CN106694059A - Ion exchange filter element and manufacturing method thereof - Google Patents
Ion exchange filter element and manufacturing method thereof Download PDFInfo
- Publication number
- CN106694059A CN106694059A CN201710062548.2A CN201710062548A CN106694059A CN 106694059 A CN106694059 A CN 106694059A CN 201710062548 A CN201710062548 A CN 201710062548A CN 106694059 A CN106694059 A CN 106694059A
- Authority
- CN
- China
- Prior art keywords
- mesh
- filter core
- ion exchange
- exchange filter
- attapulgite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an ion exchange filter element which is mainly prepared from the following raw materials in percentage by weight: 10-35% of attapulgite of 100-300 meshes, 35-60% of vermiculite of 200-400 meshes and 10-35% of a fiber adhesive of 100-300 meshes. With the adoption of the technical scheme, the ion exchange filter element disclosed by the invention is prepared by taking the attapulgite, vermiculite and fiber adhesive as raw materials; the attapulgite has an absorption effect and an ion exchange capacity and is capable of removing colors, deodorizing, removing odor and the like; due to a relatively high layer charge number, the vermiculite has a relatively high cation exchange capacity and a relatively high cation exchange adsorption capacity and is convenient for mineral salt adsorption; and the fiber adhesive contributes to molding and prevents a finished product from deforming and shrinking in the using process and the like. Moreover, the ion exchange filter element is fibriform after processing, and a micro-porous structure of the filter element is well kept.
Description
Technical field
The invention belongs to filtering material technical field, it is related to a kind of ion exchange filter core.
Background technology
In water treatment system, water is pre-processed frequently with activated carbon, the common Water treatment filter element kind of in the market
It is more single, usually active carbon filter core, polypropylene melt blown filter or ceramic element etc..Although traditional active carbon filter core tool
There is good suction-operated, chlorine residue, peculiar smell and the color that can effectively go in water removal etc., polypropylene melt blown filter and ceramic element are then
Filter effect to magazines such as silt or suspensions is preferable.Above-mentioned common filtering element for treating water is to heavy-metal ion removal and agriculture
The abilities such as medicine are very limited.Additionally, the mechanical interception ability of traditional Water treatment filter element is poor etc..
Vermiculite is a kind of natural, inorganic, nontoxic mineral matter, with ion-exchange capacity, can be used as adsorbent.
Attapulgite refers to a kind of clay mineral with attapulgite as key component, and attapulgite is also known as palygorskite or slope
Thread thin white silk used in ancient China stone, is a kind of clay mineral of zeopan containing Shuifu County for having chain layer structure.Because attapulgite has unique crystalline substance
Body structure, is allowed to cation interchangeability, water imbibition, adsorption bleaching, big specific surface area and colloid index and expansion
Physical and chemical performance and the processing performances such as appearance.
Therefore, attapulgite and vermiculite above have great application prospect in the application of water process.
The processing method of traditional filter core is generally using extrusion forming or the processing method of sinter molding.In extrusion forming
In processing, curable type generally is aided in added with glue, this glue easily blocks filter core micropore, can destroy 70% micropore, and filter material is to water
Resistance become big.Water-flowing amount diminishes, and hydrophily is deteriorated, and causes the filter core after extrusion forming is processed, and its water-flowing amount is low, filtering
Efficiency is low.In sinter molding processing, curable type is generally aided in using binding agent, after through high-temperature activation, block filter core micropore, it is right
The resistance of water becomes big.Water-flowing amount diminishes, and hydrophily is deteriorated, and causes that the filter efficiency of filter core is low, and effect is poor.
Therefore, it is necessary to studying one kind can largely keep filter core micropore, the processing method of the preferable filter core of hydrophily.
The content of the invention
In view of this, it is commutative to go to eliminate the unusual smell, go in water removal it is an object of the invention to provide a kind of ion exchange filter core
The ion of dissolving, gluey ion, heavy metal and its compound etc..
In order to reach above-mentioned purpose, the technical scheme is that：
A kind of ion exchange filter core, is mainly prepared from by the raw material of following percentage by weight：
The attapulgite 10%-25% of 100 mesh~300 mesh；
200 mesh~400 mesh vermiculites 45%~75%；
The fiber binder 10%~35% of 100 mesh~300 mesh.
Mainly it is prepared from by the raw material of following percentage by weight：
Attapulgite 15%-20% described in 100 mesh~300 purposes；
Vermiculite 55%~63% described in 200 mesh~400 purposes；
Fiber binder 20%~28% described in 100 mesh~300 purposes.
Mainly it is prepared from by the raw material of following percentage by weight：
The attapulgite 20%-25% of 100 mesh~300 mesh；
200 mesh~400 mesh vermiculites 60%~70%；
The fiber binder 10%~15% of 100 mesh~300 mesh.
The fiber binder name of an article is BiPUL 50TWG, and spinning Co., Ltd. by Japanese Japan provides.
A kind of preparation method of ion exchange filter core, comprises the following steps：
(1) prepare the attapulgite of 100 mesh~300 mesh, the fiber of mesh~300 mesh of vermiculite 100 of 200 mesh~400 mesh to glue
Mixture；
(2) stir：Raw material input temporary storage tank is carried out in mixing and stirring, temporary storage tank added with pure water, it is described
The amount of pure water is 15-22 with raw material otal investment ratio：1, the original slurry material of sticky shape is formed after stirring；
(3) it is molded：By step 2) obtained by original slurry material wet type shaped device be delivered to by pipe-line transportation system enter successively
Row suction and integer, and then be molded, obtain first product；Or, by step 2) obtained by original slurry material by pipe-line transportation system convey
Forming processes are carried out to moulding machine, first product is obtained；
(4) dry：By step 2) obtained by first product be sent to baking oven, at a temperature of 100~150 DEG C, dry 6~10 small
When, obtain finished product.
The wet type shaped device uses suction feeder, during the suction, according to suction amount and vacuum
Control the time of suction.
In the whipping process, the amount of the pure water is 18~19 with the raw material otal investment ratio：1；Institute
State in baking step, the first product dries 7.5~8.5h in 120~125 DEG C of the baking oven, obtains finished product.
The finished product is tubulose or sheet.
After adopting the above technical scheme, a kind of ion exchange filter core of the invention, with attapulgite, vermiculite and fiber binder
For raw material is made, attapulgite has suction-operated and ion-exchange capacity, can decolourize, deodorant to taste etc.；Vermiculite also has
There is ion-exchange capacity；Fiber binder contributes to shaping, prevents finished product from deforming shrink etc. in use.With it is traditional from
Sub-exchange resin is compared, and regenerating easily, pollution-free, exchange velocity are fast, exchange capacity is big, alternative ion exchange resin.
A kind of preparation method of ion exchange filter core of the present invention, by mixing, being molded and baking step, technique letter
It is single, the temperature that control is dried when drying so that the colloid of fiber binder can melt and not coking, still in fibre after processing
Dimension shape, it is ensured that quality of finished.Compared with traditional technology, the present invention is bonded using the preparation method of wet type shaping by fiber
The filtration core that agent is made, fiber binder is not easily blocked filter core micropore, the so filter of shaping also in threadiness in finished product filter core
Core remains filter core micropore, i.e., do not destroy micropore, not blocking microporous, can reduce the resistance being subject to during filter element filtering, and filtering is logical
Freely, and larger water-flowing amount can be formed, the service life of filter core can also be extended while with excellent hydrophilic.
Specific embodiment
In order to technical scheme is explained further, the present invention is explained in detail below by specific embodiment
State.In the present invention, attapulgite uses concave convex rod fibrous powder.
First, filter core makes
Embodiment one
A kind of ion exchange filter core, is mainly prepared from by the raw material of following percentage by weight：
The attapulgite 20% of 100 mesh；
The vermiculite 60% of 200 mesh；
The fiber binder 20% of 100 mesh.
The preparation method of the ion exchange filter core, comprises the following steps：
(1) raw material prepares：Prepare the fiber binder of the attapulgite, the vermiculite of 200 mesh and 100 mesh of 100 mesh；
(2) mix：By the raw material in step (1) according to the above ratio, in input temporary storage tank, temporary storage tank is equiped with automatically
Agitating device, added with pure water in temporary storage tank, amount and the ratio of input raw material otal investment of pure water are 19:1, shape after stirring
Into the original slurry material of sticky shape；
(3) it is molded：By step 2) obtained by original slurry material the slurry tank of suction feeder is delivered to by pipe-line transportation system,
The filter core cylinder of annular shape is installed on the fixed station of suction feeder, the filter core cylinder offers micropore, is easy to original slurry material to exist
The filter core of cylindrical shape is adsorbed under vacuum action.In order to prevent original slurry material through micropore, coated on the lateral wall of filter core cylinder
There is layer of non-woven fabric, then, filter core base material is adsorbed on filter core cylinder up to certain thickness.The thickness can be carried out according to actual demand
Accommodation.Further, the filter core after suction is carried out into integer, and then is molded, obtain first product；It should be noted that this
In invention, filter core may also be fabricated which tubulose or sheet etc..During suction of the filter core of different shape and specification in suction feeder
Between it is different, accommodation can be carried out according to actual conditions；
(4) dry：By step 3) obtained by first product be sent to baking oven, at a temperature of 115 DEG C, dry 8 hours, obtain into
Product, i.e. the ion exchange filter core.
Embodiment two
A kind of ion exchange filter core, is mainly prepared from by the raw material of following percentage by weight：
The attapulgite 25% of 250 mesh；
The vermiculite 50% of 400 mesh；
The fiber binder 25% of 250 mesh.
The preparation method of the ion exchange filter core, comprises the following steps：
(1) raw material prepares：Prepare the vermiculite of the attapulgite, the fiber binder of 250 mesh and 400 mesh of 250 mesh；
(2) mix：By the raw material in step (1) according to the above ratio, in input temporary storage tank, temporary storage tank is equiped with automatically
Agitating device, added with pure water in temporary storage tank, amount and the ratio of input raw material otal investment of pure water are 18:1, shape after stirring
Into the original slurry material of sticky shape；
(3) it is molded：By step 2) obtained by original slurry material the slurry tank of suction feeder is delivered to by pipe-line transportation system,
The filter core cylinder of annular shape is installed on the fixed station of suction feeder, the filter core cylinder offers micropore, is easy to original slurry material to exist
The filter core of cylindrical shape is adsorbed under vacuum action.In order to prevent original slurry material through micropore, coated on the lateral wall of filter core cylinder
There is layer of non-woven fabric, then, filter core base material is adsorbed on filter core cylinder up to certain thickness.The thickness can be carried out according to actual demand
Accommodation.Further, the filter core after suction is carried out into integer, and then is molded, obtain first product；It should be noted that this
In invention, filter core may also be fabricated which tubulose or sheet etc..During suction of the filter core of different shape and specification in suction feeder
Between it is different, accommodation can be carried out according to actual conditions；
(4) dry：By step 3) obtained by first product be sent to baking oven, at a temperature of 125 DEG C, dry 7.5 hours, obtain into
Product, i.e. the ion exchange filter core.
Embodiment three
A kind of ion exchange filter core, is mainly prepared from by the raw material of following percentage by weight：
The attapulgite 10% of 200 mesh；
The vermiculite 55% of 300 mesh；
The fiber binder 35% of 200 mesh.
The preparation method of the ion exchange filter core, comprises the following steps：
(1) raw material prepares：Prepare the vermiculite of the attapulgite, the fiber binder of 300 mesh and 300 mesh of 200 mesh；
(2) mix：By the raw material in step (1) according to the above ratio, in input temporary storage tank, temporary storage tank is equiped with automatically
Agitating device, added with pure water in temporary storage tank, amount and the ratio of input raw material otal investment of pure water are 20：1, shape after stirring
Into the original slurry material of sticky shape；
(3) it is molded：By step 2) obtained by original slurry material the slurry tank of suction feeder is delivered to by pipe-line transportation system,
The filter core cylinder of annular shape is installed on the fixed station of suction feeder, the filter core cylinder offers micropore, is easy to original slurry material to exist
The filter core of cylindrical shape is adsorbed under vacuum action.In order to prevent original slurry material through micropore, coated on the lateral wall of filter core cylinder
There is layer of non-woven fabric, then, filter core base material is adsorbed on filter core cylinder up to certain thickness.The thickness can be carried out according to actual demand
Accommodation.Further, the filter core after suction is carried out into integer, and then is molded, obtain first product；It should be noted that this
In invention, filter core may also be fabricated which tubulose or sheet etc..During suction of the filter core of different shape and specification in suction feeder
Between it is different, accommodation can be carried out according to actual conditions；
(4) dry：By step 3) obtained by first product be sent to baking oven, at a temperature of 120 DEG C, dry 8 hours, obtain into
Product, i.e. the ion exchange filter core.
Example IV
A kind of ion exchange filter core, is mainly prepared from by the raw material of following percentage by weight：
The attapulgite 15% of 200 mesh；
The vermiculite 60% of 300 mesh；
The fiber binder 25% of 200 mesh.
The preparation method of the ion exchange filter core, comprises the following steps：
(1) raw material prepares：Prepare the vermiculite of the attapulgite, the fiber binder of 300 mesh and 300 mesh of 200 mesh；
(2) mix：By the raw material in step (1) according to the above ratio, in input temporary storage tank, temporary storage tank is equiped with automatically
Agitating device, added with pure water in temporary storage tank, amount and the ratio of input raw material otal investment of pure water are 21：1, shape after stirring
Into the original slurry material of sticky shape；
(3) it is molded：By step 2) obtained by original slurry material the slurry tank of suction feeder is delivered to by pipe-line transportation system,
The filter core cylinder of annular shape is installed on the fixed station of suction feeder, the filter core cylinder offers micropore, is easy to original slurry material to exist
The filter core of cylindrical shape is adsorbed under vacuum action.In order to prevent original slurry material through micropore, coated on the lateral wall of filter core cylinder
There is layer of non-woven fabric, then, filter core base material is adsorbed on filter core cylinder up to certain thickness.The thickness can be carried out according to actual demand
Accommodation.Further, the filter core after suction is carried out into integer, and then is molded, obtain first product；It should be noted that this
In invention, filter core may also be fabricated which tubulose or sheet etc..During suction of the filter core of different shape and specification in suction feeder
Between it is different, accommodation can be carried out according to actual conditions；
(4) dry：By step 3) obtained by first product be sent to baking oven, at a temperature of 120 DEG C, dry 8 hours, obtain into
Product, i.e. the ion exchange filter core.
Embodiment five
The present embodiment and the percentage by weight that the difference of embodiment one is raw material：
The attapulgite 20% of 100 mesh；
The vermiculite 70% of 200 mesh；
The fiber binder 10% of 100 mesh.
It should be noted that 100 mesh~300 mesh attapulgites in the present invention can be commercially available gained, also can be by purchase
Attapulgite carries out cutting and grinding and then reaches corresponding granular size requirement.In the present invention, fiber binder, and vermiculite is
Commercially available gained, wherein, the fiber binder name of an article is BiPUL 50TWG, and spinning Co., Ltd. by Japanese Japan provides.
Embodiment six
The present embodiment is with the difference of any embodiment of one~embodiment of embodiment five：The making side of ion exchange filter core
Step (3) in method, in the present embodiment, the first products such as sheet is caused in step (3) shaping by moulding machine by original slurry material.
2nd, performance test
By above-described embodiment one to the made filter core for obtaining of embodiment five, Drinking Water is sampled at water-filling respectively
Reason test.Table 1 be a kind of made ion exchange filter core for obtaining of embodiment five to sample Drinking Water carry out it is water-treated
The test result report that filter test is obtained, as a result shows：After treatment, turbidity is low, and naked eyes visible is almost removed, the present invention
A kind of ion exchange filter core has preferable adsorption capacity, ion-exchange capacity and mechanical interception ability.
It should be noted that embodiment five is preferred scheme of the invention, the filter in the present invention obtained by other embodiment
The corresponding test result of projects that core is tested meets technical requirements, and its test result is same or like with following table.
The test result of table 1 is reported
Above-described embodiment and non-limiting product form of the invention and style, the ordinary skill people of any art
Appropriate change or modification that member is done to it, all should be regarded as not departing from patent category of the invention.
Claims (8)
1. a kind of ion exchange filter core, it is characterised in that be mainly prepared from by the raw material of following percentage by weight：
The attapulgite 10%-25% of 100 mesh~300 mesh；
200 mesh~400 mesh vermiculites 45%~75%；
The fiber binder 10%~35% of 100 mesh~300 mesh.
2. a kind of ion exchange filter core according to claim 1, it is characterised in that the main original by following percentage by weight
Material is prepared from：
Attapulgite 15%-20% described in 100 mesh~300 purposes；
Vermiculite 55%~63% described in 200 mesh~400 purposes；
Fiber binder 20%~28% described in 100 mesh~300 purposes.
3. a kind of ion exchange filter core according to claim 1, it is characterised in that the main original by following percentage by weight
Material is prepared from：
The attapulgite 20%-25% of 100 mesh~300 mesh；
200 mesh~400 mesh vermiculites 60%~70%；
The fiber binder 10%~15% of 100 mesh~300 mesh.
4. the preparation method of the ion exchange filter core according to any one of claim 1-3, it is characterised in that：The fibre
The dimension adhesive name of an article is BiPUL 50TWG, and spinning Co., Ltd. by Japanese Japan provides.
5. the preparation method of ion exchange filter core according to claim 1, it is characterised in that comprise the following steps：
(1) attapulgite, the fiber binder of mesh~300 mesh of vermiculite 100 of 200 mesh~400 mesh of 100 mesh~300 mesh are prepared；
(2) stir：Raw material input temporary storage tank is carried out in mixing and stirring, temporary storage tank added with pure water, it is described pure
The amount of water is 15-22 with raw material otal investment ratio：1, the original slurry material of sticky shape is formed after stirring；
(3) it is molded：By step 2) obtained by original slurry material wet type shaped device be delivered to by pipe-line transportation system inhaled successively
Material and integer, and then be molded, obtain first product；Or, by step 2) obtained by original slurry material be delivered to by pipe-line transportation system and make
Type machine carries out forming processes, obtains first product；
(4) dry：By step 2) obtained by first product be sent to baking oven, at a temperature of 100~150 DEG C, dry 6~10 hours, obtain
To finished product.
6. the preparation method of ion exchange filter core according to claim 4, it is characterised in that：The wet type shaped device is adopted
With suction feeder, during the suction, according to suction amount and the time of vacuum degree control suction.
7. the preparation method of ion exchange filter core according to claim 4, it is characterised in that：In the whipping process,
The amount of the pure water is 18~19 with the raw material otal investment ratio：1；In the baking step, the first product is in 120
In~125 DEG C of the baking oven, 7.5~8.5h is dried, obtain finished product.
8. the preparation method of the ion exchange filter core according to claim 4 or 6, it is characterised in that：The finished product is tubulose
Or sheet.