CN106753106A - Rapid curing luminescent characters ebonite and preparation method thereof - Google Patents
Rapid curing luminescent characters ebonite and preparation method thereof Download PDFInfo
- Publication number
- CN106753106A CN106753106A CN201611041910.XA CN201611041910A CN106753106A CN 106753106 A CN106753106 A CN 106753106A CN 201611041910 A CN201611041910 A CN 201611041910A CN 106753106 A CN106753106 A CN 106753106A
- Authority
- CN
- China
- Prior art keywords
- component
- epoxy resin
- parts
- ebonite
- luminescent characters
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of rapid curing luminescent characters ebonite and preparation method thereof, it presses 3 by component A and B component:1 ratio of weight and number is mixed, and wherein component A is made up of epoxy resin, AGE and anti-yellowing dose；B component is made up of modified firming agent, polyetheramine D230 and defoamer.The formula of the rapid curing luminescent characters ebonite that the present invention is provided rationally, curing rate can be effectively lifted by modified firming agent, shorten hardening time, 2~5 hours i.e. curable, and curing efficiency is high, and yellowing resistance is good, yellowing resistance is more longlasting, and light transmittance is higher, and profile pattern is good, smooth, not easy to crack, combination property is good, and properties of product are effectively ensured, increase the service life, and do not contain nonyl phenol, smell is smaller, it is harmless, use safer and environmental protection；The preparation method that the present invention is provided can quickly make rapid curing luminescent characters ebonite product, and processing step is succinct, it is easy to accomplish, productivity ratio is high.
Description
Technical field
The present invention relates to luminescent characters glue technical field, and in particular to a kind of rapid curing luminescent characters ebonite and its preparation side
Method.
Background technology
LED point luminous electron screens are used existing advertising signboard luminescent characters more and having carved the opaque luminescent characters two of shaping
The form of expression is planted, and it is to run into the pattern for having standard to be difficult to show the requirement of its specific design to put the maximum shortcoming of luminous electron screen,
And under not starting state, signboard is without visual and readable.And the opaque luminescent characters for having carved shaping can overcome the above
Shortcoming, meets the market demand.
The opaque luminescent characters for having carved shaping are mainly made up of base plate, light-emitting device and the part of opaque panel three, its
In opaque panel more by substrate, epoxy resin ebonite and epoxy resin flexible glue are constituted.The existing epoxy resin ebonite of in the market
There is the normal temperature cure time long（More than 10 hours, hardening time in winter was longer）；Chinese invention patent number 201310097278.0,
The entitled composition epoxy resin for being applied to luminescent characters discloses a kind of composition epoxy resin for being applied to luminescent characters, by
Following weight than component constitute：Epoxy resin 20~80%, curing agent 10~40%, accelerator 5~10%, diluent 4~
10%th, defoamer 0~0.5%；Although it can effectively shorten traditional hardening time, but still need 6~8 hours；But herein
On the basis of, its hardening time, yellowing resistance energy, light transmittance etc. still have the space of improvement；And it contains nonyl phenol, ties after testing
Fruit shows that nonyl phenol has endocrine disrupting, can promote Cells Proliferation of Human Breast Cancer, belongs to incretion interferent, carcinogenic substance.
Research shows, even if the concentration of this material discharge is very low, also great harmfulness.
The content of the invention
For above-mentioned deficiency, an object of the present invention is, there is provided one kind formula is reasonable, energy rapid curing, efficiency high,
And yellowing resistance is more longlasting, light transmittance is higher, and properties of product are effectively ensured, the rapid curing luminescent characters for increasing the service life are hard
Glue.
The second object of the present invention is, for above-mentioned deficiency, there is provided a kind of energy quick Fabrication goes out above-mentioned rapid curing hair
The preparation method of light word ebonite.
To achieve the above object, technical scheme provided by the present invention is：A kind of rapid curing luminescent characters ebonite, it is by A
Component and B component are 3 according to ratio of weight and number:1 ratio is mixed, wherein
Component A is made up of the component of following parts by weight：
7~9 parts of epoxy resin；
1~2 part of AGE；
Anti-yellowing dose 0.4~0.6 part；
B component is made up of the component of following parts by weight：
4~6 parts of modified firming agent；
3~5 parts of polyetheramine D230；
0.8~1.2 part of defoamer.
As a modification of the present invention, the epoxy resin include but is not limited to epoxy resin E51, epoxy resin E44,
Epoxy resin E54, epoxy resin 840S, epoxy resin CYD127, epoxy resin CYD115, epoxy resin 615, epoxy resin
One or more mixing in 616.
Used as a modification of the present invention, the AGE is preferably glycidol ethers diluent.
Used as a modification of the present invention, described anti-yellowing dose is preferably phosphite ester, can effectively delay macromolecular material
Oxidizing process, extends product service life, with good color and luster protective capability.
Used as a modification of the present invention, the modified firming agent is made up of the component of following parts by weight：
2~3 parts of polyetheramine D230；
1~3 part of IPDA (IPD)；
3~5 parts of epoxy resin E44.
Used as a modification of the present invention, the defoamer is preferably epoxy resin defoamer.
A kind of preparation method of rapid curing luminescent characters ebonite, it is comprised the following steps：
（1）Prepare component A：By 7~9 parts of epoxy resin, anti-yellowing dose of AGE and 0.4~0.6 of 1~2 part part phase at normal temperatures
Mixing, obtains component A after being sufficiently stirred for；
（2）Prepare B component：By 4~6 parts of modified firming agent, 3~5 parts of polyetheramine D230,0.8~1.2 part and 0.8~1.2
The defoamer of part is mixed at normal temperatures, and B component is obtained after being sufficiently stirred for；
（3）By ratio of weight and the number of copies it is at normal temperatures 3 by component A and B component:1 ratio is mixed, and rapid curing luminescent characters are obtained
Ebonite.
Used as a modification of the present invention, the modified firming agent is made of following steps：
The first step：The component of the following parts by weight of preparation：
2~3 parts of polyetheramine D230；
1~3 part of IPDA (IPD)；
3~5 parts of epoxy resin E44
Second step：Polyetheramine D230 and IPDA are put into agitator, the temperature of agitator is set as 45~55 degree, and speed setting is
700~1200 revs/min, mixing time is 100~150 minutes；
3rd step：Be 75~85 degree by the temperature setting of agitator after the completion for the treatment of second step, speed setting for 700~1200 turns/
Point, epoxy resin E44 is slowly then added dropwise to agitator, until completion of dropping, is obtained modified firming agent.
Beneficial effects of the present invention are：The formula of the rapid curing luminescent characters ebonite that the present invention is provided is reasonable, by modified
Curing agent can effectively lift curing rate, shorten hardening time, and 2~5 hours i.e. curable, and curing efficiency is high, and yellowing resistance
Good, yellowing resistance is more longlasting, and light transmittance is higher, and profile pattern is good, smooth, not easy to crack, and combination property is good, and product is effectively ensured
Moral character energy, increases the service life, and does not contain nonyl phenol, and smell is smaller, harmless, uses safer and environmental protection；
The preparation method that the present invention is provided can quickly make rapid curing luminescent characters ebonite product, and processing step is succinct, it is easy to accomplish,
Productivity ratio is high.
With reference to embodiment, the present invention is further described.
Specific embodiment
Embodiment 1, a kind of rapid curing luminescent characters ebonite that the present embodiment is provided, it is by component A and B component according to weight
Portion rate is 3:1 ratio is mixed, and wherein component A is made up of the component of following parts by weight：7.8 parts of epoxy resin；AGE
2 parts；Anti-yellowing dose 0.5 part；The epoxy resin include but is not limited to epoxy resin E51, epoxy resin E44, epoxy resin E54,
One kind in epoxy resin 840S, epoxy resin CYD127, epoxy resin CYD115, epoxy resin 615, epoxy resin 616 or
Various mixing.The epoxy resin is preferably epoxy resin E51 and epoxy resin E44 is mixed.In the present embodiment, the epoxy
Resin is mixed by the epoxy resin E44 of 0.8 part of epoxy resin E51 and 7 parts.
B component is made up of the component of following parts by weight：4 parts of modified firming agent；4 parts of polyetheramine D230；1 part of defoamer.
Preferably, the AGE is preferably glycidol ethers diluent.Described anti-yellowing dose is preferably phosphite ester, can have
Effect delays the oxidizing process of macromolecular material, extends product service life, with good color and luster protective capability.The defoamer
Preferably epoxy resin defoamer.
Specifically, the modified firming agent is made up of the component of following parts by weight：2 parts of polyetheramine D230；2 parts
IPDA (IPD)；5 parts of epoxy resin E44.
A kind of preparation method of rapid curing luminescent characters ebonite, it is comprised the following steps：
（1）Prepare component A：7.8 parts of epoxy resin, anti-yellowing dose of AGE and 0.5 of 2 parts part are mixed at normal temperatures, waits to fill
Component A is obtained after dividing stirring；Its epoxy resin is mixed by the epoxy resin E44 of 0.8 part of epoxy resin E51 and 7 parts.
（2）Prepare B component：By 4 parts of modified firming agent, 4 parts of polyetheramine D230 and 1 part of defoamer phase at normal temperatures
Mixing, obtains B component after being sufficiently stirred for；
（3）By ratio of weight and the number of copies it is at normal temperatures 3 by component A and B component:1 ratio is mixed, and rapid curing luminescent characters are obtained
Ebonite.
Specifically, the modified firming agent is made of following steps：
The first step：The component of the following parts by weight of preparation：2 parts of polyetheramine D230；2 parts of IPDA (IPD)；5 parts
Epoxy resin E44.
Second step：Polyetheramine D230 and IPDA are put into agitator, the temperature of agitator is set as 45~55 degree, preferably
50 degree；Speed setting is 700~1200 revs/min, preferably 800 revs/min；Mixing time is 100~150 minutes；Mixing time
It is 120 minutes.
3rd step：Treat after the completion of second step, be 75~85 degree by the temperature setting of agitator, preferably 80 degree, rotating speed sets
It is set to 700~1200 revs/min, preferably 800 revs/min, epoxy resin E44 is slowly then added dropwise to agitator, until is added dropwise
Finish, modified firming agent is obtained.The preparation method that the present invention is provided can quickly make rapid curing luminescent characters ebonite product, and work
Skill step is succinct, it is easy to accomplish, productivity ratio is high.
Embodiment 2, a kind of rapid curing luminescent characters ebonite and preparation method thereof that the present embodiment is provided, itself and embodiment 1
Essentially identical, distinctive points are the composition weight number ratio difference of component A and B component, specifically：Component A is by following weight portion
Several component compositions：7 parts of epoxy resin；1 part of AGE；Anti-yellowing dose 0.6 part；Wherein described epoxy resin is by 1 part of epoxy resin
E51 and 6 part of epoxy resin E44 is mixed.B component is made up of the component of following parts by weight：5 parts of modified firming agent；It is poly-
3 parts of ether amines D230；0.8 part of defoamer.The modified firming agent is made up of the component of following parts by weight：3 parts of polyetheramine
D230；1 part of IPDA (IPD)；3 parts of epoxy resin E44.
Embodiment 3, a kind of rapid curing luminescent characters ebonite and preparation method thereof that the present embodiment is provided, itself and embodiment 1
Essentially identical, distinctive points are the composition weight number ratio difference of component A and B component, specifically：Component A is by following weight portion
Several component compositions：9 parts of epoxy resin；1.6 parts of AGE；Anti-yellowing dose 0.4 part；Wherein described epoxy resin is by 1.2 parts of epoxy
Resin E51 and 7.8 parts of epoxy resin E44 are mixed.B component is made up of the component of following parts by weight：Modified firming agent 6
Part；5 parts of polyetheramine D230；1.2 parts of defoamer.The modified firming agent is made up of the component of following parts by weight：2.2 parts
Polyetheramine D230；3 parts of IPDA (IPD)；4 parts of epoxy resin E44.
Embodiment 4, a kind of rapid curing luminescent characters ebonite and preparation method thereof that the present embodiment is provided, itself and embodiment 1
Essentially identical, distinctive points are the composition weight number ratio difference of component A and B component, specifically：Component A is by following weight portion
Several component compositions：8.2 parts of epoxy resin；1.5 parts of AGE；Anti-yellowing dose 0.5 part；Wherein described epoxy resin is by 1.1 parts of ring
Oxygen tree fat E51 and 7.1 parts of epoxy resin E44 are mixed.B component is made up of the component of following parts by weight：It is modified solidified
5.6 parts of agent；3.2 parts of polyetheramine D230；1.1 parts of defoamer.The modified firming agent is made up of the component of following parts by weight：
2.6 parts of polyetheramine D230；1.5 parts of IPDA (IPD)；4.2 parts of epoxy resin E44.
Embodiment 5, a kind of rapid curing luminescent characters ebonite and preparation method thereof that the present embodiment is provided, itself and embodiment 1
Essentially identical, distinctive points are the composition weight number ratio difference of component A and B component, specifically：Component A is by following weight portion
Several component compositions：8.8 parts of epoxy resin；1.8 parts of AGE；Anti-yellowing dose 0.5 part；Wherein described epoxy resin is by 1.2 parts of ring
Oxygen tree fat E51 and 7.6 parts of epoxy resin E44 are mixed.B component is made up of the component of following parts by weight：It is modified solidified
4.8 parts of agent；4.6 parts of polyetheramine D230；1 part of defoamer.The modified firming agent is made up of the component of following parts by weight：2.7
The polyetheramine D230 of part；1.9 parts of IPDA (IPD)；3.5 parts of epoxy resin E44.
Above-described embodiment is only preferably implementation method of the invention, and the present invention can not enumerate out whole embodiment party
The technical scheme of one of formula, all use above-described embodiments, or the equivalent variations done according to above-described embodiment, protect in the present invention
In the range of shield.
The formula of the rapid curing luminescent characters ebonite that the present invention is provided rationally, solidification can be effectively lifted by modified firming agent
Speed, shortens hardening time, and 2~5 hours i.e. curable, and curing efficiency is high, and yellowing resistance is good, and yellowing resistance is more longlasting, thoroughly
Light rate is higher, and profile pattern is good, smooth, not easy to crack, and combination property is good, and properties of product are effectively ensured, and increases the service life,
And nonyl phenol is not contained, smell is smaller, harmless, use safer and environmental protection.
The announcement and teaching of book according to the above description, those skilled in the art in the invention can also be to above-mentioned embodiment party
Formula is changed and changed.Therefore, the invention is not limited in specific embodiment disclosed and described above, to of the invention
Some modifications and changes should also be as falling into scope of the claims of the invention.Although additionally, being used in this specification
Some specific terms, but these terms are merely for convenience of description, do not constitute any limitation to the present invention.Such as the present invention
Described in above-described embodiment, using other glue and preparation method thereof obtained from same or similarity method and component in this hair
In bright protection domain.
Claims (6)
1. a kind of rapid curing luminescent characters ebonite, it is characterised in that it is 3 according to ratio of weight and number by component A and B component:1
Ratio is mixed, wherein
Component A is made up of the component of following parts by weight：
7~9 parts of epoxy resin；
1~2 part of AGE；
Anti-yellowing dose 0.4~0.6 part；
B component is made up of the component of following parts by weight：
4~6 parts of modified firming agent；
3~5 parts of polyetheramine D230；
0.8~1.2 part of defoamer；
The modified firming agent is made up of the component of following parts by weight：
2~3 parts of polyetheramine D230；
1~3 part of IPDA；
3~5 parts of epoxy resin E44.
2. rapid curing luminescent characters ebonite according to claim 1, it is characterised in that：The epoxy resin includes but does not limit
In epoxy resin E51, epoxy resin E44, epoxy resin E54, epoxy resin 840S, epoxy resin CYD127, epoxy resin
One or more mixing in CYD115, epoxy resin 615, epoxy resin 616.
3. rapid curing luminescent characters ebonite according to claim 1, it is characterised in that：The AGE is glycidol ethers
Diluent.
4. rapid curing luminescent characters ebonite according to claim 1, it is characterised in that：Described anti-yellowing dose is phosphite ester.
5. rapid curing luminescent characters ebonite according to claim 1, it is characterised in that：The defoamer disappears for epoxy resin
Infusion.
6. a kind of preparation method of rapid curing luminescent characters ebonite, it is characterised in that：It is comprised the following steps：
（1）Prepare component A：By 7~9 parts of epoxy resin, anti-yellowing dose of AGE and 0.4~0.6 of 1~2 part part phase at normal temperatures
Mixing, obtains component A after being sufficiently stirred for；
（2）Prepare B component：By 4~6 parts of modified firming agent, 3~5 parts of polyetheramine D230 and 0.8~1.2 part of defoamer
Mix at normal temperatures, B component is obtained after being sufficiently stirred for；
（3）By ratio of weight and the number of copies it is at normal temperatures 3 by component A and B component:1 ratio is mixed, and rapid curing luminescent characters are obtained
Ebonite；
Wherein, the step（2）In modified firming agent be made of following steps：
The first step：The component of the following parts by weight of preparation：
2~3 parts of polyetheramine D230；
1~3 part of IPDA；
3~5 parts of epoxy resin E44
Second step：Polyetheramine D230 and IPDA are put into agitator, the temperature of agitator is set as 45~55 degree, and speed setting is
700~1200 revs/min, mixing time is 100~150 minutes；
3rd step：Be 75~85 degree by the temperature setting of agitator after the completion for the treatment of second step, speed setting for 700~1200 turns/
Point, epoxy resin E44 is slowly then added dropwise to agitator, until completion of dropping, is obtained modified firming agent.