions effectively is extended, use cost is reduced;There is product the performance that resistant to elevated temperatures characteristic also implies that product and has high voltage performance, product to be greatly improved.
Description
Technical field
It is specifically a kind of resistance to for the high temperature resistant in filter press the invention belongs to filter press diaphragm technical field
Corrosion diaphragm.
Background technology
With the development of solid-liquid separation technique, the field using filter press process route is constantly expanding.At present extensively
Ground is used by industries such as mine, coal, chemical industry, food, medicine, pigment, biological products, environmental protection, sewage disposals.As application is led
The expansion in domain, occurs in that some problems in the application.Under high temperature, hyperbaric environment, under strong acid, strong alkali environment, the diaphragm of filter press
Performance and service life cannot meet the use requirement of above-mentioned environment, limit its use in particular circumstances.Specifically
Problem is as follows:
1st, in the environment of high temperature (80-100 DEG C), membrane ruggedness is decreased obviously, easy fracture;
2nd, in the environment of high temperature (80-100 DEG C), the elasticity of diaphragm is recovered substantially to reduce, yielding, does not reset, and causes to lead to
Road is blocked, and forms empty room, causes filter plate to be broken;
3rd, under strong acid, strong alkali environment, diaphragm has Swelling, causes empty room, is broken filter plate;
Above mentioned problem makes current filter plate service life less than six months, increased the production cost of user.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of corrosion-and high-temp-resistant diaphragm, improve diaphragm
High temperature resistant, decay resistance, make the performance of diaphragm more uniform.
In order to solve the above technical problems, a kind of corrosion-and high-temp-resistant diaphragm that the present invention is provided, by weight will
55.8-75.8 parts of atactic copolymerized polypropene, 10-30 parts of high temperature resistant composite toughing agent, 0.1-0.3 parts of heat stabilizer, 2-8
The nucleator, 0.5-1.5 parts of antioxidant, 3-13 parts of compatilizer of part, are blended at 200-240 DEG C through double screw extruder and change
Property after obtain diaphragm special raw material, diaphragm is prepared from by diaphragm special raw material.
Atactic copolymerized polypropene has good shock resistance;Toughener can increase toughness, improve composite and resist
The auxiliary agent of impact property;Nucleator accelerates crystalline rate, increases crystal density and promote crystalline substance by changing the crystallization behavior of resin
Particle size miniaturization, reaches shortening molding cycle, improves the product transparency, lustrous surface, tensile strength, rigidity, thermal deformation temperature
The function additive of the physical and mechanical properties such as degree, impact resistance, creep resistance;Antioxidant prevents polymer aging and extends it to make
Use the life-span;Compatilizer promote incompatible polymers combine one, and then the blend stablized auxiliary agent;Ensure each material
Matter is mixed well, the performance of material is more uniformed.
Preferably, 60.8-70.8 parts of atactic copolymerized polypropene, 15-25 parts of high temperature resistant are combined by weight
Toughener, 0.15-0.25 part of heat stabilizer, 4-6 parts of nucleator, 0.75-1.25 parts of antioxidant, 6-10 parts compatible
Agent, through double screw extruder in blending and modifying at 210-240 DEG C after obtain diaphragm special raw material, diaphragm is special by diaphragm
Raw material is prepared from.
Preferably, the high temperature resistant composite toughing agent by mass fraction 5-15 parts talcum powder, 35-45 parts of white oil,
45-55 parts of hydrogenated styrene-butadiene block copolymer composition.
Preferably, the heat stabilizer is the one kind in calcium stearate, magnesium stearate, zinc stearate.
Preferably, the nucleator is the one kind in nano-calcium carbonate, talcum powder, silica.
Preferably, the antioxidant is the one kind in antioxidant 1010, antioxidant 1076, irgasfos 168.
Preferably, the compatilizer is high density polyethylene (HDPE).
After using above structure, a kind of corrosion-and high-temp-resistant diaphragm of the invention compared with prior art, with following
Advantage:High temperature resistant, it is corrosion-resistant;The service life under high temperature, strong acid, basic conditions effectively is extended, use cost is reduced;
There is product the performance that resistant to elevated temperatures characteristic also implies that product and has high voltage performance, product to be greatly improved.
Specific embodiment
The present invention is further described by the following embodiment.
Embodiment 1:
By weight by 55.8 parts of atactic copolymerized polypropene, 24 parts of high temperature resistant composite toughing agent, 0.25 part hard
Resin acid calcium, 7 parts of nano-calcium carbonate, 0.95 part of antioxidant 1010,12 parts of high density polyethylene (HDPE), exist through double screw extruder
Diaphragm special raw material is obtained at 200-240 DEG C after blending and modifying, diaphragm is prepared from by diaphragm special raw material.
The high temperature resistant composite toughing agent by 10 parts of mass fraction talcum powder, 40 parts of white oil, 50 parts of hydrogenation of benzene second
Alkene-butadiene block copolymer (SEBS) is constituted.
Survey report 1
The heat distortion temperature of diaphragm is at 94 DEG C as can be seen from the table, that is to say, that can just occur under 94 DEG C of high temperature
Deformation, diaphragm can use in high temperature environments, in high temperature environments using also implying that and can make under hyperbaric environment
With in addition, diaphragm soaks 48 hours in strong acid, strong base solution also not changing, illustrating the anti-strong acid and strong base of diaphragm.
The diaphragm high temperature resistant, high pressure resistant, corrosion-resistant that i.e. the present embodiment is provided.
Embodiment 2:
By weight by 60 parts of atactic copolymerized polypropene, 22 parts of high temperature resistant composite toughing agent, 0.25 part of tristearin
Sour magnesium, 6 parts of talcum powder, 0.95 part of antioxidant 1076,10.8 parts of high density polyethylene (HDPE), through double screw extruder in 200-
Diaphragm special raw material is obtained at 240 DEG C after blending and modifying, diaphragm is prepared from by diaphragm special raw material.
The high temperature resistant composite toughing agent by 12 parts of mass fraction talcum powder, 35 parts of white oil, 53 parts of hydrogenation of benzene second
Alkene-butadiene block copolymer (SEBS) is constituted.
Survey report 2
The heat distortion temperature of diaphragm is at 95 DEG C as can be seen from the table, that is to say, that can just occur under 95 DEG C of high temperature
Deformation, diaphragm can use in high temperature environments, in high temperature environments using also implying that and can make under hyperbaric environment
With in addition, diaphragm soaks 48 hours in strong acid, strong base solution also not changing, illustrating the anti-strong acid and strong base of diaphragm.
The diaphragm high temperature resistant, high pressure resistant, corrosion-resistant that i.e. the present embodiment is provided.
Embodiment 3:
By weight by 65.8 parts of atactic copolymerized polypropene, 20 parts of high temperature resistant composite toughing agent, 0.2 part of tristearin
Sour zinc, 5 parts of silica, 1 part of irgasfos 168,8 parts of high density polyethylene (HDPE), through double screw extruder at 200-240 DEG C
Diaphragm special raw material is obtained after lower blending and modifying, diaphragm is prepared from by diaphragm special raw material.
The high temperature resistant composite toughing agent by 10 parts of mass fraction talcum powder, 40 parts of white oil, 50 parts of hydrogenation of benzene second
Alkene-butadiene block copolymer (SEBS) is constituted.
Survey report 3
The heat distortion temperature of diaphragm is at 97 DEG C as can be seen from the table, that is to say, that can just occur under 97 DEG C of high temperature
Deformation, diaphragm can use in high temperature environments, in high temperature environments using also implying that and can make under hyperbaric environment
With in addition, diaphragm soaks 48 hours in strong acid, strong base solution also not changing, illustrating the anti-strong acid and strong base of diaphragm.
The diaphragm high temperature resistant, high pressure resistant, corrosion-resistant that i.e. the present embodiment is provided.
Embodiment 4:
By weight by 62 parts of atactic copolymerized polypropene, 30 parts of high temperature resistant composite toughing agent, 0.2 part of stearic acid
Zinc, 3 parts of silica, 1.5 parts of irgasfos 168,3.3 parts of high density polyethylene (HDPE), through double screw extruder in 200-240
Diaphragm special raw material is obtained at DEG C after blending and modifying, diaphragm is prepared from by diaphragm special raw material.
The high temperature resistant composite toughing agent by 12 parts of mass fraction talcum powder, 40 parts of white oil, 48 parts of hydrogenation of benzene second
Alkene-butadiene block copolymer (SEBS) is constituted.
Survey report 4
The heat distortion temperature of diaphragm is at 90 DEG C as can be seen from the table, that is to say, that can just occur under 90 DEG C of high temperature
Deformation, diaphragm can use in high temperature environments, in high temperature environments using also implying that and can make under hyperbaric environment
With in addition, diaphragm soaks 48 hours in strong acid, strong base solution also not changing, illustrating the anti-strong acid and strong base of diaphragm.
The diaphragm high temperature resistant, high pressure resistant, corrosion-resistant that i.e. the present embodiment is provided.
Claims (7)
1. a kind of corrosion-and high-temp-resistant diaphragm, it is characterised in that:By weight by 55.8-75.8 parts of random copolymerization poly- third
Alkene, 10-30 part of high temperature resistant composite toughing agent, 0.1-0.3 parts of heat stabilizer, 2-8 parts of nucleator, 0.5-1.5 parts anti-
Oxygen agent, 3-13 parts of compatilizer, through double screw extruder in blending and modifying at 200-240 DEG C after obtain diaphragm special raw material,
Diaphragm is prepared from by diaphragm special raw material.
2. corrosion-and high-temp-resistant diaphragm according to claim 1, it is characterised in that:By weight by 60.8-70.8
Part atactic copolymerized polypropene, 15-25 parts of high temperature resistant composite toughing agent, 0.15-0.25 parts of heat stabilizer, 4-6 parts into
Core agent, 0.75-1.25 parts of antioxidant, 6-10 parts of compatilizer, through double screw extruder in blending and modifying at 210-240 DEG C after
Diaphragm special raw material is obtained, diaphragm is prepared from by diaphragm special raw material.
3. corrosion-and high-temp-resistant diaphragm according to claim 2, it is characterised in that:The high temperature resistant composite toughing agent by
Mass fraction 5-15 parts of talcum powder, 35-45 parts of white oil, 45-55 parts of hydrogenated styrene-butadiene block copolymer group
Into.
4. corrosion-and high-temp-resistant diaphragm according to claim 2, it is characterised in that:The heat stabilizer is stearic acid
One kind in calcium, magnesium stearate, zinc stearate.
5. corrosion-and high-temp-resistant diaphragm according to claim 2, it is characterised in that:The nucleator is nano-calcium carbonate
One kind in calcium, talcum powder, silica.
6. corrosion-and high-temp-resistant diaphragm according to claim 2, it is characterised in that:The antioxidant is antioxidant
1010th, one kind in antioxidant 1076, irgasfos 168.
7. corrosion-and high-temp-resistant diaphragm according to claim 2, it is characterised in that:The compatilizer is high-density polyethylene
Alkene.