CN106811254A - Mixed injection coal dust - Google Patents
Mixed injection coal dust Download PDFInfo
- Publication number
- CN106811254A CN106811254A CN201611173433.2A CN201611173433A CN106811254A CN 106811254 A CN106811254 A CN 106811254A CN 201611173433 A CN201611173433 A CN 201611173433A CN 106811254 A CN106811254 A CN 106811254A
- Authority
- CN
- China
- Prior art keywords
- coal
- mixed
- anthracite
- coke oven
- blast furnace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to field of iron and steel smelting, more particularly to a kind of pulverized coal injection in blast furnace.The pulverized coal injection in blast furnace that the present invention is provided includes:Removing dust of coke oven, anthracite and bituminous coal;The weight ratio of the removing dust of coke oven, anthracite and bituminous coal is (5~20):(35~50):(38~45).The pulverized coal injection in blast furnace is that removing dust of coke oven is mixed to get with anthracite, bituminous coal, meets blast furnace blowing requirement, reduces the explosivity of mixed coal powder, improves the combustion rate of mixed coal powder, while reducing injection cost and pig iron cost.
Description
Technical field
The present invention relates to field of metallurgy, more particularly to a kind of mixed injection coal dust.
Background technology
The technical process that metallic iron is extract from iron-bearing mineral (the predominantly oxide of iron), mainly there is blast furnace
Method, direct-reduction process, smelting reduction process, plasma method.Wherein, blast furnace process application is relatively broad.In recent years, with domestic steel
The continuous progress of industry, and the market demand continuous expansion, how to reduce ironmaking cost and improve industrial safety
Property, increasingly paid close attention to by those skilled in the art.
The content of the invention
In view of this, the present invention provides a kind of mixed injection coal dust.
The application provides a kind of mixed injection coal dust, and it includes:Removing dust of coke oven, anthracite, bituminous coal;The coke oven dust
The weight ratio of ash, anthracite and bituminous coal is (5~20):(35~50):(38~45).
Further, the weight ratio of the removing dust of coke oven, anthracite and bituminous coal is (10~20):(40~50):40.
Further, the granularity of the mixed injection coal dust is not more than 80 mesh, wherein -200 mesh grades account for 65%.
The present invention provides a kind of mixed injection coal dust, and it is that removing dust of coke oven is mixed to get with anthracite, bituminous coal, meets
Blast furnace blowing requirement, reduces the explosivity of mixed coal powder, the combustion rate of mixed coal powder is improve, while reducing injection cost
And pig iron cost.
Specific embodiment
The invention discloses a kind of mixed injection coal dust, those skilled in the art can use for reference present disclosure, be suitably modified
Technological parameter is realized.In particular, all similar replacements and change be for a person skilled in the art it is aobvious and
It is clear to, they are considered as being included in the present invention.The method of the present invention and application are retouched by preferred embodiment
State, related personnel can substantially change not departing from present invention, spirit and scope to method described herein and application
It is dynamic or suitably change with combining and realize and apply the technology of the present invention.
Present inventor considers:Removing dust of coke oven is the dust of generation after the dedusting of coking coke dry quenching furnace first and second.Its
Moisture is relatively low, and ash content and volatilization grade close with dry coke quenching charcoal.Property is approximate with coke powder, and its volatile matter is general in 1-2% levels,
Can be regarded as anthracite.Removing dust of coke oven fixes that carbon content is higher, the bituminous coal that is used higher than current blast furnace blowing and smokeless
Coal, caloric value is approached with pulverized coal injection in blast furnace.If blast furnace blowing removing dust of coke oven, first can be allowed to be fully utilized,
The wasting of resources is avoided, part anthracite second can be substituted, blast furnace blowing cost is advantageously reduced.If making full use of this part
Resource, can reduce ironmaking system pig iron cost.
Based on above-mentioned design, the present invention provides a kind of mixed injection coal dust, and it includes:Removing dust of coke oven, anthracite, cigarette
Coal;Wherein, the weight ratio of the removing dust of coke oven, anthracite and bituminous coal is (5~20):(35~50):(38~45).
Preferably, the weight ratio of the removing dust of coke oven, anthracite and bituminous coal is (10~20):(40~50):40.
Further, the granularity of the mixed injection coal dust is not more than 80 mesh, wherein -200 mesh grades account for 65%.
The advantage of mixed injection coal dust that the present invention is provided is:Removing dust of coke oven is mixed to get with anthracite, bituminous coal,
Meet blast furnace blowing requirement, reduce the explosivity of mixed coal powder, improve the combustion rate of mixed coal powder, while reducing injection
Cost and pig iron cost.
With reference to embodiment, the present invention is expanded on further:
Embodiment 1
Removing dust of coke oven, anthracite, bituminous coal are made smaller than the fine coal of 80 mesh by coal pulverizer, wherein -200 mesh are accounted for
65%.Dry cooled coke powder weight accounts for the 10% of mixed coal powder weight in mixed coal powder, and anthracite weight accounts for mixed coal powder weight
50%, bituminous coal weight accounts for the 40% of mixed coal powder weight.
Embodiment 2
Removing dust of coke oven, anthracite, bituminous coal are made smaller than the fine coal of 80 mesh by coal pulverizer, wherein -200 mesh are accounted for
65%.Removing dust of coke oven weight accounts for the 20% of mixed coal powder weight in mixed coal powder, and anthracite weight accounts for mixed coal powder weight
40%, bituminous coal weight accounts for the 40% of mixed coal powder weight.
Comparative example
Anthracite account for 60% and bituminous coal account for 40% mixed coal powder.
The mixed coal powder prepared using above-described embodiment 1 and 2 is tested, and mixed coal powder returned fire length is respectively less than
400mm, is weak explosive coal.
The mixed coal powder of embodiment 1 and 2, and comparative example 1 is carried out into combustion rate experiment, it is as a result as follows:
The combustion rate of embodiment 1 and embodiment 2 is higher than comparative example 2-3 percentage points.
Can be drawn by above example:The mixed coal powder that the present invention is provided disclosure satisfy that blast furnace blowing requirement, reduce
The explosivity of mixed coal powder, improves the combustion rate of mixed coal powder, while reducing injection cost and pig iron cost.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (3)
1. a kind of mixed injection coal dust, it is characterised in that including:Removing dust of coke oven, anthracite, bituminous coal;The removing dust of coke oven,
The weight ratio of anthracite and bituminous coal is (5~20):(35~50):(38~45).
2. mixed injection coal dust according to claim 1, it is characterised in that the removing dust of coke oven, anthracite and bituminous coal
Weight ratio be (10~20):(40~50):40.
3. mixed injection coal dust according to claim 1, it is characterised in that the granularity of the mixed injection coal dust is not more than
80 mesh, wherein -200 mesh grades account for 65%.