CN106698454A - Nanometer EU-1 molecular sieve synthesizing method - Google Patents
Nanometer EU-1 molecular sieve synthesizing method Download PDFInfo
- Publication number
- CN106698454A CN106698454A CN201510769121.7A CN201510769121A CN106698454A CN 106698454 A CN106698454 A CN 106698454A CN 201510769121 A CN201510769121 A CN 201510769121A CN 106698454 A CN106698454 A CN 106698454A
- Authority
- CN
- China
- Prior art keywords
- accordance
- nanometer
- calcium carbonate
- molecular sieve
- obtaining
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a nanometer EU-1 molecular sieve synthesizing method. The synthesizing method comprises the following steps: firstly, mixing inorganic base, water, a template agent, an aluminum source and a silicon source to obtain gel; mixing the gel with macroporous carbon and performing ultrasonic treatment; then stirring and treating under the condition of 50 to 100 DEG C until a thick state is formed; then drying until moisture is completely evaporated; then filling a reactor, adding a quantitative amount of water to seal the reactor for performing crystallization; filtering, washing and drying an obtained solid product and roasting the obtained solid product in an oxygen or air atmosphere to obtain the nanometer EU-1 molecular sieve. The synthesizing method disclosed by the invention can be used to synthesize the nanometer EU-1 molecular sieve under the situation of a low organic template agent using amount, crystalline degree is high, and other crystal impurities are avoided.
Description
Technical field
The present invention relates to a kind of nanometer EU-1 Zeolite synthesis methods, the method that specifically a kind of high efficiency, low cost synthesizes nanoscale EU-1 molecular sieves belongs to molecular sieve catalytic material synthesis field.
Background technology
Due to high-specific surface area, good heat and hydrothermal stability, the acidity of appropriateness enrich homogeneous micropore to zeolite molecular sieve, the performance such as surface nature is adjustable, are widely used as catalyst, adsorbent, ion-exchanger and new function material.At present, the zeolite crystal size generally micron order for industrially using.As oil quality upgrading and the in poor quality increasingly of crude oil, the shortcoming of microsized zeolite are also progressively amplified, the inside diffusional resistance of such as material is excessive, catalysis activity deficiency etc..Especially nano molecular sieve can solve these problems to little crystal grain just.Typically nano molecular sieve crystal size is limited within 100nm, because the crystal grain of nano zeolite is minimum, external surface area is set substantially to increase, shorten in intracrystalline pore road, expose aperture to increase, so as to make it have reactivity higher, stronger effect adsorption capacity, be difficult to occur because diffusion-limited for those or reactant or product molecule size and zeolite aperture adjoining dimensions reaction, nano molecular sieve shows more preferably superiority.
Nano molecular sieve is typically prepared using conventional hydrothermal crystallizing synthetic method, and relative to the preparation of conventional micron zeolite, synthesis difficulty is big, and is difficult to that product is collected by filtration, and causes production cost high, is difficult large-scale production.The factor of influence nano zeolite synthesis is a lot, including Template Types and consumption, the property of the raw material such as silicon source silicon source, plastic mode, and the factor such as crystallization method can all influence the size of zeolite crystal granularity.Such as Lianhui
Ding etc. is in " Nanocrystalline zeolite EU-1:The effect
of template agent on crystal size”(Materials
Research Bulletin, 2007,42:584–590)Article in, it is noted that a kind of nanometer of synthetic method of EU-1 molecular sieves.Silicon source used is exactly pure metallic aluminum in the synthetic method, and metallic aluminium must be in tetraethyl ammonium hydroxide solution by dissolving in advance, then by plastic, last hydrothermal crystallizing synthesizes EU-1 zeolites.But the crystal size of synthetic product is only in TEAOH/SiO2(Mol ratio)Nanoscale scope is just in during higher than 0.6, the EU-1 zeolites of micron level are can only obtain less than 0.6.
The microwave synthesis method of patent CN1730391A nanometer silicate basic hole materials, its technical characteristic is the zeolite product for synthesizing nanoscale in microwave environment.The advantage of the method is short generated time, but shortcoming is but very prominent, is exactly that must use this special installation of microwave, causes synthesis high cost;And industrialized microwave equipment is there is no in current zeolite compound probability, the industrial prospect of this technology is very remote.
A kind of synthetic methods of low silica-alumina ratio beta zeolite of patent CN101205072A, its technical characteristic is, with EU-1 zeolites as initial feed, then to mix according to a certain percentage with silicon source, template etc., finally synthesizes the EU-1 zeolite products of nanoscale.Because the method must use substantial amounts of conventional EU-1 zeolites that a nanometer EU-1 zeolites are prepared as raw material, therefore synthesis cost is very expensive;If counting conventional EU-1 zeolites synthesis step in, its operating process is just more cumbersome.
There are some patented technologies in addition, a nanometer EU-1 zeolites are synthesized using additive is added in the synthetic system of zeolite.Such as the Process for the preparation of nanocrystalline of patent US 6827924
Zeolite EU-1, disclose a kind of nanometer of synthetic method of EU-1 zeolites, and it is mainly characterized by synthetic system without alkali metal ion, and template is tetraethyl ammonium hydroxide, and additive used is the organic matters such as poisonous methyl alcohol, toluene.
A kind of nanometer high specific surface EU-1 zeolite preparation methods of patent CN101717092A, it is mainly characterized by introducing alkali metal chloride in reaction system, the organic solvent additives such as the methyl alcohol of severe toxicity are particularly introduced, therefore easily jeopardizes the health and safety of operating personnel.
A kind of synthetic methods of beta zeolite in small crystal grain of patent CN1324762A, its technical characteristic has three, and one is that silicon source used is Bio-sil, and two is that EPE polyol EPE or lubricating oil etc. are added in reaction system, and three is using the segmentation crystallization method of different temperatures.
A kind of preparation methods of nano molecular sieve of patent CN101182004A, its technical characteristic is synthesis material except using conventional silicon and aluminum source, outside organic formwork agent, also using distillate, surfactant etc. can synthesize the EU-1 zeolites less than 100nm as additive.But the method can increase the difficulty of nano zeolite product separation due to the additive for having used distillate etc. sticky, can undoubtedly cause the rising of production cost.
A kind of preparation methods of nano lamellar ZSM-5 zeolite molecular sieve of patent CN103043681A, nano-sized ZSM-5 zeolite is prepared using micro emulsion method liquid.Preparation process is:Zeolite precursor liquid solution is prepared by proportioning, the zeolite precursor liquid solution that will be prepared is mixed with W/O microemulsions according to a certain percentage with oil phase, surfactant, cosurfactant, then static crystallization, it is 30nm or so ZSM-5 zeolite to synthesize molecular sieve thickness of thin layer.But the effect of this method is also poor, in high temperature crystallization process, also easy high temperature warm-up movement breaks through the constraint of microemulsion to synthesized gel rubber, causes the generation of bulky grain molecular sieve.
Current nano molecular screen method is a lot, but many problems are still suffered from building-up process to be needed to solve.One of them is that consumption of template agent is excessive needed for synthesis, synthesizes the problem of high cost.Although the ratio range of the template consumption that some technologies are given is very wide, it is verified by experiments when low template consumption, the yardstick of synthetic product often exceeds nanoscale.Also some technologies synthesize nano zeolite using the method for additive, but can bring environmental pollution again and jeopardize the problem of health.Further, the problem that nano molecular sieve product is collected is difficult to solve.Because nanocrystal particle diameter is too small, it is difficult to be collected using conventional filtration method as common micro molecular sieve, generally requires and collected using centrifugal process, this substantially increases the production cost of nano molecular sieve again.
The content of the invention
For the deficiency of existing nano molecular sieve technology, especially template consumption is excessive and product is difficult to the problem collected, the present invention provides a kind of nanometer of synthetic method of EU-1 molecular sieves, the consumption of organic formwork agent can be effectively reduced, product is collected using traditional filtering method, the synthesis cost of nano molecular sieve is substantially reduced.
The present invention provides a kind of nanometer of synthetic method of EU-1 molecular sieves, and the crystal structure of molecular sieve is EU-1 molecular sieves, and without other Crystal impurities, its crystal size is less than 100nm, the described method comprises the following steps:
(1)First that inorganic base is soluble in water, rear addition template to be dissolved adds silicon source, after silicon source is added after silicon source dissolving completely, gel is obtained after being well mixed, and the molar ratio of material is:0.3~7Na2O:25~110SiO2:A12O3:450~1600H2O:1~6 template;
(2)By step(1)The gel for obtaining mix with macropore carbon after 10~60min of ultrasonication, then stir process to viscous pasty state, is then dried, until moisture evaporating completely under the conditions of 80~180 DEG C under the conditions of 50~100 DEG C;
(3)By step(2)The mixture for obtaining loads reactor, adds a certain amount of water, and then closed reactor carries out crystallization, and reaction temperature is 180~240 DEG C, and the reaction time is 25~100h;
(4)By step(3)The solid product filtration washing for obtaining is dried, and a nanometer EU-1 molecular sieves are obtained after being then calcined in oxygen or air atmosphere.
In the synthetic method of nanometer EU-1 molecular sieves of the present invention, step(1)Described in inorganic base be one or more in NaOH, KOH, LiOH;Silicon source is one or more in sodium aluminate, aluminum sulfate, aluminium chloride, aluminum nitrate;Silicon source is one or more in White Carbon black, silica gel, Ludox or waterglass;Template is C6 (HMBr2)。
In the synthetic method of nanometer EU-1 molecular sieves of the present invention, step(1)Described in molar ratio of material be 0.5~6Na2O:30~100SiO2:A12O3:500~1500H2O:2~5 templates.
In the method for present invention synthesis nanometer EU-1 molecular sieves, step(2)Middle macropore carbon is a kind of micron-sized carbon material, and particle diameter is 0.5~100 μm, and preferably 1~70 μm, the aperture of the macropore carbon is 20~150nm, more preferably preferably 25~110nm, 30~110nm.
In the method for present invention synthesis nanometer EU-1 molecular sieves, step(2)Described in macropore carbon method be prepared by the following procedure obtain:(a)Calcium carbonate is mixed with alkali lye, then the stir process at 50~90 DEG C filters, the solid matter being filtrated to get is heat-treated 1~3h at 300~500 DEG C;(b)Will be through step(a)Calcium carbonate after treatment mixes with water and glucide, after 10~60min of stirring, 1~10h of ultrasonication;(c)By step(b)The solution for obtaining stir process to solution at 50~100 DEG C is in viscous pasty state, is then dried at 50~80 DEG C, is finally placed in nitrogen atmosphere 3~10h of charing process at 700~1000 DEG C;(d)By step(c)The material for obtaining is well mixed with acid solution, and 1~10h is processed at 50~200 DEG C, is washed out drying;(e)By step(d)The material for obtaining in a nitrogen atmosphere, in 700~1000 DEG C of 3~10h of high-temperature process, obtains macropore carbon.
In the carbon materials preparation method for material, step(a)Described in calcium carbonate be nano-calcium carbonate, the particle diameter of the nano-calcium carbonate is 30~50nm.The alkali lye is one or two in NaOH, potassium hydroxide, and the concentration of lye is 0.01~0.1mol/L, and the mass ratio of calcium carbonate and alkali lye is 1:5~1:50, preferably 1:10~1:20.
In the carbon materials preparation method for material, step(b)Described in glucide be sucrose, glucose in one or two, calcium carbonate, glucide, water mass ratio be 0.1~2:1:10~33, preferably 0.2~1:1:13~26.
In the carbon materials preparation method for material, step(c)Described in charing process carried out in nitrogen atmosphere, nitrogen flow rate be 10~50mL/min, preferably 15~40 mL/min.The charing process heating rate is 1~10 DEG C/min, is heated up with constant heating rate.Described charing process processes 4~8h at 800~950 DEG C.
In the carbon materials preparation method for material, step(d)Described in acid solution be hydrochloric acid or nitric acid, the mass concentration of acid solution is 20~60%.
In the carbon materials preparation method for material, step(d)Described in treatment conditions be at 100~180 DEG C treatment 2~7h.It is described washing be with distillation water washing, the drying be at 100~140 DEG C dry 5~15h.
In the carbon materials preparation method for material, step(e)Described in high-temperature process carried out in nitrogen atmosphere, nitrogen flow rate be 10~50mL/min, preferably 15~40 mL/min.The high-temperature process heating rate is 1~10 DEG C/min, is heated up with constant heating rate.
In the synthetic method of nanometer EU-1 molecular sieves of the present invention, step(2)Middle macropore carbon is 1 with the weight ratio of gel butt:1.5~0.1, preferably 1:1.2~0.2.
In the synthetic method of nanometer EU-1 molecular sieves of the present invention, step(2)Described in ultrasonic treatment time be 20~40min;Stir process temperature is 60~90 DEG C;Described drying temperature is 100~150 DEG C.
In the synthetic method of nanometer EU-1 molecular sieves of the present invention, step(3)Middle material mol ratio is:0.3~7Na2O:25~110SiO2:A12O3:20~220H2O:1~6 template, preferably 0.5~6Na2O:30~100SiO2:A12O3:30~200H2O:2~5 templates.
In the synthetic method of nanometer EU-1 molecular sieves of the present invention, step(3)Described in crystallization temperature be 185~220 DEG C, the reaction time be 20~80h.
In the synthetic method of nanometer EU-1 molecular sieves of the present invention, step(4)Described in washing be with distillation water washing, the drying be at 100~140 DEG C dry 5~15h, at being roasted to 300~600 DEG C be calcined 1~5h.
The nanometer EU-1 molecular sieves that the present invention is provided can serve as the adsorbent that gas, liquid mixture are separate, can also be as the carrier of catalyst or acidic catalyst component, especially in the reaction such as hydrocarbons hydrogenation cracking, hydroisomerization, alkane aromatization, alkylation and transalkylation.
Compared with prior art, the synthetic method of the nanometer EU-1 molecular sieves that the present invention is provided has advantages below:
(1)The synthetic method that the present invention is provided can synthesize a nanometer EU-1 molecular sieves in the case of low consumption of template agent, and not only crystallinity is high, and without other Crystal impurities.
(2)In the inventive method, synthesized gel rubber is mixed with special macropore carbon, gel is limited in the nano pore of macropore carbon carries out crystallization, the size of molecular sieve crystal is limited in the range of nanoscale.Also, because nano molecular sieve is in the constraint of macropore carbon, with the bulky grain that macropore carbon forms micron level, it is possible to wash the impurity such as unreacted raw material using conventional filter operation, it is to avoid use the product collection mode of highly energy-consuming as centrifugation.The porous of the macropore carbon is most important, when aperture is excessive, crystallization in the free space that gel is fled to outside macropore carbon in crystallization in macropore duct due to the constraint that high temperature warm-up movement is easily separated from duct, forms larger crystal molecular sieve, it is impossible to synthesize nano molecular sieve.
(3)In the inventive method, step(2)Described in processing method be to stir in a heated condition, make the moisture slow evaporation in mixture, until solution is changed into viscous pasty state;Then treatment is further dried again, is that a kind of dynamic is dried and static dry combination.Due to there is larger density variation between macropore carbon and synthesized gel rubber, phenomenon of phase separation is susceptible to.If using conventional static dry mode, just having most of synthesized gel rubber and cannot be introduced into inside the duct of macropore carbon.During crystallization, this partial gel can be big crystal grain or the tight viscous small particle molecular sieve being linked togather in crystallization in the free space outside macropore carbon, cannot finally synthesize the homogeneous nano molecular sieve product of crystal yardstick.
(4)In the inventive method, using through base extraction and the calcium carbonate being heat-treated as hard template, required carbon material can be obtained, calcium carbonate is pre-processed using the inventive method, the Surface electric property of calcium carbonate can be made to change, promote the calcium carbonate of a part of single dispersing form to assemble, make several calcium carbonate particles assemble to form miniature coherent condition, in order to form the template needed for macropore duct.And the surface area of material is reduced finally by high-temperature process is carried out to carbon material, the effect of regulation surface area and pore structure is reached, the mechanical strength of material can also be improved.
Brief description of the drawings
Fig. 1 is the XRD spectra of the nanometer EU-1 molecular sieves that embodiment 1 is obtained.
Fig. 2 is the TEM photos of the nanometer EU-1 molecular sieves that embodiment 1 is obtained.
Fig. 3 is the XRD spectra of the nanometer EU-1 molecular sieves that comparative example 2 is obtained.
Fig. 4 is the TEM photos of the nanometer EU-1 molecular sieves that comparative example 2 is obtained.
Specific embodiment
EU-1 Zeolite synthesis method of the invention is described in detail below by specific embodiment, but is not limited to embodiment.Sial raw material, acid, alkali and solvent for being used in the embodiment of the present invention etc. are analysis pure chemistry reagent, and the granularity of calcium carbonate used is 40nm or so.
Embodiment 1
The preparation of macropore carbon material:
(a)150g calcium carbonate is mixed with 5000mL 0.05mol/L sodium hydroxide solutions, 2h is stirred under the conditions of 70 DEG C;Then filtered, the solid sample for obtaining dries 2.5h under the conditions of 500 DEG C;
(b)To step(a)7000mL distilled water and 300g sucrose, ultrasonication 5h after stirring 30min are added in the calcium carbonate for obtaining.
(c)By step(b)The solution of preparation is placed in 70 DEG C of stirred in water bath treatment, moisture evaporation to solution is changed into viscous pasty state;Then dried under the conditions of 70 DEG C;Finally sample is placed in tube furnace, nitrogen is passed through, nitrogen flow rate is 20mL/min;With 11 DEG C/min from room temperature to 900 DEG C, constant temperature 5h;
(d)By step(c)The material for obtaining is well mixed with the hydrochloric acid solution of 5000mL 50%, and 6h is processed under the conditions of 140 DEG C, is finally washed with water to neutrality, and 10h is dried under the conditions of 100 DEG C,
(e)By step(d)The sample for obtaining is placed in tube furnace, is passed through nitrogen, and nitrogen flow rate is 30mL/min;900 DEG C are warming up to 5 DEG C/min, constant temperature 5h prepares carbon material.
Embodiment 2
(1)Take 0.85
G NaOH is dissolved in 30 mL distilled water, stirring 30
min.It is subsequently added into 0.6 g sodium aluminates, stirring 30
min.Add 2g C6s, stirring 30
min.6.5 g white carbons, stirring 30 are slowly added again
min。
(2)By step(1)The synthesized gel rubber for obtaining mixes with the macropore carbon prepared by 7.5g embodiments 1, ultrasonication 30min;Then under the conditions of 60 DEG C stir process to viscous pasty state;Then dried under the conditions of 110 DEG C, until moisture evaporating completely.
(3)Then just step(2)Gained mixture is placed in reactor, adds 7 mL water.Then closed reactor, 190 DEG C of crystallization 60h in baking oven are placed in by reactor.Then by solid product filtration washing to neutrality, 10h is dried under the conditions of 100 DEG C, last 500 DEG C of roasting 3h in air atmosphere, gained sample number into spectrum is CL1, gained sample XRD spectra and TEM photos are as depicted in figs. 1 and 2, it is pure nanometer EU-1 molecular sieves, without other impurity, properties of samples is shown in Table 1.
Embodiment 3
(1)Take 0.65
G NaOH is dissolved in 30 mL distilled water, stirring 30
min.It is subsequently added into 0.3 g sodium aluminates, stirring 30
min.Add 1.5g C6s, stirring 30
min.6.5 g white carbons, stirring 30 are slowly added again
min。
(2)By step(1)The synthesized gel rubber for obtaining mixes with the macropore carbon prepared by 10g embodiments 1, ultrasonication 30min;Then under the conditions of 70 DEG C stir process to viscous pasty state;Then dried under the conditions of 120 DEG C, until moisture evaporating completely.
(3)Then just step(2)Gained mixture is placed in reactor, adds 10 mL water.Then closed reactor, 210 DEG C of crystallization 55h in baking oven are placed in by reactor.Then by solid product filtration washing to neutrality, 10h is dried under the conditions of 100 DEG C, finally 500 DEG C of roasting 3h in air atmosphere, gained sample number into spectrum is CL2, is pure nanometer EU-1 molecular sieves, and without other impurity, properties of samples is shown in Table 1.
Embodiment 4
(1)Take 0.75
G NaOH is dissolved in 30 mL distilled water, stirring 30
min.It is subsequently added into 0.5 g aluminum nitrates, stirring 30
min.Add 0.75g C6s, stirring 30
min.5 g white carbons, stirring 30 are slowly added again
min。
(2)By step(1)The synthesized gel rubber for obtaining mixes with the macropore carbon prepared by 8g embodiments 1, ultrasonication 30min;Then under the conditions of 60 DEG C stir process to viscous pasty state;Then dried under the conditions of 110 DEG C, until moisture evaporating completely.
(3)Then just step(2)Gained mixture is placed in reactor, adds 12 mL water.Then closed reactor, 200 DEG C of crystallization 36h in baking oven are placed in by reactor.Then by solid product filtration washing to neutrality, 10h is dried under the conditions of 100 DEG C, finally 500 DEG C of roasting 3h in air atmosphere, gained sample number into spectrum is CL3, is pure nanometer EU-1 molecular sieves, and without other impurity, properties of samples is shown in Table 1.
Embodiment 5
(1)Take 0.6 g NaOH and be dissolved in 30 mL distilled water, stir 30 min.0.35 g aluminum sulfate is subsequently added into, 30 min are stirred.1g C6s are added, 30 min are stirred.5.5 g silica gel are slowly added again, stir 30 min.
(2)By step(1)The synthesized gel rubber for obtaining mixes with the macropore carbon prepared by 9g embodiments 1, ultrasonication 25min;Then under the conditions of 65 DEG C stir process to viscous pasty state;Then dried under the conditions of 130 DEG C, until moisture evaporating completely.
(3)Then just step(2)Gained mixture is placed in reactor, adds 12 mL water.Then closed reactor, 210 DEG C of crystallization 65h in baking oven are placed in by reactor.Then by solid product filtration washing to neutrality, 10h is dried under the conditions of 100 DEG C, finally 500 DEG C of roasting 3h in air atmosphere, gained sample number into spectrum is CL4, is pure nanometer EU-1 molecular sieves, and without other impurity, properties of samples is shown in Table 1.
Comparative example 1
According to conventional hydrothermal synthetic method, take 0.85 g NaOH and be dissolved in 30 mL distilled water, stir 30 min.0.6 g sodium aluminates are subsequently added into, 30 min are stirred.6g C6s are added, 30 min are stirred.6.5 g white carbons are slowly added again, stir 30 min.It is then charged into closed reactor, 200 DEG C of h of crystallization 60 in baking oven.Then by the products therefrom multiple centrifuge washing of supercentrifuge to neutrality(Conventional filtration operation cannot be carried out).Then 10h is dried under the conditions of 100 DEG C, finally 500 DEG C of roasting 3h in air atmosphere, gained sample number into spectrum is CL5, and the nanometer EU-1 molecular sieves for being, properties of samples is shown in Table 1.
Comparative example 2
According to the material proportion of embodiment 2, not having stirring to dry link carries out contrast experiment
(1)Take 0.85
G NaOH is dissolved in 30 mL distilled water, stirring 30
min.It is subsequently added into 0.6 g sodium aluminates, stirring 30
min.Add 2g C6s, stirring 30
min.6.5 g white carbons, stirring 30 are slowly added again
min。
(2)By step(1)The synthesized gel rubber for obtaining mixes with the macropore carbon prepared by 7.5g embodiments 1, ultrasonication 30min;Then dried under the conditions of 110 DEG C, until moisture evaporating completely.
(3)Then just step(2)Gained mixture is placed in reactor, adds 7 mL water.Then closed reactor, 190 DEG C of crystallization 60h in baking oven are placed in by reactor.Then by solid product filtration washing to neutrality, 10h is dried under the conditions of 100 DEG C, last 500 DEG C of roasting 3h in air atmosphere, gained sample number into spectrum is CL6, and gained sample XRD spectra and TEM photos are EU-1 molecular sieves as shown in Figure 3 and Figure 4, but crystal particle diameter skewness, both containing the small crystals less than 100nm, also comprising the big crystal taken measurements greatly more than 100nm, properties of samples is shown in Table 1.
Comparative example 3
According to the material proportion of embodiment 2, there is stirring to dry link but do not add the macropore carbon to carry out contrast experiment.
(1)Take 0.85 g NaOH and be dissolved in 30 mL distilled water, stir 30 min.0.6 g sodium aluminates are subsequently added into, 30 min are stirred.2g C6s are added, 30 min are stirred.6.5 g white carbons are slowly added again, stir 30 min.
(2)By step(1)The synthesized gel rubber ultrasonication 30min for obtaining;Then under the conditions of 60 DEG C stir process to viscous pasty state;Then dried under the conditions of 110 DEG C, until moisture evaporating completely.
(3)Then just step(2)Gained mixture is placed in reactor, adds 7 mL water.Then closed reactor, 190 DEG C of crystallization 60h in baking oven are placed in by reactor.Then by solid product filtration washing to neutrality, 10h is dried under the conditions of 100 DEG C, finally 500 DEG C of roasting 3h in air atmosphere, gained sample number into spectrum is CL7, and gained sample is EU-1 molecular sieves, but crystal yardstick is more than 100nm, nano molecular sieve is not belonging to, properties of samples is shown in Table 1.
The property of the embodiment of table 1 and comparative example gained sample.
Note:The relative crystallinity that table 1 is given is the crystallinity with CL1 as reference.
Claims (19)
1. a kind of nanometer of synthetic method of EU-1 molecular sieves, the crystal structure of molecular sieve is EU-1 molecular sieves, and without other Crystal impurities, its crystal size is less than 100nm, the described method comprises the following steps:
(1)First that inorganic base is soluble in water, rear addition template to be dissolved adds silicon source, after silicon source is added after silicon source dissolving completely, gel is obtained after being well mixed, and the molar ratio of material is:0.3~7Na2O:25~110SiO2:A12O3:450~1600H2O:1~6 template;
(2)By step(1)The gel for obtaining mix with macropore carbon after 10~60min of ultrasonication, then stir process to viscous pasty state, is then dried, until moisture evaporating completely under the conditions of 80~180 DEG C under the conditions of 50~100 DEG C;
(3)By step(2)The mixture for obtaining loads reactor, adds quantitative water, and then closed reactor carries out crystallization, and reaction temperature is 180~240 DEG C, and the reaction time is 25~100h;
(4)By step(3)The solid product filtration washing for obtaining is dried, and a nanometer EU-1 molecular sieves are obtained after being then calcined in oxygen or air atmosphere.
2. in accordance with the method for claim 1, it is characterised in that:Step(1)Described in inorganic base be one or more in NaOH, KOH, LiOH;Silicon source is one or more in sodium aluminate, aluminum sulfate, aluminium chloride, aluminum nitrate;Silicon source is one or more in White Carbon black, silica gel, Ludox or waterglass;Template is C6.
3. in accordance with the method for claim 1, it is characterised in that:Step(1)Described in molar ratio of material be 0.5~6Na2O:30~100SiO2:A12O3:500~1500H2O:2~5 templates.
4. in accordance with the method for claim 1, it is characterised in that:Step(2)Middle macropore carbon is a kind of micron-sized carbon material, and particle diameter is 0.5~100 μm, and preferably 1~70 μm, the aperture of the macropore carbon is 20~150nm, more preferably preferably 25~110nm, 30~110nm.
5. in accordance with the method for claim 1, it is characterised in that:Step(2)Described in macropore carbon method be prepared by the following procedure obtain:(a)Calcium carbonate is mixed with alkali lye, then the stir process at 50~90 DEG C filters, the solid matter being filtrated to get is heat-treated 1~3h at 300~500 DEG C;(b)Will be through step(a)Calcium carbonate after treatment mixes with water and glucide, after 10~60min of stirring, 1~10h of ultrasonication;(c)By step(b)The solution for obtaining stir process to solution at 50~100 DEG C is in viscous pasty state, is then dried at 50~80 DEG C, is finally placed in nitrogen atmosphere 3~10h of charing process at 700~1000 DEG C;(d)By step(c)The material for obtaining is well mixed with acid solution, and 1~10h is processed at 50~200 DEG C, is washed out drying;(e)By step(d)The material for obtaining in a nitrogen atmosphere, in 700~1000 DEG C of 3~10h of high-temperature process, obtains macropore carbon.
6. in accordance with the method for claim 5, it is characterised in that:Step(a)Described in calcium carbonate be nano-calcium carbonate, the particle diameter of the nano-calcium carbonate is 30~50nm.
7. in accordance with the method for claim 5, it is characterised in that:Step(a)Described in alkali lye be NaOH, potassium hydroxide in one or two, the concentration of lye be 0.01~0.1mol/L.
8. in accordance with the method for claim 5, it is characterised in that:Step(a)Middle calcium carbonate is 1 with the mass ratio of alkali lye:5~1:50, preferably 1:10~1:20.
9. in accordance with the method for claim 5, it is characterised in that:Step(b)Described in glucide be sucrose, glucose in one or two.
10. in accordance with the method for claim 5, it is characterised in that:Step(b)Middle calcium carbonate, glucide, the mass ratio of water are 0.1~2:1:10~33, preferably 0.2~1:1:13~26.
11. in accordance with the method for claim 5, it is characterised in that:Step(c)Described in charing process carried out in nitrogen atmosphere, nitrogen flow rate be 10~50mL/min, preferably 15~40 mL/min.
12. in accordance with the method for claim 11, it is characterised in that:Step(c)Described in charing process heating rate be 1~10 DEG C/min, heated up with constant heating rate, described charing process processes 4~8h at 800~950 DEG C.
13. in accordance with the method for claim 5, it is characterised in that:Step(d)Described in acid solution be hydrochloric acid or nitric acid, the mass concentration of acid solution is 20~60%.
14. in accordance with the method for claim 5, it is characterised in that:Step(d)Described in treatment conditions be at 100~180 DEG C treatment 2~7h.
15. in accordance with the method for claim 5, it is characterised in that:Step(e)Described in high-temperature process carried out in nitrogen atmosphere, nitrogen flow rate is 10~50mL/min, and preferably 15~40 mL/min, the high-temperature process heating rate is 1~10 DEG C/min, is heated up with constant heating rate.
16. in accordance with the method for claim 1, it is characterised in that:Step(2)Middle macropore carbon is 1 with the weight ratio of gel butt:1.5~0.1, preferably 1:1.2~0.2.
17. in accordance with the method for claim 1, it is characterised in that:Step(2)Described in ultrasonic treatment time be 20~40min;Stir process temperature is 60~90 DEG C;Described drying temperature is 100~150 DEG C.
18. in accordance with the method for claim 1, it is characterised in that:Step(3)Middle material mol ratio is:0.3~7Na2O:25~110SiO2:A12O3:20~220H2O:1~6 template, preferably 0.5~6Na2O:30~100SiO2:A12O3:30~200H2O:2~5 templates.
19. in accordance with the method for claim 1, it is characterised in that:Step(3)Described in crystallization temperature be 100~150 DEG C, the reaction time be 20~80h.