CN106747651B - The preparation and application method of two-component dyeing hardening sealant floor material - Google Patents
The preparation and application method of two-component dyeing hardening sealant floor material Download PDFInfo
- Publication number
- CN106747651B CN106747651B CN201611143496.3A CN201611143496A CN106747651B CN 106747651 B CN106747651 B CN 106747651B CN 201611143496 A CN201611143496 A CN 201611143496A CN 106747651 B CN106747651 B CN 106747651B
- Authority
- CN
- China
- Prior art keywords
- component
- ground
- added
- mixed solution
- distilled water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to building materials technology fields, it is desirable to provide a kind of preparation and application method of two-component dyeing hardening sealant floor material.It include: at room temperature by SnCl4Solution is added in the mixed solution of distilled water and ethyl alcohol, is sufficiently stirred down and adjusts pH value with ammonia spirit;Then surfactant is added, is ultrasonically treated after stirring;Add lithium metasilicate solution and inorganic toner;Persistently stir to get component A;Be sufficiently stirred it is lower by nanoscale boehmite colloidal sol be added distilled water in, add brightener, stir to get B component.Material of the present invention is water-based materials, will have the characteristics such as high rigidity, high-wearing feature, high glaze for concrete ground surface treatment, are the Novel terrace products for collecting concrete hardening, dyeing and integrated construction.Its preparation process is simple, and reaction process is easy to control, reaction condition is mild, also non-volatility toxic gas, no pollution to the environment in reaction, and raw material is simple, at low cost, easy for construction, is particularly suitable for the construction of large area industrialized production.
Description
Technical field
The invention belongs to the field of building materials, are a kind of systems of two-component dyeing hardening sealant floor material specifically
Standby and application method.
Background technique
Concrete is the maximum manufactured construction materials of mankind's usage amount, is widely used in all kinds of Structural Engineerings;But based on mixed
Solidifying soil material itself and construction level limitation, breakage can't bear already for many infrastructure, Industrial Plant Ground etc., and surface is cheated
Dirt, dusting, skin effect phenomenon, are played at weathering in hole, cause to wear no resistance, service life is short, does not adapt to modern production environment
Demand, be badly in need of transformation;Currently, conduct more popular on domestic and international market is to use liquid hardening agent, rigidizer material master
Have two classes: it is main component hardening sealant agent that one kind, which is with Nano silica sol (such as CN201010543000.8), wherein silicon is molten
Glue includes a large amount of silicon oxygen bonds, and the afwillite (C-S-H) for generating and capable of improving concrete abrasion-resistant performance, energy can be reacted with concrete
It is effectively improved and is promoted the performances such as concrete hardness, wearability.Another kind of is lithium base salt product, and this kind of curing agent can be mentioned substantially
The performances such as wear resistance, the glossiness of high concrete, and the common fault for the whiting that product early period limited can be avoided to occur;Such as
CN200910055825 and CN201110083155.2 etc. is disclosed all using lithium base salt as main component, is reacted with concrete
After play humidification, the performances such as compactness, glossiness for being re-introduced into other additives to increase concrete;But its effective component contains
Measure it is lower, single construct brought by concrete performance promoted few, and the gloss durability and weatherability of done product are poor, shorter
Gloss decline is obvious in time.
With being constantly progressive for social science and technology, people gradually discharge the personalization of building ground, diversified demand, start
Gradually pursue not only durable but also beautiful product, the especially diversification of concrete apparent colour, therefore, develop it is a can be big
While width improves concrete items comprehensive performance, and the terrace for being able to satisfy its color diversified demand has become the field instantly
One of the direction of each scientific research personnel's primary study.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the shortcomings of the prior art, it is close to provide a kind of two-component dyeing
The preparation and application method of envelope hardening floor material.
In order to solve the technical problem, solution of the invention is:
The present invention provides a kind of preparation methods of two-component dyeing hardening sealant floor material, comprising the following steps:
(1) SnCl for being at room temperature 0.05~0.4mol/L by concentration4The mixed solution of solution addition distilled water and ethyl alcohol
In, under the conditions of being sufficiently stirred, ammonia spirit is dropped evenly in above-mentioned solution with 70~150 drops/minute speed, is adjusted
Solution ph is 7~9.5;It is stirred while ammonium hydroxide is added dropwise with 100~400 revs/min of speed, acquisition uniformly mixes molten
Liquid;Then surfactant is added into mixed solution, is ultrasonically treated 15min after being sufficiently stirred;Sequentially add modulus be 3~
6 lithium metasilicate solution and inorganic toner;30~120min is persistently stirred with 500~1200 revs/min, is obtained molten in mixing
The component A of liquid status;
(2) under the conditions of being sufficiently stirred, distilled water is added in the nanoscale boehmite colloidal sol of solid content 20~45%
In, continue to stir 15min with 100~400 revs/min of speed;Then brightener is added, after continuing 30~70min of stirring, obtains
To the B component for being in mixed solution state;
In step (1) and (2), the additional amount of each ingredient is controlled, meets the ingredient of each component and its mass percent
Following requirements:
Percentage accounting of each ingredient of component A and B component in two component gross masses is respectively as follows:
Component A: tin tetrachloride 10~35%, lithium metasilicate 5~15%, inorganic toner 3~10%, surfactant 0.1~
1%, ethyl alcohol 5~20%, surplus are distilled water;
B component: boehmite 5~15%, brightener 0.1~0.5%, surplus are distilled water;Wherein, boehmite
Molecular formula is AlOOHnH2O, n=0.08~0.62.
In the present invention, the inorganic toner is one or more of dark green, cobalt blue, carbon black, lemon yellow or iron oxide red
Combination.
In the present invention, the surfactant is alkyl phenol polyoxyethylene ether, polyethylene glycol 2000, dodecyl benzene sulfonic acid
The combination of one or more of sodium or polyvinylpyrrolidone.
In the present invention, the brightener is the mixing liquid of benzylideneacetone and paraffin by the mass ratio of 3:1~1:5.
In the present invention, when being ultrasonically treated after addition surfactant in step (1), the frequency for controlling ultrasonic device is
2000Hz, power 350W.
In the present invention, the average grain diameter of boehmite colloidal sol is 45nm.
Invention further provides the two-component prepared using preceding method dyeing hardening sealant floor materials
Application method, comprising the following steps:
(1) ground flushing is clean and dry after being ground using grinder to mattess;It will be in mixing
The component A of solution state equably sprays or roller coating is on ground, keeps wet in 30min, the mixing of component A is fully penetrated
And it reacts with concrete;
(2) in the B component of mixed solution state according to 0.01~0.3kg/m2Dosage is equably sprayed on ground, is stood
20~60min;The polishing machine for the use of rotation speed being 500~1500rmp, with the fltting speed of 0.1~1min/m to having sprayed
It is ground on the ground for crossing B component;Cleaning ground is after the completion of grinding to get the hardening terrace for arriving completion dyeing sealing.
In the present invention, the type of the grinder is disc type, planetary or gear type, configures two-phase electricity or three-phase drive
Electricity;Grinding used is Buddha's warrior attendant piece, iron plate, resin sheet or potsherd, the mesh number of grinding is 30,80,150,300,500,800,
1000 or 2000 mesh, former choose of constructing one or more of state combination;Traveling mode of the grinder when being ground be
Horizontal, vertical each one to several times, and walking speed is uniform.
Inventive principle description:
The reinforcing effect of two-component dyeing hardening sealant floor material of the present invention is mainly realized by following three kinds of modes:
1, stannic chloride pentahydrate (SnCl4) Nanoparticulate SnO is formed under the adjusting of ammonium hydroxide after hydrolysis2Colloidal sol, and with
It under the action of surfactant is common, penetrates into inside concrete pore, fills up mixed in a manner of tiny particles content reinforced phase
Larger hole in soil is coagulated, compactness is enhanced, it is also to increase coagulation that this reaction, which is most important step during whole system enhances,
One of main reaction of native wearability;
2, the lithium metasilicate solution in component A in concrete hydrated product and unhydrated cement react, generate
The macromolecular of network-like cross-linked structure, more tiny hole keeps it further closely knit in fill concrete;
3, after the enhancing of component A effective component, boehmite (AlOOHnH in B component2O, n=0.08~0.62)
Colloidal sol infiltrates into the superficial layer of concrete under the high speed grinding effect of polishing machine under pressure, and with calcium therein from
Son, which reacts, generates the main enhancing ingredients calcium aluminate of high alumina cement;Meanwhile boundary of works area can be made during high speed grinding
Interior surface temperature may advantageously facilitate the generation of calcium aluminate in this temperature range up to 60~70 ° to seal the part such as surface layer pin hole
Hole, and terrace surface is made to form the closed entirety of approximation;
In addition, being added to inorganic toner in the present invention, it infiltrates into inside concrete, especially can be with Nanoparticulate
SnO2Colloidal sol is tightly combined, on the one hand along with the extension of time, inorganic toner can occur with the metal ion in concrete from
Son exchange is to make concrete form permanent stain;On the other hand, with SnO2Colloidal sol is together with pore in blocking concrete
Form make its colouring, under the collective effect of this two ways, certain thickness dye layer is formed inside mattess, most
Under acting on afterwards by the sealing that surface layer B component is ground, complete fine and close and color controllable, uniform color a terrace is formed.
Therefore, the present invention can be by enhancing concrete after above-mentioned three kinds of mode collective effects, and is completed at the same time incrustation.
Compared with the prior art, the advantages of the present invention are as follows:
(1) two-component dyeing hardening sealant terrace of the present invention is by with stannic chloride pentahydrate (SnCl4), lithium metasilicate solution
And nanoscale boehmite (AlOOHnH2O, n=0.08~0.62) colloidal sol curing agent as main component, can by with
Specific grinding technics is combined closely, and the Novel terrace for integrating dyeing, superhardization and polishing is prepared.
(2) it can be used to prepare complete fine and close and color controllable, uniform color terrace in the present invention, solve different crowd
The problem of to terrace diversity requirements.
(3) material in the present invention is water-based material, and easy construction, directly large area roller coating or can be sprayed into concrete
Surface is constructed, and mattess after processing has the characteristics such as high rigidity, high-wearing feature, high glaze, and gloss is more used
About persistently, surface shows gloss as waxing.
(4) present invention is the Novel terrace product for collecting concrete hardening, dyeing and integrated construction, and preparation process is simple,
Reaction process is easy to control, reaction condition is mild, also non-volatility toxic gas, no pollution to the environment, and raw material letter in reaction
It is single, it is at low cost, it is easy for construction, it is particularly suitable for the construction of large area industrialized production.
Specific embodiment
Below in conjunction with embodiment, present invention is further described in detail, it will be appreciated by those skilled in the art that
The following example is merely to illustrate the present invention, and should not be taken as limiting the scope of the invention.
Two-component provided by the invention dyes hardening sealant floor material, including component A and B component, ingredient and respectively at
It is divided to the percentage accounting in two component gross masses to be respectively as follows:
Component A: tin tetrachloride 10~35%, lithium metasilicate 5~15%, inorganic toner 3~10%, surfactant 0.1~
1%, ethyl alcohol 5~20%, surplus are distilled water;
B component: boehmite 5~15%, brightener 0.1~0.5%, surplus are distilled water;Wherein, boehmite
Molecular formula is AlOOHnH2O, n=0.08~0.62.
The preparation method of the two-component dyeing hardening sealant floor material, comprising the following steps:
(1) SnCl for being at room temperature 0.05~0.4mol/L by concentration4The mixed solution of solution addition distilled water and ethyl alcohol
In, under the conditions of being sufficiently stirred, ammonia spirit is dropped evenly in above-mentioned solution with 70~150 drops/minute speed, is adjusted
Solution ph is 7~9.5;It is stirred while ammonium hydroxide is added dropwise with 100~400 revs/min of speed, acquisition uniformly mixes molten
Liquid;Then surfactant is added into mixed solution, is ultrasonically treated 15min after being sufficiently stirred;Sequentially add modulus be 3~
6 lithium metasilicate solution and inorganic toner;30~120min is persistently stirred with 500~1200 revs/min, is obtained molten in mixing
The component A of liquid status;
(2) under the conditions of being sufficiently stirred, distilled water is added in the nanoscale boehmite colloidal sol of solid content 20~45%
In, continue to stir 15min with 100~400 revs/min of speed;Then brightener is added, after continuing 30~70min of stirring, obtains
To the B component for being in mixed solution state;
In step (1) and (2), the additional amount of each ingredient is controlled, meets the ingredient of each component and its mass percent
It is required that.
The application method of the two-component dyeing hardening sealant floor material, comprising the following steps:
(1) ground flushing is clean and dry after being ground using grinder to mattess;It will be in mixing
The component A of solution state equably sprays or roller coating is on ground, keeps wet in 30min, the mixing of component A is fully penetrated
And it reacts with concrete;
(2) it is equably sprayed on ground, stands according to 0.01~0.3kg/ ㎡ dosage in the B component of mixed solution state
20~60min;The polishing machine for the use of rotation speed being 500~1500rmp, with the fltting speed of 0.1~1min/m to having sprayed
It is ground on the ground for crossing B component;Cleaning ground is after the completion of grinding to get the hardening terrace for arriving completion dyeing sealing.
Test data in each embodiment see the table below:
The test result of terrace finished product basic performance in above table, is the concrete obtained under same execution conditions
What the comparative test carried out in ground base obtained, therefore have reference significance.
Claims (8)
1. a kind of preparation method of two-component dyeing hardening sealant floor material, which comprises the following steps:
(1) SnCl for being at room temperature 0.05~0.4mol/L by concentration4Solution is added in the mixed solution of distilled water and ethyl alcohol,
Under the conditions of being sufficiently stirred, ammonia spirit is dropped evenly in above-mentioned solution with 70~150 drops/minute speed, adjusts solution
PH value is 7~9.5;It is stirred while ammonium hydroxide is added dropwise with 100~400 revs/min of speed, obtains uniform mixed solution;So
Surfactant is added in backward mixed solution, is ultrasonically treated 15min after being sufficiently stirred;Sequentially add the silicon that modulus is 3~6
Sour lithium solution and inorganic toner;30~120min is persistently stirred with 500~1200 revs/min, is obtained in mixed solution state
Component A;
(2) under the conditions of being sufficiently stirred, the nanoscale boehmite colloidal sol of solid content 20~45% is added in distilled water, with
100~400 revs/min of speed continues to stir 15min;Then brightener is added, after continuing 30~70min of stirring, is in
The B component of mixed solution state;
In step (1) and (2), the additional amount of each ingredient is controlled, meets the ingredient of each component and its mass percent following
It is required that:
Percentage accounting of each ingredient of component A and B component in two component gross masses is respectively as follows:
Component A: tin tetrachloride 10~35%, lithium metasilicate 5~15%, inorganic toner 3~10%, surfactant 0.1~1%,
Ethyl alcohol 5~20%, surplus are distilled water;
B component: boehmite 5~15%, brightener 0.1~0.5%, surplus are distilled water;Wherein, the molecule of boehmite
Formula is AlOOHnH2O, n=0.08~0.62.
2. the method according to claim 1, wherein the inorganic toner is cobalt blue, carbon black, lemon yellow or iron oxide red
One or more of combination.
3. the method according to claim 1, wherein the surfactant is alkyl phenol polyoxyethylene ether, gathers
The combination of one or more of ethylene glycol 2000, neopelex or polyvinylpyrrolidone.
4. the method according to claim 1, wherein the brightener is benzylideneacetone and paraffin by 3:1~1:5
Mass ratio mixing liquid.
5. the method according to claim 1, wherein be added in step (1) after surfactant when being ultrasonically treated,
The frequency for controlling ultrasonic device is 2000Hz, power 350W.
6. according to the method described in claim 1, the average grain diameter of boehmite colloidal sol is 45nm.
7. using the application method for the two-component dyeing hardening sealant floor material that claim 1 the method prepares,
It is characterized in that, comprising the following steps:
(1) ground flushing is clean and dry after being ground using grinder to mattess;It will be in mixed solution
The component A of state equably sprays or roller coating is on ground, keeps wet in 30min, the mixing of component A it is fully penetrated and with
Concrete reacts;
(2) in the B component of mixed solution state according to 0.01~0.3kg/m2Dosage is equably sprayed on ground, and standing 20~
60min;The polishing machine for the use of rotation speed being 500~1500rmp, with the fltting speed of 0.1~1min/m to spray coated B group
It is ground on the ground divided;Cleaning ground is after the completion of grinding to get the hardening terrace for arriving completion dyeing sealing.
8. the method according to the description of claim 7 is characterized in that the type of the grinder is disc type, planetary or tooth
It is wheeled, configuration two-phase electricity or three-phase drive electricity;Grinding used is Buddha's warrior attendant piece, iron plate, resin sheet or potsherd, the mesh number of grinding
For 30,80,150,300,500,800,1000 or 2000 mesh, former choose of constructing one or more of states combination;Grinder
Traveling mode when being ground is horizontal, vertical each one to several times, and walking speed is uniform.