CN106736050A - A kind of silver jeweleries welding rod preparation method - Google Patents
A kind of silver jeweleries welding rod preparation method Download PDFInfo
- Publication number
- CN106736050A CN106736050A CN201611173004.5A CN201611173004A CN106736050A CN 106736050 A CN106736050 A CN 106736050A CN 201611173004 A CN201611173004 A CN 201611173004A CN 106736050 A CN106736050 A CN 106736050A
- Authority
- CN
- China
- Prior art keywords
- welding rod
- silver
- silver jeweleries
- jeweleries
- groove
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of processing method of silver jeweleries welding rod.Specific steps include：1）Fine silver material, simple brass material, borax mass ratio press 100：15：10 configurations；2）Fine silver material and simple brass material are put into container simultaneously and are heated to 330 DEG C, 20 minutes heat times；3）Temperature is heated to 1250 DEG C, fine silver material is treated, simple brass material is completely melt during for liquid, add borax；4）Uniform stirring, removes impurity in container, is incubated 25 minutes；5）Liquation is poured into groove, taking out silver jeweleries welding rod after temperature in groove drops to indoor temperature carries out hammer system；6）Silver jeweleries welding rod is put into the groove for pressing pure machine, is suppressed from big to small, a diameter of 0.4mm until being pressed into silver jeweleries welding rod.The silver jeweleries welding rod produced by the method, face of weld mobility is strong, and gloss is bright, and the silver jeweleries technique such as improve wire drawing, lacing, wire inlay connects that solid welding is qualitative, and the quality of product is exquisite, lines lines is clear.
Description
Technical field
The present invention relates to a kind of silver jeweleries auxiliary material processing method, especially a kind of processing method of silver jeweleries welding rod.
Background technology
Silver jeweleries welding rod has an excellent processing performance, molten point not high, good wetability and fills up the ability in gap,
And intensity is high, plasticity is good and the characteristics of excellent corrosion resistance, as a kind of main auxiliary material that silver jeweleries makes, is widely used in
In the making of all kinds of silver jeweleries.But traditional silver jeweleries welding rod, it is uneven that it easily produces face of weld to flow, and flowing velocity is slow,
Produce the problem of " rosin joint ".
The content of the invention
The present invention is in view of the shortcomings of the prior art, there is provided a kind of preparation method of silver jeweleries welding rod, to improve silver jeweleries product matter
Amount.Comprise the following steps that：
1）Fine silver material, simple brass material, borax mass ratio press 100：15：10 configurations；
2）Fine silver material and simple brass material are put into crucible simultaneously and are slowly heated to 330 DEG C, 20 minutes heat times；
3）Continuous heating treats fine silver material to 1250 DEG C, and simple brass material is completely melt during for liquid, addition borax, uniform stirring, clearly
Except impurity in crucible, 25 minutes are incubated；
4）Liquation in crucible is poured into stainless steel tank, is taken out after temperature in groove drops to indoor temperature；
5）Silver jeweleries welding rod is placed on smooth timber, hammer system is carried out, hammer number at 200~300 times, then with fire by silver jeweleries
Welding rod burns braised in soy sauce saturating, after cooling, then carries out hammer system, repeatedly for three times；
6）Silver jeweleries welding rod is put into the groove for pressing pure machine, is suppressed from big to small, until being pressed into a diameter of of silver jeweleries welding rod
0.4mm。
The silver jeweleries welding rod produced by the method, face of weld mobility is strong, and gloss is bright, improve wire drawing, lacing,
The silver jeweleries technique such as wire inlay connects that solid welding is qualitative, and the quality of product is exquisite, lines lines is clear.
Specific embodiment
Prepare crucible, borax, stainless steel cooling bath, Hand driving fan, charcoal fire.It is nine pure with four of 100 grams by quality proportioning
Silver material, 15 grams of simple brass material, while being put into crucible, crucible is placed in the middle of small cooking stove, uses charcoal fire heating crucible, charcoal fire to burn
Later dried with punka, crucible temperature is controlled in 330 DEG C, crucible is slowly heated, 20 minutes heat times.Then after
Continuous heating, notes the fine silver material of observation crucible, and simple brass burns braised in soy sauce saturating, after burning and braising in soy sauce thoroughly, dried with fan, the temperature of crucible
When reaching 1250 DEG C, fine silver material, simple brass material will slowly be melted, and liquation is mixed, and at this moment temperature can not be reduced, and one
It is straight to be maintained at 1250 DEG C of temperature burning refinings, until the material of crucible is all fused into liquid, at this moment by quality proportioning toward addition in crucible
10 grams of boraxs, are stirred with a carbon-point in crucible, pick up the slag in crucible, and such purpose is intended to remove the slag in crucible
Matter, makes liquation become clean, light, while also making liquation uniformly mix, is incubated 25 minutes or so.Then by the liquation in crucible
Pour into stainless steel tank, after temperature drops to indoor temperature in groove, take out, the silver jeweleries welding rod that then will be cooled down takes out.By silver
Decorations welding rod is placed on smooth timber, carries out hammer system, and then hammer number is burnt silver jeweleries welding rod with fire in 200~300 underranges
It is braised in soy sauce saturating, after cooling, then carry out hammer system.So burn refining repeatedly for three times to be made with hammer, it is therefore an objective to make the structure of silver jeweleries welding rod closeer
It is real.Finally silver jeweleries welding rod is put into the groove for pressing pure machine, is suppressed from big to small, until being pressed into a diameter of of silver jeweleries welding rod
0.4mm, is thus the silver jeweleries welding rod needed for us.
Claims (5)
1. a kind of silver jeweleries welding rod preparation method, it is characterised in that comprise the following steps：
1）Fine silver material, simple brass material, borax mass ratio press 100：15：10 configurations；
2）Fine silver material and simple brass material are put into container simultaneously and are heated to 330 DEG C, 20 minutes heat times；
3）Temperature is heated to 1250 DEG C, fine silver material is treated, simple brass material is completely melt during for liquid, add borax；
4）Uniform stirring, removes impurity in container, is incubated 25 minutes；
5）Liquation is poured into groove, taking out silver jeweleries welding rod after temperature in groove drops to indoor temperature carries out hammer system, then with fire
Silver jeweleries welding rod is burnt braised in soy sauce saturating, after cooling, then hammer system is carried out, repeatedly for three times；
6）Silver jeweleries welding rod is put into the groove for pressing pure machine, is suppressed from big to small.
2. a kind of silver jeweleries welding rod preparation method according to claim 1, it is characterised in that the step 1）It is fine silver material, pure
Brass material, borax quality are respectively 100 grams, 15 grams, 10 grams.
3. a kind of silver jeweleries welding rod preparation method according to claim 1, its feature is as the step 2）Its container can be with
It is crucible.
4. a kind of silver jeweleries welding rod preparation method according to claim 1, it is characterised in that the step 5）By silver jeweleries welding rod
Taking-up carries out hammer system, and hammer number is at 200~300 times.
5. a kind of silver jeweleries welding rod preparation method according to claim 1, it is characterised in that the step 6）Silver jeweleries welding rod pressure
A diameter of 0.4mm after system.