CN106737262A - Welding pliers and its manufacture method - Google Patents
Welding pliers and its manufacture method Download PDFInfo
- Publication number
- CN106737262A CN106737262A CN201510809416.2A CN201510809416A CN106737262A CN 106737262 A CN106737262 A CN 106737262A CN 201510809416 A CN201510809416 A CN 201510809416A CN 106737262 A CN106737262 A CN 106737262A
- Authority
- CN
- China
- Prior art keywords
- shear blade
- steel
- welding
- binding clip
- matrix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind welding pliers and its manufacture method, belong to hand-operated tools, the shear blade of existing conventional pliers is directly processed on binding clip, pliers can not be met to shear blade wearability and sharpness and hardness requirement, binding clip of the invention is to weld shear blade on matrix to constitute, and matrix uses the mass percentage content of carbon by the carbon steel of 0.35-0.65% is made, and the hardness of matrix is 30-55HRC, shear blade is made of high-speed steel, and the hardness of shear blade is 58-66HRC.The performances such as present invention selection more preferably material manufacture shear blade, raising shear blade hardness, wearability, and the service life of shear blade can be improved, and binding clip uses conventional material, reduces material cost.
Description
Technical field
The invention belongs to hand-operated tools, specifically a kind of pliers for improving cutting performance.
Background technology
Existing conventional pliers is as Figure 1-4, including two calipers 02 linked together by bearing pin 01, each caliper 02 includes the binding clip 21 and the embedding handle 22 positioned at bearing pin rear positioned at the front of bearing pin 01, there is shear blade 211 on binding clip 21, shear blade and binding clip are a kind of materials, shear blade is directly processed on binding clip, it is impossible to meet requirement of the pliers to shear blade wearability and sharpness and hardness.In other words, in order to meet it is such require, it is necessary to the material of high intensity, the cost of so whole pliers can significantly rise.
The content of the invention
The technical problem to be solved in the present invention and the technical assignment for proposing are that the shear blade for overcoming existing conventional pliers is directly processed on binding clip, pliers can not be met to shear blade wearability and the defect of sharpness and hardness requirement, there is provided one kind welding pliers and its manufacture method.
To reach above-mentioned purpose, welding clamp attached bag of the invention includes two calipers linked together by bearing pin, and each caliper includes the binding clip in front of the bearing pin and the embedding handle positioned at the bearing pin rear, it is characterized in that:Described binding clip is to weld shear blade on matrix to constitute, described matrix uses the mass percentage content of carbon by the carbon steel of 0.35-0.65% is made, the hardness of described matrix is 30-55HRC, and described shear blade is made of high-speed steel, and the hardness of the shear blade is 58-66HRC.
As optimization technique means:The carbon steel for being made described matrix is the steel alloy less than 2.5% containing at least one of Cr, Mo, V alloying element and alloying element mass percentage content.
As optimization technique means:Described matrix uses the mass percentage content of carbon by the carbon steel of 0.40-0.60% is made, and the hardness of described matrix is 40-50HRC.
As optimization technique means:The carbon steel for being made described matrix is the steel alloy less than 1.6% containing at least one of Cr, Mo, V alloying element and alloying element mass percentage content.
As optimization technique means:Described shear blade(211)Using the one kind in W6Mo5Cr4V2 steel, W6Mo5Cr4V2Al steel, W2Mo9Cr4VCo8 steel, W18Cr4V steel, the shear blade(211)Hardness be 60 ~ 64HRC.
As optimization technique means:Described shear blade is attached to the side of described matrix in en plaque.
To reach above-mentioned purpose, the manufacture method of welding pliers of the invention, it is characterized in that comprising the following steps:
1)Caliper, shear blade are manufactured respectively:It is caliper with carbon steel or steel alloy blanking, hot-forging forming, caliper includes binding clip, embedding handle, and groove profile, welding position, overall Tempering and Quenching are processed on binding clip;Shear blade is made with high-speed steel;
2)Shear blade is welded on the welding position on binding clip;
3)Grind scissors cutting blade;
4)Two calipers are assembled together by bearing pin.
As optimization technique means:Shear blade is welded on matrix using any one in melting welding, pressure welding, laser fuU penetration welding, plasma weldering, upset butt welding.
The beneficial effects of the invention are as follows:It is welded on binding clip matrix by by shear blade, binding clip matrix is produced with different materials respectively from shear blade, can be from more preferably material manufacture shear blade, improve the performances such as shear blade hardness, wearability, and the service life of shear blade can be improved, and binding clip can then use conventional material, material cost is reduced.
Brief description of the drawings
Fig. 1 is the schematic diagram of the pliers of prior art;
Fig. 2 is the rearview of Fig. 1;
Fig. 3 is a schematic diagram for caliper in Fig. 1-2;
Fig. 4 is the A-A in Fig. 3 to profile;
Fig. 5 is the schematic diagram of a caliper of the invention;
Fig. 6 is the schematic diagram of second caliper of the invention;
Fig. 7 is the schematic diagram of the third caliper of the invention;
Fig. 8-13 is several generalized sections of binding clip of the invention and shear blade(Relative to the A-A in Fig. 3 to section);
Label declaration in figure:
01- bearing pins;
02- calipers:
21- binding clips:211- shear blades, 212- matrixes, 213- supporting surfaces, 214- pins;
The embedding handles of 22-.
Specific embodiment
Below in conjunction with Figure of description, the present invention will be further described.
Welding pliers of the invention, include two calipers 02 linked together by bearing pin 01 conventional pliers as shown in Fig. 1-2, each caliper 02 includes the binding clip 21 in front of bearing pin and the embedding handle 22 positioned at bearing pin rear, there is shear blade 211 on binding clip 21, the method have the characteristics that as shown in figures 5-13, binding clip 21 includes matrix 212, and shear blade 211 is welded on matrix 212 from cutting performance better than the material of binding clip matrix;Matrix uses the mass percentage content of carbon by the carbon steel of 0.35-0.65% is made, and the hardness of matrix is 30-55HRC, and shear blade is made of high-speed steel, and the hardness of shear blade is 58-66HRC.
Further, the carbon steel for being made matrix is the steel alloy less than 2.5% containing at least one of Cr, Mo, V alloying element and alloying element mass percentage content.
Preferably, matrix uses the mass percentage content of carbon by the carbon steel of 0.40-0.60% is made, and the hardness of matrix is 40-50HRC.The carbon steel for being made matrix is the steel alloy less than 1.6% containing at least one of Cr, Mo, V alloying element and alloying element mass percentage content.
Using the one kind in W6Mo5Cr4V2 steel, W6Mo5Cr4V2Al steel, W2Mo9Cr4VCo8 steel, W18Cr4V steel, the hardness of shear blade is 60 ~ 64HRC to shear blade.
Shear blade is attached to the side of matrix in en plaque.
Binding clip matrix of the invention is produced with different materials respectively from shear blade, the performances such as shear blade hardness, wearability can be improved, and the service life of shear blade can be improved from more preferably material manufacture shear blade, and binding clip can then use conventional material, material cost is reduced.
In order to increase the stress of shear blade, it is to avoid shear blade collapsed from matrix it is de-, can be provided with matrix support shear blade supporting surface 213(Referring to Figure 10, Figure 11, Figure 13), the supporting surface 213 can be single plane or curved surface, or step surface.Also pin 214 can be set on matrix(Referring to Fig. 6, Fig. 7, Fig. 9, Figure 12), shear blade is provided with pin-and-hole, and pin is located in pin-and-hole, and pin, pin-and-hole can be circular or semicircle.The supporting surface, pin also have positioning action when shear blade is welded in addition to increasing shear blade stress.
In view of the solution of the present invention, except shear blade outside whole embedding handle can use 45# steel.
The manufacture method of welding pliers of the invention, comprises the following steps:
1)Caliper, shear blade are manufactured respectively:It is caliper with carbon steel or steel alloy blanking, hot-forging forming, caliper includes binding clip, embedding handle, and groove profile, welding position, overall Tempering and Quenching are processed on binding clip;Shear blade is made with high-speed steel;
2)Shear blade is welded on the welding position on binding clip(Used as equivalent technological means, shear blade can roll on matrix);
3)Grind scissors cutting blade;
4)Two calipers are assembled together by bearing pin.
Described one kind welded in concretely melting welding, pressure welding, laser fuU penetration welding, plasma weldering, upset butt welding.
Claims (8)
1. pliers, including two calipers linked together by bearing pin are welded, and each caliper includes the binding clip in front of the bearing pin and the embedding handle positioned at the bearing pin rear, it is characterized in that:Described binding clip(21)It is that shear blade is welded on matrix(211)Constitute, described matrix uses the mass percentage content of carbon by the carbon steel of 0.35-0.65% is made, the hardness of described matrix is 30-55HRC, described shear blade(211)It is made of high-speed steel, the hardness of the shear blade is 58-66HRC.
2. welding pliers according to claim 1, it is characterized in that:The carbon steel for being made described matrix is steel alloy of the mass percentage content containing at least one of Cr, Mo, V alloying element and alloying element less than 2.5%.
3. welding pliers according to claim 1, it is characterized in that:Described matrix uses the mass percentage content of carbon by the carbon steel of 0.40-0.60% is made, and the hardness of described matrix is 40-50HRC.
4. welding pliers according to claim 3, it is characterized in that:The carbon steel for being made described matrix is the steel alloy less than 1.6% containing at least one of Cr, Mo, V alloying element and alloying element mass percentage content.
5. welding pliers according to claim 1, it is characterized in that:Described shear blade(211)Using the one kind in W6Mo5Cr4V2 steel, W6Mo5Cr4V2Al steel, W2Mo9Cr4VCo8 steel, W18Cr4V steel, the shear blade(211)Hardness be 60 ~ 64HRC.
6. welding pliers according to claim 1, it is characterized in that:Described shear blade is attached to the side of described matrix in en plaque.
7. the manufacture method of pliers is welded, it is characterized in that comprising the following steps:
1)Caliper, shear blade are manufactured respectively:It is caliper with carbon steel or steel alloy blanking, hot-forging forming, caliper includes binding clip, embedding handle, and groove profile, welding position, overall Tempering and Quenching are processed on binding clip;Shear blade is made with high-speed steel;
2)Shear blade is welded on the welding position on binding clip;
3)Grind scissors cutting blade;
4)Two calipers are assembled together by bearing pin.
8. it is according to claim 7 welding pliers manufacture method, it is characterized in that:Shear blade is welded on matrix using any one in melting welding, pressure welding, laser fuU penetration welding, plasma weldering, upset butt welding.