CN106738981B - A kind of processing technology of plated film silica gel adhesive tape for wiper blade - Google Patents
A kind of processing technology of plated film silica gel adhesive tape for wiper blade Download PDFInfo
- Publication number
- CN106738981B CN106738981B CN201611159850.1A CN201611159850A CN106738981B CN 106738981 B CN106738981 B CN 106738981B CN 201611159850 A CN201611159850 A CN 201611159850A CN 106738981 B CN106738981 B CN 106738981B
- Authority
- CN
- China
- Prior art keywords
- silica gel
- adhesive tape
- wiper blade
- plated film
- gel adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of processing technologys of plated film silica gel adhesive tape for wiper blade, comprising the following steps: 1) rolling is kneaded；2) compression moulding；3) it sprays；4) solidify；5) finished product.The processing technology step of plated film silica gel adhesive tape for wiper blade of the invention is simple, and manufactured silica gel adhesive tape for wiper blade has very wide use temperature range (- 60 DEG C -200 DEG C), and anti-aging, ozone resistants is also significantly better than rubber adhesive tape；Again because silica gel adhesive tape coating is aqueous fluorinated material, frictional force is reduced when so that silica gel strip surface is with glass contact, the power of windscreen wiper can be reduced, protect the surface of glass；In actual use in addition to the performance for having wiper rubber adhesive tape, also there is water repellent performance, so that silica gel adhesive tape for wiper blade is after carrying out a period of time friction with glass, one layer of silica gel grease coating film can be formed in glass surface, rainwater falls within and is just gathered into many droplets on vehicle glass, automobile under steam, the effect that droplet is easily carried away by the wind, the rainy day when driving, the front sight of driver can be apparent.
Description
Technical field
The present invention relates to a kind of processing technologys of plated film silica gel adhesive tape for wiper blade.
Background technique
Tradition adhesive tape for wiper blade is made of natural rubber either synthetic rubber at present, and it is multiple that adhesive tape for wiper blade formula is made
It is miscellaneous, it needs to merge a variety of auxiliary chemicals with rubber, such as: anti-aging agent, antitack agent, filler, softening agent etc.；And add
Work complex process needs just complete the process by several procedures such as plasticating, being kneaded, vulcanize, form, handle, divide, vulcanize
It also needs to add auxiliary chemicals (vulcanizing agent) in process.Therefore, environment and personnel are good in traditional adhesive tape for wiper blade production process
Health is affected.In addition, the use temperature range of traditional adhesive tape for wiper blade is relatively narrow (- 40 DEG C -80 DEG C), it is anti-aging, ozone resistants
Range is also relatively narrow.
Summary of the invention
In order to solve the above technical problems, the present invention provides a kind of processing technology of plated film silica gel adhesive tape for wiper blade.
The processing technology of plated film silica gel adhesive tape for wiper blade of the invention, comprising the following steps:
1) rolling is kneaded, and high anti-tear silica gel, low temperature resistant silica gel and vulcanizing agent are carried out rolling mixing according to a certain percentage, made
High anti-tear silica gel, low temperature resistant silica gel and vulcanizing agent are thoroughly mixed；
2) it compression moulding: by the silica gel material being kneaded by compacted products aequum, is put into die forming machine and is suppressed
Molding；
3) it sprays: surface physics cleaning will be carried out by the good semi-finished product of step 2) compression moulding, and increase coating attachment system
Number, carries out even application processing to its surface with Teflon water paint；
4) solidify: the product after the spray treatment of surface be put into baking oven, toasted 10-15 minutes at a temperature of 80-160 DEG C,
Teflon water paint is set to be solidificated in product surface；
5) finished product: the product after step 4) solidifies is subjected to physics cutting by specification and size, ultimately forms plated film
Silica gel adhesive tape for wiper blade finished product.
The processing technology of plated film silica gel adhesive tape for wiper blade of the invention, in step 1), the anti-tear silica gel of height: low temperature resistant silicon
Glue: vulcanizing agent is equal to 0.8-1.5:0.8-1.5:0.01-0.03.
The processing technology of plated film silica gel adhesive tape for wiper blade of the invention, in step 3): being used when increasing coating attachment coefficient
Plasma device is surface-treated semi-finished product.
The processing technology of plated film silica gel adhesive tape for wiper blade of the invention, in step 3), the Teflon water paint is by gathering
Tetrafluoroethene, silicone emulsion, molybdenum disulfide, distilled water and water-borne wax are according to 4.7-5.2:0.3-0.35:0.6-0.7:0.8-
1.5:0.33-0.4 ratio mix.
Compared with prior art the invention has the benefit that the processing technology of plated film silica gel adhesive tape for wiper blade of the invention walks
Rapid simple, manufactured silica gel adhesive tape for wiper blade has very wide use temperature range (- 60 DEG C -200 DEG C), anti-aging, ozone-resistant
Property is also significantly better than rubber adhesive tape；Again because silica gel adhesive tape coating is aqueous fluorinated material, so that silica gel strip surface and glass contact
When reduce frictional force, the power of windscreen wiper can be reduced, protect the surface of glass；Except the property for having wiper rubber adhesive tape in actual use
Can be outer, also there is water repellent performance, so that silica gel adhesive tape for wiper blade, after carrying out a period of time friction with glass, meeting is in glass surface shape
At one layer of silica gel grease coating film, rainwater falls within and is just gathered into many droplets on vehicle glass, automobile under steam, droplet easily quilt
The effect that wind is taken away, the rainy day when driving, the front sight of driver can be apparent.
Specific embodiment
With reference to embodiment, the embodiment of the present invention is furthur described in detail.Following embodiment is used for
Illustrate the present invention, but is not intended to limit the scope of the invention.
Embodiment 1
A kind of processing technology of plated film silica gel adhesive tape for wiper blade, comprising the following steps:
1) rolling is kneaded, and high anti-tear silica gel, low temperature resistant silica gel and vulcanizing agent are carried out rolling mixing according to a certain percentage, made
High anti-tear silica gel, low temperature resistant silica gel and vulcanizing agent are thoroughly mixed；
2) it compression moulding: by the silica gel material being kneaded by compacted products aequum, is put into die forming machine and is suppressed
Molding；
3) it sprays: surface physics cleaning will be carried out by the good semi-finished product of step 2) compression moulding, and increase coating attachment system
Number, carries out even application processing to its surface with Teflon water paint；
4) solidify: the product after the spray treatment of surface is put into baking oven, toasted 10 minutes at a temperature of 80 DEG C, make Teflon
Water paint is solidificated in product surface；
5) finished product: the product after step 4) solidifies is subjected to physics cutting by specification and size, ultimately forms plated film
Silica gel adhesive tape for wiper blade finished product.
The processing technology of plated film silica gel adhesive tape for wiper blade of the invention, in step 1), the anti-tear silica gel of height: low temperature resistant silicon
Glue: vulcanizing agent is equal to 0.8:0.8:0.01.
The processing technology of plated film silica gel adhesive tape for wiper blade of the invention, in step 3): being used when increasing coating attachment coefficient
Plasma device is surface-treated semi-finished product.
The processing technology of plated film silica gel adhesive tape for wiper blade of the invention, in step 3), the Teflon water paint is by gathering
Tetrafluoroethene, silicone emulsion, molybdenum disulfide, distilled water and water-borne wax according to 4.7:0.3:0.6:0.8:0.33 ratio mixing and
At water-borne wax is aqueous polyethylene wax cream.
Embodiment 2
A kind of processing technology of plated film silica gel adhesive tape for wiper blade, comprising the following steps:
1) rolling is kneaded, and high anti-tear silica gel, low temperature resistant silica gel and vulcanizing agent are carried out rolling mixing according to a certain percentage, made
High anti-tear silica gel, low temperature resistant silica gel and vulcanizing agent are thoroughly mixed；
2) it compression moulding: by the silica gel material being kneaded by compacted products aequum, is put into die forming machine and is suppressed
Molding；
3) it sprays: surface physics cleaning will be carried out by the good semi-finished product of step 2) compression moulding, and increase coating attachment system
Number, carries out even application processing to its surface with Teflon water paint；
4) solidify: the product after the spray treatment of surface is put into baking oven, toasted 10 minutes at a temperature of 100 DEG C, make Teflon
Imperial water paint is solidificated in product surface；
5) finished product: the product after step 4) solidifies is subjected to physics cutting by specification and size, ultimately forms plated film
Silica gel adhesive tape for wiper blade finished product.
The processing technology of plated film silica gel adhesive tape for wiper blade of the invention, in step 1), the anti-tear silica gel of height: low temperature resistant silicon
Glue: vulcanizing agent is equal to 1:1:0.02.
The processing technology of plated film silica gel adhesive tape for wiper blade of the invention, in step 3): being used when increasing coating attachment coefficient
Plasma device is surface-treated semi-finished product.
The processing technology of plated film silica gel adhesive tape for wiper blade of the invention, in step 3), the Teflon water paint is by gathering
Tetrafluoroethene, silicone emulsion, molybdenum disulfide, distilled water and water-borne wax are mixed according to the ratio of 5:0.3:0.6:1:0.33,
Water-borne wax is aqueous polyethylene wax cream.
Embodiment 3
A kind of processing technology of plated film silica gel adhesive tape for wiper blade, comprising the following steps:
1) rolling is kneaded, and high anti-tear silica gel, low temperature resistant silica gel and vulcanizing agent are carried out rolling mixing according to a certain percentage, made
High anti-tear silica gel, low temperature resistant silica gel and vulcanizing agent are thoroughly mixed；
2) it compression moulding: by the silica gel material being kneaded by compacted products aequum, is put into die forming machine and is suppressed
Molding；
3) it sprays: surface physics cleaning will be carried out by the good semi-finished product of step 2) compression moulding, and increase coating attachment system
Number, carries out even application processing to its surface with Teflon water paint；
4) solidify: the product after the spray treatment of surface is put into baking oven, toasted 15 minutes at a temperature of 160 DEG C, make Teflon
Imperial water paint is solidificated in product surface；
5) finished product: the product after step 4) solidifies is subjected to physics cutting by specification and size, ultimately forms plated film
Silica gel adhesive tape for wiper blade finished product.
The processing technology of plated film silica gel adhesive tape for wiper blade of the invention, in step 1), the anti-tear silica gel of height: low temperature resistant silicon
Glue: vulcanizing agent is equal to 1.5:1.5:0.03.
The processing technology of plated film silica gel adhesive tape for wiper blade of the invention, in step 3): being used when increasing coating attachment coefficient
Plasma device is surface-treated semi-finished product.
The processing technology of plated film silica gel adhesive tape for wiper blade of the invention, in step 3), the Teflon water paint is by gathering
Tetrafluoroethene, silicone emulsion, molybdenum disulfide, distilled water and water-borne wax according to 5.2:0.35:0.6:1.5:0.4 ratio mixing and
At water-borne wax is aqueous polyethylene wax cream.
Test
Under equal conditions, to test and comparison such as the following table 1 of wiper rubber adhesive tape, silica gel adhesive tape for wiper blade:
The test and comparison of 1 wiper rubber adhesive tape of table, silica gel adhesive tape for wiper blade
It is compared and is found by table 1, using silica gel adhesive tape for wiper blade made of processing technology of the present invention relative to traditional rubber rain
Frictioning bar has good anti-aging property, and coefficient of friction is small, so that frictional force is reduced when silica gel strip surface and glass contact, it can
The power for reducing windscreen wiper, protects the surface of glass；In actual use in addition to the performance for having wiper rubber adhesive tape, also there is water repellent
Performance, so that silica gel adhesive tape for wiper blade after carrying out a period of time friction with glass, can form one layer of silica gel grease in glass surface
Coated film, rainwater fall within and are just gathered into many droplets on vehicle glass, and under steam, droplet is easily carried away by the wind automobile, in the rainy day
When driving, the front sight of driver can be apparent.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, several improvements and modifications, these improvements and modifications can also be made
Also it should be regarded as protection scope of the present invention.
Claims (1)
1. a kind of processing technology of plated film silica gel adhesive tape for wiper blade, which comprises the following steps:
1) rolling is kneaded, and high anti-tear silica gel, low temperature resistant silica gel and vulcanizing agent are carried out rolling mixing according to a certain percentage, make highly resistance
Silica gel, low temperature resistant silica gel and vulcanizing agent is torn to be thoroughly mixed；The anti-tear silica gel of height: low temperature resistant silica gel: vulcanizing agent is equal to 0.8-
1.5:0.8-1.5:0.01-0.03；
2) it compression moulding: by the silica gel material being kneaded by compacted products aequum, is put into die forming machine and is pressed；
3) it sprays: surface physics cleaning will be carried out by the good semi-finished product of step 2 compression moulding, increase coating attachment coefficient, use
Teflon water paint carries out even application processing to its surface；Using plasma device to semi-finished product when increasing coating attachment coefficient
It is surface-treated；The Teflon water paint is by polytetrafluoroethylene (PTFE), silicone emulsion, molybdenum disulfide, distilled water and water-borne wax
It is mixed according to the ratio of 4.7-5.2:0.3-0.35:0.6-0.7:0.8-1.5:0.33-0.4；
4) solidify: the product after the spray treatment of surface is put into baking oven, toasted 10-15 minutes at a temperature of 80-160 DEG C, make spy
Fluorine dragon water paint is solidificated in product surface；
5) finished product: the product after step 4) solidifies is subjected to physics cutting by specification and size, ultimately forms plated film silica gel
Adhesive tape for wiper blade finished product.