CN106752420A - A kind of chlorosulfonation base ethene composite anticorrosion coating for adding organic Modification of Montmorillonite zinc powder - Google Patents
A kind of chlorosulfonation base ethene composite anticorrosion coating for adding organic Modification of Montmorillonite zinc powder Download PDFInfo
- Publication number
- CN106752420A CN106752420A CN201611010843.5A CN201611010843A CN106752420A CN 106752420 A CN106752420 A CN 106752420A CN 201611010843 A CN201611010843 A CN 201611010843A CN 106752420 A CN106752420 A CN 106752420A
- Authority
- CN
- China
- Prior art keywords
- zinc powder
- montmorillonite
- minutes
- concentration
- chlorosulfonation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of chlorosulfonation base ethene composite anticorrosion coating for adding organic Modification of Montmorillonite zinc powder, it is made from the following raw materials in parts by weight:Chlorosulfonated polyethylene latex 60 65, polychloroprene latex 35 40, polyoxyethylene aliphatic alcohol ether 78, appropriate deionized water, silane coupler KH5602.5 3, lanthana 23, cerium sesquioxide 1.5 2, concentration are for the salpeter solution of 65wt% is appropriate, concentration is ammonium bicarbonate soln, rutile type titanium white 10 12, methyl acrylate 1 1.5, calgon 0.8 1, flake zinc powder 67, organic montmorillonite 34, Ludox 8 9.5, the potassium hydroxide 1 1.2 of 50wt%.The paint machine excellent performance that the present invention is made, the surface adhesion forces such as metal are good, covering power, floating capacity and screening ability advantages, antiseptic property is excellent, and process is simple is easy to Industry Control, is worthy to be popularized.
Description
Technical field
Answered the present invention relates to technical field, more particularly to a kind of chlorosulfonation base ethene for adding organic Modification of Montmorillonite zinc powder
Close anticorrosive paint.
Background technology
Corrosion and corrosion protection is the industry distinct issues such as chemical industry, light industry, metallurgy, electric power, weaving, printing and dyeing, ship processed, building.
Caused damage because of corrosion every year huge, anticorrosive work is particularly important, chloro-sulfonated polyethylene anti-corrosive coating, with excellent
Good rotproofness, particularly splendid pliability, is used widely, once once deep by people in the industry along with inexpensive
The favor of scholar.With developing rapidly for modern industry level, propose that higher, tightened up to bear environment rotten to anticorrosive paint
The ability of erosion.The antiseptic property of the chlorosulfonated polythylene coatings of conventional formulation production is typically extremely difficult to require.Conventional chlorine sulphur
It is mostly solvent type to change polyethylene anti-corrosion coating, not only causes the waste of a large amount of solvents, and solvent for use is poisonous, Yi Hui
Hair, pollutes to environment, does not meet environmental requirement, and water paint has technique cleaning, advanced technology, low emission, low energy
Consumption, safe and harmless advantage, therefore, research hydrophilic chlorosulfonated polyethylene anticorrosive coating has great social benefit and economy
Benefit.
《The development of water chlorosulfonated polyethylene anti-corrosion coatings》With chlorosulfonated polyethylene latex and water-base epoxy tree in one text
Fat is compounded, and water-based anticorrosive paint is made by evaporating kettle removed under reduced pressure solvent, and the coating property being made is excellent, strong adaptability, is applied
Nonpoisonous and tasteless during brush, nonflammable, production process is simple, easy construction.Due to the addition of aqueous epoxy resins, painting is improve
Corrosion Protection is reduced while the adhesive force of material, it is impossible to be effectively improved the combination property of chlorosulfonated polyethylene, Gu need
Hydrophilic chlorosulfonated polyethylene coating is further modified, to meet the demand of industry development.
The content of the invention
The object of the invention is exactly to make up the defect of prior art, there is provided a kind of organic Modification of Montmorillonite zinc powder of addition
Chlorosulfonation base ethene composite anticorrosion coating.
The present invention is achieved by the following technical solutions:
A kind of chlorosulfonation base ethene composite anticorrosion coating for adding organic Modification of Montmorillonite zinc powder, by the raw material system of following weight portion
Into:Chlorosulfonated polyethylene latex 60-65, polychloroprene latex 35-40, polyoxyethylene aliphatic alcohol ether 7-8, appropriate deionized water, silane
Coupling agent KH5602.5-3, lanthana 2-3, cerium sesquioxide 1.5-2, concentration are for the salpeter solution of 65wt% is appropriate, concentration is
The ammonium bicarbonate soln of 50wt%, rutile type titanium white 10-12, methyl acrylate 1-1.5, calgon 0.8-1, scale
Shape zinc powder 6-7, organic montmorillonite 3-4, Ludox 8-9.5, potassium hydroxide 1-1.2.
A kind of chlorosulfonation base ethene composite anti-corrosive for adding organic Modification of Montmorillonite zinc powder is applied according to claims 1
Material, is prepared from by following specific method:
(1)Chlorosulfonated polyethylene latex is mixed with polychloroprene latex, in input emulsifier, is subsequently adding, polyoxyethylene fatty alcohol
The deionized water of ether and total amount equivalent, stirs to form primary emulsion with the speed of 200-300 turns/part, then is sent to rotation
In evaporator, gone out with 70-80 revs/min of speed rotary evaporation in the case where vacuum is 0.01-0.03MPa, 65-70 DEG C of temperature organic
Solvent, obtains mixing latex;
(2)Lanthana, cerium sesquioxide are mixed, the 2-2.5 times of concentration measured is added in the salpeter solution of 65wt%, stirring is extremely
It is completely dissolved, is subsequently adding the concentration with nitric acid equivalent for the ammonium bicarbonate soln of 50wt% carries out precipitation reaction, it is heavy by what is obtained
Starch is filtered, and is put into after being cleaned with deionized water in vacuum drying chamber with 60-70 DEG C of drying, calcination 60-90 minutes after taking-up, is obtained
To modified RE;
(3)It is stand-by by potassium hydroxide solution is formed in 6-7 times of deionized water measured of potassium hydroxide solution, then Ludox is heated
To 60-70 DEG C, constant temperature adds above-mentioned potassium hydroxide solution while stirring after stirring 30-40 minutes, with 300-400 revs/min of speed
Degree stirring adds flake zinc powder, organic montmorillonite after 10-15 minutes, continues to stir 40-50 minutes under constant temperature, obtains mixing slurry
Material;
(4)Silane coupler KH560 is dissolved in the 4-5 times of deionized water measured, step is subsequently adding(2)The product for obtaining, surpasses
Sound adds step after disperseing 30-40 minutes(1)、(3)The product for obtaining, dispersion adds remaining residual components after 10-15 minutes, uses
Mechanical agitation 2-3 hours, it is finally putting on grinder and grinds, crosses 400 mesh sieves and obtain final product.
It is an advantage of the invention that:The present invention uses water prescription, and safety non-toxic is environmentally friendly, first with chlorosulfonation
Polyethylene latex carries out composite modified with polychloroprene latex, improves fire-retardant, the ageing-resistant performance of coating;By silane coupler
KH560 and modified RE compounding are added in coating, excellent with coating system compatibility performance, and rare earth ion numerous empty rail
Road can catch unstable free radical, cause it to lose activity, and be conducive to stabilization, improve corrosion resistance and resistance to ag(e)ing,
Rare earth ion can also form coordinate bond with the hydroxyl in coating molecule, methylol isopolarity group simultaneously, coating is produced coordination
Polymerization drying, so as to improve the quick-drying of paint film.
The present invention is mixed the compositions such as Ludox and organo montmorillonite by a series of reaction, then is answered with flake zinc powder
Match somebody with somebody, the moisture dispersibility of zinc powder can be improved, so as to improve the mechanical strength of coating and the slickness of film;Present invention system
Into paint machine excellent performance, the surface adhesion forces such as metal are good, covering power, floating capacity and screening ability advantage are prominent
Go out, antiseptic property is excellent, process is simple is easy to Industry Control, be worthy to be popularized.
Specific embodiment
A kind of chlorosulfonation base ethene composite anticorrosion coating for adding organic Modification of Montmorillonite zinc powder, by following weight portion(It is public
Jin)Raw material be made:Chlorosulfonated polyethylene latex 60, polychloroprene latex 35, polyoxyethylene aliphatic alcohol ether 7, appropriate deionized water, silicon
Alkane coupling agent KH5602.5, lanthana 2, cerium sesquioxide 1.5, concentration are for the salpeter solution of 65wt% is appropriate, concentration is 50wt%
Ammonium bicarbonate soln, rutile type titanium white 10, methyl acrylate 1, calgon 0.8, flake zinc powder 6, You Jimeng
De- stone 3, Ludox 8, potassium hydroxide 1.
A kind of chlorosulfonation base ethene composite anti-corrosive for adding organic Modification of Montmorillonite zinc powder is applied according to claims 1
Material, is prepared from by following specific method:
(1)Chlorosulfonated polyethylene latex is mixed with polychloroprene latex, in input emulsifier, is subsequently adding, polyoxyethylene fatty alcohol
The deionized water of ether and total amount equivalent, stirs to form primary emulsion, then be sent to rotary evaporation with the speed of 200 turns/part
In device, organic solvent is gone out with 70 revs/min of speed rotary evaporation in the case where vacuum is 0.01MPa, 65 DEG C of temperature, obtain epoxy glue
Breast;
(2)Lanthana, cerium sesquioxide are mixed, 2 times of concentration of amount is added in the salpeter solution of 65wt%, stirring is to complete
Dissolving, is subsequently adding the concentration with nitric acid equivalent for the ammonium bicarbonate soln of 50wt% carries out precipitation reaction, the sediment that will be obtained
Filtering, is put into vacuum drying chamber with 60 DEG C of drying after being cleaned with deionized water, and calcination 60 minutes after taking-up obtain modified dilute
Soil;
(3)It is stand-by by potassium hydroxide solution is formed in 6 times of deionized waters of amount of potassium hydroxide solution, then Ludox is heated to
60 DEG C, constant temperature adds above-mentioned potassium hydroxide solution while stirring after stirring 30 minutes, is stirred 10 minutes with 300 revs/min of speed
Flake zinc powder, organic montmorillonite are added afterwards, continues to stir 40 minutes under constant temperature, obtain mixed slurry;
(4)Silane coupler KH560 is dissolved in 4 times of deionized waters of amount, step is subsequently adding(2)The product for obtaining, ultrasound
Dispersion adds step after 30 minutes(1)、(3)The product for obtaining, dispersion adds remaining residual components after 10 minutes, uses mechanical agitation
2 hours, it is finally putting on grinder and grinds, crosses 400 mesh sieves and obtain final product.
Coating property to the present embodiment is tested, and fineness is less than 50 μm, and adhesive force reaches 1 grade, acid resistance (10% sulphur
Acid) alkali resistance (10% NaOH) salt water resistance 7 days is non-foaming, do not fall off, non-corrosive.
Claims (2)
1. a kind of chlorosulfonation base ethene composite anticorrosion coating for adding organic Modification of Montmorillonite zinc powder, it is characterised in that by following
The raw material of weight portion is made:Chlorosulfonated polyethylene latex 60-65, polychloroprene latex 35-40, polyoxyethylene aliphatic alcohol ether 7-8, go from
Sub- appropriate amount of water, silane coupler KH5602.5-3, lanthana 2-3, cerium sesquioxide 1.5-2, concentration are the salpeter solution of 65wt%
In right amount, concentration is ammonium bicarbonate soln, rutile type titanium white 10-12, methyl acrylate 1-1.5, the calgon of 50wt%
0.8-1, flake zinc powder 6-7, organic montmorillonite 3-4, Ludox 8-9.5, potassium hydroxide 1-1.2.
2. a kind of chlorosulfonation base ethene composite anti-corrosive for adding organic Modification of Montmorillonite zinc powder is applied according to claims 1
Material, it is characterised in that be prepared from by following specific method:
(1)Chlorosulfonated polyethylene latex is mixed with polychloroprene latex, in input emulsifier, is subsequently adding, polyoxyethylene fatty alcohol
The deionized water of ether and total amount equivalent, stirs to form primary emulsion with the speed of 200-300 turns/part, then is sent to rotation
In evaporator, gone out with 70-80 revs/min of speed rotary evaporation in the case where vacuum is 0.01-0.03MPa, 65-70 DEG C of temperature organic
Solvent, obtains mixing latex;
(2)Lanthana, cerium sesquioxide are mixed, the 2-2.5 times of concentration measured is added in the salpeter solution of 65wt%, stirring is extremely
It is completely dissolved, is subsequently adding the concentration with nitric acid equivalent for the ammonium bicarbonate soln of 50wt% carries out precipitation reaction, it is heavy by what is obtained
Starch is filtered, and is put into after being cleaned with deionized water in vacuum drying chamber with 60-70 DEG C of drying, calcination 60-90 minutes after taking-up, is obtained
To modified RE;
(3)It is stand-by by potassium hydroxide solution is formed in 6-7 times of deionized water measured of potassium hydroxide solution, then Ludox is heated
To 60-70 DEG C, constant temperature adds above-mentioned potassium hydroxide solution while stirring after stirring 30-40 minutes, with 300-400 revs/min of speed
Degree stirring adds flake zinc powder, organic montmorillonite after 10-15 minutes, continues to stir 40-50 minutes under constant temperature, obtains mixing slurry
Material;
(4)Silane coupler KH560 is dissolved in the 4-5 times of deionized water measured, step is subsequently adding(2)The product for obtaining, surpasses
Sound adds step after disperseing 30-40 minutes(1)、(3)The product for obtaining, dispersion adds remaining residual components after 10-15 minutes, uses
Mechanical agitation 2-3 hours, it is finally putting on grinder and grinds, crosses 400 mesh sieves and obtain final product.