CN106830671B - Optical glass and optical element - Google Patents

Optical glass and optical element Download PDF

Info

Publication number
CN106830671B
CN106830671B CN201710156101.1A CN201710156101A CN106830671B CN 106830671 B CN106830671 B CN 106830671B CN 201710156101 A CN201710156101 A CN 201710156101A CN 106830671 B CN106830671 B CN 106830671B
Authority
CN
China
Prior art keywords
glass
optical
less
equal
optical glass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201710156101.1A
Other languages
Chinese (zh)
Other versions
CN106830671A (en
Inventor
袁伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chengdu Guangming Optoelectronics Co Ltd
Original Assignee
Chengdu Guangming Optoelectronics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chengdu Guangming Optoelectronics Co Ltd filed Critical Chengdu Guangming Optoelectronics Co Ltd
Priority to CN201910445596.9A priority Critical patent/CN110015845B/en
Priority to CN201710156101.1A priority patent/CN106830671B/en
Publication of CN106830671A publication Critical patent/CN106830671A/en
Application granted granted Critical
Publication of CN106830671B publication Critical patent/CN106830671B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention provide a kind of refractive index be 1.78~1.83, the optical glass that Abbe number is 48~53.The weight percent composition of optical glass, cation contains: Si4+: greater than 0 but be less than or equal to 15%；B3+: greater than 0 but be less than or equal to 20%, wherein Si4+/B3+It is 0.5~1；La3+: 42~58%；Gd3+: 18~33%；Y3+: 1~15%；Ta5+: greater than 0 but be less than or equal to 10%；Zr4+: 0~10%；Its anion contains O2‑And F‑, wherein F‑/O2‑For greater than 0 but less than or equal to 0.3.The present invention is designed by reasonable component, introduces suitable rare earth ion La3+、Gd3+、Y3+And a small amount of F‑, the dispersion of glass is reduced, the optical glass with high refractive low dispersive characteristic is obtained, which is suitable for the optical element of high-quality.

Description

Optical glass and optical element
Technical field
The present invention relates to a kind of optical glass, optical glass more particularly to a kind of high refractive low dispersive and by the glass The prefabricated component and optical element that glass is formed.
Background technique
The lens that high-refraction low-dispersion optical glass for mold is formed can eliminate optics with the lens combination of high-refraction high-dispersion The color difference of system, so that optical system is more compact, has better performance.Therefore, folding especially of the present invention The market demand of the glass for the high refractive low dispersive that the rate of penetrating is 1.78~1.83, Abbe number is 48~53 will increase.
For the glass of high refractive low dispersive, in the case where keeping the higher situation of refractive index, so that dispersion becomes smaller, it is above-mentioned Glass is market needs, but such " limit " glass is rare.Containing a large amount of in optical glass disclosed in CN1377847 Nb2O5, and its dispersion is still higher, is not able to satisfy the requirement now for high refractive low dispersive glass.
Summary of the invention
Technical solution to be solved by this invention is to provide that a kind of refractive index is 1.78~1.83, Abbe number is 48~53 Optical glass.
The present invention also provides a kind of prefabricated component and optical element that above-mentioned glass is formed.
The technical proposal for solving the technical problem of the invention is: optical glass, the weight percent group of cation At containing: Si4+: greater than 0 but be less than or equal to 15%；B3+: greater than 0 but be less than or equal to 20%, wherein Si4+/B3+For 0.5~ 1；La3+: 42~58%；Gd3+: 18~33%；Y3+: 1~15%；Ta5+: greater than 0 but be less than or equal to 10%；Zr4+: 0~ 10%；Its anion contains O2-And F-, wherein F-/O2-For greater than 0 but less than or equal to 0.3.
Further, also contain: Nb5+: 0~5%；Zn2++Sr2++Ba2+: 0~10%；Sb3+: 0~0.2%.
Optical glass, the weight percent composition of cation are as follows: Si4+: greater than 0 but be less than or equal to 15%；B3+: it is big In 0 but be less than or equal to 20%, wherein Si4+/B3+It is 0.5~1；La3+: 42~58%；Gd3+: 18~33%；Y3+: 1~ 15%；Ta5+: greater than 0 but be less than or equal to 10%；Zr4+: 0~10%；Nb5+: 0~5%；Zn2++Sr2++Ba2+: 0~10%； Sb3+: 0~0.2%；Its anion contains O2-And F-, wherein F-/O2-For greater than 0 but less than or equal to 0.3；Si4+/F-It is 0.3 ~1.5.
Further, in which: Si4+/F-It is 0.3~0.9；And/or (Ta5++Zr4+)/(La3++Gd3++Y3+) be greater than 0 but Less than or equal to 0.3.
Further, wherein Si4+: 1~10%；And/or B3+: 1~15%；And/or La3+: 42~55%；And/or Gd3 +: 20~31%；And/or Y3+: 2~13%；And/or Ta5+: 1~8%；And/or Zr4+: 0.5~8%.
Further, the content of the ion meet one of following 4 kinds of conditions or more than one:
1)Si4+/F-It is 0.3~0.7；
2)(Ta5++Zr4+)/(La3++Gd3++Y3+) it is 0.05~0.2；
3)Si4+/B3+It is 0.62~1；
4)F-/O2-It is 0.05~0.2.
Further, wherein Si4+: 2~9%；And/or B3+: 1~13%；And/or Zn2++Sr2++Ba2+: 0~7%； And/or Sb3+: 0~0.1%；Without containing Nb5+、W6+、Ti4+。
Further, the weight percent composition of anion contains: F-: 5~20%；O2-: 80~95%.
Further, the weight percent composition of anion contains: F-: 7~19%；O2-: 81~93%.
Further, the glass refraction is 1.78~1.83, and Abbe number is 48~53.
Gas preform is made of above-mentioned optical glass.
Optical element is made of above-mentioned optical glass.
The beneficial effects of the present invention are: designing by reasonable component, suitable rare earth ion La is introduced in optical glass3 +、Gd3+、Y3+And a small amount of F-, the dispersion of glass is reduced, obtains the optical glass with high refractive low dispersive characteristic, and should The prefabricated component that optical glass is formed, the optical glass are suitable for the optical element of high-quality.
Specific embodiment
Component contained by optical glass of the present invention will be described in detail belows, the content of each component is being not particularly illustrated In the case where, cationic components content refers to that the cation accounts for the percentage of all cationic total weights, the anionic component content Refer to that the anion accounts for the percentage of whole anion total weights.Si4+/F-Ratio refer to Si4+Account for whole cation weights hundred Divide ratio and F-Account for the ratio of whole anion weight percent.In addition, mentioning rule in the following description (except special instruction) It also include the specified value when below definite value or more than specified value.
Si4+It is that glass generates body cation constituent, a certain amount of Si4+The viscosity that glass can be increased, prevents glass from analysing Crystalline substance improves chemical durability of glass, prevents glass devitrification.If Si4+Content it is very little, glass is easy crystallization, and refractive index cannot Reach required range；But if Si4+Content be higher than 15%, the meltability of optical glass reduces, and glass will devitrification.Cause This, Si4+Content be greater than 0 but be less than or equal to 15%, preferably 1~10%.Further preferably 2~9%.
B3+It is also a kind of optical glass network generation body component, there is preferable fluxing action, suitable B3+To inhibition glass Crystallization it is very good.If B3+Content it is very little, glass melting is very poor, and glass is easy devitrification, it is more difficult to form glass；But such as Fruit B3+Content be higher than 20%, the chemical stability of glass can be poor.Therefore, B3+Content be greater than 0 but to be less than or equal to 20%, preferably 1~15%, further preferably 1~13%.
It, need to be by Si since the lanthanide glass of high refractive low dispersive is relatively narrow at glass range4+Content and B3+The ratio Si of content4+/ B3+Control is in reasonable range, and glass has suitable high temperature viscosity within this range, can prevent the crystallization of glass.Through sending out Bright National People's Congress's quantity research discovery, controls Si4+/B3+When being 0.5~1, when preferably 0.62~1, glass of the invention has preferable High temperature viscosity and it is not easy crystallization.
La3+It is the core component to form high-refractivity and low-dispersion glass.If La3+Content be lower than 42%, refractive index is not Required range can be reached；But if La3+Content be higher than 58%, thermal stability be deteriorated, glass easily crystallization, devitrification It is inclined to very big.Therefore, La3+Content be 42~58%, preferably 42~55%.
Gd3+Glass refraction and dispersion can be adjusted, the stability of glass is improved.If Gd3+Content be lower than 18%, The optical constant of glass cannot reach required range；But if Gd3+Content be higher than 33%, thermal stability be deteriorated, Glass easily crystallization, tendency towards devitrification are very big.Therefore, Gd3+Content be 18~33%, preferably 20~31%.
The present invention is by introducing appropriate Y3+With La3+Consolute is capable of forming the glass of better heat stability.If Y3+Contain Amount is lower than 1%, and the optical constant of glass cannot reach required range；But if Y3+Content be higher than 15%, glass is easily Crystallization, it is easy to devitrification.Therefore, Y3+Content be 1~15%, preferably 2~13%.
Ta5+Optical glass refractive index can be significantly improved, the crystallization of glass is inhibited.If Ta5+Content it is very little, glass It is easy crystallization；But if Ta5+Content be higher than 10%, the dispersion of glass will increase dramatically, and the purpose of low dispersion, and meeting is not achieved So that the meltdown property of glass is deteriorated, can also greatly improve glass production cost.Therefore, Ta5+Content be greater than 0 but to be less than or wait In 10%, preferably 1~8%.
Zr4+The refractive index that can be improved optical glass improves the chemical stability of glass, can also prevent glass devitrification, Reduce crystallization temperature.In the present invention, if its content is higher than 10%, glass is difficult to melt, and smelting temperature rises, and is easy to cause glass Occurs field trash inside glass.Therefore, Zr4+Content be 0~10%, preferably 0.5~8%.
The present inventor is the study found that by Ta5+、Zr4+The sum of content and La3+、Gd3+、Y3+The sum of content ratio (Ta5 ++Zr4+)/(La3++Gd3++Y3+) greater than 0 but less than or equal in 0.3 range, glass inherent quality is preferable, is not easy out for control Now expect the situations such as calculus, field trash, and very good to the crystallization for inhibiting glass, preferably (Ta5++Zr4+)/(La3++Gd3++Y3+) It is 0.05~0.2.
Nb5+There is larger effect to realization glass high refractive index, but if Nb5+Content be more than 5%, the dispersion of glass will Can be very big, it cannot get the glass of low dispersion.Therefore, Nb5+Content be 0~5%, preferably do not contain Nb5+.In addition, of the invention W is not contained in glass yet6+、Ti4+Both sharply increase the ion of dispersion.
Ba2+、Zn2+、Sr2+The refractive index and dispersion of glass can be adjusted.When its total amount is more than 10%, glass is easy Devitrification.Therefore, Ba2+、Zn2+、Sr2+Total content (Zn2++Sr2++Ba2+) it is 0~10%, preferably 0~7%.
Sb3+It is used in the present invention as clarifying agent, content is 0~0.2%, preferably 0~0.1%.
In the present invention, anion contains O2-And F-。
F-It is neccessary composition of the invention, can be effectively reduced the dispersion of glass, realizes the requirement of the low dispersion of glass, separately The transition temperature of glass can also be reduced outside.If F-Content be lower than 5%, cannot achieve the purpose that reduce glass dispersion；But such as Fruit F-Content be higher than 20%, glass volatilization greatly, cause the constant data of glass very unstable, production difficulty is big, while easily The refractive index of glass is caused not reach requirement range.Therefore, F-Content be 5~20%, preferably 7~19%.
O2-It is also the necessary anion of the present invention, is capable of forming stable glass, prevents glass devitrification.Therefore, O2-Contain Amount is 80~95%, preferably 81~93%.
The present inventor is the study found that by F-Content and O2The ratio F of content-/O2-When control is within the scope of reasonable, glass The volatilization of glass is small, is capable of the constant data of stabilized glass, reduces striped, increases the meltbility of glass.Therefore, F-/O2-For greater than 0 But it is less than or equal to 0.3, preferably 0.05~0.2.
In addition, working as Si4+Content and F-The ratio Si of content4+/F-When control is within the scope of reasonable, can effectively it inhibit This devitrification at the extremely narrow glass of glass range, additionally it is possible to increase the transmitance of glass.Therefore, Si4+/F-It is 0.3~1.5, preferably It is 0.3~0.9, further preferably 0.3~0.7.
Optical glass provided by the invention is made according to preparation method well known to those skilled in the art, it may be assumed that by raw material into Row fusing, clarification, stirring homogenizing, be cooled to suitable temperature molding, can be obtained refractive index provided by the present invention be 1.78~ 1.83, the optical glass with high refractive low dispersive performance that Abbe number is 48~53.
The test method of each performance parameter of optical glass provided by the invention is as follows:
Refractive index (nd), Abbe number (vd) are according to " 7962.1-2010 colouless optical glass test method refractive index of GB/T And abbe number " test.
By above-mentioned test, the refractive index (nd) of obtained optical glass of the invention is 1.78~1.83, Abbe number It (vd) is 48~53.
Degree of staining (the λ of glass80/λ5): using have two optical polish planes parallel to each other with a thickness of 10 ± The glass sample of 0.1mm measures spectral transmission, is calculated according to its result.
After measured, the transmittance of glass of the present invention reaches corresponding wavelength X when 80%80In 395nm hereinafter, preferably 390nm or less.
The present invention also provides a kind of optical precast product and optical element, the optical precast product and element are by optics of the present invention Glass is formed by, therefore the optical precast product and optical element have all characteristics of aforementioned present invention optical glass.This hair Bright optical glass has the performance of high refractive low dispersive, and refractive index (nd) is 1.78~1.83, and Abbe number is 48~53.This hair The optical precast product and optical element of bright offer can preferably eliminate the color difference of optical system, so that optical system is more stepped up It gathers, has better performance, it can be achieved that device miniaturization, light-weighted demand.
Embodiment
In order to further appreciate that technical solution of the present invention, the present invention will be described preferably in conjunction with following specific embodiment Embodiment.It should be noted that and understand, these embodiments are intended merely to be better described the features of the present invention and excellent Point, not restricted claim of the invention.
The optical glass component (being indicated respectively with anions and canons weight percent) that the embodiment of the present invention 1~30 provides And its corresponding performance is as shown in Table 1 to Table 3.By by optical glass in each embodiment of 1~table of table 3 it is various cation and The corresponding oxide of anion, fluoride, carbonate etc. are weighed according to its ratio, and it is molten that optical glass is added after being sufficiently mixed uniformly In furnace, under technological temperature appropriate after fusing, clarification, stirring are homogenized, are cooled to suitable temperature, by the glass of this melting It is poured into metal die preheated in advance and forms and anneal, required optical glass can be obtained.
The composition and respective performances of a kind of optical glass with high refractive low dispersive provided by the invention be such as: refractive index (nd), dispersion (nF-nC), Abbe number (vd), degree of staining (λ80/λ5) result all in the Examples 1 to 30 of 1~table of table 3 table Show.
Table 1
Table 2
Table 3
From above-described embodiment as can be seen that its refractive index (nd) of optical glass provided by the invention be 1.78~1.83, Ah Shellfish number is 48~53, has the characteristics that high refractive low dispersive, transmitance are high, can preferably eliminate the color difference of optical system, thus So that optical system is more compact, have better performance, it can be achieved that device miniaturization, light-weighted demand.

Claims (11)

1. optical glass, which is characterized in that the weight percent composition of its cation contains: Si4+: greater than 0 but it is less than or equal to 15%；B3+: greater than 0 but be less than or equal to 20%, wherein Si4+/B3+It is 0.60~1；La3+: 42~58%；Gd3+: 18~ 33%；Y3+: 1~15%；Ta5+: greater than 0 but be less than or equal to 10%；Zr4+: 0~10%；
Its anion contains O2-And F-, wherein F-/O2-For greater than 0 but less than or equal to 0.3, the glass refraction is 1.78 ~1.83, Abbe number is 48~53.
2. optical glass as described in claim 1, which is characterized in that also contain: Nb5+: 0~5%；Zn2++Sr2++Ba2+: 0~ 10%；Sb3+: 0~0.2%.
3. optical glass, which is characterized in that the weight percent composition of its cation are as follows: Si4+: greater than 0 but it is less than or equal to 15%；B3+: greater than 0 but be less than or equal to 20%, wherein Si4+/B3+It is 0.60~1；La3+: 42~58%；Gd3+: 18~ 33%；Y3+: 1~15%；Ta5+: greater than 0 but be less than or equal to 10%；Zr4+: 0~10%；Nb5+: 0~5%；Zn2++Sr2++ Ba2+: 0~10%；Sb3+: 0~0.2%；
Its anion contains O2-And F-, wherein F-/O2-For greater than 0 but less than or equal to 0.3；
Si4+/F-It is 0.3~1.5, the glass refraction is 1.78~1.83, and Abbe number is 48~53.
4. the optical glass as described in claim 1-3 any claim, which is characterized in that wherein: Si4+/F-For 0.3~ 0.9；And/or (Ta5++Zr4+)/(La3++Gd3++Y3+) it is greater than 0 but to be less than or equal to 0.3.
5. the optical glass as described in claim 1-3 any claim, which is characterized in that wherein, Si4+: 1~10%；With/ Or B3+: 1~15%；And/or La3+: 42~55%；And/or Gd3+: 20~31%；And/or Y3+: 2~13%；And/or Ta5+: 1 ~8%；And/or Zr4+: 0.5~8%.
6. the optical glass as described in claim 1-3 any claim, which is characterized in that the content of the ion meet with One of lower 4 kinds of conditions or more than one:
1)Si4+/F-It is 0.3~0.7；
2)(Ta5++Zr4+)/(La3++Gd3++Y3+) it is 0.05~0.2；
3)Si4+/B3+It is 0.62~1；
4)F-/O2-It is 0.05~0.2.
7. the optical glass as described in claim 1-3 any claim, which is characterized in that wherein, Si4+: 2~9%；With/ Or B3+: 1~13%；And/or Zn2++Sr2++Ba2+: 0~7%；And/or Sb3+: 0~0.1%；Without containing Nb5+、W6+、Ti4+。
8. the optical glass as described in claim 1-3 any claim, which is characterized in that the weight percent of its anion Composition contains: F-: 5~20%；O2-: 80~95%.
9. the optical glass as described in claim 1-3 any claim, which is characterized in that the weight percent of its anion Composition contains: F-: 7~19%；O2-: 81~93%.
10. gas preform is made of optical glass described in claim 1-9 any claim.
11. optical element is made of optical glass described in claim 1-9 any claim.
CN201710156101.1A 2017-03-16 2017-03-16 Optical glass and optical element Active CN106830671B (en)