CN106758204A - A kind of arrangement antibacterial process of the knitting fabric of cap - Google Patents

A kind of arrangement antibacterial process of the knitting fabric of cap Download PDF

Info

Publication number
CN106758204A
CN106758204A CN201611040447.7A CN201611040447A CN106758204A CN 106758204 A CN106758204 A CN 106758204A CN 201611040447 A CN201611040447 A CN 201611040447A CN 106758204 A CN106758204 A CN 106758204A
Authority
CN
China
Prior art keywords
mass parts
knitting fabric
antibacterial
arrangement
fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611040447.7A
Other languages
Chinese (zh)
Inventor
张锦轩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong City Tongzhou District Ding Ding Hat Factory
Original Assignee
Nantong City Tongzhou District Ding Ding Hat Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong City Tongzhou District Ding Ding Hat Factory filed Critical Nantong City Tongzhou District Ding Ding Hat Factory
Priority to CN201611040447.7A priority Critical patent/CN106758204A/en
Publication of CN106758204A publication Critical patent/CN106758204A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of arrangement antibacterial process of the knitting fabric of cap, comprise the following steps：1~2 mass parts hydroxypropyl methyl cellulose, 1.2 mass parts guanidine bactericides, 1.8 mass parts polyoxyethylene polyamines, the mixing of 2.1 mass parts nanometric magnesium hydroxides are put into 20 mass parts deionized waters, is stirred；It is slowly added to 0.4 mass parts sorbitan fatty acid ester, 1.2 mass parts Herba Schizonepetae volatile oils, 2.5 mass parts THPCs, 1.8 mass parts aloe rheochrysins simultaneously again, continues to stir, it is uniform to being sufficiently mixed, dressing liquid is obtained；Then antimicrobial treatment is carried out.The postfinishing process of the knitting fabric of cap of the present invention, the fabric after its arrangement has excellent fire-retardant, antibacterial, crease-resistant, antistatic performance, and washability is strong, and can improve the anti-microbial property of fabric, and good anti-bacterial effect, use time is long.

Description

A kind of arrangement antibacterial process of the knitting fabric of cap
Technical field
The invention belongs to textile technology field, and in particular to a kind of arrangement antibacterial process of the knitting fabric of cap.
Background technology
With continuing to develop for society, the continuous improvement of technical merit, requirement of the people in terms of dressing is also constantly being carried The various performances of garment material are particularly had a new requirement by height, such as antistatic, antibacterial, antiviral, environmentally friendly, healthy. At present oneself is studied through there is a preliminary achievement for the antistatic property of garment material, but for its antibacterial, antiviral treatment Research is also in bud.
The content of the invention
Goal of the invention：The present invention is directed to deficiency of the prior art, propose it is a kind of with excellent fire-retardant, antibacterial, it is crease-resistant, Antistatic performance, and washability is strong, and the anti-microbial property of fabric, the arrangement of the knitting fabric of cap of good anti-bacterial effect can be improved Antibacterial process.
Technical scheme：A kind of arrangement antibacterial process of the knitting fabric of cap of the present invention, comprises the following steps：
1）1~2 mass parts hydroxypropyl methyl cellulose, 1.2 mass parts guanidines are put into 20 mass parts deionized waters to resist Microbial inoculum, 1.8 mass parts polyoxyethylene polyamines, the mixing of 2.1 mass parts nanometric magnesium hydroxides, stir；
2）It is slowly added to 0.4 mass parts sorbitan fatty acid ester, 1.2 mass parts Herba Schizonepetae volatile oils, 2.5 matter simultaneously again Amount part THPC, 1.8 mass parts aloe rheochrysins, continue to stir, uniform to being sufficiently mixed, and dressing liquid is obtained；
3）Fabric is padded treatment in dressing liquid, constant temperature drying after taking-up；
4）First time antimicrobial treatment：Knitting fabric dewater treatment is then immersed in nano-antibacterial liquid, is warming up to 40-50 DEG C, Immersion 1-2 hours, is then warming up to 60-80 DEG C again, soaks 2-3 hours；
5）Second antimicrobial treatment：Antibiotic finishing solution is coated in the surface of knitting fabric, then at a temperature of 60-80 DEG C Carry out drying forming, drying time is 2-4 minutes, and baking crosslinking is then carried out at a temperature of 100-150 DEG C, the time is 5-8 minutes；
6）Reduction cleaning treatment：Knitting fabric is put into cleaning solution and is cleaned；
7）Post processing：It is dehydrated successively, loose-drying, tentering shape and check.
Further, the nano-antibacterial liquid is made up of nano silver/silver chloride dispersion liquid and nano-silver ionic binding agent.
Further, the antibiotic finishing solution is mixed by bamboo vinegar, coating agent and additive.
Further, the step 6）In knitting fabric first pass through tenter dryer drying, then by heat setting machine dry Roasting crosslinking.
Further, the step 7）In cleaning solution ph values be 5-5.5, cleaning temperature be 40-55 DEG C, clearly The time is washed for 10-20 minutes.
Beneficial effect：The postfinishing process of all-cotton knitting fabric of the present invention, the fabric after its arrangement have it is excellent it is fire-retardant, Antibacterial, crease-resistant, antistatic performance, and washability is strong, and the anti-microbial property of fabric, good anti-bacterial effect, use time can be improved It is long.
Specific embodiment
With reference to specific embodiment, the invention will be further described：
Embodiment 1
A kind of after-finishing production process of all-cotton knitting fabric, comprises the following steps：
1）1 mass parts hydroxypropyl methyl cellulose, 1.2 mass parts guanidine antibacterials are put into 20 mass parts deionized waters Agent, 1.8 mass parts polyoxyethylene polyamines, the mixing of 2.1 mass parts nanometric magnesium hydroxides, stir；
2）It is slowly added to 0.4 mass parts sorbitan fatty acid ester, 1.2 mass parts Herba Schizonepetae volatile oils, 2.5 matter simultaneously again Amount part THPC, 1.8 mass parts aloe rheochrysins, continue to stir, uniform to being sufficiently mixed, and dressing liquid is obtained；
3）Fabric is padded treatment in dressing liquid, constant temperature drying after taking-up；
4）First time antimicrobial treatment：Knitting fabric dewater treatment is then immersed in nano-antibacterial liquid, is warming up to 40 DEG C, leaching Bubble 1 hour, is then warming up to 60 DEG C again, soaks 2 hours；
5）Second antimicrobial treatment：Antibiotic finishing solution is coated in the surface of knitting fabric, is then entered at a temperature of 60 DEG C Row drying forming, drying time is 2 minutes, and baking crosslinking is then carried out at a temperature of 100 DEG C, and the time is 5 minutes；
6）Reduction cleaning treatment：Knitting fabric is put into cleaning solution and is cleaned；
7）Post processing：It is dehydrated successively, loose-drying, tentering shape and check.
Further, the nano-antibacterial liquid is made up of nano silver/silver chloride dispersion liquid and nano-silver ionic binding agent.
Further, the antibiotic finishing solution is mixed by bamboo vinegar, coating agent and additive.
Further, the step 6）In knitting fabric first pass through tenter dryer drying, then by heat setting machine dry Roasting crosslinking.
Further, the step 7）In cleaning solution ph values be 5-5.5, cleaning temperature be 40 DEG C, cleaning Time is 10 minutes.
Embodiment 2
A kind of after-finishing production process of all-cotton knitting fabric, comprises the following steps：
1）2 mass parts hydroxypropyl methyl celluloses, 1.2 mass parts guanidine antibacterials are put into 20 mass parts deionized waters Agent, 1.8 mass parts polyoxyethylene polyamines, the mixing of 2.1 mass parts nanometric magnesium hydroxides, stir；
2）It is slowly added to 0.4 mass parts sorbitan fatty acid ester, 1.2 mass parts Herba Schizonepetae volatile oils, 2.5 matter simultaneously again Amount part THPC, 1.8 mass parts aloe rheochrysins, continue to stir, uniform to being sufficiently mixed, and dressing liquid is obtained；
3）Fabric is padded treatment in dressing liquid, constant temperature drying after taking-up；
4）First time antimicrobial treatment：Knitting fabric dewater treatment is then immersed in nano-antibacterial liquid, is warming up to 50 DEG C, leaching Bubble 2 hours, is then warming up to 80 DEG C again, soaks 3 hours；
5）Second antimicrobial treatment：Antibiotic finishing solution is coated in the surface of knitting fabric, is then entered at a temperature of 80 DEG C Row drying forming, drying time is 4 minutes, and baking crosslinking is then carried out at a temperature of 150 DEG C, and the time is 8 minutes；
6）Reduction cleaning treatment：Knitting fabric is put into cleaning solution and is cleaned；
7）Post processing：It is dehydrated successively, loose-drying, tentering shape and check.
Further, the nano-antibacterial liquid is made up of nano silver/silver chloride dispersion liquid and nano-silver ionic binding agent.
Further, the antibiotic finishing solution is mixed by bamboo vinegar, coating agent and additive.
Further, the step 6）In knitting fabric first pass through tenter dryer drying, then by heat setting machine dry Roasting crosslinking.
Further, the step 7）In cleaning solution ph values be 5-5.5, cleaning temperature be 55 DEG C, during cleaning Between be 20 minutes.
Embodiment 3
A kind of after-finishing production process of all-cotton knitting fabric, comprises the following steps：
1）1.5 mass parts hydroxypropyl methyl celluloses, 1.2 mass parts guanidine antibacterials are put into 20 mass parts deionized waters Agent, 1.8 mass parts polyoxyethylene polyamines, the mixing of 2.1 mass parts nanometric magnesium hydroxides, stir；
2）It is slowly added to 0.4 mass parts sorbitan fatty acid ester, 1.2 mass parts Herba Schizonepetae volatile oils, 2.5 matter simultaneously again Amount part THPC, 1.8 mass parts aloe rheochrysins, continue to stir, uniform to being sufficiently mixed, and dressing liquid is obtained；
3）Fabric is padded treatment in dressing liquid, constant temperature drying after taking-up；
4）First time antimicrobial treatment：Knitting fabric dewater treatment is then immersed in nano-antibacterial liquid, is warming up to 45 DEG C, leaching Bubble 1.5 hours, is then warming up to 70 DEG C again, soaks 2.5 hours；
5）Second antimicrobial treatment：Antibiotic finishing solution is coated in the surface of knitting fabric, is then entered at a temperature of 70 DEG C Row drying forming, drying time is 3 minutes, and baking crosslinking is then carried out at a temperature of 100-150 DEG C, and the time is 6 minutes ；
6）Reduction cleaning treatment：Knitting fabric is put into cleaning solution and is cleaned；
7）Post processing：It is dehydrated successively, loose-drying, tentering shape and check.
Further, the nano-antibacterial liquid is made up of nano silver/silver chloride dispersion liquid and nano-silver ionic binding agent.
Further, the antibiotic finishing solution is mixed by bamboo vinegar, coating agent and additive.
Further, the step 6）In knitting fabric first pass through tenter dryer drying, then by heat setting machine dry Roasting crosslinking.
Further, the step 7）In cleaning solution ph values be 5-5.5, cleaning temperature be 45 DEG C, cleaning Time is 15 minutes.
The above, is only presently preferred embodiments of the present invention, and any formal limitation is not made to the present invention, though So the present invention is disclosed above with preferred embodiment, but is not limited to the present invention, any to be familiar with this professional technology people Member, without departing from the scope of the present invention, when making a little change or modification using the technology contents of the disclosure above It is the Equivalent embodiments of equivalent variations, as long as being the content without departing from technical solution of the present invention, according to technical spirit of the invention Any simple modification, equivalent variations and the modification made to above example, still fall within the range of technical solution of the present invention.

Claims (5)

1. the arrangement antibacterial process of the knitting fabric of a kind of cap, it is characterised in that：Comprise the following steps：
1）1~2 mass parts hydroxypropyl methyl cellulose, 1.2 mass parts guanidines are put into 20 mass parts deionized waters to resist Microbial inoculum, 1.8 mass parts polyoxyethylene polyamines, the mixing of 2.1 mass parts nanometric magnesium hydroxides, stir；
2）It is slowly added to 0.4 mass parts sorbitan fatty acid ester, 1.2 mass parts Herba Schizonepetae volatile oils, 2.5 matter simultaneously again Amount part THPC, 1.8 mass parts aloe rheochrysins, continue to stir, uniform to being sufficiently mixed, and dressing liquid is obtained；
3）Fabric is padded treatment in dressing liquid, constant temperature drying after taking-up；
4）First time antimicrobial treatment：Knitting fabric dewater treatment is then immersed in nano-antibacterial liquid, is warming up to 40-50 DEG C, Immersion 1-2 hours, is then warming up to 60-80 DEG C again, soaks 2-3 hours；
5）Second antimicrobial treatment：Antibiotic finishing solution is coated in the surface of knitting fabric, then at a temperature of 60-80 DEG C Carry out drying forming, drying time is 2-4 minutes, and baking crosslinking is then carried out at a temperature of 100-150 DEG C, the time is 5-8 minutes；
6）Reduction cleaning treatment：Knitting fabric is put into cleaning solution and is cleaned；
7）Post processing：It is dehydrated successively, loose-drying, tentering shape and check.
2. the arrangement antibacterial process of the knitting fabric of a kind of cap according to claim 1, it is characterised in that：The nanometer resists Bacterium solution is made up of nano silver/silver chloride dispersion liquid and nano-silver ionic binding agent.
3. the arrangement antibacterial process of the knitting fabric of a kind of cap according to claim 1, it is characterised in that：The antibacterial is whole Reason liquid is mixed by bamboo vinegar, coating agent and additive.
4. the arrangement antibacterial process of the knitting fabric of a kind of cap according to claim 1, it is characterised in that：The step 6） In knitting fabric first pass through tenter dryer drying, then by heat setting machine bakee be crosslinked.
5. the arrangement antibacterial process of the knitting fabric of a kind of cap according to claim 1, it is characterised in that：The step 7） In cleaning solution ph values be 5-5.5, cleaning temperature be 40-55 DEG C, scavenging period be 10-20 minutes.
CN201611040447.7A 2016-11-24 2016-11-24 A kind of arrangement antibacterial process of the knitting fabric of cap Pending CN106758204A (en)