CN106751330A - A kind of heat resistance composite decorating board preparation method high - Google Patents
A kind of heat resistance composite decorating board preparation method high Download PDFInfo
- Publication number
- CN106751330A CN106751330A CN201611231900.2A CN201611231900A CN106751330A CN 106751330 A CN106751330 A CN 106751330A CN 201611231900 A CN201611231900 A CN 201611231900A CN 106751330 A CN106751330 A CN 106751330A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat resistance
- styrene
- method high
- decorating board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heat resistance composite decorating board preparation method high, following processing step is included:Prepare following raw material:57 60 parts of styrene vinyl chloride graft copolymer, 10 12 parts of 28 32 part, day bamboo fibre of plant refuse, 50 60 parts of water, 10 13 parts of cumyl peroxide crosslinking agent, 13 parts of HBCD, 68 parts of atoleine, 46 parts of tetrabromoethane fire retardant, 34 parts of antioxidant, styrene mass percent is 20 25% in styrene vinyl chloride graft copolymer;The problems such as present invention solves decorative panel preponderance, flaggy heat resistance is poor.
Description
Technical field
The present invention relates to building decoration field, a kind of heat resistance composite decorating board preparation method high is particularly belonged to.
Background technology
At present, decorative panel is the thermosetting being made of HTHP adhesive by after chemical treatment with various special paper
Property laminated plastic, plate face has various wood grains or a pattern, and light is smooth, bright in colour attractive in appearance, while having higher wear-resisting, resistance to
The good physical properties such as cold, fire prevention, but heat resistance is general.
The content of the invention
It is an object of the invention to provide a kind of heat resistance composite decorating board preparation method high, decorative panel weight mistake is solved
Again, the problems such as flaggy heat resistance is poor.
The technical solution adopted by the present invention is as follows:
A kind of heat resistance composite decorating board preparation method high, includes following processing step:
A, the following raw material of preparation:57-60 parts of styrene-vinyl chloride graft copolymer, plant refuse 28-32 parts, day
Bamboo fibre 10-12 parts, water 50-60 parts, 10-13 parts of cumyl peroxide crosslinking agent, HBCD 1-3 parts, liquid
Paraffin 6-8 parts, 4-6 parts, antioxidant 3-4 parts of tetrabromoethane fire retardant;
B, first just green plants discarded object, day bamboo fibre, by mechanical crushing powder, are subsequently adding HBCD and water
The 10-15% immersion 4-6h of gross weight, are then made the raw material ball that particle diameter is 2-5mm through nodulizer, and 2- is dried at 100-140 DEG C
3h, obtains final product lightweight aggregate;
C, lightweight aggregate and other leftover materials together put into mixer, 18-20 stirred with 1200-1300r/min speed
After minute, surplus stock, then 1100-1200r/min speed is added to stir 28-30 minutes, temperature control is made at 110-130 DEG C
Mixed material feeding press is obtained to be suppressed.
Styrene mass percent is 20-25% in described styrene-vinyl chloride graft copolymer.
Compared with prior art, the present invention has the advantages that:
1st, decorative panel of the invention, manufacture craft is simple, and self-extinguishment effectively prevents fire.
2nd, decorative panel fracture resistance of the invention is superior, is also not in the phenomenon of sheet material embrittlement.
3rd, any toxic and harmful release such as formaldehydeless, toluene of light decorative plate of the invention, environmental-protecting performance is high.
Specific embodiment
A kind of heat resistance composite decorating board preparation method high, includes following processing step:
A, the following raw material of preparation:57-60 parts of styrene-vinyl chloride graft copolymer, plant refuse 28-32 parts, day
Bamboo fibre 10-12 parts, water 50-60 parts, 10-13 parts of cumyl peroxide crosslinking agent, HBCD 1-3 parts, liquid
Paraffin 6-8 parts, 4-6 parts of tetrabromoethane fire retardant, antioxidant 3-4 parts, styrene in styrene-vinyl chloride graft copolymer
Mass percent is 20-25%;
B, first just green plants discarded object, day bamboo fibre, by mechanical crushing powder, are subsequently adding HBCD and water
The 10-15% immersion 4-6h of gross weight, are then made the raw material ball that particle diameter is 2-5mm through nodulizer, and 2- is dried at 100-140 DEG C
3h, obtains final product lightweight aggregate;
C, lightweight aggregate and other leftover materials together put into mixer, 18-20 stirred with 1200-1300r/min speed
After minute, surplus stock, then 1100-1200r/min speed is added to stir 28-30 minutes, temperature control is made at 110-130 DEG C
Mixed material feeding press is obtained to be suppressed.
The performance test of decorative panel of the present invention:
Hardness(Shore A):56;
Tensile strength(MPa):13.5;
Elongation at break(%):356;
Oil resistivity:100 DEG C × 50h of 20# machine oil, elongation at break conservation rate 82.0%, tensile strength retention 81.7%;
Resistance to ozone:26 DEG C, 24h, ozone concentration 0.025%, without cracking;
It is ageing-resistant:120 DEG C, 80h, tensile strength retention 90.1%, elongation at break conservation rate 92.7%.
Claims (2)
1. a kind of heat resistance composite decorating board preparation method high, it is characterised in that include following processing step:
A, the following raw material of preparation:57-60 parts of styrene-vinyl chloride graft copolymer, plant refuse 28-32 parts, day
Bamboo fibre 10-12 parts, water 50-60 parts, 10-13 parts of cumyl peroxide crosslinking agent, HBCD 1-3 parts, liquid
Paraffin 6-8 parts, 4-6 parts, antioxidant 3-4 parts of tetrabromoethane fire retardant;
B, first just green plants discarded object, day bamboo fibre, by mechanical crushing powder, are subsequently adding HBCD and water
The 10-15% immersion 4-6h of gross weight, are then made the raw material ball that particle diameter is 2-5mm through nodulizer, and 2- is dried at 100-140 DEG C
3h, obtains final product lightweight aggregate;
C, lightweight aggregate and other leftover materials together put into mixer, 18-20 stirred with 1200-1300r/min speed
After minute, surplus stock, then 1100-1200r/min speed is added to stir 28-30 minutes, temperature control is made at 110-130 DEG C
Mixed material feeding press is obtained to be suppressed.
2. heat resistance according to claim 1 composite decorating board preparation method high, it is characterised in that described styrene-
Styrene mass percent is 20-25% in vinyl chloride graft copolymer.