CN106826570A - Metal tube surface cleaning treatment technique - Google Patents
Metal tube surface cleaning treatment technique Download PDFInfo
- Publication number
- CN106826570A CN106826570A CN201710052811.XA CN201710052811A CN106826570A CN 106826570 A CN106826570 A CN 106826570A CN 201710052811 A CN201710052811 A CN 201710052811A CN 106826570 A CN106826570 A CN 106826570A
- Authority
- CN
- China
- Prior art keywords
- metal tube
- greasy dirt
- sandblasting
- pipe
- tube surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of process of surface treatment, more particularly to a kind of metal tube surface cleaning treatment technique, it belongs to cooling wall buried-pipe system field.It comprises the following steps:A, the macroscopic greasy dirt of outer surface of metal pipe is cleared up;Check compressed air and diamond dust used whether there is greasy dirt before b, sandblasting, it is qualified after can carry out sandblasting;C, diamond dust blasting treatment is carried out to metal tube using special tooling;D, metal tube surface is sprayed with alcohol-based solvent, removed because of the pipe surface dust residual that sandblasting is formed;E, with black light lamp check metal tube surface whether with the presence of greasy dirt;F, operating process need to wear special clean white glove, it is to avoid bare-handed touch causes secondary pollution.The beneficial effects of the invention are as follows:Surface sand-blasting is carried out with diamond dust, the iron rust and oxide skin on surface is removed, increases its fastness combined with body;Black light lamp can detect surface whether there is greasy dirt;Wear special clean white glove, it is to avoid bare-handed touch causes secondary pollution to pipe.
Description
Technical field
The present invention relates to a kind of process of surface treatment, more particularly to a kind of metal tube surface cleaning treatment technique, it belongs to
Cooling wall buried-pipe system field.
Background technology
Blast furnace copper cooling stave has rolling to drill and casting two kinds of forms of pipe laying.Casting pipe laying cooling wall water channel is embedment water
Tube cavity, its cooling effect depends on the thermal conductivity and the fusion situation between pipe and body of pipe material.Pipe laying before casting
Surface cleanness degree, is to combine one of principal element of effect between influence pipe and body.
General at present has following two surface cleaning processing modes:1st, blasting treatment is carried out to steel tube surface, the technique
Be easy to so that steel tube surface have dust remaining, be unfavorable for postorder cast interface combine.2nd, to nickel tube sand for surface paper burnishing part
Reason, and, drying clean with alcohol washes;This kind of processing mode causes that nickel tube is surface-treated not thoroughly, and drying control is improper easily
Nickel tube surface is produced oxidation, so as to cause surface second to pollute, thus the effect that nickel tube surface combined with body can be influenceed.With
Upper processing mode is without corresponding treatment effect detection method, it is difficult to ensure whether surface cleaning is thorough.
The content of the invention
The present invention is directed to above-mentioned deficiency, there is provided a kind of to metal tube surface cleaning treatment, more thoroughly metal tube surface is clear
Clean handling process.
The technical scheme that the present invention solves above-mentioned technical problem is as follows:
A kind of metal tube surface cleaning treatment technique, comprises the following steps:
A, the macroscopic greasy dirt of outer surface of metal pipe is cleared up;
Check compressed air and diamond dust used whether there is greasy dirt before b, sandblasting, it is qualified after can carry out sandblasting;
C, diamond dust blasting treatment is carried out to metal tube using special tooling;
D, metal tube surface is sprayed with alcohol-based solvent, removed because of the pipe surface dust residual that sandblasting is formed;
E, with black light lamp check metal tube surface whether with the presence of greasy dirt, according to circumstances determine whether to carry out at secondary cleaning
Reason;
F, operating process need to wear special clean white glove, it is to avoid bare-handed touch causes secondary pollution.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, if unused more than 48 hours after black light lamp inspection, it is necessary to carry out black light lamp reinspection to the metal tube, to disappear
Except the reduction of the cleaning effect caused by standing time is long, according to circumstances determine whether to carry out secondary cleaning treatment.
The beneficial effects of the invention are as follows:Surface sand-blasting is carried out with diamond dust, the iron rust and oxide skin on surface can be removed, increased
Plus its fastness for being combined with body;Black light lamp can detect surface whether there is greasy dirt;Wear special clean white glove, it is to avoid bare-handed to touch
Touch, be avoided that secondary pollution of the hand to pipe.
Specific embodiment
Principle of the invention and feature are described below, example is served only for explaining the present invention, is not intended to limit
Determine the scope of the present invention.
1st, a kind of metal tube surface cleaning treatment technique, comprises the following steps:
A, the macroscopic greasy dirt of outer surface of metal pipe is cleared up.
Check compressed air and diamond dust used whether there is greasy dirt before b, sandblasting, it is qualified after can carry out sandblasting.
C, diamond dust blasting treatment is carried out to metal tube using special tooling;Sandblasting is to drive to spray by heavy-duty motor
Blade rotates at a high speed, silicon carbide abrasive is carried out spray treatment to pipe surface under the action of the centrifugal force, not only can thoroughly remove
Iron rust, oxide and dirt, and in the presence of the fierce impact of abrasive material and frictional force, moreover it is possible to required for reaching pipe surface
Even roughness degree;Meanwhile, can be with the physisorption on enlarged pipe surface after rust cleaning.
D, metal tube surface is sprayed with alcohol-based solvent, removed because of the pipe surface dust residual that sandblasting is formed.
E, with black light lamp check metal tube surface whether with the presence of greasy dirt;If black light lamp is unused more than 48 hours after checking,
Needs carry out black light lamp reinspection to the metal tube;The reduction of the cleaning effect caused by standing time is long is eliminated, according to circumstances
Determine whether to carry out secondary cleaning treatment.
F, operating process need to wear special clean white glove, it is to avoid bare-handed touch causes secondary pollution.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all it is of the invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc. should be included within the scope of the present invention.
Claims (2)
1. a kind of metal tube surface cleaning treatment technique, it is characterised in that comprise the following steps:
A, the macroscopic greasy dirt of outer surface of metal pipe is cleared up;
Check compressed air and diamond dust used whether there is greasy dirt before b, sandblasting, it is qualified after can carry out sandblasting;
C, diamond dust blasting treatment is carried out to metal tube using special tooling;
D, metal tube surface is sprayed with alcohol-based solvent, removed because of the pipe surface dust residual that sandblasting is formed;
E, with black light lamp check metal tube surface whether with the presence of greasy dirt, according to circumstances determine whether to carry out secondary cleaning treatment;
F, operating process need to wear special clean white glove, it is to avoid bare-handed touch causes secondary pollution.
2. metal tube surface cleaning treatment technique according to claim 1, it is characterised in that:If exceeding after black light lamp inspection
48 hours unused, it is necessary to carry out black light lamp reinspection to the metal tube.