CN106807120A - A kind of modified organic silicon defoamer and preparation method thereof - Google Patents
A kind of modified organic silicon defoamer and preparation method thereof Download PDFInfo
- Publication number
- CN106807120A CN106807120A CN201611234149.1A CN201611234149A CN106807120A CN 106807120 A CN106807120 A CN 106807120A CN 201611234149 A CN201611234149 A CN 201611234149A CN 106807120 A CN106807120 A CN 106807120A
- Authority
- CN
- China
- Prior art keywords
- organic silicon
- silicon defoamer
- modified organic
- preparation
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of modified organic silicon defoamer and preparation method thereof, and by weight percentage, modified organic silicon defoamer includes:Dimethicone 60 80%;White carbon 5 25%;Tween 1 5%;Poly- methyl polyoxyethylene ether 1 3%;AEO 1 4%;Sodium carboxymethylcellulose 5 25%;Sorbic acid 0.1 2%;Catalyst 0.1 0.3%.It is rapid that the present invention dissolves CMC in emulsion-type organic silicon defoamer preparation technology, dissolution time significantly shortens, and need not individually pre-dispersed dose, the stability of product can further be improved on original Process ba- sis using the method simultaneously, therefore the method greatlys save time, energy consumption and the cost of whole preparation technology, and improves product quality.
Description
Technical field
The present invention relates to defoamer production field, more particularly to a kind of modified organic silicon defoamer and its preparation side
Method.
Background technology
In order to ensure the quality of emulsion-type organic silicon defoamer, emulsify preparation technology in often need by using chemistry,
Machinery or other methods strengthen its stability.It is mainly by adding sodium carboxymethylcellulose in chemical method at present
(Abbreviation CMC)Realized with increasing the viscosity of system, but solubility of the CMC in water is not high, and course of dissolution is also quite very long,
Directly CMC is added to the water, occurs that a large amount of clear gum things are suspended in reactor surface after stirring, formed " flake ",
Constantly adhere to on wall and agitator simultaneously, cause feedstock portions to waste, even if the CMC in water also usually needs stirring
Could substantially completely dissolve within 4-6 hours.On the other hand the polysaccharide structures that it has, when temperature is raised, its solubility drops on the contrary
It is low, and emulsion-type organic silicon defoamer often needs to be carried out at a temperature of 60-75 DEG C in preparation process, thus more increases it
The degree of difficulty of water is dissolved in actual production, so as to cause course of dissolution slow, wastage of material further, the froth breaking is ultimately resulted in
The quality of agent is affected.
Therefore, prior art has yet to be improved and developed.
The content of the invention
In view of above-mentioned the deficiencies in the prior art, it is an object of the invention to provide a kind of modified organic silicon defoamer and its system
Preparation Method, it is intended to the problems such as solving the poor solubility property that organic silicon defoamer is present in the prior art, product stability difference.
A kind of modified organic silicon defoamer, wherein:By weight percentage, including:
Dimethicone 60-80%;
White carbon 5-25%;
Tween 1-5%;
Poly- methyl polyoxyethylene ether 1-3%;
AEO 1-4%;
Sodium carboxymethylcellulose 5-25%;
Sorbic acid 0.1-2%;
Catalyst 0.1-0.3%.
A kind of preparation method of modified organic silicon defoamer as described above, wherein:Sequentially added in 55-80 DEG C of water
Dimethicone, white carbon, tween, poly- methyl polyoxyethylene ether, AEO, sodium carboxymethylcellulose, sorb
Acid, catalyst, are stirred mixing, are finally cooled to normal temperature.
The present invention dissolves CMC rapidly in emulsion-type organic silicon defoamer preparation technology, and dissolution time is by original 4-6
Hour is reduced to 1-1.5 hour, and need not individually pre-dispersed dose, while can be in original Process ba- sis using the method
The upper stability for further improving product, therefore the method greatlys save time, energy consumption and the cost of whole preparation technology, and
And improve product quality.
Specific embodiment
The present invention provides a kind of non-organic silicon high-performance defoamer and preparation method thereof, to make the purpose of the present invention, technology
Scheme and effect are clearer, clear and definite, and the present invention is described in more detail below.It should be appreciated that described herein specific
Embodiment is only used to explain the present invention, is not intended to limit the present invention.
Embodiment 1:
A kind of modified organic silicon defoamer, wherein:By weight percentage, including:
Dimethicone 65%;
White carbon 15%;
Tween 5%;
Poly- methyl polyoxyethylene ether 2.5%;
AEO 3%;
Sodium carboxymethylcellulose 8%;
Sorbic acid 1.4%;
Catalyst 0.1%.
The present invention also provides a kind of preparation method of modified organic silicon defoamer as described in Example 1, wherein:At 55 DEG C
Water in sequentially add dimethicone, white carbon, tween, poly- methyl polyoxyethylene ether, AEO, carboxymethyl
Sodium cellulosate, sorbic acid, catalyst, are stirred mixing, are finally cooled to normal temperature.
Embodiment 2:
A kind of modified organic silicon defoamer, wherein:By weight percentage, including:
Dimethicone 70%;
White carbon 10%;
Tween 3%;
Poly- methyl polyoxyethylene ether 2%;
AEO 2%;
Sodium carboxymethylcellulose 12%;
Sorbic acid 0.7%;
Catalyst 0.3%.
The present invention also provides a kind of preparation method of modified organic silicon defoamer as described in Example 2, wherein:At 80 DEG C
Water in sequentially add dimethicone, white carbon, tween, poly- methyl polyoxyethylene ether, AEO, carboxymethyl
Sodium cellulosate, sorbic acid, catalyst, are stirred mixing, are finally cooled to normal temperature.
The present invention dissolves CMC rapidly in emulsion-type organic silicon defoamer preparation technology, and dissolution time is by original 4-6
Hour is reduced to 1-1.5 hours, and need not individually pre-dispersed dose, while can be on original Process ba- sis using the method
The stability of product is further improved, therefore the method greatlys save time, energy consumption and the cost of whole preparation technology, and
Improve product quality.
It should be appreciated that application of the invention is not limited to above-mentioned citing, and for those of ordinary skills, can
To be improved according to the above description or converted, all these modifications and variations should all belong to the guarantor of appended claims of the present invention
Shield scope.
Claims (2)
1. a kind of modified organic silicon defoamer, it is characterised in that:By weight percentage, including:
Dimethicone 60-80%;
White carbon 5-25%;
Tween 1-5%;
Poly- methyl polyoxyethylene ether 1-3%;
AEO 1-4%;
Sodium carboxymethylcellulose 5-25%;
Sorbic acid 0.1-2%;
Catalyst 0.1-0.3%.
2. a kind of preparation method of modified organic silicon defoamer as claimed in claim 1, it is characterised in that:At 55-80 DEG C
Dimethicone, white carbon, tween, poly- methyl polyoxyethylene ether, AEO, carboxymethyl are sequentially added in water fine
The plain sodium of dimension, sorbic acid, catalyst, are stirred mixing, are finally cooled to normal temperature.