CN106810274A - A kind of carbon zinc refractory material - Google Patents
A kind of carbon zinc refractory material Download PDFInfo
- Publication number
- CN106810274A CN106810274A CN201510870838.0A CN201510870838A CN106810274A CN 106810274 A CN106810274 A CN 106810274A CN 201510870838 A CN201510870838 A CN 201510870838A CN 106810274 A CN106810274 A CN 106810274A
- Authority
- CN
- China
- Prior art keywords
- parts
- carbon
- refractory material
- zinc
- bonding agents
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of carbon zinc refractory material, contain carbon 10-15 parts, carbon-containing bonding agents 3-5 parts, zinc powder 10-15 parts, silica sand 4-10 parts, aluminum oxide 5-10 parts, sodium metasilicate 3-5 parts, boric acid 0.5-1.5 parts, mineralizer 2-3 parts, agglutinant 0.5-1.5 parts., used as metallurgy refractory material, inoxidizability is strong, excellent fire retarding performance for carbon zinc refractory material of the invention.
Description
Technical field
The present invention relates to metallurgical refractory material, more particularly to a kind of carbon zinc refractory material.
Background technology
The conventional antioxidant of carbon containing refractory has aluminium powder, silica flour, boron carbide etc., but these are anti-oxidant
The addition of agent often causes the fusing point reduction of refractory material.
The content of the invention
In order to have the carbon containing refractory of inoxidizability and heat-resisting quantity advantage in providing concurrently, the present invention provide with
Lower technical scheme：
A kind of carbon zinc refractory material, contains carbon 10-15 parts, carbon-containing bonding agents 3-5 parts, zinc powder 10-15
Part, silica sand 4-10 parts, aluminum oxide 5-10 parts, sodium metasilicate 3-5 parts, boric acid 0.5-1.5 parts, mineralizer
2-3 parts, agglutinant 0.5-1.5 parts.
Further, the carbon is one or more in graphite, carbon black and needle coke.
Further, the carbon-containing bonding agents are pitch liquation, tar liquid, thermoplastic phenolic resin liquid
With one or more in the mixture of methenamine.
Further, 12 parts of carbon, 4 parts of carbon-containing bonding agents, 15 parts of zinc powder, 6 parts of silica sand, aluminum oxide 8 are contained
Part, 4 parts of sodium metasilicate, 1 part of boric acid, 2 parts of mineralizer, 1 part of agglutinant.
The beneficial effects of the present invention are：Used as metallurgy refractory material, inoxidizability is strong, fire resistance is excellent
It is different.
Specific embodiment
Embodiment 1,
A kind of carbon zinc refractory material, contains 10 parts of carbon, 3 parts of carbon-containing bonding agents, 10 parts of zinc powder, silica sand 4
Part, 5 parts of aluminum oxide, 3 parts of sodium metasilicate, 0.5 part of boric acid, 2 parts of mineralizer, 0.5 part of agglutinant
The carbon is graphite and carbon black.
The carbon-containing bonding agents are pitch liquation.
Embodiment 2,
A kind of carbon zinc refractory material, contains 12 parts of carbon, 4 parts of carbon-containing bonding agents, 12 parts of zinc powder, silica sand
6 parts, 8 parts of aluminum oxide, 4 parts of sodium metasilicate, 1 part of boric acid, 3 parts of mineralizer, 1 part of agglutinant.
The carbon is needle coke.
The carbon-containing bonding agents are tar liquid.
With above-mentioned according to desirable embodiment of the present invention as enlightenment, by above-mentioned description, related work people
Member can carry out various changes and amendments without departing from the scope of the technological thought of the present invention' completely.
The technical scope of this invention is not limited to the content on specification, it is necessary to according to right
To determine its technical scope.
Claims (4)
1. a kind of carbon zinc refractory material, it is characterised in that：Contain carbon 10-15 parts, carbon-containing bonding agents 3-5
Part, zinc powder 10-15 parts, silica sand 4-10 parts, aluminum oxide 5-10 parts, sodium metasilicate 3-5 parts, boron
It is sour 0.5-1.5 parts, mineralizer 2-3 parts, agglutinant 0.5-1.5 parts.
2. a kind of carbon zinc refractory material as claimed in claim 1, it is characterised in that：The carbon be graphite,
One or more in carbon black and needle coke.
3. a kind of carbon zinc refractory material as claimed in claim 1, it is characterised in that：The carbon-containing bonding agents
For in the mixture of pitch liquation, tar liquid, thermoplastic phenolic resin liquid and methenamine
One or more.
4. a kind of carbon zinc refractory material as claimed in claim 1, it is characterised in that：Containing 12 parts of carbon,
4 parts of carbon-containing bonding agents, 15 parts of zinc powder, 6 parts of silica sand, 8 parts of aluminum oxide, 4 parts of sodium metasilicate, boron
1 part of acid, 2 parts of mineralizer, 1 part of agglutinant.