CN106810804A - A kind of automobile lampshade moulding material and preparation method thereof - Google Patents
A kind of automobile lampshade moulding material and preparation method thereof Download PDFInfo
- Publication number
- CN106810804A CN106810804A CN201611126178.6A CN201611126178A CN106810804A CN 106810804 A CN106810804 A CN 106810804A CN 201611126178 A CN201611126178 A CN 201611126178A CN 106810804 A CN106810804 A CN 106810804A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylate
- standby
- organosilicon
- polycarbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of automobile lampshade moulding material,The material matched by following parts by weight is made,Including 50 60 parts of polymethyl methacrylate,6 14 parts of polystyrene,15 20 parts of polyarylsulfone (PAS),18 25 parts of polycarbonate,11 14 parts of styrene-acrylonitrile,8 12 parts of transparent polyamide,6 10 parts of phenyltrimethoxysila,e,12 16 parts of acrylate,9 10 parts of organosilicon,48 parts of BP,13 15 parts of carboxymethylcellulose calcium,58 parts of alumina silicate,13 16 parts of calcium silicates,78 parts of aerosil,69 parts of glass fibre,12 14 parts of aminoethyl piperazine,15 20 parts of 10 15 parts of IPD and cobalt naphthenate,Automobile lampshade moulding material translucent effect of the invention is good,Structural strength is high,With abrasion resistant effect higher.
Description
Technical field
The present invention relates to a kind of automobile lampshade moulding material and preparation method thereof.
Background technology
Injection is a kind of method that industrial products produce moulding.Product is usually using rubber injection mold and plastic injection.Injection
Can also dispensing molding die platen press and casting die.Injection (mo(u)lding) machine (abbreviation injector or injection machine) is by thermoplastic or heat
Solidity material is made the main former of variously-shaped plastic products using mould for plastics, and injection moulding is by injection
Machine and mould are realized.Rubber injection mold：Injection molding of rubber is a kind of life for directly vulcanizing sizing material from machine barrel injection model
Product method.The advantage of rubber injection mold is：Though category intermittently operated, short molding cycle, production efficiency is high to eliminate embryo material beam worker
Sequence, labour intensity is small, and product quality is excellent.Plastic injection：Plastic injection is a kind of method of plastic products, the plastics that will be melted
Noted into plastic product mold using pressure, cooling shaping obtains wanting various working of plastics.There is the machine dedicated for being molded
Tool injection machine.Most currently used plastics are polystyrene.The shape of gained is exactly often end product, in installation or conduct
Other processing are no longer needed before final finished use.Many thin portions, such as lug boss, rib, screw thread, can be in injection mould
Formed out in modeling single stepping.Injection is a kind of common approach that plastic raw materials are used.But precise injection molding is then to pursue to beat
Make high-precision injecting products.Precise injection molding has two indices：One is equipment precision, and another is that mask error precise injection molding is gathered around
There is most superior injection Related product.
Automobile lampshade as automobile important accessory, less use glass is made now, but existing plastic lantern
Cover translucent effect is bad, and structural strength is not high, without abrasion resistant effect higher.
The content of the invention
In view of this, good it is an object of the present invention to provide a kind of translucent effect, structural strength is high, with abrasion resistant effect higher
Automobile lampshade moulding material.
In order to solve the above-mentioned technical problem, the technical scheme is that：
A kind of automobile lampshade moulding material, the material matched by following parts by weight is made, including poly-methyl methacrylate
Ester 50-60 parts, polystyrene 6-14 parts, polyarylsulfone (PAS) 15-20 parts, polycarbonate 18-25 parts, styrene-acrylonitrile 11-14 parts, thoroughly
Bright polyamide 8-12 parts, phenyltrimethoxysila,e 6-10 parts, acrylate 12-16 parts, organosilicon 9-10 parts, BP
4-8 parts, carboxymethylcellulose calcium 13-15 parts, alumina silicate 5-8 parts, calcium silicates 13-16 parts, aerosil 7-8 parts, glass fibers
6-9 parts, aminoethyl piperazine 12-14 parts, IPD 10-15 parts and cobalt naphthenate 15-20 parts of dimension.
Preferably, be made up of the material that following parts by weight are matched, including 50 parts of polymethyl methacrylate, polyphenyl second
6 parts of alkene, 15 parts of polyarylsulfone (PAS), 18 parts of polycarbonate, 11 parts of styrene-acrylonitrile, 8 parts of transparent polyamide, phenyltrimethoxysila,e
6 parts, 12 parts of acrylate, 9 parts of organosilicon, 4 parts of BP, 13 parts of carboxymethylcellulose calcium, 5 parts of alumina silicate, calcium silicates 13
Part, 7 parts of aerosil, 6 parts of glass fibre, 12 parts of aminoethyl piperazine, 10 parts of IPD and 15 parts of cobalt naphthenate.
Preferably, be made up of the material that following parts by weight are matched, including 55 parts of polymethyl methacrylate, polyphenyl second
10 parts of alkene, 17.5 parts of polyarylsulfone (PAS), 21.5 parts of polycarbonate, 12.5 parts of styrene-acrylonitrile, 10 parts of transparent polyamide, phenyl front three
8 parts of TMOS, 14 parts of acrylate, 9.5 parts of organosilicon, 6 parts of BP, 14 parts of carboxymethylcellulose calcium, alumina silicate 6.5
Part, 14.5 parts of calcium silicates, 7.5 parts of aerosil, 7.5 parts of glass fibre, 13 parts of aminoethyl piperazine, IPD
12.5 parts and 17.5 parts of cobalt naphthenate.
Preferably, be made up of the material that following parts by weight are matched, including 60 parts of polymethyl methacrylate, polyphenyl second
14 parts of alkene, 20 parts of polyarylsulfone (PAS), 25 parts of polycarbonate, 14 parts of styrene-acrylonitrile, 12 parts of transparent polyamide, phenyl trimethoxy silicon
10 parts of alkane, 16 parts of acrylate, 10 parts of organosilicon, 8 parts of BP, 15 parts of carboxymethylcellulose calcium, 8 parts of alumina silicate, silicic acid
16 parts of calcium, 8 parts of aerosil, 9 parts of glass fibre, 14 parts of aminoethyl piperazine, 15 parts of IPD and cobalt naphthenate
20 parts.
The invention solves the problems that another technical problem be that a kind of preparation method of automobile lampshade moulding material is provided, including with
Lower step：
1) by polymethyl methacrylate 50-60 parts, polystyrene 6-14 parts, polyarylsulfone (PAS) 15-20 parts, polycarbonate 18-
25 parts, styrene-acrylonitrile 11-14 parts, transparent polyamide 8-12 parts, phenyltrimethoxysila,e 6-10 parts, acrylate 12-
It is standby during 16 parts, organosilicon 9-10 parts are put into drying box；
2) regulating step 1) in drying box temperature be 48-50 DEG C, drying time be 12-16 minutes, it is standby；
3) by BP 4-8 parts, carboxymethylcellulose calcium 13-15 parts, alumina silicate 5-8 parts, calcium silicates 13-16 parts, gas
Aerosil 7-8 parts, glass fibre 6-9 parts, aminoethyl piperazine 12-14 parts, IPD 10-15 parts and cobalt naphthenate
It is standby in 15-20 parts of input reactor；
4) temperature of regulation reactor is 110-120 DEG C, and mixing speed is 400-500r/min, is reacted 5-10 minutes, then
By step 2) gained raw material be added in reactor, regulation heating-up temperature be 150-160 DEG C, mixing speed keep it is constant, reaction
Time is 2-3, standby
5) by step 4) during gained raw material puts into autoclave, regulation air pressure is 12-15 times of atmospheric pressure, standing 3-5 minutes,
It is standby；
6) by step 5) gained raw material input injection machine in heating be in molten condition, inject mould.
The technology of the present invention effect major embodiment is in the following areas：The polymethyl methacrylate of addition, polystyrene, poly- virtue
Sulfone, polycarbonate, styrene-acrylonitrile, transparent polyamide, phenyltrimethoxysila,e, acrylate, organosilicon keep printing opacity
Effect is good, and structural strength is high；The alumina silicate of addition, calcium silicates, aerosil, glass fibre and aminoethyl piperazine tool
There is abrasion resistant effect higher.
Specific embodiment
Embodiment 1
A kind of automobile lampshade moulding material, the material matched by following parts by weight is made, and is matched by following parts by weight
Material be made, including 50 parts of polymethyl methacrylate, 6 parts of polystyrene, 15 parts of polyarylsulfone (PAS), 18 parts of polycarbonate, benzene second
11 parts of alkene acrylonitrile, 8 parts of transparent polyamide, 6 parts of phenyltrimethoxysila,e, 12 parts of acrylate, 9 parts of organosilicon, Oxybenzene
4 parts of formyl, 13 parts of carboxymethylcellulose calcium, 5 parts of alumina silicate, 13 parts of calcium silicates, 7 parts of aerosil, 6 parts of glass fibre, ammonia
15 parts of 12 parts of ethyl piperazidine, 10 parts of IPD and cobalt naphthenate.
1) by 50 parts of polymethyl methacrylate, 6 parts of polystyrene, 15 parts of polyarylsulfone (PAS), 18 parts of polycarbonate, styrene third
11 parts of alkene nitrile, 8 parts of transparent polyamide, 6 parts of phenyltrimethoxysila,e, 12 parts of acrylate, 9 parts of organosilicon put into drying box
In, it is standby；
2) regulating step 1) in drying box temperature be 48-50 DEG C, drying time be 12-16 minutes, it is standby；
3) by 4 parts of BP, 13 parts of carboxymethylcellulose calcium, 5 parts of alumina silicate, 13 parts of calcium silicates, aerosil 7
It is standby in part, 6 parts of glass fibre, 12 parts of aminoethyl piperazine, 10 parts of IPD and 15 parts of input reactors of cobalt naphthenate
With；
4) temperature of regulation reactor is 110-120 DEG C, and mixing speed is 400-500r/min, is reacted 5-10 minutes, then
By step 2) gained raw material be added in reactor, regulation heating-up temperature be 150-160 DEG C, mixing speed keep it is constant, reaction
Time is 2-3, standby
5) by step 4) during gained raw material puts into autoclave, regulation air pressure is 12-15 times of atmospheric pressure, standing 3-5 minutes,
It is standby；
6) by step 5) gained raw material input injection machine in heating be in molten condition, inject mould.
Embodiment 2
A kind of automobile lampshade moulding material, the material matched by following parts by weight is made, and is matched by following parts by weight
Material be made, including 55 parts of polymethyl methacrylate, 10 parts of polystyrene, 17.5 parts of polyarylsulfone (PAS), 21.5 parts of polycarbonate,
12.5 parts of styrene-acrylonitrile, 10 parts of transparent polyamide, 8 parts of phenyltrimethoxysila,e, 14 parts of acrylate, organosilicon 9.5
Part, 6 parts of BP, 14 parts of carboxymethylcellulose calcium, 6.5 parts of alumina silicate, 14.5 parts of calcium silicates, 7.5 parts of aerosil,
17.5 parts of 7.5 parts of glass fibre, 13 parts of aminoethyl piperazine, 12.5 parts of IPD and cobalt naphthenate.
1) by 55 parts of polymethyl methacrylate, 10 parts of polystyrene, 17.5 parts of polyarylsulfone (PAS), 21.5 parts of polycarbonate, benzene
12.5 parts of ethylene, propylene nitrile, 10 parts of transparent polyamide, 8 parts of phenyltrimethoxysila,e, 14 parts of acrylate, 9.5 parts of organosilicon
It is standby in putting into drying box；
2) regulating step 1) in drying box temperature be 48-50 DEG C, drying time be 12-16 minutes, it is standby；
3) by 6 parts of BP, 14 parts of carboxymethylcellulose calcium, 6.5 parts of alumina silicate, 14.5 parts of calcium silicates, gas phase dioxy
7.5 parts of SiClx, 7.5 parts of glass fibre, 13 parts of aminoethyl piperazine, 17.5 parts of inputs of 12.5 parts of IPD and cobalt naphthenate
It is standby in reactor；
4) temperature of regulation reactor is 110-120 DEG C, and mixing speed is 400-500r/min, is reacted 5-10 minutes, then
By step 2) gained raw material be added in reactor, regulation heating-up temperature be 150-160 DEG C, mixing speed keep it is constant, reaction
Time is 2-3, standby
5) by step 4) during gained raw material puts into autoclave, regulation air pressure is 12-15 times of atmospheric pressure, standing 3-5 minutes,
It is standby；
6) by step 5) gained raw material input injection machine in heating be in molten condition, inject mould.
Embodiment 3
A kind of automobile lampshade moulding material, the material matched by following parts by weight is made, and is matched by following parts by weight
Material be made, including 60 parts of polymethyl methacrylate, 14 parts of polystyrene, 20 parts of polyarylsulfone (PAS), 25 parts of polycarbonate, benzene second
14 parts of alkene acrylonitrile, 12 parts of transparent polyamide, 10 parts of phenyltrimethoxysila,e, 16 parts of acrylate, 10 parts of organosilicon, oxidation
8 parts of benzoyl, 15 parts of carboxymethylcellulose calcium, 8 parts of alumina silicate, 16 parts of calcium silicates, 8 parts of aerosil, 9 parts of glass fibre,
20 parts of 14 parts of aminoethyl piperazine, 15 parts of IPD and cobalt naphthenate.
1) by 60 parts of polymethyl methacrylate, 14 parts of polystyrene, 20 parts of polyarylsulfone (PAS), 25 parts of polycarbonate, styrene
14 parts of acrylonitrile, 12 parts of transparent polyamide, 10 parts of phenyltrimethoxysila,e, 16 parts of acrylate, 10 parts of organosilicon are put into
It is standby in drying box；
2) regulating step 1) in drying box temperature be 48-50 DEG C, drying time be 12-16 minutes, it is standby；
3) by 8 parts of BP, 15 parts of carboxymethylcellulose calcium, 8 parts of alumina silicate, 16 parts of calcium silicates, aerosil 8
It is standby in part, 9 parts of glass fibre, 14 parts of aminoethyl piperazine, 15 parts of IPD and 20 parts of input reactors of cobalt naphthenate
With；
4) temperature of regulation reactor is 110-120 DEG C, and mixing speed is 400-500r/min, is reacted 5-10 minutes, then
By step 2) gained raw material be added in reactor, regulation heating-up temperature be 150-160 DEG C, mixing speed keep it is constant, reaction
Time is 2-3, standby
5) by step 4) during gained raw material puts into autoclave, regulation air pressure is 12-15 times of atmospheric pressure, standing 3-5 minutes,
It is standby；
6) by step 5) gained raw material input injection machine in heating be in molten condition, inject mould.
Experimental example
Experimental subjects：Choose general-utility car lampshade, imported auto lampshade is carried out with automobile lampshade moulding material of the invention
Contrast.
Requirement of experiment：Above-mentioned general-utility car lampshade, imported auto lampshade and automobile lampshade moulding material chi of the invention
It is very little in the same size.
Experimental technique：Compression strength is tested using intensity test machine；Anti-wear performance is resistance to using ASTM D3884
Mill test method is detected；Light transmittance is detected by light transmittance tester using GB2680-1994 standards.
Concrete outcome is as shown in the table：
With reference to upper table, the data of different automobile lampshades gained under identical experimental technique, automobile of the invention are contrasted
The compression strength of lamp shade forming material is higher, and more preferably, light transmittance is higher for abrasion resistant effect.
The technology of the present invention effect major embodiment is in the following areas：The polymethyl methacrylate of addition, polystyrene, poly- virtue
Sulfone, polycarbonate, styrene-acrylonitrile, transparent polyamide, phenyltrimethoxysila,e, acrylate, organosilicon keep printing opacity
Effect is good, and structural strength is high；The alumina silicate of addition, calcium silicates, aerosil, glass fibre and aminoethyl piperazine tool
There is abrasion resistant effect higher.
Certainly, it is more than representative instance of the invention, in addition, the present invention can also have other various specific implementations
The technical scheme that mode, all use equivalents or equivalent transformation are formed, all falls within the scope of protection of present invention.
Claims (5)
1. a kind of automobile lampshade moulding material, it is characterised in that：The material matched by following parts by weight is made, including poly- methyl
Methyl acrylate 50-60 parts, polystyrene 6-14 parts, polyarylsulfone (PAS) 15-20 parts, polycarbonate 18-25 parts, styrene-acrylonitrile
11-14 parts, transparent polyamide 8-12 parts, phenyltrimethoxysila,e 6-10 parts, acrylate 12-16 parts, organosilicon 9-10 parts,
BP 4-8 parts, carboxymethylcellulose calcium 13-15 parts, alumina silicate 5-8 parts, calcium silicates 13-16 parts, aerosil 7-8
Part, glass fibre 6-9 parts, aminoethyl piperazine 12-14 parts, IPD 10-15 parts and cobalt naphthenate 15-20 parts.
2. a kind of automobile lampshade moulding material as claimed in claim 1, it is characterised in that：The material matched by following parts by weight
Material is made, including 50 parts of polymethyl methacrylate, 6 parts of polystyrene, 15 parts of polyarylsulfone (PAS), 18 parts of polycarbonate, styrene third
11 parts of alkene nitrile, 8 parts of transparent polyamide, 6 parts of phenyltrimethoxysila,e, 12 parts of acrylate, 9 parts of organosilicon, BP 4
Part, 13 parts of carboxymethylcellulose calcium, 5 parts of alumina silicate, 13 parts of calcium silicates, 7 parts of aerosil, 6 parts of glass fibre, aminoethyl piperazine
15 parts of 12 parts of piperazine, 10 parts of IPD and cobalt naphthenate.
3. a kind of automobile lampshade moulding material as claimed in claim 1, it is characterised in that：The material matched by following parts by weight
Material is made, including 55 parts of polymethyl methacrylate, 10 parts of polystyrene, 17.5 parts of polyarylsulfone (PAS), 21.5 parts of polycarbonate, benzene second
12.5 parts of alkene acrylonitrile, 10 parts of transparent polyamide, 8 parts of phenyltrimethoxysila,e, 14 parts of acrylate, 9.5 parts of organosilicon, oxygen
Change 6 parts of benzoyl, 14 parts of carboxymethylcellulose calcium, 6.5 parts of alumina silicate, 14.5 parts of calcium silicates, 7.5 parts of aerosil, glass
17.5 parts of 7.5 parts of fiber, 13 parts of aminoethyl piperazine, 12.5 parts of IPD and cobalt naphthenate.
4. a kind of automobile lampshade moulding material as claimed in claim 1, it is characterised in that：The material matched by following parts by weight
Material is made, including 60 parts of polymethyl methacrylate, 14 parts of polystyrene, 20 parts of polyarylsulfone (PAS), 25 parts of polycarbonate, styrene third
14 parts of alkene nitrile, 12 parts of transparent polyamide, 10 parts of phenyltrimethoxysila,e, 16 parts of acrylate, 10 parts of organosilicon, Oxybenzene first
8 parts of acyl, 15 parts of carboxymethylcellulose calcium, 8 parts of alumina silicate, 16 parts of calcium silicates, 8 parts of aerosil, 9 parts of glass fibre, ammonia second
20 parts of 14 parts of base piperazine, 15 parts of IPD and cobalt naphthenate.
5. a kind of preparation method of automobile lampshade moulding material, it is characterised in that：Comprise the following steps：
1) by polymethyl methacrylate 50-60 parts, polystyrene 6-14 parts, polyarylsulfone (PAS) 15-20 parts, polycarbonate 18-25 parts,
Styrene-acrylonitrile 11-14 parts, transparent polyamide 8-12 parts, phenyltrimethoxysila,e 6-10 parts, acrylate 12-16 parts,
It is standby during organosilicon 9-10 parts is put into drying box；
2) regulating step 1) in drying box temperature be 48-50 DEG C, drying time be 12-16 minutes, it is standby；
3) by BP 4-8 parts, carboxymethylcellulose calcium 13-15 parts, alumina silicate 5-8 parts, calcium silicates 13-16 parts, gas phase two
Silica 7-8 parts, glass fibre 6-9 parts, aminoethyl piperazine 12-14 parts, IPD 10-15 parts and cobalt naphthenate 15-
It is standby in 20 parts of input reactors；
4) temperature of regulation reactor is 110-120 DEG C, and mixing speed is 400-500r/min, is reacted 5-10 minutes, then will step
Rapid 2) gained raw material is added in reactor, and regulation heating-up temperature is 150-160 DEG C, and mixing speed is kept for constant, the reaction time
It is 2-3, it is standby
5) by step 4) during gained raw material puts into autoclave, regulation air pressure is 12-15 times of atmospheric pressure, and standing 3-5 minutes is standby
With；
6) by step 5) gained raw material input injection machine in heating be in molten condition, inject mould.