CN106747153A - 一种碱性玄武岩纤维石英混凝土 - Google Patents
一种碱性玄武岩纤维石英混凝土 Download PDFInfo
- Publication number
- CN106747153A CN106747153A CN201611029345.5A CN201611029345A CN106747153A CN 106747153 A CN106747153 A CN 106747153A CN 201611029345 A CN201611029345 A CN 201611029345A CN 106747153 A CN106747153 A CN 106747153A
- Authority
- CN
- China
- Prior art keywords
- parts
- concrete
- alkali
- basalt fiber
- fiber quartz
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于玄武岩复合材料制造技术领域，涉及碱性玄武岩混凝土的制造,尤其涉及一种碱性玄武岩纤维石英混凝土，其特征包括：石英混凝土包括以下组分：硅酸盐水泥、水、粉煤灰、矿粉、碎石、氧化铝、玄武岩纤维、酚醛树脂、硅酸镁和氧化镁。
Description
技术领域
本发明属于玄武岩复合材料制造技术领域，涉及碱性玄武岩混凝土的制造,尤其涉及一种碱性玄武岩纤维石英混凝土。
背景技术
混凝土可以追溯到古老的年代，其所用的胶凝材料为粘土、石灰、石膏、火山灰等。自19世纪20 年代出现了波特兰水泥后，由于用它配制成的混凝土具有工程所需要的强度和耐久性，而且原料易得，造价较低，特别是能耗较低，因而用途极为广泛（见无机胶凝材料）。
20世纪初，有人发表了水灰比等学说，初步奠定了混凝土强度的理论基础。以后，相继出现了轻集料混凝土、加气混凝土及其他混凝土，各种混凝土外加剂也开始使用。60年代以来，广泛应用减水剂，并出现了高效减水剂和相应的流态混凝土；高分子材料进入混凝土材料领域，出现了聚合物混凝土；多种纤维被用于分散配筋的纤维混凝土。现代测试技术也越来越多地应用于混凝土材料科学的研究。
混凝土有多种分类方法，最常见的有以下几种：
按胶凝材料
1 )无机胶凝材料混凝土，无机胶凝材料混凝土包括石灰硅质胶凝材料混凝土 (如硅酸盐混凝土)、硅酸盐水泥系混凝土 (如硅酸盐水泥、普通水泥，矿渣水泥，粉煤灰水泥、火山灰质水泥、早强水泥混凝土等). 钙铝水泥系混凝土 (如高铝水泥、纯铝酸盐水泥、喷射水泥，超速硬水泥混凝土等)、石膏混凝土、镁质水泥混凝土、硫磺混凝土、水玻璃氟硅酸钠混凝土、金属混凝土 (用金属代替水泥作胶结材料> 等。
2)有机胶凝材料混凝土。有机胶凝材料混凝土主要有沥青混凝土和聚合物水泥混凝土、树脂混凝土、聚合物浸渍混凝土等。 此外，无机与有机复合的胶体材料混凝土，还可以分聚合物水泥混凝土和聚合物辑靛混凝土。
按表观密度
混凝土按照表观密度的大小可分为：重混凝土、普通混凝土、轻质混凝土。这三种混凝土不同之处就是骨料的不同。
重混凝土是表观密度大于2500公斤/立方米，用特别密实和特别重的集料制成的。如重晶石混凝土、钢屑混凝土等，它们具有不透x射线和γ射线的性能；常由重晶石和铁矿石配制而成。
普通混凝土即是我们在建筑中常用的混凝土，表观密度为1950～2500Kg/立方米，主要以砂、石子为主要集料配制而成，是土木工程中最常用的混凝土品种。
轻质混凝土是表观密度小于1950公斤/立方米的混凝土。它又可以分为三类：
1．轻集料混凝土，其表观密度在800～1950公斤/立方米，轻集料包括浮石、火山渣、陶粒、膨胀珍珠岩、膨胀矿渣、矿渣等。
2．多空混凝土（泡沫混凝土、加气混凝土），其表观密度是300～1000公斤/立方米。泡沫混凝土是由水泥浆或水泥砂浆与稳定的泡沫制成的。加气混凝土是由水泥、水与发气剂制成的。
3．大孔混凝土（普通大孔混凝土、轻骨料大孔混凝土），其组成中无细集料。普通大孔混凝土的表观密度范围为1500～1900公斤/立方米，是用碎石、软石、重矿渣作集料配制的。轻骨料大孔混凝土的表观密度为500～1500公斤/立方米，是用陶粒、浮石、碎砖、矿渣等作为集料配制的。
现有技术中混凝土的强度虽然很高了，但是在某些天气恶劣的情况下依旧不能满足要求，比如在高寒或者极热的情况下依旧容易发生质量问题。
发明内容
为了解决现有技术中的问题，本发明提供了一种碱性玄武岩纤维石英混凝土。
一种碱性玄武岩纤维石英混凝土，其特征包括：石英混凝土包括以下组分：硅酸盐水泥、水、粉煤灰、矿粉、碎石、氧化铝、玄武岩纤维、酚醛树脂、硅酸镁和氧化镁。
所述的一种碱性玄武岩纤维石英混凝土，其特点是：各组分的重量份为:
硅酸盐水泥 600-800份
水 450-650份
粉煤灰 150-350份
矿粉 150-350份
碎石 800-1100份
氧化铝 180-200份
玄武岩纤维 50-100份
酚醛树脂 150-200份
硅酸镁 20-35份
氧化镁 220-250份。
所述的一种碱性玄武岩纤维石英混凝土，其特点是：各组分的重量份为:
硅酸盐水泥 600份
水 450份
粉煤灰 150份
矿粉 150份
碎石 800份
氧化铝 200份
玄武岩纤维 100份
酚醛树脂 200份
硅酸镁 35份
氧化镁 250份。
所述的一种碱性玄武岩纤维石英混凝土，其特点是：各组分的重量份为:
硅酸盐水泥 800份
水 650份
粉煤灰 350份
矿粉 350份
碎石 1100份
氧化铝 180份
玄武岩纤维 50份
酚醛树脂 150份
硅酸镁 20份
氧化镁 220份。
具体实施方式
实施例1
一种碱性玄武岩纤维石英混凝土，其特征包括：石英混凝土包括以下组分：硅酸盐水泥、水、粉煤灰、矿粉、碎石、氧化铝、玄武岩纤维、酚醛树脂、硅酸镁和氧化镁。
所述的一种碱性玄武岩纤维石英混凝土，其特点是：各组分的重量份为:
硅酸盐水泥 600-800份
水 450-650份
粉煤灰 150-350份
矿粉 150-350份
碎石 800-1100份
氧化铝 180-200份
玄武岩纤维 50-100份
酚醛树脂 150-200份
硅酸镁 20-35份
氧化镁 220-250份。
实施例2
所述的一种碱性玄武岩纤维石英混凝土，其特点是：各组分的重量份为:
硅酸盐水泥 600份
水 450份
粉煤灰 150份
矿粉 150份
碎石 800份
氧化铝 200份
玄武岩纤维 100份
酚醛树脂 200份
硅酸镁 35份
氧化镁 250份。
实施例3
所述的一种碱性玄武岩纤维石英混凝土，其特点是：各组分的重量份为:
硅酸盐水泥 800份
水 650份
粉煤灰 350份
矿粉 350份
碎石 1100份
氧化铝 180份
玄武岩纤维 50份
酚醛树脂 150份
硅酸镁 20份
氧化镁 220份。
Claims (4)
1.一种碱性玄武岩纤维石英混凝土，其特征包括：石英混凝土包括以下组分：硅酸盐水泥、水、粉煤灰、矿粉、碎石、氧化铝、玄武岩纤维、酚醛树脂、硅酸镁和氧化镁。
2.根据权利要求1所述的一种碱性玄武岩纤维石英混凝土，其特点是：其特点是：所述的一种碱性玄武岩纤维石英混凝土，各组分的重量份为:
硅酸盐水泥 600-800份
水 450-650份
粉煤灰 150-350份
矿粉 150-350份
碎石 800-1100份
氧化铝 180-200份
玄武岩纤维 50-100份
酚醛树脂 150-200份
硅酸镁 20-35份
氧化镁 220-250份。
3.根据权利要求1所述的一种碱性玄武岩纤维石英混凝土，其特点是：其特点是：所述的一种碱性玄武岩纤维石英混凝土，各组分的重量份为:
硅酸盐水泥 600份
水 450份
粉煤灰 150份
矿粉 150份
碎石 800份
氧化铝 200份
玄武岩纤维 100份
酚醛树脂 200份
硅酸镁 35份
氧化镁 250份。
4.根据权利要求1所述的一种碱性玄武岩纤维石英混凝土，其特点是：所述的一种碱性玄武岩纤维石英混凝土，各组分的重量份为:
硅酸盐水泥 800份
水 650份
粉煤灰 350份
矿粉 350份
碎石 1100份
氧化铝 180份
玄武岩纤维 50份
酚醛树脂 150份
硅酸镁 20份
氧化镁 220份。