CN106751338A - A kind of lower shrinkage, high thermal stability impact-resistant polystyrene material and preparation method thereof - Google Patents
A kind of lower shrinkage, high thermal stability impact-resistant polystyrene material and preparation method thereof Download PDFInfo
- Publication number
- CN106751338A CN106751338A CN201611212442.8A CN201611212442A CN106751338A CN 106751338 A CN106751338 A CN 106751338A CN 201611212442 A CN201611212442 A CN 201611212442A CN 106751338 A CN106751338 A CN 106751338A
- Authority
- CN
- China
- Prior art keywords
- thermal stability
- impact
- high thermal
- lower shrinkage
- resistant polystyrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of lower shrinkage, high thermal stability impact-resistant polystyrene material and preparation method thereof, belongs to technical field of polymer materials, its component for including following weight portion:60 85 parts of high-impact polystyrene resin, 5 10 parts of toughener, 10 30 parts of reinforcing agent of filling, 0.2 0.5 parts of antioxidant, 0.2 0.5 parts of lubricant.The present invention is in lower shrinkage, high thermal stability impact-resistant polystyrene materials process is prepared by adding toughener, filling reinforcing agent, antioxidant and lubricant, obtained polystyrene material shrinkage factor is within 0.5%, the dimensional stability having had at a higher temperature, has expanded the temperature in use scope of material and increased HIPS dimensional stabilitys at relatively high temperatures;Lower shrinkage, high thermal stability impact-resistant polystyrene material prepared by the present invention, according to the examination criteria of the industry, notch impact strength is more than 9KJ/m2, bending modulus be more than 2000MPa, show good toughness.
Description
Technical field
The invention belongs to technical field of polymer materials, specifically a kind of lower shrinkage, high thermal stability impact-resistant polystyrene
Material and preparation method thereof.
Background technology
High impact polystyrene (HIPS) is the two-phase mixture being mutually made up of with continuous polystyrene the rubber phase of elastomer
Based polymer, with excellent mechanical performance and processing characteristics, price is relatively low, with cost performance higher, is widely used in TV
The large scale product such as shell and air-conditioning inner structural members after machine.HIPS is non-crystalline material, and glass transition temperature is heated than relatively low
In the case of be easily deformed, influence the assembling of product and follow-up be continuing with.The present invention is with impact-resistant polystyrene as matrix
Resin, talcum powder is reinforcing filler, and the addition of talcum powder causes that HIPS segments are moved when being heated and hindered by certain, from
And improve the thermal stability of HIPS.
The content of the invention
It is an object of the invention to provide a kind of lower shrinkage, high thermal stability impact-resistant polystyrene material and its preparation side
Method, it is possible to reduce deformations of the high-impact HIPS when being heated, it is ensured that the assembling of product and use.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of lower shrinkage, high thermal stability impact-resistant polystyrene material, including following weight portion component:
Further scheme, the high-impact polystyrene resin refers to the melt flow rate (MFR) under the conditions of 200 DEG C/5kg
It is the polystyrene resin of 2-10g/10min.
Further scheme, the toughener is styrene-butadiene-polystyrene block copolymer SBS or polyphenyl second
Alkene-Ethylene/Butylene-polystyrene triblock copolymer SEBS.
Further scheme, the filling reinforcing agent is talcum powder, and the particle diameter for filling reinforcing agent is 1-10 μm.
Further scheme, the antioxidant is four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol esters
With three [2.4- di-tert-butyl-phenyls] phosphite esters with 1:The weight of 1-2 is formed than compounding.
Further scheme, the lubricant is the one kind in calcium stearate, Tissuemat E, ethylene bis stearamide, silicone
Or several mixtures.
It is another object of the present invention to provide a kind of lower shrinkage, high thermal stability impact-resistant polystyrene material, system
Preparation Method, comprises the following steps:
(1) high-impact polystyrene resin, toughener, filling reinforcing agent, antioxidant and profit are weighed by above-mentioned part by weight
Lubrication prescription, releases after mixing 5-10min in high-speed mixer together;
(2) above-mentioned mixed material addition double screw extruder is carried out into melting mixing, is extruded, cooling, pelletizing, drying are
Lower shrinkage of the invention, high thermal stability material are obtained, the temperature range that each section of extruder is 170-210 DEG C.
Beneficial effects of the present invention:
(1) present invention in lower shrinkage, high thermal stability impact-resistant polystyrene materials process is prepared by add toughener,
Filling reinforcing agent, antioxidant and lubricant, obtained polystyrene material shrinkage factor within 0.5%, at a higher temperature
With good dimensional stability, the temperature in use scope of material is expanded and increased HIPS dimensionally stables at relatively high temperatures
Property;
(2) lower shrinkage, high thermal stability impact-resistant polystyrene material prepared by the present invention, the detection mark according to the industry
Standard, notch impact strength is more than 9KJ/m2, bending modulus be more than 2000MPa, show good toughness.
Specific embodiment
The present invention is described in further detail with reference to specific embodiment.
The all raw materials of the present invention are commercially available.
Toughener is styrene-butadiene-polystyrene block copolymer SBS or polystyrene-second in embodiment 1-5
Alkene-butylene-polystyrene triblock copolymer SEBS;Filling reinforcing agent is the talcum powder that particle diameter is 1-10 μm;Antioxidant is four
[β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester and three [2.4- di-tert-butyl-phenyls] phosphite esters are with 1:
The weight of 1-2 is formed than compounding;Lubricant be calcium stearate, Tissuemat E, ethylene bis stearamide, silicone in one kind or
Several mixtures.
Lower shrinkage, high thermal stability impact-resistant polystyrene material in embodiment 1-5 be the raw material shown in table 1 by weight
Part composition, specific preparation method is comprised the following steps:
(1) high-impact polystyrene resin, toughener, filling reinforcing agent, antioxidant and profit are weighed by above-mentioned part by weight
Lubrication prescription, releases after mixing 5-10min in high-speed mixer together;
(2) above-mentioned mixed material addition double screw extruder is carried out into melting mixing, is extruded, cooling, pelletizing, drying are
Lower shrinkage of the invention, high thermal stability material are obtained, the temperature range that each section of extruder is 170-210 DEG C.
In addition, preparing comparative example by the preparation method and raw material of embodiment 1, it differs only in and is not added with toughener and filling
Reinforcing agent.
Such as it is of the invention prepare component in add scratch resistance liniment, antistatic additive, colouring agent function additive, make composite wood
There are material individual features also to be protected by the present invention.
The composition of preparing raw material in the specific embodiment of table 1
Wherein the particle diameter of talcum powder 1 is 10 microns, and the particle diameter of talcum powder 2 is 1 micron, is molded sample preparation, and gained batten is entered
Row test, as a result as shown in table 2:
The performance test results (ISO) of the lower shrinkage of table 2, high thermal stability impact-resistant polystyrene material
Be can be seen that from upper table 2, the stretching of lower shrinkage, high thermal stability impact-resistant polystyrene material prepared by the present invention is strong
The mechanical performances such as degree, elongation at break are similar with comparative example, and bending modulus, notch impact strength show apparently higher than comparative example
Go out good toughness, shrinkage factor is significantly lower than comparative example, with low-shrinkage energy, heat distortion temperature is higher than comparative example, higher
At a temperature of the dimensional stability that has had, expanded the temperature in use scope of material and increased HIPS at relatively high temperatures
Dimensional stability.
The above-mentioned description to embodiment is to be understood that and apply this hair for ease of those skilled in the art
It is bright.Person skilled in the art obviously can easily make various modifications to case study on implementation, and described herein one
As principle be applied in other embodiment without by performing creative labour.Therefore, the invention is not restricted to implementation case here
Example, those skilled in the art's announcement of the invention, not departing from improvement that scope made and modification all should be
Within protection scope of the present invention.
Claims (7)
1. a kind of lower shrinkage, high thermal stability impact-resistant polystyrene material, it is characterised in that the component including following weight portion:
High-impact polystyrene resin 60-85 parts
Toughener 5-10 parts
10-30 parts of reinforcing agent of filling
Antioxidant 0.2-0.5 parts
Lubricant 0.2-0.5 parts.
2. lower shrinkage according to claim 1, high thermal stability impact-resistant polystyrene material, it is characterised in that the height
Impact-resistant polystyrene resin refers to that the melt flow rate (MFR) under the conditions of 200 DEG C/5kg is the polystyrene tree of 2-10g/10min
Fat.
3. lower shrinkage according to claim 1, high thermal stability impact-resistant polystyrene material, it is characterised in that the increasing
Tough dose is that styrene-butadiene-polystyrene block copolymer SBS or polystyrene-ethylene-butylene-polystyrene three are embedding
Section copolymer SEBS.
4. lower shrinkage according to claim 1, high thermal stability impact-resistant polystyrene material, it is characterised in that described to fill out
Reinforcing agent is filled for talcum powder, and the particle diameter for filling reinforcing agent is 1-10 μm.
5. lower shrinkage according to claim 1, high thermal stability impact-resistant polystyrene material, it is characterised in that described anti-
Oxygen agent be four [β-(3,5- di-tert-butyl-hydroxy phenyls)Propionic acid] pentaerythritol ester and three [2.4- di-tert-butyl-phenyls] phosphorous
Acid esters is with 1:The weight of 1-2 is formed than compounding.
6. lower shrinkage according to claim 1, high thermal stability impact-resistant polystyrene material, it is characterised in that the profit
Lubrication prescription is one or several the mixture in calcium stearate, Tissuemat E, ethylene bis stearamide, silicone.
7. lower shrinkage as described in claim any one of 1-6, high thermal stability impact-resistant polystyrene material, it is characterised in that
Comprise the following steps:
(1)High-impact polystyrene resin, toughener, filling reinforcing agent, antioxidant and lubricant are weighed by above-mentioned part by weight,
Released after mixing 5-10min in high-speed mixer together;
(2)Above-mentioned mixed material addition double screw extruder is carried out into melting mixing, is extruded, cooling, pelletizing, drying to obtain
Lower shrinkage of the invention, high thermal stability material, the temperature range that each section of extruder are 170-210 DEG C.