CN106811689B - A kind of preparation method of tensile strength >=2000MPa hot forming steel - Google Patents
A kind of preparation method of tensile strength >=2000MPa hot forming steel Download PDFInfo
- Publication number
- CN106811689B CN106811689B CN201710030911.2A CN201710030911A CN106811689B CN 106811689 B CN106811689 B CN 106811689B CN 201710030911 A CN201710030911 A CN 201710030911A CN 106811689 B CN106811689 B CN 106811689B
- Authority
- CN
- China
- Prior art keywords
- hot forming
- tensile strength
- 2000mpa
- forming steel
- hot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
Claims (5)