CN106763159B - A kind of zinc-containing alloy bearing based on kollag - Google Patents
A kind of zinc-containing alloy bearing based on kollag Download PDFInfo
- Publication number
- CN106763159B CN106763159B CN201710033125.8A CN201710033125A CN106763159B CN 106763159 B CN106763159 B CN 106763159B CN 201710033125 A CN201710033125 A CN 201710033125A CN 106763159 B CN106763159 B CN 106763159B
- Authority
- CN
- China
- Prior art keywords
- self
- lubricating bearing
- inner ring
- ball
- outer ring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of zinc-containing alloy bearing based on kollag, including self-lubricating bearing outer ring, self-lubricating bearing inner ring, self-lubricating bearing ball and self-lubricating bearing cap;The medial surface of the self-lubricating bearing outer ring is provided with outer ring ball and slot is mounted, and the lateral surface of the self-lubricating bearing inner ring is provided with inner ring ball and slot is mounted;It is both provided with several kollag embedded holes on the self-lubricating bearing outer ring and the self-lubricating bearing inner ring, the axis of several kollag embedded holes is along the radial setting of the self-lubricating bearing outer ring and the self-lubricating bearing inner ring, slot is mounted around the outer ring ball for several kollag embedded holes and slot setting is mounted in the inner ring ball, and slot is mounted for several kollag embedded hole connections outer ring ball and slot is mounted in the inner ring ball.The present invention has the characteristics that easy to assembly, high mechanical strength, high lubricating effect.
Description
Technical field
The present invention relates to a kind of alloy cast article technical field, especially a kind of zinc-containing alloy based on kollag
Bearing.
Background technology
Self-lubricating bearing is by processing several aligned orderlies, size hole appropriate on bearing matrix, then to hole
Middle embedded solid lubricant, to replace tradition to rely on a kind of novel bearing of film lubrication bearing;It is with friction coefficient
It is low, service life is long, convenient for safeguard and the good advantage of wear-resisting property under low-speed heave-load.Self-lubricating bearing in the prior art
Employed in kollag deteriorate in an environment with high humidity comparatively fast, service life compared with serious curtailment in dry environment,
I.e. water-resistance is poor, and more uncertainty is brought to actual production operation.
Zinc-containing alloy is that manufactured a kind of High Strength Wear-Resistance Material after alloying element is added in pure zinc, mainly by aluminium member
The compositions such as element, copper, element silicon, magnesium elements, titanium elements, boron element and rare earth element;Since the solid solution of alloying element is strong
Change and second-phase strength acts on so that zinc-containing alloy not only improves intensity, but also is generated because the structure of various elements is different
Hard feature, can be widely used in mechanical industry to form unique not only wear-resisting but also oleophylic characteristic
For wear resistant appliances such as manufacture bearing shell, axle sleeve, sliding block and turbines;It the advantage is that:Mechanical drive part can be improved
Service life, keep mechanical processing precision;In the period that can be safeguarded with prolonged mechanical, improve production efficiency;To lubricating oil
Compatibility is good, and thermal conductivity height, rapid heat dissipation, seizure resistance are good.
Invention content
For overcome the deficiencies in the prior art, the present invention provides a kind of zinc-containing alloy bearing based on kollag,
With preferable water-resistance, and have the characteristics that easy to assembly, high mechanical strength, high lubricating effect, meets actual operation requirements.
The technical solution adopted by the present invention to solve the technical problems is:
A kind of zinc-containing alloy bearing based on kollag, including self-lubricating bearing outer ring and self-lubricating bearing inner ring,
The self-lubricating bearing outer ring and self-lubricating bearing inner ring coaxial package setting, and the self-lubricating bearing outer ring and described
Self-lubricating bearing ball, the self-lubricating bearing outer ring and the self-lubricating bearing inner ring are provided between self-lubricating bearing inner ring
Axial both ends be also respectively provided with the first self-lubricating bearing cap and the second self-lubricating bearing cap;The self-lubricating axis
The medial surface of bearing outer-ring, which is provided with, coordinates the outer ring ball of the self-lubricating bearing ball that slot, the self-lubricating bearing is mounted
The lateral surface of inner ring, which is provided with, coordinates the inner ring ball of the self-lubricating bearing ball that slot is mounted;Outside the self-lubricating bearing
Several kollag embedded holes are both provided on circle and the self-lubricating bearing inner ring, each kollag embedded hole
In be filled with kollag, the kollag includes the component of following mass percent:Graphite 41.0~43.0%,
The mineral base that the Viscosity Index of molybdenum disulfide 1.7~1.9%, calcium-sodium soap grease 7.5~10.0% and surplus is 115~125
Oil;The axis of several kollag embedded holes is along the self-lubricating bearing outer ring and the self-lubricating bearing inner ring
Radial to be arranged, slot is mounted around the outer ring ball in the kollag embedded hole on the self-lubricating bearing outer ring
Setting, and the kollag embedded hole on the self-lubricating bearing outer ring connects the outer ring ball and slot is mounted;
Slot setting, and institute is mounted around the inner ring ball in the kollag embedded hole on the self-lubricating bearing inner ring
It states the kollag embedded hole on self-lubricating bearing inner ring and connects the inner ring ball limit installation slot.
As a further improvement of the above technical scheme, the axially distributed setting of medial surface of the self-lubricating bearing outer ring
Outer ring ball described in having two groups is mounted slot, the outer ring ball limit described in two groups of the medial surface of the self-lubricating bearing outer ring
Outer ring ball limit protrusion is additionally provided between mounting groove;The lateral surface of the self-lubricating bearing inner ring is axially distributed to be provided with
Inner ring ball described in two groups is mounted slot, the lateral surface of the self-lubricating bearing inner ring inner ring ball limit peace described in two groups
Inner ring ball limit protrusion is additionally provided between tankage.
As a further improvement of the above technical scheme, the first self-lubricating bearing cap and second self-lubricating
Bearing package lid is both provided with the fixed support column of ball limit, and the fixed support column of ball limit is outside the self-lubricating bearing
The axial setting of circle and the self-lubricating bearing inner ring, and the fixed support column of ball limit is set to the self-lubricating bearing
Between outer ring and the self-lubricating bearing inner ring.
Compared with prior art, the beneficial effects of the invention are as follows:
A kind of zinc-containing alloy bearing based on kollag provided by the present invention, in conjunction with used kollag
It can be used under conditions of -20 DEG C~80 DEG C, and there is certain water-resistance in wet environment;In addition, the present invention provides
Bearing have the characteristics of easy to assembly, high mechanical strength, high lubricating effect, and friction coefficient is low, service life is long, convenient for dimension
Shield, wear-resisting property is good under low-speed heave-load, disclosure satisfy that actual operation requirements.
Description of the drawings
Present invention will be further explained below with reference to the attached drawings and examples.
Fig. 1 is a kind of structural schematic diagram of zinc-containing alloy bearing based on kollag of the present invention.
Specific implementation mode
Referring to Fig.1, Fig. 1 is the structural schematic diagram of a specific embodiment of the invention.
As shown in Figure 1, a kind of zinc-containing alloy bearing based on kollag, including self-lubricating bearing outer ring 10 and Zi Run
Plain besring inner ring 20, the self-lubricating bearing outer ring 10 and 20 coaxial package of self-lubricating bearing inner ring setting, and it is described from
It is provided with self-lubricating bearing ball 30, the self-lubricating bearing between lubrication bearing outer ring 10 and the self-lubricating bearing inner ring 20
Outer ring 10 and the axial both ends of the self-lubricating bearing inner ring 20 are also respectively provided with the first self-lubricating bearing cap 40 and
Two self-lubricating bearing caps 50;The medial surface of the self-lubricating bearing outer ring 10 is provided with the cooperation self-lubricating bearing ball
Slot 11 is mounted in 30 outer ring ball, and the lateral surface of the self-lubricating bearing inner ring 20 is provided with the cooperation self-lubricating bearing
Slot 21 is mounted in the inner ring ball of ball 30;It is all provided on the self-lubricating bearing outer ring 10 and the self-lubricating bearing inner ring 20
Several kollag embedded holes 12 are equipped with, kollag, institute are filled in each kollag embedded hole 12
State the component that kollag includes following mass percent:Graphite 41.0~43.0%, molybdenum disulfide 1.7~1.9%, calcium sodium base
The mineral base oil that lubricating grease 7.5~10.0% and the Viscosity Index of surplus are 115~125;Several kollags are embedding
Enter the axis in hole 12 along the radial setting of the self-lubricating bearing outer ring 10 and the self-lubricating bearing inner ring 20, the profit certainly
The kollag embedded hole 12 on slide-bar bearing outer-ring 10 is mounted slot 11 around the outer ring ball and is arranged, and described
The kollag embedded hole 12 on self-lubricating bearing outer ring 10 connects the outer ring ball and slot 11 is mounted;It is described from
The setting of slot 21, and institute is mounted around the inner ring ball in the kollag embedded hole 12 lubricated on bearing inner race 20
It states the kollag embedded hole 12 on self-lubricating bearing inner ring 20 and connects the inner ring ball limit installation slot 21.
It converts friction to rolling friction by using the self-lubricating bearing ball 30, to reduce the self-lubricating bearing
Friction between outer ring 10 and the self-lubricating bearing inner ring 20, and the kollag embedded hole 12 is set and is moistened by filling
Lubrication prescription further decreases frictional force;In addition, slot 11 is mounted around the outer ring ball in the kollag embedded hole 12
Slot 21 is mounted with the inner ring ball to be arranged, convenient for by the rolling of the self-lubricating bearing ball 30 by kollag
It evenly spreads out;Self-lubricating bearing ball 30 can ensure the self-lubricating bearing outer ring 10 described in axially distributed two groups of setting
With the stress equalization of the self-lubricating bearing inner ring 20.
Specifically, the medial surface of the self-lubricating bearing outer ring 10 is axially distributed be provided with two groups described in outer ring ball limit
The medial surface of position mounting groove 11, the self-lubricating bearing outer ring 10 is also set between slot 11 is mounted in outer ring ball described in two groups
It is equipped with outer ring ball limit protrusion 13;The lateral surface of the self-lubricating bearing inner ring 20 is axially distributed be provided with two groups described in
It encloses ball and is mounted slot 21, slot 21 is mounted in the lateral surface of the self-lubricating bearing inner ring 20 inner ring ball described in two groups
Between be additionally provided with inner ring ball limit protrusion 22.The first self-lubricating bearing cap 40 and second self-lubricating bearing
Cap 50 is both provided with the fixed support column 41 of ball limit, and the fixed support column 41 of ball limit is along the self-lubricating bearing
The axial setting of outer ring 10 and the self-lubricating bearing inner ring 20, and the fixed support column of ball limit 41 be set to it is described from
It lubricates between bearing outer ring 10 and the self-lubricating bearing inner ring 20.Above structure is convenient for self-lubricating bearing ball 30 described in two groups
Installation.
The preferable implementation of the present invention is illustrated above, certainly, the present invention can also use and above-mentioned implementation
The different form of mode, those skilled in the art under the premise of without prejudice to spirit of that invention made by equivalent transformation
Or corresponding change, it should all belong to the scope of protection of the present invention interior.
Claims (3)
1. a kind of zinc-containing alloy bearing based on kollag, it is characterised in that:Including self-lubricating bearing outer ring(10)With oneself
Lubricate bearing inner race(20), the self-lubricating bearing outer ring(10)With the self-lubricating bearing inner ring(20)Coaxial package is arranged,
And the self-lubricating bearing outer ring(10)With the self-lubricating bearing inner ring(20)Between be provided with self-lubricating bearing ball(30),
The self-lubricating bearing outer ring(10)With the self-lubricating bearing inner ring(20)Axial both ends be also respectively provided with first from moisten
Plain besring cap(40)With the second self-lubricating bearing cap(50);The self-lubricating bearing outer ring(10)Medial surface setting
There is the cooperation self-lubricating bearing ball(30)Outer ring ball slot is mounted(11), the self-lubricating bearing inner ring(20)'s
Lateral surface is provided with the cooperation self-lubricating bearing ball(30)Inner ring ball be mounted slot(21);The self-lubricating bearing
Outer ring(10)With the self-lubricating bearing inner ring(20)On be both provided with several kollag embedded holes(12), each described solid
Body lubricant embedded hole(12)In be filled with kollag, the kollag includes the group of following mass percent
Point:The Viscosity Index of graphite 41.0~43.0%, molybdenum disulfide 1.7~1.9%, calcium-sodium soap grease 7.5~10.0% and surplus
For 115~125 mineral base oil;Several kollag embedded holes(12)Axis outside the self-lubricating bearing
Circle(10)With the self-lubricating bearing inner ring(20)Radial setting, the self-lubricating bearing outer ring(10)On the solid profit
Lubrication prescription embedded hole(12)Slot is mounted around the outer ring ball(11)Setting, and the self-lubricating bearing outer ring(10)On
The kollag embedded hole(12)It connects the outer ring ball and slot is mounted(11);The self-lubricating bearing inner ring(20)
On the kollag embedded hole(12)Slot is mounted around the inner ring ball(21)Setting, and the self-lubricating axis
Hold inner ring(20)On the kollag embedded hole(12)It connects the inner ring ball and slot is mounted(21).
2. a kind of zinc-containing alloy bearing based on kollag according to claim 1, it is characterised in that:It is described to moisten certainly
Slide-bar bearing outer-ring(10)Medial surface it is axially distributed be provided with two groups described in outer ring ball slot is mounted(11), described from profit
Slide-bar bearing outer-ring(10)Medial surface outer ring ball described in two groups slot is mounted(11)Between be additionally provided with outer ring ball limit
Position protrusion(13);The self-lubricating bearing inner ring(20)Lateral surface it is axially distributed be provided with two groups described in inner ring ball limit
Mounting groove(21), the self-lubricating bearing inner ring(20)Lateral surface inner ring ball described in two groups slot is mounted(21)Between
It is additionally provided with inner ring ball limit protrusion(22).
3. a kind of zinc-containing alloy bearing based on kollag according to claim 2, it is characterised in that:Described first
Self-lubricating bearing cap(40)With the second self-lubricating bearing cap(50)It is both provided with the fixed support column of ball limit
(41), the fixed support column of ball limit(41)Along the self-lubricating bearing outer ring(10)With the self-lubricating bearing inner ring
(20)Axial setting, and the fixed support column of ball limit(41)It is set to the self-lubricating bearing outer ring(10)With it is described
Self-lubricating bearing inner ring(20)Between.