CN106690644A - Shoe sole, shoe and shoe making method - Google Patents
Shoe sole, shoe and shoe making method Download PDFInfo
- Publication number
- CN106690644A CN106690644A CN201510455429.4A CN201510455429A CN106690644A CN 106690644 A CN106690644 A CN 106690644A CN 201510455429 A CN201510455429 A CN 201510455429A CN 106690644 A CN106690644 A CN 106690644A
- Authority
- CN
- China
- Prior art keywords
- sole
- filler
- shape
- methods according
- opening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a shoe sole, a shoe with the shoe sole, and a corresponding shoe making method. According to one embodiment, the shoe sole comprises a lower portion in a three-dimensional shape, and filler, wherein the filler is formed in the lower portion in a perfusion mode.
Description
Technical field
The application is related to shoe-making field, in particular it relates to a kind of sole and the footwear with the sole,
And corresponding manufacturing method of shoes.
Background technology
Existing sole, especially midsole, material selection often be faced with compressive deformation and footwear
The compromise of bottom weight.In general, sole (such as traditional EVA with larger compressive deformation
Midsole) durability it is poor, and there is the sole of excellent durability (such as in traditional PU
Bottom) and often there is larger weight.
The content of the invention
The application is directed to a kind of sole, has while with excellent durability lighter
Weight.
The application also proposed footwear and corresponding manufacturing method of shoes with the sole.
According to the one side of the application, it is proposed that a kind of sole, including with 3D shape
Bottom；And perfusion is formed in the filler in the bottom.
In embodiments, the bottom can be formed by the flexible material of such as fabric；The filling
Thing can be thermosets, such as polyurethane or polyurethane foam.
In embodiments, the sole can further include to be bonded on the big of the lower section of the bottom
Bottom.
In embodiments, the sole can further include to stick to the upper surface of the bottom
First leakproof film, is used to prevent the filler from leaking.
In embodiments, the sole can further include to be covered in the upper of the top of the bottom
Portion, wherein, the filler perfusion is formed between the top and the bottom.
In embodiments, the sole can further include to stick to the lower surface on the top
Second leakproof film, is used to prevent the filler from leaking.
In embodiments, the top of the sole can have opening, and the filler is by described
Opening is perfused between the top and the bottom.
In embodiments, the bottom of the sole can have opening, and the filler is by described
Opening is perfused between the top and the bottom.
In embodiments, the 3D shape of the bottom is formed by being molded sizing.
According to the another aspect of the application, it is proposed that a kind of footwear, it has vamp and according to the above
Described sole.
According to the another aspect of the application, it is proposed that a kind of manufacturing method of shoes, including：Molding is formed
Sole bottom with 3D shape；Sole top is covered on the sole bottom；In sole
Filler is injected between top and sole bottom；And by vamp, sole top and sole bottom
It is bonded together.
In embodiments, the method further includes that big bottom is bonded on the lower section of sole bottom.
In embodiments, filler is injected between sole top and sole bottom includes：It is logical
Cross the opening on sole top or the opening injection filler of sole bottom.
In embodiments, the step of filler is injected between sole top and sole bottom exists
Carried out after vamp, sole top and sole bottom are all bonded together, or only by footwear
Bottom top together with sole lower bond after carry out.
In embodiments, the method is further included under the lower surface and sole on sole top
The upper plastic uptake leakproof film at least one of the upper surface in portion.
In embodiments, sole bottom is formed by the flexible material of such as fabric；Filler is
The thermosets of such as polyurethane or polyurethane foam.
According to the another aspect of the application, it is proposed that a kind of manufacturing method of shoes, including：Molding is formed
Sole bottom with 3D shape；Filler is injected on the sole bottom；And by footwear
Face is together with the sole lower bond after injection filler.
In embodiments, the method is further included：Big bottom is bonded under sole bottom
Side.
In embodiments, the method is further included：The plastic uptake on the upper surface of sole bottom
Leakproof film.
In embodiments, sole bottom is formed by the flexible material of such as fabric；Filler is
The thermosets of such as polyurethane or polyurethane foam.
Brief description of the drawings
Fig. 1 shows the sole bottom of the molding according to first embodiment；
Fig. 2 shows the sole bottom with application of anti-leakage layers according to first embodiment；
Fig. 3 shows the sole top according to first embodiment；
Fig. 4 shows vamp according to first embodiment, sole top and sole bottom；
Fig. 5 shows the shoe body according to first embodiment；
Fig. 6 shows the schematic diagram that filler is injected according to first embodiment；
Fig. 7 shows the shoe body injected according to first embodiment and formed after filler；
Fig. 8 shows the product shoes according to first embodiment；
Fig. 9 shows the sole top according to second embodiment；
Figure 10 shows the shoe body according to second embodiment；
Figure 11 shows the schematic diagram that filler is injected according to second embodiment；
Figure 12 shows the shoe body injected according to second embodiment and formed after filler；
Figure 13 shows the sole top and sole bottom according to the 3rd implementation method；
Figure 14 shows the schematic diagram that filler is injected according to the 3rd implementation method；
Figure 15 shows vamp according to the 3rd implementation method, sole and big bottom；
Figure 16 shows the schematic diagram that filler is injected according to the 4th implementation method；
Figure 17 shows vamp according to the 4th implementation method, sole and big bottom；
Figure 18, Figure 19 and Figure 20 show the sole top according to the 5th implementation method；
Figure 21, Figure 22 and Figure 23 show the sole bottom according to the 5th implementation method；
Figure 24 shows the sole top and sole bottom according to the 5th implementation method；
Figure 25 A show vamp according to the 5th implementation method, sole top and sole bottom；
Figure 25 B show vamp, sole top and the sole of the modification according to the 5th implementation method
Bottom；
Figure 26 shows the shoe body according to the 5th implementation method；
Figure 27 shows the schematic diagram that filler is injected according to the 5th implementation method；
Figure 28 shows the shoe body injected according to the 5th implementation method and formed after filler；
Figure 29 shows vamp according to the 5th implementation method, sole and big bottom；And
Figure 30 shows vamp according to the 5th implementation method, sole and another big bottom.
Specific embodiment
According to the application, it is proposed that the sole (midsole) constituted with two kinds of materials, i.e. by first
Material formed the sole bottom with 3D shape, and be made up of the second material injection (or
Perfusion) it is formed in the filler of sole bottom.
In one embodiment, sole bottom is formed by the flexible material of such as fabric, filler
It is such as thermosetting such as polyurethane (polyurethane, PU) or polyurethane foam (PU foam)
Property material.In various embodiments, sole bottom can be by any appropriate flexible material structure
Into filler can be other heat fixation materials, for example, PPG (e.g., Tianjin
The TMD-5000 of the factory of petrochemical industry three) and polyisocyanates (MDI, e.g., the PAPI-27 of Dow companies).
The sole of above-mentioned formation is midsole, and big bottom can be bonded on the lower section of above-mentioned sole bottom.
In the upper surface of the bottom of above-mentioned midsole, one layer of leakproof film can be stained with, be used to prevent
Filler spills.The leakproof film for example can be TPU (thermoplastic polyurethane) film, it is also possible to
The film formed for other plastic foils or by spray adhesive.Leakproof film can be by adhesive
Adhesion, or adhered to by vacuum forming.Leakproof film can also be adhered to by other appropriate ways
On the upper surface of sole bottom.
Selected as one kind, sole bottom directly can be formed by the flexible material of leakproof.
In the top of the sole bottom with 3D shape, sole top is could be covered with, from
And cavity is formed between sole top and bottom, so that filler can be molded is formed in sole
In cavity between upper and lower part.In this case, also may be used on the lower surface on sole top
To adhere to one layer of leakproof film, it is used to prevent the filler from leaking.The leakproof film and sole bottom
Leakproof film on upper surface can simultaneously in the presence of or only exist one, and can be identical
Material or different materials." injection ", " injection " or " perfusion " herein refers to filling out
Fill material to be injected into cavity, and be not proper injection.
In the case of with sole top and sole bottom, top or bottom can have opening,
Filler is allowed to be injected between upper and lower part by the opening on top or bottom.
The 3D shape of above-mentioned sole bottom is for example formed by being molded sizing.
Vamp can be bonded together with above-described sole, to form product shoes.Exist
In the case of sole top, between sole top and sole bottom inject filler the step of
Carried out after vamp, sole top and sole bottom are all bonded together, or only by footwear
Bottom top together with sole lower bond after carry out.It is, the engagement of vamp and sole can
With inject filler before or after carry out.The filler of injection is typically liquid or fluid.
After injecting the mould being made up of the desired shape of sole bottom and sole top, infusion can be with
According to the mold shape expansion and solidification that are pre-designed.
Can also not have sole top, but directly in the sole bottom shape with 3D shape
Into concave shape in inject filler, then by vamp and injection filler after sole bottom
It is bonded together.The mode of engagement is included but is not limited to suture, bonded, ultra-sonic welded etc..
Can also be by vamp and sole in the case of sole top, the step of injection filler
Lower bond is carried out afterwards together.
Several illustrative embodiments of the application are described below in conjunction with accompanying drawing.
Fig. 1 to Fig. 8 show sole according to the illustrative embodiments of the application first, footwear and
Manufacturing method of shoes.
As described above, an implementation method according to the application, forms the filler note of midsole
Modeling is formed in the cavity between sole top and sole bottom.The midsole being consequently formed is by sole
" bagged articles " (pouch) that top and sole bottom are collectively forming is surrounded.Noted by by filler
Enter " bagged articles " that sole top and sole bottom be collectively forming and form midsole, eliminate by into
The step of midsole of shape is aligned with sole top and sole bottom.
Fig. 1 shows that the material 102 to form sole bottom is molded as the footwear with 3D shape
Bottom 104.Specifically, the material 102 for forming sole bottom is placed in mold (punch-pin)
Between 101 and lower mould (cavity plate) 103, being formed by mold treatment has specific three dimensional shape
Sole bottom 104.Mold 101 and lower mould 103 have and desired sole three-dimensional shaped
The corresponding shape of shape.Forming the material 102 of sole bottom can be adapted for any of molding sizing
Suitable material, such as fabric or other flexible materials.The sole bottom 104 of formation is suitable to surround
Filler.
On the one hand, the material of sole filler can have low-density, so that sole (with
And footwear) lightweight.On the other hand, sole bottom can make footwear as the protective layer of filler
Bottom is wear-resisting.
Fig. 2 shows that optional application of anti-leakage layers 203 is coated over the sole bottom 202 of molding sizing
On.As illustrated, by glue spraying 201 the sole bottom 202 with 3D shape upper table
Face forms mucous membrane, and leakproof film 203 is adsorbed on the sole bottom 202 by glue spraying.Leakproof film
203 can be formed on sole bottom 202 with plastic uptake (such as by vacuum forming), it is also possible to
Stick to by other means on sole bottom 202.It is stained with the sole bottom 204 of leakproof film
Also figure 2 illustrates.The leakproof film of use can be thermoplastic polyurethane TPU, or
Other plastics or atomizing adhesive.
Fig. 3 shows sole top 301.The shoe-pad that sole top 301 can be known as.
Can also further have extra shoe-pad outside sole top 301.Adopt on sole top 301
Material can be identical or different with sole bottom.For example, sole top 301 can by with
The identical or different fabric in sole bottom is formed, it is also possible to formed by other appropriate materials.Can
Selection of land, can adhere to leakproof film 302 on the lower surface on sole top 301.Equally, leakproof film
302 can be formed on the lower surface on sole top 301 with plastic uptake (such as by vacuum forming),
Can also stick to by other means on the lower surface on sole top 301.It is stained with leakproof film
Sole top 303 also figure 3 illustrates.The leakproof film of use can be thermoplastic polyurethane
TPU, or other plastics.Fig. 3 is further illustrated to have on sole top 303 and opened
Mouth 304.
Fig. 4 shows vamp 401, the sole top 402 with opening 403 and with three-dimensional
The sole bottom 404 of shape.As illustrated, vamp 401, the sole top with opening 403
402 and the sole bottom 404 with 3D shape can be stitched together along dotted line.Above-mentioned three
Individual part can also be bonded together by other any appropriate modes.For example, can pass through
Adhesive bonding together, or by ultra-sonic welded is bonded together.
Fig. 5 shows the shoe body that vamp, sole top are formed afterwards together with sole lower bond.
Fig. 6 to show and inject filler in the shoe body shown in Fig. 5 by the opening on sole top
Schematic diagram.Filler is injected into sole top and sole bottom by the opening on sole top
Between cavity in.In the case of with leakproof film, the opening that filler passes through sole top
It is injected into the cavity between the leakproof film of the leakproof film on sole top and sole bottom.Injection
Filler can be liquid or fluid.The shape that the filler of injection cavity is adapted to cavity exists
Expanded in the cavity and solidified.The filler of injection shape (or by filler fill it is " packed
The shape of thing ") limited by the shape of the mold with intended shape and lower mould.That injects fills out
The material for filling thing preferably can be the thermosets of such as polyurethane or polyurethane foam.Root
According to one embodiment, the primary raw material of the injection filler of use can be PPG and many
Isocyanates (MDI).
When polyurethane foam, material for example can be that multicomponent polyether combined material is (cold
Curing A, B material, such as respectively PPG and polyisocyanates (MDI), wherein,
PPG can be using the TMD-5000 of the factory of Plant of Tianjin Petrochemical Company three, polyisocyanates (MDI)
Can be using the PAPI-27 of Dow companies), the equipment of use for example can be low pressure reaction perfusion
Machine.
The process of injection is mainly including charging, material feeding, solidification, the demoulding, deburring, solidify afterwards etc..
During charging, the emptying valve of A, B batch can is first turned on, in A, B batch can
Material low pressure list index back to zero after open material inlet valve, closed after A, B material of the scheduled volume that feeds
Valve；A, B batch can emptying valve, A, B batch can low pressure control are closed after A, B material are added
System is in >=0.2Mpa.
, it is necessary to carry out die temperance control in shot process.Specifically, start electric heating water tank to give
Mould is heated, and by water temperature control at 80-95 DEG C, blobs die temperance control is in 45 ± 3 DEG C, self-priming bubble
Die temperance control is at 58 ± 3 DEG C.The starting device under above-mentioned environmental condition, and equipment is adjusted to just
Normal production status, by material temperature control at 25-28 DEG C.A expects and the proportioning of B material can for example set
It is set to 100:52 (being tracked by A, B barrel of rotating speed display table on low pressure reaction bottler placer switch board).
Then material feeding is carried out.
After the completion of mould material feeding, solidified under the temperature conditions for ensureing mould.In example
Property embodiment in, hardening time be no less than 4 minutes.After the completion of solidification, the demoulding can be carried out and repaiied
Side.Further, the product for obtaining can also further carry out normal temperature cure, for example, at least 12
Hour.
Fig. 7 shows the schematic diagram of the shoe body formed after injection filler.It can be seen that, in footwear
There is the opening as injection hole on the top of bottom.
Fig. 8 show including injection after shoe body 802, big bottom 803 and shoe-pad 801 finished product
Footwear 804.Big bottom 803 can have 3D shape corresponding with sole bottom.Big bottom 803 can
With on the lower surface for sticking to sole bottom, it is also possible to otherwise with the following table of sole bottom
Face engages.
Fig. 9 to Figure 12 show sole according to the illustrative embodiments of the application second, footwear and
Manufacturing method of shoes.Present embodiment is with the difference of first embodiment, opening as inlet
Mouth is formed on sole bottom.
For simplicity, repeated no more with same section in first embodiment, it is corresponding attached
Figure is also not repeated to show (Fig. 1, Fig. 2, Fig. 4 and Fig. 8 are also applied for second embodiment).
Fig. 9 shows the sole top 901 in second embodiment, thereon without opening.
Alternatively, leakproof film 902 can be adhered on the lower surface on sole top 901.Equally, leakproof
Film 902 can be formed on sole top 901 with plastic uptake (such as by vacuum forming), also may be used
To stick to by other means on sole top 901.The leakproof film of use can be thermoplasticity
Polyurethane TPU, or other plastics.After Fig. 9 further illustrates plastic uptake leakproof film
Sole top 903.
Figure 10 shows the shoe body that vamp, sole top are formed afterwards together with sole lower bond.
As shown in Figure 10, the bottom (on sole bottom) of sole has opening 1001, is opened by this
Mouth can be injected the filler into.
Figure 11 shows and filling is injected in the shoe pattern shown in Figure 10 by the opening of sole bottom
The schematic diagram of thing.
Figure 12 shows the schematic diagram of the shoe body formed after injection filler.It can be seen that, in footwear
Bottom has the opening as inlet.
Figure 13 to Figure 15 shows sole, the footwear according to the illustrative embodiments of the application the 3rd
And manufacturing method of shoes.Present embodiment is with the difference of first embodiment, by sole top
Carry out the injection process of filler afterwards together with sole lower bond, after the completion of injection, will
Vamp and the sole being molded are bonded together.
For simplicity, repeated no more with same section in first embodiment, it is corresponding attached
Figure is also not repeated to show (Fig. 1, Fig. 2, Fig. 3 and Fig. 8 are also applied for the 3rd implementation method).
As shown in figure 13, with opening 1302 sole top 1301 and with 3D shape
Sole bottom 1303 can be stitched together along dotted line.It should be appreciated that the two can also be by it
Its any appropriate mode is bonded together.For example, can by adhesive bonding together,
Or be bonded together by ultra-sonic welded.Figure 13 further illustrates the He of sole top 1301
Sole bottom 1303 be bonded together after sole (midsole) 1304.
Figure 14 shows the opening by sole top in the sole (midsole) shown in Figure 13
Inject the schematic diagram of filler.When being filled, vamp is not yet bonded to sole.
Figure 15 shows that the sole 1502 after the completion of injection can be with vamp 1501, big bottom 1503
It is bonded together.The mode of engagement for example can be bonding, or other junctures.
Figure 16 and Figure 17 show sole, the footwear according to the illustrative embodiments of the application the 4th
And manufacturing method of shoes.Present embodiment is that sole does not have with the difference of first three implementation method
Single sole top.
As shown in figure 16, directly injection moulding is carried out on the sole bottom with 3D shape.
Figure 17 shows that the sole 1702 after the completion of injection can be with vamp 1701, big bottom 1703
It is bonded together.Wherein, the upper surface of the sole 1702 after the completion of injection is the filler of injection
The surface formed after solidification, rather than the sole top used in such as preceding claims.
Figure 18 to Figure 29 shows sole, the footwear according to the illustrative embodiments of the application the 5th
And manufacturing method of shoes.Present embodiment is that sole top has with the difference of first embodiment
The 3D shape being at least partly consistent with sole bottom, and sole bottom and sole top Jun Bao
Include at least a portion heel of a shoe.Here, sole top has and is at least partly consistent with sole bottom
3D shape refer to the shape on sole top and the shape phase of the top edge of sole bottom
Match somebody with somebody, especially the form fit of the heel region of the heel region on sole top and sole bottom.
In the case where the sole top and the sole bottom link together, the two be collectively forming including
The sole of portion of midfoot heel or at least a portion heel.
Figure 18, Figure 19 and Figure 20 show the sole top according to the 5th implementation method.As schemed
Shown in 18, the material layer for forming sole top is placed in mold (cavity plate) 1801 and lower mould
Between (punch-pin) 1804, the sole top with specific three dimensional shape is formed by mold treatment
1805.The material layer can be for example made up of two-layer, respectively foam or spongy layer 1802 and bottom
Layer of cloth 1803.Figure 19 shows that the lower surface on the sole top 1805 to be formed is pasted after glue spraying
Leakproof film 1901, forms sole top 1902.Leakproof film 1901 for example can be with plastic uptake (for example
By vacuum forming) it is formed on the lower surface on sole top 1805.Figure 20 shows and pastes
The sole top 2001 formed after having the sole top 1902 of leakproof film pruned.Such as Figure 20 institutes
Show, pruning the sole top after shaping includes the heel parts of part.
Figure 21, Figure 22 and Figure 23 show the sole bottom according to the 5th implementation method.As schemed
Shown in 21, the material 2102 for forming sole bottom is placed in mold (cavity plate) 2101 and lower mould
Between tool (punch-pin) 2103, formed under the sole with specific three dimensional shape by mold treatment
Portion 2104.The sole bottom 2104 of shaping also includes the heel parts of part.Also, shaping
Sole top there is the 3D shape that is consistent of part with the sole bottom of shaping.Figure 22 shows
Leakproof film 2201 is pasted after the upper surface glue spraying of the sole bottom 2104 of shaping, to form tool
There is the sole bottom 2202 of leakproof film.Leakproof film 2201 for example can be with plastic uptake (such as by true
Sky shaping) it is formed on the upper surface of sole bottom 2104.Figure 23 shows and is covered with leakproof
The sole bottom 2202 of film, and prune the sole bottom 2301 after shaping.
Figure 24 shows sole top and sole after the pruning shaping according to the 5th implementation method
Bottom.As shown in figure 24, sole top 2401 is contained in the 3D shape of sole bottom 2402
In and be partly consistent therewith.Sole 2403 is formed together with sole upper bond at sole bottom,
Wherein certain cavity is formed between sole bottom and sole top.
Figure 25 A show vamp according to the 5th implementation method, sole top and sole bottom.
As illustrated, the sole top being contained in sole bottom from top to bottom include bottom cloth layer 2501,
Foam or spongy layer 2502 and leakproof film 2503；Sole bottom includes leakproof film 2504 from top to bottom
With bottom cloth layer 2505.Vamp 2506 has and formation behind sole bottom and sole upper bond
The shape that the edge of sole 2507 is consistent.In this embodiment, as shown in Figure 25 B, make
Be a kind of selection, molded portion can on be extended down to heel, form different shapes to be molded, both
Aesthetic appearance can be increased, the protection provided heel can be also provided.On sole in Figure 25 B
Portion's (including bottom cloth layer 2511, foam or spongy layer 2512 and leakproof film 2513) and Figure 25 A
In sole top it is identical, the sole bottom (leakproof film 2514 and bottom cloth layer 2515) in Figure 25 B
With the shape that the difference of the sole bottom in Figure 25 A is heel position.
Figure 26 show vamp and sole be stitched together after shoe body 2601.Vamp and sole
Between for example by sewing splice behind paste joint strip 2602 be stitched together.Sole bottom has opens
Mouth 2603.
Figure 27 shows the schematic diagram that filler is injected according to the 5th implementation method.As illustrated,
Filler is injected into the cavity between sole bottom and sole top.
Figure 28 shows the shoe body after the completion of injection.It can be seen that, sole has opening.
Figure 29 show by big bottom 2902 be attached to injection after the completion of shoe body 2901, with formed
Product shoes 2903.Although the big bottom for showing is full slice system, it will be appreciated that as shown in figure 30,
The big bottom 3001 of split blade type can also be used.It is, being corresponded to using the big bottom of multi-disc different
Sole site.The big bottom of burst or multiple-piece is also applied for other implementation methods.
In various embodiments, sole bottom can also be made up of leakproof film, without using
Tissue layer.In various embodiments, opening may be located at sole top or sole bottom.
In various embodiments, sole bottom must have, and be used to provide guarantor for filler
Shield, and sole top is then not required.In the case of with sole top, sole top
Only can be made up of leakproof film, it is also possible to be made up of both leakproof film and fabric.Filled out for injecting
The opening of thing is filled positioned at the upper surface of sole or lower surface.
According to presently filed embodiment, sole (midsole) is by such as textile material with three
The sole bottom and such as PU or PU foams injection for tieing up shape are formed in the filler of sole bottom
Constitute.By sole bottom to the parcel of filler, the sole at such as PU bottoms is not being influenceed
On the premise of energy, the overall density of sole is reduced, thus reduce weight.
Existing footwear material midsole, is typically mostly EVA expanded materials, and it is partially PU separately to have
Expanded material.The advantage of EVA midsoles is light, and density is typically in 0.2-0.3g/cm3；Resilience
Property 35%-55%, it is moderate；Have the disadvantage that compressed shape variability is poor, 60%-35% wears and easily becomes long
Shape, poor durability.And general PU foaming midsole advantage is that compressed shape variability is smaller, typically all
Below 10%, durability is good；Resilience is preferable, in 45%-65%；Have the disadvantage that density is big,
It is heavier typically in 0.3-0.4g/cm3.Novel insole mentioned by the application, is retaining tradition
Outside the resilience high of PU foaming midsoles and the small advantage of compressed shape variability, can be density domination 0.2
Below g/cm3, accomplishes both lightweights, and the durable midsole of resilience high.
The illustrative embodiments of the application are illustrated above by reference to accompanying drawing.This area skill
Art personnel should be appreciated that the appropriate deformation and modification of implementations described herein are equally applicable
In the present invention, and it is within the scope of the present invention.
Claims (31)
1. a kind of sole, including：
Bottom with 3D shape；And
Filler, the filler perfusion is formed in the bottom.
2. sole according to claim 1, wherein, the bottom is soft by such as fabric
Property material is formed.
3. sole according to claim 1, wherein, the filler is thermosets,
Such as polyurethane or polyurethane foam.
4. sole according to claim 1, further includes：
Big bottom, is bonded on the lower section of the bottom.
5. sole according to claim 1, further includes：
First leakproof film, sticks to the upper surface of the bottom, is used to prevent the filler from letting out
Leakage.
6. sole according to claim 1, further includes：
Top, is covered in the top of the bottom,
Wherein, the filler perfusion is formed between the top and the bottom.
7. sole according to claim 6, further includes：
Second leakproof film, sticks to the lower surface on the top, is used to prevent the filler from letting out
Leakage.
8. sole according to claim 6, wherein, the top has opening, described
Filler is perfused between the top and the bottom by the opening.
9. sole according to claim 6, wherein, the bottom has opening, described
Filler is perfused between the top and the bottom by the opening.
10. sole according to claim 1, wherein, the 3D shape of the bottom is
Formed by being molded sizing.
11. soles according to claim 6, wherein, the top have with it is described under
The 3D shape that portion is at least partly consistent, it is preferable that the top is shape by molding sizing
Into.
12. soles according to claim 11, wherein, the bottom and the top are equal
Including at least a portion heel of a shoe.
13. soles according to claim 1, wherein, the bottom by leakproof flexibility
Material is formed.
14. soles according to claim 6, wherein, the top and/or bottom are by preventing
The flexible material of leakage is formed.
A kind of 15. footwear, the sole with vamp and according to any of the above claim.
A kind of 16. manufacturing method of shoes, including：
Molding forms the sole bottom with 3D shape；
Sole top is covered on the sole bottom；
Filler is injected between sole top and sole bottom；And
By vamp, sole top together with sole lower bond.
17. methods according to claim 16, further include：
Big bottom is bonded on the lower section of sole bottom.
18. methods according to claim 16, wherein, in sole top and sole bottom
Between inject filler include：
Filler is injected by the opening on sole top or the opening of sole bottom.
19. methods according to claim 16, wherein, in sole top and sole bottom
Between inject filler the step of vamp, sole top and sole bottom are all being bonded on one
Rise after carry out, or only by sole top together with sole lower bond after carry out.
20. methods according to claim 16, further include：
Pasted on the lower surface on sole top and at least one of the upper surface of sole bottom anti-
Leakage film.
21. methods according to claim 16, wherein, the sole bottom is by for example knitting
The flexible material of thing is formed.
22. methods according to claim 16, wherein, the filler is thermosetting material
Material, such as polyurethane or polyurethane foam.
23. methods according to claim 16, further include：
Molding form the sole top, wherein, the sole top have with the sole under
The 3D shape that portion is at least partly consistent.
24. methods according to claim 23, wherein, the sole bottom and the footwear
Bottom top includes at least a portion heel of a shoe.
25. soles according to claim 16, wherein, the sole top and/or sole
Bottom is formed by the flexible material of leakproof.
A kind of 26. manufacturing method of shoes, including：
Molding forms the sole bottom with 3D shape；
Filler is injected on the sole bottom；And
By vamp together with the sole lower bond after injection filler.
27. methods according to claim 26, further include：
Big bottom is bonded on the lower section of sole bottom.
28. methods according to claim 26, further include：
Leakproof film is pasted on the upper surface of sole bottom.
29. methods according to claim 26, wherein, the sole bottom is by for example knitting
The flexible material of thing is formed.
30. methods according to claim 26, wherein, the filler is thermosetting material
Material, such as polyurethane or polyurethane foam.
31. methods according to claim 26, wherein, the sole bottom is by leakproof
Flexible material is formed.