CN106757177A - A kind of preparation method of the anti-corrosion zinc cathode aluminum plate of band coating - Google Patents
A kind of preparation method of the anti-corrosion zinc cathode aluminum plate of band coating Download PDFInfo
- Publication number
- CN106757177A CN106757177A CN201611141607.7A CN201611141607A CN106757177A CN 106757177 A CN106757177 A CN 106757177A CN 201611141607 A CN201611141607 A CN 201611141607A CN 106757177 A CN106757177 A CN 106757177A
- Authority
- CN
- China
- Prior art keywords
- aluminum plate
- cathode aluminum
- zinc
- zinc cathode
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of preparation method of the anti-corrosion zinc cathode aluminum plate of band coating, common zinc cathode aluminum plate is surface-treated, obtain de-oiling, the clean zinc cathode aluminum plate of removal of impurities and surface, then well mixed liquid coating is sprayed on the perishable area of zinc cathode aluminum plate using spraying method, cured treatment, obtains the anti-corrosion zinc cathode aluminum plate of band coating.Present invention process investment is small, technological process is simple, low, pollution-free, extensive with prospect without particular/special requirement, energy consumption to equipment.
Description
Technical field
The present invention relates to non-ferrous zinc metallurgical technology and material antiseptic technical field, more particularly to a kind of band coating
Anti-corrosion zinc cathode aluminum plate preparation method.
Background technology
The minus plate of zinc by wet method is to roll plate with fine aluminium, and positive plate is with lead-silver alloy, lead-silver multicomponent alloy
Manufacture.In process of production, minus plate is submerged in solution of zinc sulfate in a cell with the plate face overwhelming majority of positive plate,
In the presence of direct current, respectively there is discharge depositing in negative electrode, anode, and the zinc in zinc sulfate is deposited the plate for being attached to minus plate
On face, total electrochemical reaction formula of its electrolytic deposition is：
ZnSO4+H2O+еZn+H2SO4+1/2O2
In process of production, beyond the exposed solution of zinc sulfate in a cell of zinc cathode aluminum plate and aluminium sheet two side ends part, by
Acted on F, Cl by sulfuric acid in for a long time, corroded especially severe.Although the negative electrode plate face being immersed in electrolytic cell solution of zinc sulfate
Substantially it is intact, but because of plate face neck and plate face two side ends seriously corroded, it is impossible to it is continuing with, causes minus plate service life short,
Increased production cost.As the reduction of zinc concentrate resource, electrolytic zinc raw material are increasingly complicated, fluorine/chlorine in solution of zinc sulfate is caused
Ion is exceeded, and is fluorine ion to minus plate corrosion impact the biggest factor, therefore causes minus plate extent of corrosion to aggravate.
Patent CN2887892Y is proposed and prevented with one layer of the plate neck surface painting of positive plate in the minus plate of zinc by wet method
The method of rotten layer extends the decay resistance of electrolytic zinc negative and positive machine plate, but is only coated with one layer of epoxy resin or heatproof preserving timber
Material, the extension life-span is partially short, average energy 60 days.
Patent CN201495302U discloses a kind of preparation method of electrolytic zinc anode plate, proposes using naked in pole plate upper end
Seemingly bar is installed at dew position on the electrolyte, and the anti-corrosion bar described in it is made of synthetic material, is installed in pole plate
Top will not be damaged because by the corrosion of severe gas, thus can extend the service life of minus plate.
Patent CN101781780B proposes a kind of method for improving corrosion resistance of cathode aluminum plate for zinc electrolysis, and it is used
Special ROLLING OIL, using conventional two rollers are irreversible, batch (-type) machine is rolled to aluminium, immediately using treatment silicon after rolling
Sour sodium carries out subsequent treatment, obtains the aluminium donkey-hide gelatin plate of surfacing, and larger, the comparatively dense oxide surface layer of generation thickness,
So as to improve its decay resistance.Its service life is set to improve more than three times.
Patent CN102953093A proposes a kind of Zinc electrolysis minus plate anticorrosive coat and preparation method thereof, and it uses spraying
Or the mode of blade coating coats anticorrosive paint, the anticorrosive paint at liquid level line to the position between conducting beam that the negative electrode principal columns of a hall easily corrodes
It is made up of bottom, intermediate layer and top layer.By the use of the corrosion-inhibiting coating, the service life of minus plate substantially can be extended 1/3
~1/2, the replacement frequency of aluminium sheet is reduced, so as to save the production cost of electrowinning zinc, improve productivity effect.
United States Patent (USP) US005498322A is proposed and is made zinc electrolysis minus plate with aluminium alloy, by add magnesium, silicon, iron,
The elements such as copper, zinc, so that cold rolling method is rolled to plate, so as to aluminium alloy plate is obtained, the aluminium sheet of gained improves anti-corruption
Corrosion energy, so as to extend the service life of negative electrode.Aluminium is the active metal of comparing, is easily corroded, and especially electrolytic zinc is used
Minus plate it is exposed outside liquid level line and aluminium sheet two side ends part, previously mentioned anti-corrosion method, all not enough clearly, operative employee
Skill is relative complex, and on how improving resistance to F performance of the zinc cathode aluminum plate to zinc electrolyte, reducing and removing F or zinc cost of material
Do not mentioned more.
In sum, the decay resistance of zinc cathode aluminum plate how is improved, increasing the service life of aluminium sheet, while raising zinc
Cathode aluminum plate is reduced and removes F or zinc cost of material to the resistance to F performances of zinc electrolyte, is the problem for needing further exploration.
The content of the invention
A kind of deficiency it is an object of the invention to be directed to prior art, there is provided the system of the anti-corrosion zinc cathode aluminum plate of band coating
Preparation Method.
The technical scheme is that：
A kind of preparation method of the anti-corrosion zinc cathode aluminum plate of band coating, comprises the following steps：
A, zinc cathode aluminum plate surface treatment procedure：Common zinc cathode aluminum plate is carried out into surface acid-washing, polishing, washing, ethanol washing
Operation treatment, obtains de-oiling, the clean zinc cathode aluminum plate of removal of impurities and surface；
B, coating mixed processes：By component silicone rubber, adjacent benzene polyester resin, phenol polyester resin and epoxy resin in stirring condition
Under be sufficiently mixed, obtain well mixed liquid coating；
C, spraying process：Liquid coating obtained by step B is sprayed on the perishable area of the zinc minus plate that processing of step A is crossed,
Obtain band coating zinc cathode aluminum plate；
D, curing process：Step C gained coating zinc cathode aluminum plates are carried out into gel, hardening and maturation process, band coating is obtained
Anti-corrosion zinc cathode aluminum plate；
As a further improvement on the present invention, ethanol washing can wash away zinc negative electrode in described zinc cathode aluminum plate surface treatment procedure
The obstinate greasy dirt of surface of aluminum plate, while the cleaning on surface can be ensured.
As a further improvement on the present invention, component silicone rubber, adjacent benzene polyester resin, benzene in described coating mixed processes
The mass percent of phenol polyester resin and epoxy resin is 3~8%：10~18%：30~45%：30~55%.
As a further improvement on the present invention, described curing process includes gel, three processes of hardening and curing, gel
Time is 20~50min；Firm time is 90~240min；Curing time is 4~8h.
As a further improvement on the present invention, gel and maturation process are carried out at room temperature in described curing process, firmly
It is 75~90 DEG C to change treatment temperature.
The beneficial effects of the present invention are：
The position spray on polymer anticorrosive coat perishable to zinc cathode aluminum plate, as shown in figure 1, to being exposed to solution or air originally
In perishable zinc cathode aluminum plate isolated, so as to reach the service life of extension zinc cathode aluminum plate；This zinc cathode aluminum plate table
Ethanol washing procedure is to borrow ethanol to be dissolved each other with some greasy dirts in the treatment process of face, so as to reach the effect of cleaning greasy dirt, together
When ethanol it is volatile, reached drying and the cleanliness factor on zinc cathode aluminum plate surface, it is ensured that the bonding of coating and zinc cathode aluminum plate
Dynamics.
The uniform mixing of the three kinds of polymeric coating layers for using, striking during shelling zinc can be withstood on hardness strength
Hit；In electrolytic process, acid steam penetrates into aluminum substrate surface by crackle, in the Surface Creation white acidic crystalline material of aluminium
Zinc sulfate is crystallized.With increasing that zinc sulfate is crystallized, cause polymeric coating layer to swell, polymeric coating layer is departed from aluminum substrate,
So as to lose to the effect of the corrosion protection of zinc minus plate, hydrophobic substance silicon rubber is added in the coating, it is to avoid zinc sulfate
Crystallization is produced in aluminium surface, so as to further improve the antiseptic property of coating with insulating properties, exactly this is with anticorrosive coat
Zinc cathode aluminum plate can contain dilute sulfuric acid or F in zinc electrolyte-Deng corrosion；Tested by multiple zinc electro-deposition, the height
Molecular coatings stable chemical nature in zinc electrodeposition process, will not be subject to sulfuric acid or F-Deng corrosion failure, while also will not be right
Electrodeposition process is impacted.
The preparation technology flow of the anti-corrosion zinc cathode aluminum plate of band coating of the present invention is simple, to equipment without particular/special requirement, operation
Simply, industrialized production is easily realized, the decay resistance of zinc cathode aluminum plate can be effectively improved, increase anti-F performances（Conventional zinc electricity
F contents are required in below 80mg/L in solution liquid, and by the improvement of zinc cathode aluminum plate, F contents can bring up in zinc electrolyte
More than 200mg/L）, so as to improve the structure of zinc raw material；The service life of zinc cathode aluminum plate is extended more than 90 days, reduce enterprise
The replacement frequency of minus plate, reduces zinc abstraction cost；The preparation method of the anti-corrosion zinc cathode aluminum plate of this band coating invests small, energy consumption
Low, pollution-free, three wastes are produced, environment-friendly；It is a kind of preparation side of economic, efficient band coating anti-corrosion zinc cathode aluminum plate
Method, application prospect is extensive.
Brief description of the drawings
Fig. 1 is process chart of the invention.
Specific embodiment
In order that technical problem solved by the invention, technical scheme and beneficial effect become more apparent, below in conjunction with
Embodiment, is described in further detail to the present invention.It should be appreciated that specific embodiment described herein is used only for explaining this
Invention, is not intended to limit the present invention, and the present invention includes the other embodiment in the range of its technological thought and and its deformation.
In the present invention, the surface cleanness sometimes according to minus plate also add the step such as washing or ethanol washing, or subtract
The step such as washing or ethanol washing is lacked, but as long as typical process flow is constant, then the present invention can also be applied.
A kind of preparation method of the anti-corrosion zinc cathode aluminum plate of band coating is the embodiment of the invention provides, Fig. 1 is referred to.
The present invention is further described below by specific embodiment.
Embodiment 1
Step A, zinc cathode aluminum plate surface treatment procedure：Common zinc cathode aluminum plate is carried out into surface acid-washing, polishing, washing, ethanol
Washing procedure treatment, obtains de-oiling, the clean zinc cathode aluminum plate of removal of impurities and surface；
Step B, coating mixed processes：It is silicon rubber, adjacent benzene polyester resin, phenol polyester resin and epoxy resin, matter by component
The coating that amount percentage is respectively 3%, 10%, 32%, 55% is sufficiently mixed under agitation, obtains well mixed liquid and applies
Material；
Step C, spraying process：Liquid coating obtained by step B is sprayed on the perishable of the zinc minus plate that processing of step A is crossed
Area, obtains band coating zinc cathode aluminum plate；
Step D, curing process：Step C gained coating zinc cathode aluminum plates are carried out the Gel Treatment of 20min at ambient temperature,
It is again the cure process of 240min through 75 DEG C of temperature, time, the maturation process of 4h is finally carried out at ambient temperature, obtains band and apply
The anti-corrosion zinc cathode aluminum plate of layer.
The anti-corrosion zinc cathode aluminum plate and conventional cathode plate of the band coating for preparing as minus plate, it is individually placed to same
Contrast Zinc electrolysis are carried out in electrolytic cell and in the different zinc electrolyte of F contents, obtains separating out zinc, as a result shown：Band coating it is anti-
The resistance to F abilities of rotten zinc cathode aluminum plate reach 240mg/L, and the resistance to F abilities of conventional cathode plate are only 100 mg/L；It is normal in F contents
Detected through decay resistance in zinc electrolyte, service life is extended 95 days.
Embodiment 2
Step A, zinc cathode aluminum plate surface treatment procedure：Common zinc cathode aluminum plate is carried out into surface acid-washing, polishing, washing, ethanol
Washing procedure treatment, obtains de-oiling, the clean zinc cathode aluminum plate of removal of impurities and surface；
Step B, coating mixed processes：It is silicon rubber, adjacent benzene polyester resin, phenol polyester resin and epoxy resin, matter by component
The coating that amount percentage is respectively 8%, 15%, 30%, 47% is sufficiently mixed under agitation, obtains well mixed liquid and applies
Material；
Step C, spraying process：Liquid coating obtained by step B is sprayed on the perishable of the zinc minus plate that processing of step A is crossed
Area, obtains band coating zinc cathode aluminum plate；
Step D, curing process：Step C gained coating zinc cathode aluminum plates are carried out the Gel Treatment of 50min at ambient temperature,
It is again the cure process of 90min through 90 DEG C of temperature, time, the maturation process of 8h is finally carried out at ambient temperature, obtains band and apply
The anti-corrosion zinc cathode aluminum plate of layer.
The anti-corrosion zinc cathode aluminum plate and conventional cathode plate of the band coating for preparing as minus plate, it is individually placed to same
Contrast Zinc electrolysis are carried out in electrolytic cell and in the different zinc electrolyte of F contents, obtains separating out zinc, as a result shown：Band coating it is anti-
The resistance to F abilities of rotten zinc cathode aluminum plate reach 280mg/L, and the resistance to F abilities of conventional cathode plate are only 90 mg/L；In the normal zinc of F contents
Detected through decay resistance in electrolyte, service life is extended 115 days.
Embodiment 3
Step A, zinc cathode aluminum plate surface treatment procedure：Common zinc cathode aluminum plate is carried out into surface acid-washing, polishing, washing, ethanol
Washing procedure treatment, obtains de-oiling, the clean zinc cathode aluminum plate of removal of impurities and surface；
Step B, coating mixed processes：It is silicon rubber, adjacent benzene polyester resin, phenol polyester resin and epoxy resin, matter by component
The coating that amount percentage is respectively 8%, 18%, 45%, 30% is sufficiently mixed under agitation, obtains well mixed liquid and applies
Material；
Step C, spraying process：Liquid coating obtained by step B is sprayed on the perishable of the zinc minus plate that processing of step A is crossed
Area, obtains band coating zinc cathode aluminum plate；
Step D, curing process：Step C gained coating zinc cathode aluminum plates are carried out the Gel Treatment of 45min at ambient temperature,
It is again the cure process of 180min through 85 DEG C of temperature, time, the maturation process of 6h is finally carried out at ambient temperature, obtains band and apply
The anti-corrosion zinc cathode aluminum plate of layer.
The anti-corrosion zinc cathode aluminum plate and conventional cathode plate of the band coating for preparing as minus plate, it is individually placed to same
Contrast Zinc electrolysis are carried out in electrolytic cell and in the different zinc electrolyte of F contents, obtains separating out zinc, as a result shown：Band coating it is anti-
The resistance to F abilities of rotten zinc cathode aluminum plate reach 310mg/L, and the resistance to F abilities of conventional cathode plate are only 85 mg/L；In the normal zinc of F contents
Detected through decay resistance in electrolyte, service life is extended 130 days.
Comparative example 1
Step A：Cathode plate surface treatment：Sandblasting is carried out to cathode plate surface by the way of dry spray first, is then with concentration
8% sodium hydroxide solution alkali cleaning, with the salpeter solution pickling that bulking value concentration is 20%；
Step B, spraying：In the weight ratio that the road thickness of cathode plate surface sprayed coating 2 is 200 μm of epoxy zinc chromate primers, paint and curing agent
It is 8：1, dried in the air dry oven that temperature is 60 DEG C, then spray the organic-silicon-modified resin painting that 2 road thickness are 400 μm
Material, it is 10 with the weight ratio of curing agent：1, solidify in the air dry oven that temperature is 60 DEG C, finally spraying 2 road thickness is
300 μm of polysiloxanes antisepsis finishing paint, it is 25 with the weight ratio of curing agent：2, then it is placed in the air dry oven that temperature is 60 DEG C
Middle solidification, obtains the Zinc electrolysis minus plate of corrosion-inhibiting coating；
The Zinc electrolysis minus plate and conventional cathode plate of the corrosion-inhibiting coating for preparing as Zinc electrolysis negative plate, it is individually placed to
Contrast Zinc electrolysis are carried out in same electrolytic cell and in the different zinc electrolyte of F contents, obtains separating out zinc, examined through decay resistance
Survey, when the electrodeposition time reaching 25 days, anticorrosive coat protuberance occurs because of zinc sulfate crystallization, and service life is extended 45 days, corrosion-resistant
Poor-performing.
Found from embodiment 1-3, the anti-corrosion zinc cathode aluminum plate of the band coating that the present invention is prepared has corrosion resistance
Can, the service life of minus plate is obviously prolonged more than 90 days；Resistance to F high-Corrosive power, the structure of zinc raw material can be changed, reduce
Raw material acquisition cost；The replacement frequency of minus plate is reduced, it is possible to decrease the production cost of zinc electrolysis, improves productivity effect.
Compared with comparative example 1, because of the addition of hydrophobic substance silicon rubber in this method, it is therefore prevented that zinc sulfate crystallization is sticked to
On coating and its surrounding, it is to avoid the protuberance of coating, and because of three kinds of high molecular mixing, improve the anti-percussion ability of coating with
Insulating properties, the service life of zinc cathode aluminum plate is obviously prolonged, while having resistance to F high-Corrosive power；The present invention is a kind of warp
Ji, the preparation method of the anti-corrosion zinc cathode aluminum plate of efficient band coating, application prospect are extensive.
Presently preferred embodiments of the present invention is the foregoing is only, is not intended to limit the invention, it is all in essence of the invention
Any modification, equivalent and improvement made within god and principle etc., should be included within the scope of the present invention.
Claims (4)
1. the preparation method of the anti-corrosion zinc cathode aluminum plate of a kind of band coating, it is characterised in that comprise the following steps：
A, zinc cathode aluminum plate surface treatment procedure：Common zinc cathode aluminum plate is carried out into surface acid-washing, polishing, washing, ethanol washing
Operation treatment, obtains de-oiling, the clean zinc cathode aluminum plate of removal of impurities and surface；
B, coating mixed processes：By component silicone rubber, adjacent benzene polyester resin, phenol polyester resin and epoxy resin in stirring condition
Under be sufficiently mixed, obtain well mixed liquid coating；
C, spraying process：Liquid coating obtained by step B is sprayed on the perishable area of the zinc minus plate that processing of step A is crossed,
Obtain band coating zinc cathode aluminum plate；
D, curing process：Step C gained coating zinc cathode aluminum plates are carried out into curing process, the anti-corrosion zinc negative electrode aluminium of band coating is obtained
Plate；
A kind of preparation method of the anti-corrosion zinc cathode aluminum plate of band coating according to claim 1, it is characterised in that：The step
In rapid A, the obstinate greasy dirt on zinc cathode aluminum plate surface can be washed away using ethanol washing, while the cleaning on surface can be ensured.
2. the preparation method of the anti-corrosion zinc cathode aluminum plate of a kind of band coating according to claim 1, it is characterised in that：It is described
In step B, the mass percent of the component silicone rubber, adjacent benzene polyester resin, phenol polyester resin and epoxy resin for 3~
8%：10~18%：30~45%：30~55%.
3. the preparation method of the anti-corrosion zinc cathode aluminum plate of a kind of band coating according to claim 1, it is characterised in that：It is described
In step D, curing process includes gel, three processes of hardening and curing, and gel time is 20~50min；Firm time is 90
~240min；Curing time is 4~8h.
4. the preparation method of the anti-corrosion zinc cathode aluminum plate of a kind of band coating according to claim 1 or 4, it is characterised in that：
In the step D, gel and maturation process are carried out at room temperature, and cure process temperature is 75~90 DEG C.