CN106738781A - A kind of compound resin processing technology - Google Patents
A kind of compound resin processing technology Download PDFInfo
- Publication number
- CN106738781A CN106738781A CN201611218954.5A CN201611218954A CN106738781A CN 106738781 A CN106738781 A CN 106738781A CN 201611218954 A CN201611218954 A CN 201611218954A CN 106738781 A CN106738781 A CN 106738781A
- Authority
- CN
- China
- Prior art keywords
- resin
- extruder
- processing technology
- raw material
- extrusion molding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of compound resin processing technology, comprise the following steps, dispensing, dispensing is carried out respectively to the first resin raw material, the second resin raw material；Cleaning extruder, is respectively washed the first extruder, the second extruder, and clean composite machine head；Extrusion molding, after composite machine head mixes, unified extrusion molding；Traction；Cooling；Dry；Stretching；Batch cutting；Packaging and warehousing.Compound resin processing technology of the invention, the first extruder, the second extruder are provided with, can be to compound resin after composite machine head mixing, unified extrusion molding, greatly improve shaping efficiency, and, matting is increased before processing, it is ensured that the quality of extrusion molding compound resin, reduce impurity, and coordinate air-cooled using water-cooled, and cooling effect is improved, have a good application prospect.
Description
Technical field
The present invention relates to compound resin processing technique field, and in particular to a kind of compound resin processing technology.
Background technology
At present, in naval stores process, before processing, the operation without cleaning mould can cause naval stores
There is more impurity or deformation, and, for the processing of compound resin, carried out using single extruding machine, it is necessary to will
The raw material of resin mix after extrusion molding again, trouble of getting the raw materials ready, and, influence processing efficiency is relatively low.
The content of the invention
The purpose of the present invention is after overcoming existing being carried out using single extruding machine, it is necessary to the raw material of resin is mixed
Extrusion molding, trouble of getting the raw materials ready again, and naval stores occurs the problem of impurity or deformation.Compound resin of the invention processes work
Skill, is provided with the first extruder, the second extruder, can be to compound resin after composite machine head mixing, unified extrusion molding, greatly
Big raising shaping efficiency, and, matting is increased before processing, it is ensured that the quality of extrusion molding compound resin, reduce miscellaneous
Matter, and coordinate air-cooled using water-cooled, cooling effect is improved, have a good application prospect
In order to achieve the above object, the technical solution adopted in the present invention is：
A kind of compound resin processing technology, it is characterised in that：Comprise the following steps,
Step（1）, dispensing carries out dispensing respectively to the first resin raw material, the second resin raw material；
Step（2）, extruder is cleaned, the first extruder, the second extruder are respectively washed, and clean composite machine head；
Step（3）, the first resin raw material is put into the first extruder by extrusion molding, and the second resin raw material is put into the first extruder,
And after composite machine head mixes, unified extrusion molding；
Step（4）, draw, the hybrid resin of extrusion molding is drawn；
Step（5）, cool down, the hybrid resin for pulling out is cooled down by recirculated water-cooling and air-cooling；
Step（6）, dry, to the hybrid resin after cooling, it is dried；
Step（7）, stretch, dry hybrid resin is further stretched；
Step（8）, cutting is batched, to the hybrid resin after stretching, carry out batching cutting；
Step（9）, packaging and warehousing.
A kind of foregoing compound resin processing technology, it is characterised in that：First resin raw material is ABS resin particle,
The second resin raw material ABA resin particles.
A kind of foregoing compound resin processing technology, it is characterised in that：Step（2）, by cleaning agent by the first extruder,
Second extruder, the cavity of composite machine head are cleaned up, and are then cleaned by clear water.
A kind of foregoing compound resin processing technology, it is characterised in that：The water temperature of the recirculated water cooling be maintained at 20 DEG C-
Between 30 DEG C.
A kind of foregoing compound resin processing technology, it is characterised in that：The drying uses heated-air drying, hot blast temperature
It is 40 DEG C.
A kind of foregoing compound resin processing technology, it is characterised in that：Packaging and warehousing includes beating hybrid resin material volume
Code.
The beneficial effects of the invention are as follows：Compound resin processing technology of the invention, is provided with the first extruder, the second extrusion
Machine, can be to compound resin after composite machine head mixing, and unified extrusion molding greatly improves shaping efficiency, and, before processing
Increased matting, it is ensured that the quality of extrusion molding compound resin, reduce impurity, and coordinate air-cooled using water-cooled, improve cold
But effect, has a good application prospect.
Brief description of the drawings
Fig. 1 is the flow chart of compound resin processing technology of the invention.
Specific embodiment
Below in conjunction with Figure of description, the present invention is further illustrated.
As shown in figure 1, compound resin processing technology of the invention, comprises the following steps,
Step（1）, dispensing carries out dispensing respectively to the first resin raw material, the second resin raw material；
Step（2）, extruder is cleaned, the first extruder, the second extruder are respectively washed, and clean composite machine head；
Step（3）, the first resin raw material is put into the first extruder by extrusion molding, and the second resin raw material is put into the first extruder,
And after composite machine head mixes, unified extrusion molding；
Step（4）, draw, the hybrid resin of extrusion molding is drawn；
Step（5）, cool down, the hybrid resin for pulling out is cooled down by recirculated water-cooling and air-cooling；
Step（6）, dry, to the hybrid resin after cooling, it is dried；
Step（7）, stretch, dry hybrid resin is further stretched；
Step（8）, cutting is batched, to the hybrid resin after stretching, carry out batching cutting；
Step（9）, packaging and warehousing.
First resin raw material is ABS resin particle, and the second resin raw material ABA resin particles are provided with first
Extruder, the second extruder, can be to compound resin after composite machine head mixing, and unified extrusion molding greatly improves shaping effect
Rate；
The present invention is cleaned up the cavity of the first extruder, the second extruder, composite machine head by cleaning agent, then by clear
Water is cleaned, it is ensured that cleaning quality, it is ensured that the quality of extrusion molding compound resin, reduces impurity.
The water temperature of the recirculated water cooling is maintained between 20 DEG C -30 DEG C, and the drying uses heated-air drying, and hot blast temperature is
40℃。
Packaging and warehousing of the invention includes the stamp to hybrid resin material volume, facilitates stock, picks and places, and improves the effect of management
Rate.
In sum, compound resin processing technology of the invention, is provided with the first extruder, the second extruder, can be right
After composite machine head mixing, unified extrusion molding greatly improves shaping efficiency to compound resin, and, increased before processing clear
Wash operation, it is ensured that the quality of extrusion molding compound resin, reduce impurity, and coordinate air-cooled using water-cooled, improve cooling effect, tool
There is good application prospect.
General principle of the invention, principal character and advantage has been shown and described above.The technical staff of the industry should
Understand, the present invention is not limited to the above embodiments, simply original of the invention is illustrated described in above-described embodiment and specification
Reason, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes and improvements
All fall within the protetion scope of the claimed invention.The claimed scope of the invention is by appending claims and its equivalent circle.
It is fixed.
Claims (6)
1. a kind of compound resin processing technology, it is characterised in that：Comprise the following steps,
Step（1）, dispensing carries out dispensing respectively to the first resin raw material, the second resin raw material；
Step（2）, extruder is cleaned, the first extruder, the second extruder are respectively washed, and clean composite machine head；
Step（3）, the first resin raw material is put into the first extruder by extrusion molding, and the second resin raw material is put into the first extruder,
And after composite machine head mixes, unified extrusion molding；
Step（4）, draw, the hybrid resin of extrusion molding is drawn；
Step（5）, cool down, the hybrid resin for pulling out is cooled down by recirculated water-cooling and air-cooling；
Step（6）, dry, to the hybrid resin after cooling, it is dried；
Step（7）, stretch, dry hybrid resin is further stretched；
Step（8）, cutting is batched, to the hybrid resin after stretching, carry out batching cutting；
Step（9）, packaging and warehousing.
2. a kind of compound resin processing technology according to claim 1, it is characterised in that：First resin raw material is
ABS resin particle, the second resin raw material ABA resin particles.
3. a kind of compound resin processing technology according to claim 1, it is characterised in that：Step（2）, will by cleaning agent
First extruder, the second extruder, the cavity of composite machine head are cleaned up, and are then cleaned by clear water.
4. a kind of compound resin processing technology according to claim 1, it is characterised in that：The water temperature of the recirculated water cooling
It is maintained between 20 DEG C -30 DEG C.
5. a kind of compound resin processing technology according to claim 1, it is characterised in that：The drying uses hot air drying
Dry, hot blast temperature is 40 DEG C.
6. a kind of compound resin processing technology according to claim 1, it is characterised in that：Packaging and warehousing is included to compound tree
The stamp of fat material volume.