CN106808750A - A kind of Compound Fabric of bacteriostatic antistatic - Google Patents

A kind of Compound Fabric of bacteriostatic antistatic Download PDF

Info

Publication number
CN106808750A
CN106808750A CN201611182648.0A CN201611182648A CN106808750A CN 106808750 A CN106808750 A CN 106808750A CN 201611182648 A CN201611182648 A CN 201611182648A CN 106808750 A CN106808750 A CN 106808750A
Authority
CN
China
Prior art keywords
layer
intermediate layer
compound fabric
surface layer
braiding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611182648.0A
Other languages
Chinese (zh)
Inventor
朱建林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201611182648.0A priority Critical patent/CN106808750A/en
Publication of CN106808750A publication Critical patent/CN106808750A/en
Pending legal-status Critical Current

Abstract

The present invention relates to Compound Fabric technical field, a kind of especially Compound Fabric of bacteriostatic antistatic, it includes superficial layer, intermediate layer and bottom surface layer, described superficial layer is covered in the upper surface in intermediate layer, bottom surface layer is covered in the lower surface in intermediate layer, wherein superficial layer is formed by the braiding of tossa yarn, and bottom surface layer is formed by the braiding of flax fiber yarn, and intermediate layer is formed by bamboo fiber garn braiding；Described superficial layer, it is bonded together by adhesive between intermediate layer and bottom surface layer.A kind of Compound Fabric of the bacteriostatic antistatic obtained by the present invention, by the control of rational structure design and thickness, the antistatic property and biocidal property of Compound Fabric can effectively be realized, superficial layer antistatic property is more, bottom surface layer and intermediate layer bacteriostasis property more, preferably improve the overall performance of Compound Fabric.

Description

A kind of Compound Fabric of bacteriostatic antistatic
Technical field
The present invention relates to Compound Fabric technical field, especially a kind of Compound Fabric of bacteriostatic antistatic.
Background technology
Current Compound Fabric passes through compound rear its thickness of multilayer fabric greatly, firm increased its in the case where thickness increases Degree；And using Compound Fabric its fastness is relied primarily at present, it is used primarily in some and the region such as often rubs against.But for function The technology of the Compound Fabric of property is in shortcoming state.
The content of the invention
There is provided a kind of rational in infrastructure the invention aims to solve the deficiency of above-mentioned technology, with preferable jail Also there is the Compound Fabric of the bacteriostatic antistatic of other functions in the case of degree.
In order to achieve the above object, the present invention designed by a kind of bacteriostatic antistatic Compound Fabric, it include superficial layer, in Interbed and bottom surface layer, described superficial layer are covered in the upper surface in intermediate layer, and bottom surface layer is covered in the lower surface in intermediate layer, wherein Superficial layer is formed by the braiding of tossa yarn, and bottom surface layer is formed by the braiding of flax fiber yarn, and intermediate layer is by bamboo fiber garn braiding Into；Described superficial layer, it is bonded together by adhesive between intermediate layer and bottom surface layer.
The thickness of described superficial layer is 0.4-0.8mm, and the thickness in intermediate layer is 0.5-0.8mm, and the thickness of bottom surface layer is 0.8-1.2mm, and thickness control after three is compound is in 2-2.5mm.
A kind of Compound Fabric of the bacteriostatic antistatic obtained by the present invention, by the control of rational structure design and thickness, The antistatic property and biocidal property of Compound Fabric can be effectively realized, more, bottom surface layer and intermediate layer press down superficial layer antistatic property Bacterium performance more, preferably improves the overall performance of Compound Fabric.
Brief description of the drawings
Fig. 1 is the structural representation of invention.
Specific embodiment
Below by embodiment combination accompanying drawing, the invention will be further described.
Embodiment 1：
As shown in figure 1, a kind of Compound Fabric of bacteriostatic antistatic of the present embodiment description, it includes superficial layer 1, intermediate layer 2 and bottom Surface layer 3, described superficial layer 1 is covered in the upper surface in intermediate layer 2, and bottom surface layer 3 is covered in the lower surface in intermediate layer 2, wherein table Surface layer 1 is formed by the braiding of tossa yarn, and bottom surface layer 3 is formed by the braiding of flax fiber yarn, and intermediate layer 2 is by bamboo fiber garn braiding Into；Described superficial layer 1, it is bonded together by adhesive between intermediate layer 2 and bottom surface layer 3.The thickness of described superficial layer 1 It is 0.4mm, the thickness in intermediate layer 2 is 0.5mm, and the thickness of bottom surface layer 3 is 1.2mm.
Embodiment 2：
As shown in figure 1, a kind of Compound Fabric of bacteriostatic antistatic of the present embodiment description, it includes superficial layer 1, intermediate layer 2 and bottom Surface layer 3, described superficial layer 1 is covered in the upper surface in intermediate layer 2, and bottom surface layer 3 is covered in the lower surface in intermediate layer 2, wherein table Surface layer 1 is formed by the braiding of tossa yarn, and bottom surface layer 3 is formed by the braiding of flax fiber yarn, and intermediate layer 2 is by bamboo fiber garn braiding Into；Described superficial layer 1, it is bonded together by adhesive between intermediate layer 2 and bottom surface layer 3.The thickness of described superficial layer 1 It is 0.8mm, the thickness in intermediate layer 2 is 0.8mm, and the thickness of bottom surface layer 3 is 0. mm.
Embodiment 3：
As shown in figure 1, a kind of Compound Fabric of bacteriostatic antistatic of the present embodiment description, it includes superficial layer 1, intermediate layer 2 and bottom Surface layer 3, described superficial layer 1 is covered in the upper surface in intermediate layer 2, and bottom surface layer 3 is covered in the lower surface in intermediate layer 2, wherein table Surface layer 1 is formed by the braiding of tossa yarn, and bottom surface layer 3 is formed by the braiding of flax fiber yarn, and intermediate layer 2 is by bamboo fiber garn braiding Into；Described superficial layer 1, it is bonded together by adhesive between intermediate layer 2 and bottom surface layer 3.The thickness of described superficial layer 1 It is 0.6mm, the thickness in intermediate layer 2 is 0.7mm, and the thickness of bottom surface layer 3 is 1mm.

Claims (2)

1. a kind of Compound Fabric of bacteriostatic antistatic, it is characterized in that：It includes superficial layer, intermediate layer and bottom surface layer, described surface Layer is covered in the upper surface in intermediate layer, and bottom surface layer is covered in the lower surface in intermediate layer, and wherein superficial layer is woven by tossa yarn Form, bottom surface layer is formed by the braiding of flax fiber yarn, intermediate layer is formed by bamboo fiber garn braiding；Described superficial layer, intermediate layer It is bonded together by adhesive and bottom surface layer between.
2. the Compound Fabric of a kind of bacteriostatic antistatic according to claim 1, it is characterized in that：The thickness of described superficial layer is 0.4-0.8mm, the thickness in intermediate layer is 0.5-0.8mm, the thickness after the thickness of bottom surface layer is 0.8-1.2mm, and three is compound Control is in 2-2.5mm.
CN201611182648.0A 2016-12-20 2016-12-20 A kind of Compound Fabric of bacteriostatic antistatic Pending CN106808750A (en)