CN106746973A - A kind of phase-changing and temperature-regulating dry powder and mortar - Google Patents
A kind of phase-changing and temperature-regulating dry powder and mortar Download PDFInfo
- Publication number
- CN106746973A CN106746973A CN201611104185.6A CN201611104185A CN106746973A CN 106746973 A CN106746973 A CN 106746973A CN 201611104185 A CN201611104185 A CN 201611104185A CN 106746973 A CN106746973 A CN 106746973A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- phase
- changing
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of phase-changing and temperature-regulating dry powder and mortar, by following parts by weight into being grouped into：20~25 parts of cement, 18~22 parts of miberal powder, 3~5 parts of dispersed latex powder, 25~30 parts of glass bead, 10~15 parts of nickel powder, 6~10 parts of organo-silicon compound, 1~3 part of graphite powder, 2~4 parts of cellulose, 3~6 parts of PE powder, 6~8 parts of nano ferriferrous oxide.It is an object of the invention to provide a kind of phase-changing and temperature-regulating dry powder and mortar, quality is flexible, have the advantages that not absorb water, it is not stratified, do not isolate, not sagging, do not fall off, liquid-impermeable, while having the effect of extraordinary phase-changing and temperature-regulating.
Description
Technical field
The present invention relates to a kind of dry powder and mortar, specially a kind of phase-changing and temperature-regulating dry powder and mortar.
Background technology
In recent years, energy shortage problem is one of national urgent problem.In national Eleventh Five-Year Plan tackling of key scientific and technical problems
The mesh of research work in to(for) energy-saving material is paid much attention to.Temperature adjustment phase-change material can absorb in phase transition process or discharge substantial amounts of
Latent heat, can be widely applied to heat storage and domain of control temperature, rapidly be developed in American-European countries over nearly 20 years.Phase transformation
Energy-storage composite material is a kind of hot functional composite material, energy can be stored in its carrier in the form of latent heat of phase change, real
Existing conversion of the energy between different space-time positions.The storage and utilization of energy are realized using the latent heat of phase change of phase-change material, is had
Help improve efficiency and exploitation regenerative resource, in recent years in energy science and material science one it is very active before
Along research direction.
Phase change temperature adjustment mortar on the market is and adds some phase-change materials in mortar to be obtained at present, and its shortcoming exists
In：Quality is poor, be easily layered, ftracture, come off, easily water suction become tide, the problems such as there is sepage, these are all those skilled in the art
The urgent problem for solving.
The content of the invention
The purpose of the present invention is directed to problem above, there is provided a kind of phase-changing and temperature-regulating dry powder and mortar, long service life, quality is soft
It is tough, have the advantages that not absorb water, it is not stratified, do not isolate, not sagging, do not fall off, liquid-impermeable, while having extraordinary phase to modify tone
The effect of temperature.
To realize object above, the technical solution adopted by the present invention is：A kind of phase-changing and temperature-regulating dry powder and mortar, by following weight
Number into being grouped into：By following parts by weight into being grouped into：20~25 parts of cement, 18~22 parts of miberal powder, dispersed latex powder 3
~5 parts, 25~30 parts of glass bead, 10~15 parts of nickel powder, 6~10 parts of organo-silicon compound, 1~3 part of graphite powder, cellulose 2
~4 parts, 3~6 parts of PE powder, 6~8 parts of nano ferriferrous oxide.
In the case of preferably, a kind of phase-changing and temperature-regulating dry powder and mortar, by following parts by weight into being grouped into：20 parts of cement, ore deposit
18 parts of powder, 3 parts of dispersed latex powder, 25 parts of glass bead, 10 parts of nickel powder, 6 parts of organo-silicon compound, 1 part of graphite powder, cellulose 2
Part, 3 parts of PE powder, 6 parts of nano ferriferrous oxide.
In the case of preferably, a kind of phase-changing and temperature-regulating dry powder and mortar, by following parts by weight into being grouped into：23 parts of cement, ore deposit
20 parts of powder, 3 parts of dispersed latex powder, 28 parts of glass bead, 13 parts of nickel powder, 8 parts of organo-silicon compound, 2 parts of graphite powder, cellulose 3
Part, 5 parts of PE powder, 7 parts of nano ferriferrous oxide.
In the case of preferably, a kind of phase-changing and temperature-regulating dry powder and mortar, by following parts by weight into being grouped into：25 parts of cement, ore deposit
22 parts of powder, 5 parts of dispersed latex powder, 30 parts of glass bead, 15 parts of nickel powder, 10 parts of organo-silicon compound, 3 parts of graphite powder, cellulose 4
Part, 6 parts of PE powder, 8 parts of nano ferriferrous oxide.
In the case of preferably, the dispersed latex powder is high polymer polyacrylamide.
In the case of preferably, the cellulose is any one in polyester fiber, Fypro, polyacrylonitrile fibre.
A kind of preparation method of phase-changing and temperature-regulating dry powder and mortar, by cement, miberal powder, dispersed latex powder, glass bead, nickel powder,
Organo-silicon compound, graphite powder, cellulose, PE powder, nano ferriferrous oxide are placed in a reservoir, carry out uniform stirring, are stirred
Discharge packaging by after mixing uniformly.
Beneficial effects of the present invention：
1st, a kind of phase-changing and temperature-regulating dry powder and mortar that the present invention is provided, quality is flexible, with not absorbing water, it is not stratified, do not isolate,
Not sagging, do not fall off, liquid-impermeable the advantages of, while having the effect of extraordinary phase-changing and temperature-regulating.
2nd, a kind of preparation method of phase-changing and temperature-regulating dry powder and mortar, the method is simple, easy to operate, and production efficiency is high, it is easy to push away
Wide and implementation.
Specific embodiment
Explaination is further made to the present invention by the following examples.
Embodiment 1：
A kind of phase-changing and temperature-regulating dry powder and mortar, by following parts by weight into being grouped into：By following parts by weight into packet
Into：20 parts of cement, 18 parts of miberal powder, 3 parts of dispersed latex powder, 25 parts of glass bead, 10 parts of nickel powder, 6 parts of organo-silicon compound, graphite
1 part of powder, 2 parts of cellulose, 3 parts of PE powder, 6 parts of nano ferriferrous oxide.
Preferably, the dispersed latex powder is high polymer polyacrylamide.
Preferably, the cellulose is any one in polyester fiber, Fypro, polyacrylonitrile fibre.
A kind of preparation method of phase-changing and temperature-regulating dry powder and mortar, by cement, miberal powder, dispersed latex powder, glass bead, nickel powder,
Organo-silicon compound, graphite powder, cellulose, PE powder, nano ferriferrous oxide are placed in a reservoir, carry out uniform stirring, are stirred
Discharge packaging by after mixing uniformly.
Embodiment 2：
A kind of phase-changing and temperature-regulating dry powder and mortar, by following parts by weight into being grouped into：By following parts by weight into packet
Into：23 parts of cement, 20 parts of miberal powder, 3 parts of dispersed latex powder, 28 parts of glass bead, 13 parts of nickel powder, 8 parts of organo-silicon compound, graphite
2 parts of powder, 3 parts of cellulose, 5 parts of PE powder, 7 parts of nano ferriferrous oxide.
Preferably, the dispersed latex powder is high polymer polyacrylamide.
Preferably, the cellulose is any one in polyester fiber, Fypro, polyacrylonitrile fibre.
A kind of preparation method of phase-changing and temperature-regulating dry powder and mortar, by cement, miberal powder, dispersed latex powder, glass bead, nickel powder,
Organo-silicon compound, graphite powder, cellulose, PE powder, nano ferriferrous oxide are placed in a reservoir, carry out uniform stirring, are stirred
Discharge packaging by after mixing uniformly.
Embodiment 3：
A kind of phase-changing and temperature-regulating dry powder and mortar, by following parts by weight into being grouped into：By following parts by weight into packet
Into：25 parts of cement, 22 parts of miberal powder, 5 parts of dispersed latex powder, 30 parts of glass bead, 15 parts of nickel powder, 10 parts of organo-silicon compound, stone
3 parts of ink powder, 4 parts of cellulose, 6 parts of PE powder, 8 parts of nano ferriferrous oxide.
Preferably, the dispersed latex powder is high polymer polyacrylamide.
Preferably, the cellulose is any one in polyester fiber, Fypro, polyacrylonitrile fibre.
A kind of preparation method of phase-changing and temperature-regulating dry powder and mortar, by cement, miberal powder, dispersed latex powder, glass bead, nickel powder,
Organo-silicon compound, graphite powder, cellulose, PE powder, nano ferriferrous oxide are placed in a reservoir, carry out uniform stirring, are stirred
Discharge packaging by after mixing uniformly.
It should be noted that herein, term " including ", "comprising" or its any other variant be intended to non-row
His property is included, so which key element process, method, article or equipment including a series of key elements not only include, and
And also include other key elements being not expressly set out, or also include for this process, method, article or equipment institute are intrinsic
Key element.
A kind of phase-changing and temperature-regulating dry powder and mortar provided by the present invention is described in detail above, herein to the present invention
Principle and implementation method be set forth, the explanation of above example is only intended to help and understands the method for the present invention and its core
Thought is thought；Simultaneously for those of ordinary skill in the art, according to thought of the invention, in specific embodiment and model is applied
Place and will change, in sum, this specification content should not be construed as limiting the invention.
Claims (7)
1. a kind of phase-changing and temperature-regulating dry powder and mortar, it is characterised in that by following parts by weight into being grouped into：20~25 parts of cement,
18~22 parts of miberal powder, 3~5 parts of dispersed latex powder, 25~30 parts of glass bead, 10~15 parts of nickel powder, 4~6 parts of alumina powder, stone
1~3 part of ink powder, 2~4 parts of asbestos fibre, 3~6 parts of PE powder, 6~8 parts of nano ferriferrous oxide.
2. a kind of phase-changing and temperature-regulating dry powder and mortar according to claim 1, it is characterised in that by the composition of following parts by weight
Composition：20 parts of cement, 18 parts of miberal powder, 3 parts of dispersed latex powder, 25 parts of glass bead, 10 parts of nickel powder, 6 parts of organo-silicon compound, stone
1 part of ink powder, 2 parts of cellulose, 3 parts of PE powder, 6 parts of nano ferriferrous oxide.
3. a kind of phase-changing and temperature-regulating dry powder and mortar according to claim 1, it is characterised in that by the composition of following parts by weight
Composition：23 parts of cement, 20 parts of miberal powder, 3 parts of dispersed latex powder, 28 parts of glass bead, 13 parts of nickel powder, 8 parts of organo-silicon compound, stone
2 parts of ink powder, 3 parts of cellulose, 5 parts of PE powder, 7 parts of nano ferriferrous oxide.
4. a kind of phase-changing and temperature-regulating dry powder and mortar according to claim 1, it is characterised in that by the composition of following parts by weight
Composition：25 parts of cement, 22 parts of miberal powder, 5 parts of dispersed latex powder, 30 parts of glass bead, 15 parts of nickel powder, 10 parts of organo-silicon compound,
3 parts of graphite powder, 4 parts of cellulose, 6 parts of PE powder, 8 parts of nano ferriferrous oxide.
5. a kind of phase-changing and temperature-regulating dry powder and mortar according to any one in claim 1-4, it is characterised in that the dispersion
Latex powder is high polymer polyacrylamide.
6. a kind of phase-changing and temperature-regulating dry powder and mortar according to claim 1-4, it is characterised in that the cellulose is fine polyester
Any one in dimension, Fypro, polyacrylonitrile fibre.
7. a kind of preparation method of the phase-changing and temperature-regulating dry powder and mortar according to any one in claim 1-6, its feature exists
In by cement, miberal powder, dispersed latex powder, glass bead, nickel powder, organo-silicon compound, graphite powder, cellulose, PE powder, receiving
Rice ferroso-ferric oxide place in a reservoir, carry out uniform stirring, after stirring can discharging pack.