CN106750604A - A kind of instrument beam sizing material - Google Patents
A kind of instrument beam sizing material Download PDFInfo
- Publication number
- CN106750604A CN106750604A CN201710002949.9A CN201710002949A CN106750604A CN 106750604 A CN106750604 A CN 106750604A CN 201710002949 A CN201710002949 A CN 201710002949A CN 106750604 A CN106750604 A CN 106750604A
- Authority
- CN
- China
- Prior art keywords
- parts
- carbon black
- sizing material
- rubbers
- crosslinking agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of instrument beam sizing material, following components is included according to mass fraction：50~70 parts of natural rubbers, 25~45 parts of fluorosioloxane rubber, 5~15 parts of EP rubbers, 15~30 parts of carbon black N762,10~20 parts of carbon black N660,2~6 parts of zinc oxide, acetoxylsilane crosslinking agent more than 3~5 parts, 1~3 part of organotin, 2~4 parts of vulcanizing agent DCP, 1~1.5 part of assistant crosslinking agent PDM, 1~2 part of protection wax, 0.5~1.5 part of antioxidant A W, 1~2 part of accelerant CZ, 1~2 part of altax, 1~2 part of anti-scorching agent CTP, 3~5 parts of processing oils.Instrument beam sizing material of the present invention, with good rebound performance and damping effect, and acid and alkali-resistance, oil resistant, fatigue durability is good, and long service life is suitable for instrument damping.
Description
Technical field
The present invention relates to rubber field, and in particular to a kind of instrument beam sizing material.
Background technology
In the environment of plant, starting for the equipment such as lathe causes judder, and the instrument in same environment then needs surely
It is fixed just to have accurate test result.In this case, instrument needs to be placed on ability normal work on beam.Beam
It is most common vibration dampening tool, rubber has good effectiveness in vibration suppression because of its high resiliency, therefore is commonly used for the material of beam.
In the factory, usually in heavy wool, the environment of many soda acids, Rubber shock-absorbing pad is required to so multiple beam
Remain to keep cushioning effect for a long time under miscellaneous use condition.
The content of the invention
Regarding to the issue above, the purpose of the present invention is to propose to a kind of instrument beam sizing material, with good resilience
Energy and damping effect, and acid and alkali-resistance, oil resistant, fatigue durability are good, and long service life is suitable for instrument damping.
To achieve these goals, the invention provides following technical scheme：A kind of instrument beam sizing material, according to matter
Amount number includes following components：50~70 parts of natural rubbers, 25~45 parts of fluorosioloxane rubber, 5~15 parts of EP rubbers, 15~30 parts
Carbon black N762,10~20 parts of carbon black N660,2~6 parts of zinc oxide, acetoxylsilane crosslinking agent more than 3~5 parts, 1~3 part it is organic
Tin, 2~4 parts of vulcanizing agent DCP, 1~1.5 part of assistant crosslinking agent PDM, 1~2 part of protection wax, 0.5~1.5 part of antioxidant A W, 1~2 part
Accelerant CZ, 1~2 part of altax, 1~2 part of anti-scorching agent CTP, 3~5 parts of processing oils.
Preferably, the instrument beam sizing material includes following components according to mass fraction：50 parts of natural rubbers, 35 parts
Fluorosioloxane rubber, 15 parts of EP rubbers, 15 parts of carbon black N762,10 parts of carbon black N660,2 parts of zinc oxide, acetoxylsilanes more than 3 parts are handed over
Connection agent, 2 parts of organotins, 2.5 parts of vulcanizing agent DCP, 1 part of assistant crosslinking agent PDM, 1 part of protection wax, 1.5 parts of antioxidant A W, 1 part of promotion
Agent CZ, 2 parts of altaxs, 2 parts of anti-scorching agent CTPs, 3 parts of processing oils.
Preferably, the instrument beam sizing material includes following components according to mass fraction：The instrument beam is used
Sizing material includes following components according to mass fraction：70 parts of natural rubbers, 25 parts of fluorosioloxane rubber, 5 parts of EP rubbers, 25 parts of carbon blacks
N762,20 parts of carbon black N660,6 parts of zinc oxide, acetoxylsilane crosslinking agent more than 4 parts, 3 parts of organotins, 4 parts of vulcanizing agent DCP,
1.5 parts of assistant crosslinking agent PDM, 2 parts of protection waxes, 0.5 part of antioxidant A W, 2 parts of accelerant CZs, 1 part of altax, 1 part of antiscorching agent
CTP, 5 parts of processing oils.
Preferably, the instrument beam sizing material includes following components according to mass fraction：60 parts of natural rubbers, 30 parts
Fluorosioloxane rubber, 10 parts of EP rubbers, 30 parts of carbon black N762,15 parts of carbon black N660,4 parts of zinc oxide, acetoxylsilanes more than 4 parts are handed over
Connection agent, 2 parts of organotins, 2 parts of vulcanizing agent DCP, 1 part of assistant crosslinking agent PDM, 1.5 parts of protection waxes, 1 part of antioxidant A W, 1 part of accelerator
CZ, 1 part of altax, 2 parts of anti-scorching agent CTPs, 4 parts of processing oils.
Preferably, the natural rubber, fluorosioloxane rubber, the number sum of EP rubbers and carbon black N762, carbon black N660
The ratio of number sum is 2.5~4: 1.
The present invention natural rubber, fluorosioloxane rubber, EP rubbers are shared in proportion, make sizing material have good high temperature resistant,
Oil resistant, acid-proof alkaline, while also using elasticity with good.The addition of carbon black N762, carbon black N660, can assign sizing material
Elasticity higher and tearing toughness.
Instrument beam sizing material of the invention, it is with good rebound performance and damping effect and acid and alkali-resistance, resistance to
Oil, fatigue durability is good, long service life, is suitable for instrument damping.
Specific embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of embodiment of the invention, rather than whole embodiments.Based on the embodiment in the present invention, this area is common
The every other embodiment that technical staff is obtained under the premise of creative work is not made, belongs to the model of present invention protection
Enclose.
The present invention proposes a kind of instrument beam sizing material, and following components is included according to mass fraction：50~70 parts natural
Rubber, 25~45 parts of fluorosioloxane rubber, 5~15 parts of EP rubbers, 15~30 parts of carbon black N762,10~20 parts of carbon black N660,2~6
Part zinc oxide, acetoxylsilane crosslinking agent more than 3~5 parts, 1~3 part of organotin, 2~4 parts of vulcanizing agent DCP, 1~1.5 part help friendship
Connection agent PDM, 1~2 part of protection wax, 0.5~1.5 part of antioxidant A W, 1~2 part of accelerant CZ, 1~2 part of altax, 1~2 part
Anti-scorching agent CTP, 3~5 parts of processing oils.
Embodiment 1
A kind of instrument beam sizing material, following components is included according to mass fraction：50 parts of natural rubbers, 35 parts of fluorine silicon rubbers
Glue, 15 parts of EP rubbers, 15 parts of carbon black N762,10 parts of carbon black N660,2 parts of zinc oxide, acetoxylsilane crosslinking agent, 2 more than 3 parts
Part organotin, 2.5 parts of vulcanizing agent DCP, 1 part of assistant crosslinking agent PDM, 1 part of protection wax, 1.5 parts of antioxidant A W, 1 part of accelerant CZ, 2
Part altax, 2 parts of anti-scorching agent CTPs, 3 parts of processing oils.
Embodiment 2
A kind of instrument beam sizing material includes following components according to mass fraction：70 parts of natural rubbers, 25 parts of fluorine silicon rubbers
Glue, 5 parts of EP rubbers, 25 parts of carbon black N762,20 parts of carbon black N660,6 parts of zinc oxide, acetoxylsilane crosslinking agent, 3 more than 4 parts
Part organotin, 4 parts of vulcanizing agent DCP, 1.5 parts of assistant crosslinking agent PDM, 2 parts of protection waxes, 0.5 part of antioxidant A W, 2 parts of accelerant CZs, 1
Part altax, 1 part of anti-scorching agent CTP, 5 parts of processing oils.
Embodiment 3
A kind of instrument beam sizing material, following components is included according to mass fraction：60 parts of natural rubbers, 30 parts of fluorine silicon rubbers
Glue, 10 parts of EP rubbers, 30 parts of carbon black N762,15 parts of carbon black N660,4 parts of zinc oxide, acetoxylsilane crosslinking agent, 2 more than 4 parts
Part organotin, 2 parts of vulcanizing agent DCP, 1 part of assistant crosslinking agent PDM, 1.5 parts of protection waxes, 1 part of antioxidant A W, 1 part of accelerant CZ, 1 part
Altax, 2 parts of anti-scorching agent CTPs, 4 parts of processing oils.
Embodiment 4
A kind of instrument beam sizing material, following components is included according to mass fraction：55 parts of natural rubbers, 30 parts of fluorine silicon rubbers
Glue, 15 parts of EP rubbers, 20 parts of carbon black N762,15 parts of carbon black N660,5 parts of zinc oxide, acetoxylsilane crosslinking agent, 2 more than 3 parts
Part organotin, 2 parts of vulcanizing agent DCP, 1 part of assistant crosslinking agent PDM, 1 part of protection wax, 1.5 parts of antioxidant A W, 1 part of accelerant CZ, 1 part
Altax, 1 part of anti-scorching agent CTP, 4 parts of processing oils.
Correlated performance test is carried out with sizing material to the instrument beam prepared by above-described embodiment, table 1 is performance test knot
Really.
The embodiment properties of product test result of table 1
As can be seen from Table 1, instrument beam sizing material of the invention has good rebound performance, while also maintaining
The performances such as preferable hardness, intensity.
Above-described is only the preferred embodiment of the present invention, it is noted that for one of ordinary skill in the art
For, without departing from the concept of the premise of the invention, various modifications and improvements can be made, these belong to the present invention
Protection domain.
Claims (5)
1. a kind of instrument beam sizing material, it is characterised in that the instrument beam sizing material according to mass fraction include with
Lower component：50~70 parts of natural rubbers, 25~45 parts of fluorosioloxane rubber, 5~15 parts of EP rubbers, 15~30 parts of carbon black N762,10
~20 parts of carbon black N660,2~6 parts of zinc oxide, acetoxylsilane crosslinking agent more than 3~5 parts, 1~3 part of organotin, 2~4 parts of sulphur
Agent DCP, 1~1.5 part of assistant crosslinking agent PDM, 1~2 part of protection wax, 0.5~1.5 part of antioxidant A W, 1~2 part of accelerant CZ, 1
~2 parts of altaxs, 1~2 part of anti-scorching agent CTP, 3~5 parts of processing oils.
2. instrument beam sizing material according to claim 1, it is characterised in that the instrument beam sizing material according to
Mass fraction includes following components：50 parts of natural rubbers, 35 parts of fluorosioloxane rubber, 15 parts of EP rubbers, 15 parts of carbon black N762,10 parts
Carbon black N660,2 parts of zinc oxide, acetoxylsilane crosslinking agent more than 3 parts, 2 parts of organotins, 2.5 parts of vulcanizing agent DCP, 1 part help crosslinking
Agent PDM, 1 part of protection wax, 1.5 parts of antioxidant A W, 1 part of accelerant CZ, 2 parts of altaxs, 2 parts of anti-scorching agent CTPs, 3 parts of processing oils.
3. instrument beam sizing material according to claim 1, it is characterised in that the instrument beam sizing material according to
Mass fraction includes following components：70 parts of natural rubbers, 25 parts of fluorosioloxane rubber, 5 parts of EP rubbers, 25 parts of carbon black N762,20 parts
Carbon black N660,6 parts of zinc oxide, acetoxylsilane crosslinking agent more than 4 parts, 3 parts of organotins, 4 parts of vulcanizing agent DCP, 1.5 parts help crosslinking
Agent PDM, 2 parts of protection waxes, 0.5 part of antioxidant A W, 2 parts of accelerant CZs, 1 part of altax, 1 part of anti-scorching agent CTP, 5 parts of processing oils.
4. instrument beam sizing material according to claim 1, it is characterised in that the instrument beam sizing material according to
Mass fraction includes following components：60 parts of natural rubbers, 30 parts of fluorosioloxane rubber, 10 parts of EP rubbers, 30 parts of carbon black N762,15 parts
Carbon black N660,4 parts of zinc oxide, acetoxylsilane crosslinking agent more than 4 parts, 2 parts of organotins, 2 parts of vulcanizing agent DCP, 1 part of assistant crosslinking agent
PDM, 1.5 parts of protection waxes, 1 part of antioxidant A W, 1 part of accelerant CZ, 1 part of altax, 2 parts of anti-scorching agent CTPs, 4 parts of processing oils.
5. according to any described instrument beam sizing material of Claims 1 to 4, it is characterised in that the natural rubber, fluorine silicon
Rubber, the number sum of EP rubbers and carbon black N762, the ratio of the number sum of carbon black N660 are 2.5~4: 1.