CN106811755A - A kind of nickel base superalloy chrome-plated process - Google Patents
A kind of nickel base superalloy chrome-plated process Download PDFInfo
- Publication number
- CN106811755A CN106811755A CN201710109923.4A CN201710109923A CN106811755A CN 106811755 A CN106811755 A CN 106811755A CN 201710109923 A CN201710109923 A CN 201710109923A CN 106811755 A CN106811755 A CN 106811755A
- Authority
- CN
- China
- Prior art keywords
- nickel base
- base superalloy
- washing
- chrome
- activation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of nickel base superalloy chrome-plated process, using two kinds of electro-active method elder generation anode activations activation of cathode again, the effective passivation layer and dust for removing Surface Creation before nickel base superalloy chromium plating, activate the metal lattice of nickel base superalloy, improve the adhesion of chrome-faced, method is simple and easy to apply, and pollution wastes small.Specific technological process is an electrochemical deoiling → washing → time anode activation → washing → secondary cathode activation → → 50 DEG C of hot water wash → chromium plating of washing.
Description
Technical field
The present invention relates to nickel base superalloy chrome-faced technique, closed in high temperature again using after electrochemical acid activating pretreatment
Gold surface chromium plating.
Background technology
Nickel base superalloy is due to itself there is stronger self-passivation ability, it is generally difficult to surface electro-deposition is carried out to it, but
In reparation or some special occasions, it is necessary to its chrome-faced.Therefore a kind of having in nickel base superalloy electroplating surface is developed
Efficacious prescriptions method just has certain realistic meaning, particularly meets aviation reparation, the job requirements of robot industry.
The content of the invention
The technical problems to be solved by the invention are directed to above-mentioned prior art and provide a nickel base superalloy chrome-faced
Technique, belongs to a kind of simple and effective, low stain, the nickel base superalloy chrome-faced method of coating performance stabilization.
The present invention the used technical scheme that solves the above problems is:A kind of nickel base superalloy chrome-plated process, including change
An oil removing → washing → time anode activation → washing → secondary cathode activation → → 50 DEG C of hot water wash → chromium plating of washing are learned,
Wherein, electrochemical degreasing solution formula and technological parameter:
Anode activation solution formula and technological parameter:
Secondary cathode activated solution is formulated and technological parameter:
Cr-plating Bath is formulated and technological parameter:
Compared with prior art, the advantage of the invention is that:Using two kinds of electro-active methods, (first anode activation again live by negative electrode
Change), the passivation layer and dust of Surface Creation before nickel base superalloy chromium plating are effectively removed, activate the metal of nickel base superalloy
Lattice, improves the adhesion of chrome-faced, and method is simple and easy to apply, and pollution wastes small.
Specific embodiment
The present invention is described in further detail with reference to embodiments.
The present embodiment nickel base superalloy chrome-faced be using two kinds of electro-active methods effectively remove passivation layer and
Dust, for the smooth chromium plating of high-temperature alloy surface provides favourable conditions, improves the adhesion of chromium plating, and method is simple and easy to apply, plating effect
It is really good.
Specifically, an electrochemical deoiling → washing → time anode activation → washing → secondary cathode activation → → 50 DEG C of heat of washing
Washing → chromium plating,
Wherein, electrochemical degreasing solution formula and technological parameter:
Anode activation solution formula and technological parameter:
Secondary cathode activated solution is formulated and technological parameter:
Cr-plating Bath is formulated and technological parameter:
In addition to the implementation, present invention additionally comprises having other embodiment, all use equivalents or equivalence replacement
The technical scheme that mode is formed, all should fall within the scope of the hereto appended claims.
Claims (1)
1. a kind of nickel base superalloy chrome-plated process, it is characterised in that:Including electrochemical deoiling → washing → time anode activation →
Washing → secondary cathode activation → → 50 DEG C of hot water wash → chromium plating of washing,
Wherein, electrochemical degreasing solution formula and technological parameter:
Anode activation solution formula and technological parameter:
Secondary cathode activated solution is formulated and technological parameter:
Cr-plating Bath is formulated and technological parameter: