CN106747145A - A kind of cement mortar for being applied to handicraft production - Google Patents
A kind of cement mortar for being applied to handicraft production Download PDFInfo
- Publication number
- CN106747145A CN106747145A CN201710079472.4A CN201710079472A CN106747145A CN 106747145 A CN106747145 A CN 106747145A CN 201710079472 A CN201710079472 A CN 201710079472A CN 106747145 A CN106747145 A CN 106747145A
- Authority
- CN
- China
- Prior art keywords
- cement
- handicraft
- cement mortar
- parts
- cellulose ether
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of cement mortar for being applied to handicraft production, by cement, cellulose ether, polyacrylamide, quartz sand, water reducer, early strength agent, defoamer, starch ether, the component mixed preparing such as water is formed for the invention.The cement mortar for being applied to handicraft production of the invention, mainly with quick hardening sulphoaluminate cement as main material, greatly reduces the cost of handicraft production, and add appropriate early strength agent to cause that hardening of cement speed is fast, operating procedure is simple, and reverse mould by 1 day, production efficiency is high.The additives such as additional cellulose ether in addition, polyacrylamide, starch ether so that cement mortar has good water-retaining property, and the hydration process of cement has been effectively ensured.Water reducer, sodium gluconate, defoamer of addition etc., effectively increase cement mortar application property, and the intensity after hardening of cement, the advantages of handicraft surface is smooth complete.
Description
Technical field
The present invention relates to chemical building material field, and in particular to a kind of cement mortar for being applied to handicraft production.
Background technology
Current handicraft manufacturer is mainly with resin as primary raw material, is molded by die casting, is made various making
Personage, animal, elder brother bird, scenery with hills and waters of type lifelike image attractive in appearance etc., and can be made into various simulated effects.Such as：Imitative copper, imitative gold, imitative silver,
The resin craft manufacturers such as imitative crystal, imitative agate, parian, artificial white marble, imitative redwood.But given birth to by raw material of resin
There is complex process in the handicraft of product, hardening time is more long, and the material for using has certain pollution, the problems such as relatively costly.
The content of the invention
Present invention aim at, there is provided a kind of cement mortar for being applied to handicraft production, the technical side that the present invention is used
Case is as follows：
A kind of cement mortar for being applied to handicraft production, it is characterised in that be mixed with by weight percentage by following components
Form：
Cement 20-30 parts
Cellulose ether 0.1-3 parts
Polyacrylamide 0.1-3 parts
Quartz sand 30-60 parts
Water reducer 0.1-3 parts
Early strength agent 0.1-3 parts
Defoamer 0.1-3 parts
Starch ether 0.1-3 parts
Water 10-30 parts.
One of preferably, described cement is quick hardening sulphoaluminate cement.
One of preferably, described cellulose ether is by hydroxypropyl methyl cellulose ether, hydroxyethyl methyl fiber
Plain ether mixing composition.
One of preferably, described hydroxypropyl methyl cellulose ether viscosity is in the map.s of 15-20 ten thousand.
One of preferably, the molecular weight of described polyacrylamide is in 15-20 ten thousand.
One of preferably, described starch ether is hydroxypropyl starch ether.
One of preferably, the water reducer is poly carboxylic acid series water reducer.
One of preferably, it also includes 0.1-3 parts of sodium gluconate.
The present invention is relative to the beneficial effect of prior art：The cement mortar for being applied to handicraft production of the invention,
It is main to greatly reduce the cost of handicraft production with quick hardening sulphoaluminate cement as main material, and add appropriate morning strong
Agent causes that hardening of cement speed is fast, and operating procedure is simple, and reverse mould by 1 day, production efficiency is high.Additional cellulose ether in addition,
The additives such as polyacrylamide, starch ether so that cement mortar has good water-retaining property, have been effectively ensured the aquation mistake of cement
Journey.Water reducer, sodium gluconate, defoamer of addition etc., effectively increase cement mortar application property, and after hardening of cement
Intensity, the advantages of handicraft surface is smooth complete.
Specific embodiment
Design of the invention and the technique effect for producing are clearly and completely described below with reference to embodiment, with
It is completely understood by the purpose of the present invention, feature and effect.Obviously, described embodiment is that a part of the invention is implemented
Example, rather than whole embodiments, based on embodiments of the invention, those skilled in the art is not before creative work is paid
Obtained other embodiment is put, the scope of protection of the invention is belonged to.
Embodiment 1：A kind of cement mortar for being applied to handicraft production, it is characterised in that by following components by weight hundred
Divide ratio to be mixed with to form：
23 parts of cement
1 part of cellulose ether
0.5 part of polyacrylamide
50 parts of quartz sand
0.3 part of water reducer
0.2 part of early strength agent
0.5 part of defoamer
0.5 part of starch ether
24 parts of water.
Embodiment 2：A kind of cement mortar for being applied to handicraft production, it is characterised in that by following components by weight hundred
Divide ratio to be mixed with to form：
26 parts of quick hardening sulphoaluminate cement
1.5 parts of cellulose ether
0.2 part of polyacrylamide
41.8 parts of quartz sand
0.5 part of poly carboxylic acid series water reducer
0.4 part of early strength agent
0.8 part of defoamer
0.5 part of hydroxypropyl starch ether
0.3 part of sodium gluconate
28 parts of water.
Wherein, above-mentioned cellulose ether is made up of hydroxypropyl methyl cellulose ether, ethoxyl methyl cellulose ether mixing,
Hydroxypropyl methyl cellulose ether viscosity is in the map.s of 15-20 ten thousand.
Wherein, the molecular weight of the above-mentioned polyacrylamide stated is in 15-20 ten thousand.
Better embodiment of the invention is illustrated above, but the invention is not limited to the implementation
Example, those of ordinary skill in the art can also make a variety of equivalent modifications or replace on the premise of without prejudice to spirit of the invention
Change, these equivalent modifications or replacement are all contained in the application claim limited range.
Claims (8)
1. it is a kind of to be applied to the cement mortar that handicraft is produced, it is characterised in that to mix system by weight percentage by following components
It is standby to form：
Cement 20-30 parts
Cellulose ether 0.1-3 parts
Polyacrylamide 0.1-3 parts
Quartz sand 30-60 parts
Water reducer 0.1-3 parts
Early strength agent 0.1-3 parts
Defoamer 0.1-3 parts
Starch ether 0.1-3 parts
Water 10-30 parts.
2. it is according to claim 1 to be applied to the cement mortar that handicraft is produced, it is characterised in that described cement is fast
Hardening sulphoaluminate cement.
3. it is according to claim 1 to be applied to the cement mortar that handicraft is produced, it is characterised in that described cellulose ether
It is made up of hydroxypropyl methyl cellulose ether, ethoxyl methyl cellulose ether mixing.
4. it is according to claim 1 to be applied to the cement mortar that handicraft is produced, it is characterised in that described hydroxypropyl first
Base viscosity of cellulose ether is in the map.s of 15-20 ten thousand.
5. it is according to claim 1 to be applied to the cement mortar that handicraft is produced, it is characterised in that described polyacrylamide
The molecular weight of amine is in 15-20 ten thousand.
6. the cement mortar for being applied to handicraft production according to claim 1, it is characterised in that described starch ether is
Hydroxypropyl starch ether.
7. it is according to claim 1 to be applied to the cement mortar that handicraft is produced, it is characterised in that the water reducer is poly-
Carboxylic acid water reducing agent.
8. it is according to claim 1 to be applied to the cement mortar that handicraft is produced, it is characterised in that it also includes 0.1-3
Part sodium gluconate.