CN106756465A - A kind of heat-preserving hose antirust joint - Google Patents
A kind of heat-preserving hose antirust joint Download PDFInfo
- Publication number
- CN106756465A CN106756465A CN201611224748.5A CN201611224748A CN106756465A CN 106756465 A CN106756465 A CN 106756465A CN 201611224748 A CN201611224748 A CN 201611224748A CN 106756465 A CN106756465 A CN 106756465A
- Authority
- CN
- China
- Prior art keywords
- antirust
- heat
- joint
- oil
- preserving hose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heat-preserving hose antirust joint, specific preparation process is as follows:Prepare casting steel ingot, each chemical composition mass percent in its molten steel:2.32%≤C≤2.46%, 1.45%≤Si≤1.75%, 2.32%≤Mn≤2.68%, 0.008≤P≤0.018%, 0.35%≤Cr≤0.45%, 0.35%≤Co≤0.65%, 0.45%≤Mo≤0.55%, 0.1≤V≤0.12%, balance of Fe and inevitable impurity;Special alloy formula and anti-corrosion treatment process in manufacture craft of the present invention so that the rustless property of joint is especially prominent, while abrasion resistance properties are obviously improved.
Description
Technical field
The present invention relates to metal hose field, a kind of heat-preserving hose antirust joint is particularly belonged to.
Background technology
Heat-preserving hose is the important composition part in modern industrial equipment connecting pipeline.Heat-preserving hose product includes defeated oil suction
Sebific duct, steam sebific duct, sand blast hose, defeated chemical suction hose, food hose, oxygen rubber pipe and various special hoses etc..Extensively should
For industries such as machinery, chemical industry, oil, metallurgy, food.Because the liquid that the joint of heat-preserving hose passes through is more, easily causes and connect
The phenomenon of first-born rust.
The content of the invention
It is an object of the invention to provide a kind of heat-preserving hose antirust joint, in manufacture craft special alloy formula and
Anti-corrosion treatment process so that the rustless property of joint is especially prominent, while abrasion resistance properties are obviously improved.
Technical scheme is as follows:
A kind of heat-preserving hose antirust joint, specific preparation process is as follows:
1)Prepare casting steel ingot, each chemical composition mass percent in its molten steel:2.32%≤C≤2.46%, 1.45%≤Si≤
1.75%, 2.32%≤Mn≤2.68%, 0.008≤P≤0.018%, 0.35%≤Cr≤0.45%, 0.35%≤Co≤0.65%,
0.45%≤Mo≤0.55%, 0.1≤V≤0.12%, balance of Fe and inevitable impurity;
2)It is heat-treated after casting, casting steel ingot is heated to 750-780 DEG C and is incubated 0.4-0.7h, is forged
4-6 times, oil cooling is reheated to 400 DEG C -420 DEG C of temperature range and is incubated 0.5-0.8h to after 40 DEG C, then sprays cold
But process;
3)The part that forges after to heat treatment is machined, and processes joint design size, and pack carburizing is carried out after machining
Treatment, the steel ball after Carburization Treatment is put into antirust oil and is soaked, and temperature is 85-95 DEG C in oil, and soak time is 30-40min,
Antirust oil is made up of the raw material of following weight portion:Melamine cyanurate 20-25, epoxyoleic acid butyl ester 12-14, cyclohexanone 3-
5th, potassium peroxydisulfate 6-7, barium metaborate 2.5-4.5, methenamine 4.5-6.5, methylisobutylketone 3-5, deionized water 65-70.
The antirust oil is made up of the raw material of following weight portion:Melamine cyanurate 22, epoxyoleic acid butyl ester 13, ring
Hexanone 4, potassium peroxydisulfate 6.5, barium metaborate 3.5, methenamine 5.5, methylisobutylketone 4, deionized water 68.
Special alloy formula in manufacture craft of the invention:0.35%≤Cr≤0.45%, 0.35%≤Co≤0.65%, most
Joint is put into the anti-corrosion treatment process soaked in antirust solution afterwards so that the rustless property of joint is especially prominent, while wear-resistant
Performance is obviously improved.
Specific embodiment
A kind of heat-preserving hose antirust joint, specific preparation process is as follows:
1)Prepare casting steel ingot, each chemical composition mass percent in its molten steel:2.32%≤C≤2.46%, 1.45%≤Si≤
1.75%, 2.32%≤Mn≤2.68%, 0.008≤P≤0.018%, 0.35%≤Cr≤0.45%, 0.35%≤Co≤0.65%,
0.45%≤Mo≤0.55%, 0.1≤V≤0.12%, balance of Fe and inevitable impurity;
2)It is heat-treated after casting, casting steel ingot is heated to 750-780 DEG C and is incubated 0.4-0.7h, is forged
4-6 times, oil cooling is reheated to 400 DEG C -420 DEG C of temperature range and is incubated 0.5-0.8h to after 40 DEG C, then sprays cold
But process;
3)The part that forges after to heat treatment is machined, and processes joint design size, and pack carburizing is carried out after machining
Treatment, the steel ball after Carburization Treatment is put into antirust oil and is soaked, and temperature is 85-95 DEG C in oil, and soak time is 30-40min,
Antirust oil is made up of the raw material of following weight portion:Melamine cyanurate 22, epoxyoleic acid butyl ester 13, cyclohexanone 4, persulfuric acid
Potassium 6.5, barium metaborate 3.5, methenamine 5.5, methylisobutylketone 4, deionized water 68.
Obtained joint performance detection data is as follows in the embodiment of the present invention:Tensile strength sigma b (MPa):>=756, surrender
Intensity σ s (MPa):>=650, contraction percentage of area ψ (%):>=45, be put into humidity under 86-93% environment, surface-brightening without
Rusty stain.
Claims (2)
1. a kind of heat-preserving hose antirust joint, it is characterised in that specific preparation process is as follows:
1)Prepare casting steel ingot, each chemical composition mass percent in its molten steel:2.32%≤C≤2.46%, 1.45%≤Si≤
1.75%, 2.32%≤Mn≤2.68%, 0.008≤P≤0.018%, 0.35%≤Cr≤0.45%, 0.35%≤Co≤0.65%,
0.45%≤Mo≤0.55%, 0.1≤V≤0.12%, balance of Fe and inevitable impurity;
2)It is heat-treated after casting, casting steel ingot is heated to 750-780 DEG C and is incubated 0.4-0.7h, is forged
4-6 times, oil cooling is reheated to 400 DEG C -420 DEG C of temperature range and is incubated 0.5-0.8h to after 40 DEG C, then sprays cold
But process;
3)The part that forges after to heat treatment is machined, and processes joint design size, and pack carburizing is carried out after machining
Treatment, the steel ball after Carburization Treatment is put into antirust oil and is soaked, and temperature is 85-95 DEG C in oil, and soak time is 30-40min,
Antirust oil is made up of the raw material of following weight portion:Melamine cyanurate 20-25, epoxyoleic acid butyl ester 12-14, cyclohexanone 3-
5th, potassium peroxydisulfate 6-7, barium metaborate 2.5-4.5, methenamine 4.5-6.5, methylisobutylketone 3-5, deionized water 65-70.
2. heat-preserving hose according to claim 1 antirust joint, it is characterised in that the antirust oil is by following weight portion
Raw material composition:Melamine cyanurate 22, epoxyoleic acid butyl ester 13, cyclohexanone 4, potassium peroxydisulfate 6.5, barium metaborate 3.5,
Methenamine 5.5, methylisobutylketone 4, deionized water 68.