CN106750875A - A kind of plastic bowl - Google Patents
A kind of plastic bowl Download PDFInfo
- Publication number
- CN106750875A CN106750875A CN201510800672.5A CN201510800672A CN106750875A CN 106750875 A CN106750875 A CN 106750875A CN 201510800672 A CN201510800672 A CN 201510800672A CN 106750875 A CN106750875 A CN 106750875A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic bowl
- bowl
- polypropylene
- bowl according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of plastic bowl, the plastic bowl is by following parts by weight into being grouped into：Polypropylene：100 parts, reinforcing fiber：20-30 parts, coupling agent：3-5 parts, compatilizer：3-5 parts, toughener：5-10 parts, vanillic aldehyde：10-20 parts, fire retardant：10-20 parts, antioxidant：1-3 parts, age resister：1-3 parts.Plastic bowl of the present invention is made from polypropylene plastics, light weight, intensity are high, do not absorb water, excellent in mechanical performance, easy to carry, durable and environmental protection.And, the present invention also adds the auxiliary agents such as reinforcing fiber, vanillic aldehyde and fire retardant in polypropylene matrix, improves the performances such as antibiotic property, the intensity of bowl.
Description
Technical field
The present invention relates to a kind of bowl, more particularly to a kind of plastic bowl.
Background technology
Bowl be people at present using the vessel of most common diet, be family, hotel,
A kind of indispensable daily necessities of the occasions such as restaurant.Prior art reclaimed water bowl material category
Various, ceramic bowl is easily broken, and stainless steel water bowl is relatively costly, and plastics water bowl cost
Low, moulding is changeable, be not afraid of and beat, and is loved by people, but plastics water at high temperature
Bowl is yielding or discharges harmful substance, unhealthful.
The content of the invention
The present invention is directed to the above-mentioned problems in the prior art, there is provided it is a kind of it is durable,
The plastic bowl of environmental protection.
The purpose of the present invention can be realized by following technical proposal：A kind of plastic bowl, it is described
Plastic bowl is by following parts by weight into being grouped into：Polypropylene：100 parts, reinforcing fiber：
20-30 parts, coupling agent：3-5 parts, compatilizer：3-5 parts, toughener：5-10 parts, vanilla
Aldehyde：10-20 parts, fire retardant：10-20 parts, antioxidant：1-3 parts, age resister：1-3
Part.
In a kind of above-mentioned plastic bowl, the reinforcing fiber is in carbon fiber, glass fibre
One or two.
It is a diameter of 10-30 μm of the reinforcing fiber, long in a kind of above-mentioned plastic bowl
Footpath ratio is (20-50)：1.
In a kind of above-mentioned plastic bowl, the coupling agent is titanate coupling agent.
In a kind of above-mentioned plastic bowl, the compatilizer be maleic anhydride inoculated polypropylene,
One or two in maleic anhydride grafted ethene-propylene copolymer.
In a kind of above-mentioned plastic bowl, the toughener is the one kind in MPE, LDPE.
In a kind of above-mentioned plastic bowl, the fire retardant is phosphorus-nitrogen combustion inhibitor.
Compared with prior art, plastic bowl of the present invention is made from polypropylene plastics, quality
Gently, intensity is high, do not absorb water, excellent in mechanical performance, easy to carry, durable and environmental protection.
And, the present invention also adds reinforcing fiber, vanillic aldehyde and fire-retardant in polypropylene matrix
The auxiliary agents such as agent, improve the performances such as antibiotic property, the intensity of bowl.
Specific embodiment
The following is specific embodiment of the invention, further is made to technical scheme
Description, but the present invention is not limited to these embodiments.
Embodiment 1：
Weigh 100 parts of raw material polypropylene, 20 parts of reinforcing fiber, 3 parts of coupling agent, compatilizer 3
Part, 5 parts of toughener, 10 parts of vanillic aldehyde, 10 parts of fire retardant, 1 part of antioxidant, age resister
1 part.It is then placed in mixing in low mixed machine, is discharged after material is well mixed, is put into parallel
Extruding pelletization in unidirectional double screw extruder.Then pellet is added in barrel, is heated to melting
State.Then the feed liquid of molten condition is expelled in the mould after heating, is molded after cooling
Plastic bowl is obtained.
Embodiment 2：
Weigh 100 parts of raw material polypropylene, 25 parts of reinforcing fiber, 4 parts of coupling agent, compatilizer 4
Part, 8 parts of toughener, 15 parts of vanillic aldehyde, 15 parts of fire retardant, 2 parts of antioxidant, age resister
2 parts.It is then placed in mixing in low mixed machine, is discharged after material is well mixed, is put into parallel
Extruding pelletization in unidirectional double screw extruder.Then pellet is added in barrel, is heated to melting
State.Then the feed liquid of molten condition is expelled in the mould after heating, is molded after cooling
Plastic bowl is obtained.
Embodiment 3：
Weigh 100 parts of raw material polypropylene, 30 parts of reinforcing fiber, 5 parts of coupling agent, compatilizer 5
Part, 10 parts of toughener, 20 parts of vanillic aldehyde, 20 parts of fire retardant, 3 parts of antioxidant is anti-aging
3 parts of agent.It is then placed in mixing in low mixed machine, is discharged after material is well mixed, is put into flat
Extruding pelletization in row unidirectional double screw extruder.Then pellet is added in barrel, is heated to melt
Melt state.Then the feed liquid of molten condition is expelled in the mould after heating, is opened after cooling
Mould to obtain plastic bowl.
Specific embodiment described herein is only to the spiritual theory for example of the present invention
It is bright.Those skilled in the art can be to described specific embodiment
Make various modifications or supplement or substituted using similar mode, but without departing from the present invention
Spirit or surmount scope defined in appended claims.
Although some specific implementations have been made a detailed description and have been cited to the present invention
Example, but to those skilled in the art, as long as without departing from spirit of the invention
It is obvious that can be made various changes with scope or corrected.
Claims (7)
1. a kind of plastic bowl, it is characterised in that the plastic bowl by following parts by weight into
It is grouped into：Polypropylene：100 parts, reinforcing fiber：20-30 parts, coupling agent：3-5 parts,
Compatilizer：3-5 parts, toughener：5-10 parts, vanillic aldehyde：10-20 parts, fire retardant：10-20
Part, antioxidant：1-3 parts, age resister：1-3 parts.
2. a kind of plastic bowl according to claim 1, it is characterised in that the enhancing
Fiber be carbon fiber, glass fibre in one or two.
3. a kind of plastic bowl according to claim 2, it is characterised in that the enhancing
A diameter of 10-30 μm of fiber, draw ratio is (20-50)：1.
4. a kind of plastic bowl according to claim 1, it is characterised in that the coupling
Agent is titanate coupling agent.
5. a kind of plastic bowl according to claim 1, it is characterised in that described compatible
Agent is in maleic anhydride inoculated polypropylene, maleic anhydride grafted ethene-propylene copolymer
Plant or two kinds.
6. a kind of plastic bowl according to claim 1, it is characterised in that the toughness reinforcing
Agent is the one kind in MPE, LDPE.
7. a kind of plastic bowl according to claim 1, it is characterised in that described fire-retardant
Agent is phosphorus-nitrogen combustion inhibitor.