CN106699134A - Acid-resistant purple sand material - Google Patents
Acid-resistant purple sand material Download PDFInfo
- Publication number
- CN106699134A CN106699134A CN201611158288.0A CN201611158288A CN106699134A CN 106699134 A CN106699134 A CN 106699134A CN 201611158288 A CN201611158288 A CN 201611158288A CN 106699134 A CN106699134 A CN 106699134A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- mud
- acidproof
- sand material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses an acid-resistant purple sand material which comprises the following components in parts by weight: 30-40 parts of aluminum oxide, 10-15 parts of silicon nitride, 10-15 parts of silicon oxide, 5-10 parts of kieselguhr and 5-10 parts of tourmaline. Compared with a conventional technique, the acid-resistant purple sand material is prepared from various raw materials in a compounding manner, has the effect of purple clay, and has the property of acid resistance.
Description
Technical field
The invention belongs to electrothermal dark-red pottery field, and in particular to a kind of acidproof boccaro material.
Background technology
The origin cause of formation of violet sand earthenware clay, belongs to inland lake and strand liminetic facies sedimentary deposit, by external force sedimentary mineralization, it is buried in
Among middle of a mountain.Purple mud and green mud are all originated in Jia Nikuang.First mud is a kind of ridge clay, aubergine, color chalybeate first, therefore named first
Mud.At most, purple mud, green mud reserves are less, and purple mud only accounts for the 3-4% of gross reserves for first mud reserves in first mud ore deposit.During purple mud is first mud
One interlayer, green mud is the interlayer in purple interburden layer, therefore has the title of " mud, Yan Zhongyan in mud ".So, the pug of boccaro, also only
Having could obtain under conditions of a large amount of produces days pottery.Because this depth is hidden under rock stratum among " the first mud " of hundreds of meters depths
Purple mud, it is necessary to sorted out from first mud, there is no a large amount of of daily pottery to use first mud, purple mud also just to have no way of obtaining.Therefore, such as
It is the problem for being worth research that what is re-dubbed using boccaro material and is applicable various conditions.
The content of the invention
Goal of the invention：The purpose of the present invention is to solve the shortcomings of the prior art, there is provided a kind of acidproof boccaro material.
Technical scheme：In order to reach foregoing invention purpose, the present invention is specifically achieved like this：A kind of acidproof boccaro
Material, including following parts by weight component：30 ~ 40 parts of aluminum oxide, 10 ~ 15 parts of silicon nitrides, 10 ~ 15 parts of silica, 5 ~ 10 parts of silicon
Diatomaceous earth, 5 ~ 10 parts of tourmaline.
Wherein, the fineness of each raw material is less than 200 mesh.
A kind of preferred scheme, is made up of the component of following parts by weight：30 parts of aluminum oxide, 15 parts of silicon nitrides, 10 parts of oxidations
Silicon, 5 parts of diatomite, 10 parts of tourmaline.
Beneficial effect：The present invention is compounded compared with conventional art using each raw material, reaches the effect of purple mud, and have
There is acidproof characteristic.
Specific embodiment
Embodiment 1：
A kind of acidproof boccaro material, is made up of the component of following parts by weight：30 parts of aluminum oxide, 10 parts of silicon nitrides, 10 parts of silica,
5 parts of diatomite, 5 parts of tourmaline.
Embodiment 2：
A kind of acidproof boccaro material, is made up of the component of following parts by weight：40 parts of aluminum oxide, 15 parts of silicon nitrides, 15 parts of silica,
10 parts of diatomite, 10 parts of tourmaline.
Embodiment 3：
A kind of acidproof boccaro material, is made up of the component of following parts by weight：35 parts of aluminum oxide, 12 parts of silicon nitrides, 13 parts of silica,
6 parts of diatomite, 9 parts of tourmaline.
Embodiment 4：
A kind of acidproof boccaro material, is made up of the component of following parts by weight：32 parts of aluminum oxide, 14 parts of silicon nitrides, 11 parts of silica,
8 parts of diatomite, 7 parts of tourmaline.
Claims (3)
1. a kind of acidproof boccaro material, it is characterised in that the component including following parts by weight：30 ~ 40 parts of aluminum oxide, 10 ~ 15 parts
Silicon nitride, 10 ~ 15 parts of silica, 5 ~ 10 parts of diatomite, 5 ~ 10 parts of tourmaline.
2. acidproof boccaro material according to claim 1, it is characterised in that the fineness of each raw material is less than 200 mesh.
3. acidproof boccaro material according to claim 1, it is characterised in that be made up of the component of following parts by weight：30 parts
Aluminum oxide, 15 parts of silicon nitrides, 10 parts of silica, 5 parts of diatomite, 10 parts of tourmaline.