CN106747471A - A kind of fabric dividing cutter - Google Patents
A kind of fabric dividing cutter Download PDFInfo
- Publication number
- CN106747471A CN106747471A CN201710043393.8A CN201710043393A CN106747471A CN 106747471 A CN106747471 A CN 106747471A CN 201710043393 A CN201710043393 A CN 201710043393A CN 106747471 A CN106747471 A CN 106747471A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric dividing
- dividing cutter
- beta
- silicon nitride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention proposes a kind of fabric dividing cutter, and its raw material is respectively according to each composition proportion of mass fraction:75 98.5 parts of beta-silicon nitride powder, 5 10 parts of metal oxide, 5 10 parts of rare earth oxide, 05 parts of transition metal carbide, 03 parts of bonding agent, 04 parts of aluminium nitride, are also added with 1.5 times of deionized waters of amount of beta-silicon nitride powder in the raw material of the fabric dividing cutter.Using material manufactures such as silicon nitrides, with preferable wearability, thermal conductivity, while radiating rate is fast, blade toughness is greatly improved the fabric dividing cutter, not easy to break when using, so as to improve its service life.
Description
Technical field
The present invention relates to a kind of cutter, more particularly to a kind of fabric dividing cutter.
Background technology
Roller cutter is a kind of fabric dividing apparatus, generally includes a handle and the discoid knife installed in the handle end
Piece, the outer rim of blade is blade, when using, blade is released into handle, its blade is contacted with cloth, and control blade is along cloth
Roll.For some thicker cloth, in order to avoid situation about not cutting off occurs, it will usually which handle is erected into certain angle,
Cut cloth in the position for being slightly away from handle using blade.Due to the wear-resisting difference of blade material, and it is integrally formed, causes blade bulk strength
Relatively low, poor toughness is easily broken off at blade, so as to cause to cause the damage of cutter, influences its service life.
The content of the invention
The present invention proposes a kind of fabric dividing cutter, solves the problems, such as cutter poor toughness in the prior art and is easily broken off.
The technical proposal of the invention is realized in this way:
A kind of fabric dividing cutter, its raw material is respectively according to each composition proportion of mass fraction:Beta-silicon nitride powder 75-98.5 parts,
Metal oxide 5-10 parts, rare earth oxide 5-10 parts, transition metal carbide 0-5 parts, bonding agent 0-3 parts, aluminium nitride 0-4
Part, 1.5 times of deionized waters of amount of beta-silicon nitride powder are also added with the raw material of the fabric dividing cutter.
Preferred scheme is that the metal oxide is aluminum oxide or magnesia.
Preferred scheme is that the rare earth oxide is yttria, neodymia, luteium oxide, lanthanum sesquioxide, cerium oxide
In one kind.
Preferred scheme is that the transition metal carbide is titanium carbide or tungsten carbide.
Preferred scheme is that the binding agent is polyvinyl alcohol.
Preferred scheme is to be respectively according to each composition proportion of mass fraction in the raw material:80 parts of beta-silicon nitride powder, oxidation
10 parts of aluminium, 3.5 parts of rare earth oxide, 1.5 parts of transition metal carbide, 3 parts of binding agent, 2 parts of aluminium nitride, are additionally added silicon nitride powder
1.5 times of deionized waters of amount of body.
Preferred scheme is to be respectively according to each composition proportion of mass fraction in the raw material:75 parts of beta-silicon nitride powder, oxidation
10 parts of aluminium, 7 parts of rare earth oxide, 1.5 parts of transition metal carbide, 3 parts of binding agent, 3.5 parts of aluminium nitride, are additionally added silicon nitride powder
1.5 times of deionized waters of amount of body.
Preferred scheme is to be respectively according to each composition proportion of mass fraction in the raw material:90 parts of beta-silicon nitride powder, oxidation
2.5 parts of aluminium, 3 parts of rare earth oxide, 1.5 parts of transition metal carbide, 3 parts of binding agent, 0 part of aluminium nitride, are additionally added silicon nitride powder
1.5 times of deionized waters of amount of body.
Preferred scheme is that the fabric dividing cutter is circular plate body, and its middle part is provided with the first location hole, and the fabric dividing cutter includes
The pars intermedia of circular plate and the annular blade formed by the outward-dipping extension of periphery of the pars intermedia, outside the blade
Edge forms the side sword of acute angle shape.
Preferred scheme is that the pars intermedia is respectively equipped with the second positioning of a circle in the opposite sides of the first location hole
Hole.
Beneficial effects of the present invention are:
Fabric dividing cutter of the invention uses the material manufactures such as silicon nitride, with preferable wearability, thermal conductivity, while radiating
Speed is fast, and blade toughness is greatly improved, not easy to break when using, so as to improve its service life.
Brief description of the drawings
In order to illustrate more clearly about the embodiment of the present invention or technical scheme of the prior art, below will be to embodiment or existing
The accompanying drawing to be used needed for having technology description is briefly described, it should be apparent that, drawings in the following description are only this
Some embodiments of invention, for those of ordinary skill in the art, on the premise of not paying creative work, can be with
Other accompanying drawings are obtained according to these accompanying drawings.
Fig. 1 is the front view of fabric dividing cutter of the present invention;
Fig. 2 is the side view of Fig. 1.
In figure:
10th, pars intermedia;20th, blade;11st, the first location hole;12nd, mounting hole;110th, mesopore;111st, bar hole.
Specific embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation is described, it is clear that described embodiment is only a part of embodiment of the invention, rather than whole embodiments.It is based on
Embodiment in the present invention, it is every other that those of ordinary skill in the art are obtained under the premise of creative work is not made
Embodiment, belongs to the scope of protection of the invention.
As shown in Figures 1 and 2, the fabric dividing cutter is circular plate body, and its middle part is provided with the first location hole 11.The fabric dividing cutter
Pars intermedia 10 including circular plate and the annular blade 20 for being formed, institute outward-dipping are extended by the periphery of the pars intermedia 10
The outward flange for stating blade 20 forms the side sword of acute angle shape.First location hole 11 is located at the middle part of pars intermedia 10.The pars intermedia 10
The second location hole 12 of a circle is respectively equipped with the opposite sides of the first location hole 11.First location hole 11 includes circular
Mesopore 110 and two bar holes 111 for being stretched out by the opposite sides of mesopore 110 and being connected with mesopore 11.First positioning
The setting of the location hole 12 of hole 11 and second can preferably position fabric dividing cutter, make it be difficult to slide, and improve its security.
The raw material of the fabric dividing cutter is respectively according to each composition proportion of mass fraction:Beta-silicon nitride powder 75-98.5 parts, metal
Oxide 5-10 parts, rare earth oxide 5-10 parts, transition metal carbide 0-5 parts, bonding agent 0-3 parts, aluminium nitride 0-4 parts.Should
1.5 times of deionized waters of amount of beta-silicon nitride powder are also added with the raw material of fabric dividing cutter.The metal oxide concretely oxygen
Change aluminium, magnesia etc..The rare earth oxide concretely yttria, neodymia, luteium oxide, lanthanum sesquioxide, oxidation
One kind in cerium.The transition metal carbide concretely titanium carbide or tungsten carbide.The binding agent concretely polyethylene
Alcohol.
The fabric dividing cutter uses the material manufactures such as silicon nitride, with preferable wearability, thermal conductivity, while radiating rate
Hurry up, blade toughness is greatly improved, not easy to break when using, so as to improve its service life.
During specific implementation, match somebody with somebody according to each composition of mass fraction in the raw material of the better embodiment of fabric dividing cutter one of the invention
Than being respectively:80 parts of beta-silicon nitride powder, 10 parts of aluminum oxide, 3.5 parts of rare earth oxide, 1.5 parts of transition metal carbide, binding agent
3 parts, 2 parts of aluminium nitride, additionally, being additionally added 1.5 times of deionized waters of amount of beta-silicon nitride powder.
During specific implementation, according to each composition of mass fraction in the raw material of the another better embodiment of fabric dividing cutter of the invention
Proportioning can also be respectively:It is 75 parts of beta-silicon nitride powder, 10 parts of aluminum oxide, 7 parts of rare earth oxide, 1.5 parts of transition metal carbide, viscous
3 parts of agent of knot, 3.5 parts of aluminium nitride, additionally, being additionally added 1.5 times of deionized waters of amount of beta-silicon nitride powder.
During specific implementation, according to each composition of mass fraction in the raw material of the another better embodiment of fabric dividing cutter of the invention
Proportioning can also be respectively:90 parts of beta-silicon nitride powder, 2.5 parts of aluminum oxide, 3 parts of rare earth oxide, 1.5 parts of transition metal carbide,
3 parts of binding agent, 0 part of aluminium nitride, additionally, being additionally added 1.5 times of deionized waters of amount of beta-silicon nitride powder.
Presently preferred embodiments of the present invention is the foregoing is only, is not intended to limit the invention, it is all in essence of the invention
Within god and principle, any modification, equivalent substitution and improvements made etc. should be included within the scope of the present invention.
Claims (10)
1. a kind of fabric dividing cutter, it is characterised in that:The raw material of the fabric dividing cutter is respectively according to each composition proportion of mass fraction:
Beta-silicon nitride powder 75-98.5 parts, metal oxide 5-10 parts, rare earth oxide 5-10 parts, transition metal carbide 0-5 parts, it is viscous
Agent 0-3 parts, aluminium nitride 0-4 parts is connect, 1.5 times of deionized waters of amount of beta-silicon nitride powder are also added with the raw material of the fabric dividing cutter.
2. fabric dividing cutter as claimed in claim 1, it is characterised in that:The metal oxide is aluminum oxide or magnesia.
3. fabric dividing cutter as claimed in claim 1, it is characterised in that:The rare earth oxide be yttria, neodymia,
One kind in luteium oxide, lanthanum sesquioxide, cerium oxide.
4. fabric dividing cutter as claimed in claim 1, it is characterised in that:The transition metal carbide is titanium carbide, tungsten carbide.
5. fabric dividing cutter as claimed in claim 1, it is characterised in that:The binding agent is polyvinyl alcohol.
6. fabric dividing cutter as claimed in claim 1, it is characterised in that:According to each composition proportion of mass fraction point in the raw material
It is not:80 parts of beta-silicon nitride powder, 10 parts of aluminum oxide, 3.5 parts of rare earth oxide, 1.5 parts of transition metal carbide, 3 parts of binding agent,
2 parts of aluminium nitride, is additionally added 1.5 times of deionized waters of amount of beta-silicon nitride powder.
7. fabric dividing cutter as claimed in claim 1, it is characterised in that:According to each composition proportion of mass fraction point in the raw material
It is not:75 parts of beta-silicon nitride powder, 10 parts of aluminum oxide, 7 parts of rare earth oxide, 1.5 parts of transition metal carbide, 3 parts of binding agent, nitrogen
Change 3.5 parts of aluminium, be additionally added 1.5 times of deionized waters of amount of beta-silicon nitride powder.
8. fabric dividing cutter as claimed in claim 1, it is characterised in that:According to each composition proportion of mass fraction point in the raw material
It is not:90 parts of beta-silicon nitride powder, 2.5 parts of aluminum oxide, 3 parts of rare earth oxide, 1.5 parts of transition metal carbide, 3 parts of binding agent,
0 part of aluminium nitride, is additionally added 1.5 times of deionized waters of amount of beta-silicon nitride powder.
9. fabric dividing cutter according to any one of claims 1 to 8, it is characterised in that:The fabric dividing cutter is circular plate body,
Its middle part is provided with the first location hole, and the fabric dividing cutter includes the pars intermedia of circular plate and leaned outward by the periphery of the pars intermedia
Tiltedly extend the annular blade for being formed, the outward flange of the blade forms the side sword of acute angle shape.
10. fabric dividing cutter as claimed in claim 9, it is characterised in that:The pars intermedia is in the opposite sides of the first location hole
It is respectively equipped with the second location hole of a circle.