CN106680201A - Equipment and method for testing interface bonding strength - Google Patents

Equipment and method for testing interface bonding strength Download PDF

Info

Publication number
CN106680201A
CN106680201A CN201510761174.4A CN201510761174A CN106680201A CN 106680201 A CN106680201 A CN 106680201A CN 201510761174 A CN201510761174 A CN 201510761174A CN 106680201 A CN106680201 A CN 106680201A
Authority
CN
China
Prior art keywords
sample
layer
chassis
cambium layer
equipment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510761174.4A
Other languages
Chinese (zh)
Other versions
CN106680201B (en
Inventor
张小军
李龙
周德敬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yinbang Clad Material Co Ltd
Original Assignee
Yinbang Clad Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yinbang Clad Material Co Ltd filed Critical Yinbang Clad Material Co Ltd
Priority to CN201510761174.4A priority Critical patent/CN106680201B/en
Publication of CN106680201A publication Critical patent/CN106680201A/en
Application granted granted Critical
Publication of CN106680201B publication Critical patent/CN106680201B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses equipment and a method for testing interface bonding strength. The equipment comprises a fixing device, a sliding device and a test sample holding device, wherein the fixing device comprises a base, a first bearing seat, a second bearing seat, a first rotating shaft and a second rotating shaft; the sliding device comprises a guide rail and a pulley; the guide rail is fixedly connected with the base of the fixing device; the guide rail limits the movement of the pulley along the guide rail; the test sample holding device comprises a chassis and a press plate, the pulley of the sliding device is fixedly at the lower part of the chassis; and the press plate is used for fixing the end of a test sample to the chassis. With the equipment and the method for testing interface bonding strength, the test sample interface bonding strength testing results are stable and reliable, and the bonding strength results of different batches are highly comparable. The equipment and the method of the invention overcome the problems in evaluating interface bonding strength of an aluminum steel composite strips for a brazed heat exchanger by using tension shearing, tearing, pressure shearing or conventional methods, including fracture of the aluminum layer and difficulty in evaluation.

Description

The method of testing of equipment and interface bond strength for interface bond strength test
Technical field
The invention belongs to meet metal material performance test technical field, more particularly to for interface cohesion The equipment of strength test, and the method for testing of the interface bond strength realized using the equipment.
Background technology
Aluminum steel composite band material used by brazing heat exchanger is by being combined that aluminum, bimetal copper-steel are composited Band, its finished product thickness is that between 1.3mm~1.6mm, cladding aluminum layer thickness is in 0.075mm~0.1mm Between, it is very thin due to coating aluminum layer thickness, cut, tear using conventional drawing, compression shear etc. evaluates interface The method of bond strength, aluminium lamination can rupture, it is difficult to evaluate, therefore to soldering aluminum steel in prior art The evaluation of the interface bond strength of composite strip can only adopt bend test, but the bend test method can only Qualitative detection evaluate aluminum steel interface bond strength whether meet the requirements, for need quantitatively judge bond strength Experimentation and do not apply to.
Spirit of the invention and principle are, because the final purposes of aluminum steel composite band material is that soldering thereon dissipates Hot fin, it is of the invention under industrial soldering system condition, in one layer of aluminum steel composite band material aluminum side soldering 4343/3003 aluminium alloy compound plate, thickness is 1mm~4mm, and 4343 thickness account for total thickness 8%~15%, Thickness due to having thickeied aluminum steel composite band material aluminum side, so as to ensure to determine using methods such as traditional tears Amount evaluates the bond strength at interface.But traditional tear mode aluminum steel angle of tear is unstable during tear, Size variation, causes testing result fluctuating margin big, as a result unreliable, and different batches storeroom is difficult Contrasted.
The content of the invention
The first object of the present invention is to provide a kind of equipment for interface bond strength test, to solve to pass The tear mode aluminum steel angle of tear of system is unstable during tear, causes testing result fluctuating margin big, As a result insecure technical problem.
The second object of the present invention is to provide a kind of aluminum steel composite band material interface bond strength method of testing, with Solution can not be tested the interface bond strength of aluminum steel composite band material at present using tear mode, and Traditional tear mode aluminum steel angle of tear is unstable during tear, causes testing result fluctuating margin big, As a result insecure technical problem.
In order to realize above-mentioned first purpose, the present invention provides a kind of equipment for interface bond strength test, The equipment is tested the interface bond strength of sample, and the sample includes the first shape be combineding with each other Stratification and the second cambium layer;The equipment includes:Fixing device, carriage and sample holding device;
The fixing device includes pedestal, first bearing seat, second bearing seat, first rotating shaft and second turn Axle;The first bearing seat is fixed on the pedestal, and it is relative that the first rotating shaft is arranged on two positions First bearing seat between;The second bearing seat is fixed on the pedestal, and second rotating shaft is installed Between the relative second bearing seat in two positions;The first rotating shaft and second rotating shaft are parallel to each other Arrange;
The carriage includes guide rail and pulley;The guide rail is fixedly connected with the pedestal of fixing device; The guide rail limits the pulley and moves along guide rail;
The sample holding device includes chassis and pressing plate, and the pulley of carriage is fixed on the chassis Bottom;The pressing plate includes the first pressing plate and the second pressing plate, and first pressing plate is arranged on the one end on chassis, For one end of sample to be fixed on into the chassis;Second pressing plate is arranged on the other end on chassis, uses In first cambium layer or the second cambium layer of the other end of sample are fixed on into the chassis;
The distance between the first rotating shaft and chassis slightly larger than sample thickness, second rotating shaft and bottom The distance between disk is more than the distance between first rotating shaft and chassis.
The equipment for being used for interface bond strength test as above of the invention, further, the specimen holder Holding device also includes rule, and the rule is fixed on the chassis, and for measuring aluminum steel layer position is separated Put the distance of change.
The equipment for being used for interface bond strength test as above of the invention, further, first pressure Plate and the second pressing plate are bolted on respectively the chassis.
The equipment for being used for interface bond strength test as above of the invention, further, the sample bag Include the aluminium lamination soldering connection of enhancement layer and aluminum steel composite band material, the enhancement layer and aluminum steel composite band material;Institute The aluminium lamination for stating enhancement layer and aluminum steel composite band material is the first cambium layer, and the steel layer of aluminum steel composite band material is second Cambium layer;Or the aluminium lamination of the enhancement layer and aluminum steel composite band material be the second cambium layer, aluminum steel composite band The steel layer of material is the first cambium layer.
The equipment for being used for interface bond strength test as above of the invention, further, the enhancement layer For aluminium alloy compound plate.Preferably, the aluminium alloy compound plate is 4343 aluminium alloys and 3003 aluminium alloys Composite plate.
In order to realize above-mentioned second purpose, the present invention provides a kind of aluminum steel composite band material interface bond strength and surveys Method for testing, methods described utilizes the equipment for interface bond strength test described in as above any one to carry out, Comprise the following steps:
It is prepared by step 1, sample;Form to be tested in the aluminium lamination side soldering enhancement layer of aluminum steel composite band material Sample, specimen width is d;The aluminium lamination of the enhancement layer and aluminum steel composite band material be the first cambium layer, aluminum steel The steel layer of composite strip is the second cambium layer;Preferably, the enhancement layer is 4343 aluminium alloys and 3003 The composite plate of aluminium alloy;
Step 2, fixed sample;Divide first cambium layer and the second cambium layer of sample one end by prefabricated From, the cambium layer of sample first and the second cambium layer are initially separated into position and are arranged on first rotating shaft lower section, try The unsegregated one end of sample cambium layer is fixed on chassis by the first pressing plate;The detached one end of sample cambium layer First cambium layer bypasses the second rotating shaft, and second cambium layer of the detached one end of sample cambium layer is by the second pressure Plate is fixed on chassis;First cambium layer of the detached one end of sample cambium layer is applied using omnipotent mechanics machine Constant force, speed is v;
Step 3, as a result calculates, and after test is stable, the first cambium layer is with the second cambial angle β, then aluminum steel interface bond strength be calculated as follows, F combination=Fsin β/d.
The invention has the beneficial effects as follows:
When testing sample using bond strength test equipment in section of the present invention, start aluminum steel during detection Angle of tear α gradually becomes β angles during stable tear with the movement of sample, and it is aluminum steel stably to tear state Interface is initially separated, and the state of β angles steady change scope≤5% during stable tear so that inspection Survey result is reliable and stable, different batches material bond strength result comparison is strong.
Due to the aluminium lamination side soldering enhancement layer in aluminum steel composite band material, brazing heat exchanger use is overcome Aluminum steel composite band material cladding aluminum layer thickness is very thin, is cut, is torn using conventional drawing, compression shear etc. evaluates boundary The method of face bond strength, aluminium lamination can rupture, it is difficult to the problem of evaluation.
Description of the drawings
By the detailed description made in conjunction with the following drawings, above-mentioned and/or other aspects of the present invention and excellent Point will be apparent from and be easier to understand, and these accompanying drawings are simply schematic, are not intended to limit the present invention, Wherein:
Fig. 1 is the equipment for interface bond strength test of an embodiment of the present invention when tear starts Schematic diagram;
Fig. 2 is the equipment for interface bond strength test of an embodiment of the present invention when tear is stable Schematic diagram;
Fig. 3 is the top view of the equipment for interface bond strength test of an embodiment of the present invention;
Fig. 4 is the sample structure schematic diagram of an embodiment of the present invention.
In accompanying drawing, the list of parts representated by each label is as follows:
1st, pedestal;
2nd, guide rail;
3rd, pulley;
4th, bearing block;
5th, rotating shaft;
6th, bolt;
7th, chassis;
8th, the second cambium layer;
9th, the first cambium layer;91st, 3003 aluminium alloy;92nd, 4343 aluminium alloy;93rd, aluminium lamination;
10th, pressing plate;
11st, rule.
Specific embodiment
Hereinafter, the equipment for interface bond strength test and the boundary of the present invention are described with reference to the accompanying drawings The embodiment of the method for testing of face bond strength.
The embodiment that here is recorded is the specific specific embodiment of the present invention, for illustrating the present invention's Design, is explanatory and exemplary, be should not be construed as to embodiment of the present invention and the scope of the invention Restriction.Except the enforcement exception that here is recorded, those skilled in the art can also be wanted based on the application right Book and description disclosure of that are asked using obvious other technical schemes, these technical scheme bags Include the technical scheme for making any obvious substitutions and modifications using the embodiment recorded to here.
The accompanying drawing of this specification is schematic diagram, aids in illustrating the design of the present invention, it is schematically indicated each portion The shape divided and its mutual relation.Note that for the ease of clearly showing each of the embodiment of the present invention The structure of part, not according to the drafting of identical ratio between each accompanying drawing.Identical reference marker is used for table Show identical part.
Fig. 1 illustrates the equipment for interface bond strength test of an embodiment of the present invention, the equipment For testing the interface bond strength of sample, the sample includes the first cambium layer be combineding with each other 9 and second cambium layer 8;The equipment includes:Fixing device, carriage and sample holding device;
The fixing device include pedestal 1, bearing block 4 (including first bearing seat, second bearing seat), Rotating shaft 5 (including first rotating shaft and the second rotating shaft);The first bearing seat is fixed on the pedestal, The first rotating shaft is arranged between two relative first bearing seats in position;The second bearing seat is fixed On the pedestal, second rotating shaft is arranged between two relative second bearing seats in position;It is described First rotating shaft and second rotating shaft are arranged in parallel;As shown in figure 1, the quantity of first bearing seat is Two, the quantity of second bearing seat is two, also, the line and second bearing between first bearing seat Line distance between seat is L.
The carriage includes guide rail 2 and pulley 3;The guide rail 2 is consolidated with the pedestal 1 of fixing device Fixed connection;The guide rail 2 limits the pulley 3 and moves along guide rail;As shown in figure 1, the quantity of pulley For four, chassis lower section is equidistantly fixed on.In a kind of implementation process, have on the bracing frame of pulley Spacing hole, spacing hole passes through guide rail, while pulley and base into contact, can slide walking on pedestal.
As shown in figure 3, the sample holding device includes chassis 7 and pressing plate 10, the pulley of carriage 3 bottoms for being fixed on the chassis 7;The pressing plate 10 includes the first pressing plate and the second pressing plate, described the One pressing plate is arranged on the one end on chassis, for one end of sample to be fixed on into the chassis;Second pressure Plate is arranged on the other end on chassis, for by first cambium layer 9 or the second cambium layer of the other end of sample 8 are fixed on the chassis;
The distance between the first rotating shaft 5 and chassis 7 slightly larger than sample thickness, second rotating shaft The distance between 5 and chassis 7 are more than the distance between first rotating shaft and chassis.Can be seen that in Fig. 1 Difference in height between first rotating shaft and the second rotating shaft is h.
In the equipment for interface bond strength test of the above embodiment of the present invention, the sample holder Device also includes rule 11, and the rule 11 is fixed on the chassis 7, for measuring aluminum steel layer The distance of separation point position change..Projection of the rule with first rotating shaft and the second rotating shaft on chassis is mutually hung down It is straight to arrange.
In the equipment for interface bond strength test of the above embodiment of the present invention, first pressing plate 10 and second pressing plate 10 respectively the chassis 7 is fixed on by bolt 6.
In the equipment for interface bond strength test of the above embodiment of the present invention, the sample includes The aluminium lamination soldering connection of enhancement layer and aluminum steel composite band material, the enhancement layer and aluminum steel composite band material;As schemed Shown in 4, the aluminium lamination of the enhancement layer and aluminum steel composite band material is the first cambium layer 9, aluminum steel composite band material Steel layer 93 be the second cambium layer 8;Or the aluminium lamination of the enhancement layer and aluminum steel composite band material is the second shape Stratification 8, the steel layer of aluminum steel composite band material is the first cambium layer 9.
When needing to test the sample including aluminum steel composite band material, in order to realize enhancement layer and aluminum steel The strength of brazed joint of aluminium lamination in composite strip, the enhancement layer is aluminium alloy compound plate.Preferably, institute State the composite plate that aluminium alloy compound plate is 4343 aluminium alloys 92 and 3003 aluminium alloys 91.
Aluminum steel composite band material interface bond strength method of testing is carried out using the above embodiment of the present invention equipment, Comprise the following steps:
It is prepared by step 1, sample;Form to be tested in the aluminium lamination side soldering enhancement layer of aluminum steel composite band material Sample, specimen width is d;The aluminium lamination of the enhancement layer and aluminum steel composite band material be the first cambium layer, aluminum steel The steel layer of composite strip is the second cambium layer;Preferably, the enhancement layer is 4343 aluminium alloys and 3003 The composite plate of aluminium alloy;
Step 2, fixed sample;Divide first cambium layer and the second cambium layer of sample one end by prefabricated From, the cambium layer of sample first and the second cambium layer are initially separated into position and are arranged on first rotating shaft lower section, try The unsegregated one end of sample cambium layer is fixed on chassis by the first pressing plate;The detached one end of sample cambium layer First cambium layer bypasses the second rotating shaft, and second cambium layer of the detached one end of sample cambium layer is by the second pressure Plate is fixed on chassis;During on-test, the first cambium layer and the second cambial angle are α (such as Fig. 1 In illustrate), constant is applied to first cambium layer of the detached one end of sample cambium layer using omnipotent mechanics machine Power, speed is v;
Step 3, as a result calculates, and after test is stable, the first cambium layer is with the second cambial angle β, then aluminum steel interface bond strength be calculated as follows, F combination=Fsin β/d.
When testing sample using bond strength test equipment in section of the present invention, start aluminum steel during detection Angle of tear α with the β angles (as illustrated in Fig. 2) when the movement of sample gradually becomes stable tear, surely Surely tear state be that aluminum steel interface is initially separated, and β angles during stable tear steady change scope≤ 5% state so that testing result is reliable and stable, the bond strength result comparison of different batches material is strong.
Due to the aluminium lamination side soldering enhancement layer in aluminum steel composite band material, brazing heat exchanger use is overcome Aluminum steel composite band material cladding aluminum layer thickness is very thin, is cut, is torn using conventional drawing, compression shear etc. evaluates boundary The method of face bond strength, aluminium lamination can rupture, it is difficult to the problem of evaluation.
Each technical characteristic of above-mentioned disclosure is not limited to disclosed and further feature combination, this area skill Art personnel can also according to the purpose of invention carry out between each technical characteristic other combination, to realize the present invention Purpose be defined.

Claims (8)

1. a kind of equipment for interface bond strength test, the equipment is used to tie the interface of sample Close intensity to be tested, the sample includes the first cambium layer and the second cambium layer be combineding with each other;It is described Equipment includes:Fixing device, carriage and sample holding device, it is characterised in that:
The fixing device includes pedestal, first bearing seat, second bearing seat, first rotating shaft and second turn Axle;The first bearing seat is fixed on the pedestal, and it is relative that the first rotating shaft is arranged on two positions First bearing seat between;The second bearing seat is fixed on the pedestal, and second rotating shaft is installed Between the relative second bearing seat in two positions;The first rotating shaft and second rotating shaft are parallel to each other Arrange;
The carriage includes guide rail and pulley;The guide rail is fixedly connected with the pedestal of fixing device; The guide rail limits the pulley and moves along guide rail;
The sample holding device includes chassis and pressing plate, and the pulley of carriage is fixed on the chassis Bottom;The pressing plate includes the first pressing plate and the second pressing plate, and first pressing plate is arranged on the one end on chassis, For one end of sample to be fixed on into the chassis;Second pressing plate is arranged on the other end on chassis, uses In first cambium layer or the second cambium layer of the other end of sample are fixed on into the chassis;
The distance between the first rotating shaft and chassis slightly larger than sample thickness, second rotating shaft and bottom The distance between disk is more than the distance between first rotating shaft and chassis.
2. it is according to claim 1 for interface bond strength test equipment, it is characterised in that The sample holding device also includes rule, and the rule is fixed on the chassis, for measuring aluminum The distance of steel layer separation point position change.
3. it is according to claim 1 for interface bond strength test equipment, it is characterised in that First pressing plate and the second pressing plate are bolted on respectively the chassis.
4. according to any one of claim 1-3 for interface bond strength test equipment, its It is characterised by, the sample includes enhancement layer and aluminum steel composite band material, the enhancement layer and aluminum steel composite band The aluminium lamination soldering connection of material;The aluminium lamination of the enhancement layer and aluminum steel composite band material be the first cambium layer, aluminum steel The steel layer of composite strip is the second cambium layer;Or the aluminium lamination of the enhancement layer and aluminum steel composite band material is the Two cambium layer, the steel layer of aluminum steel composite band material is the first cambium layer.
5. the equipment of interface bond strength test is used for according to claim 4, it is characterised in that The enhancement layer is aluminium alloy compound plate.
6. the equipment of interface bond strength test is used for according to claim 5, it is characterised in that The aluminium alloy compound plate is the composite plate of 4343 aluminium alloys and 3003 aluminium alloys.
7. a kind of aluminum steel composite band material interface bond strength method of testing, it is characterised in that methods described Carry out for the equipment of interface bond strength test using described in claim any one of 1-3, including with Lower step:
It is prepared by step 1, sample;Form to be tested in the aluminium lamination side soldering enhancement layer of aluminum steel composite band material Sample, specimen width is d;The aluminium lamination of the enhancement layer and aluminum steel composite band material be the first cambium layer, aluminum steel The steel layer of composite strip is the second cambium layer;
Step 2, fixed sample;First cambium layer of sample one end and second is formed by prefabrication process Layer is separated, and the cambium layer of sample first and the second cambium layer is initially separated into position and is arranged on first rotating shaft lower section, The unsegregated one end of sample cambium layer is fixed on chassis by the first pressing plate;The detached one end of sample cambium layer The first cambium layer bypass the second rotating shaft, second cambium layer of the detached one end of sample cambium layer passes through second Pressing plate is fixed on chassis;First cambium layer of the detached one end of sample cambium layer is applied using omnipotent mechanics machine Plus constant force, speed is v;
Step 3, as a result calculates, and after test is stable, the first cambium layer is with the second cambial angle β, then aluminum steel interface bond strength be calculated as follows, F combination=Fsin β/d.
8. the equipment of interface bond strength test is used for according to claim 7, it is characterised in that The enhancement layer is the composite plate of 4343 aluminium alloys and 3003 aluminium alloys.
CN201510761174.4A 2015-11-10 2015-11-10 For the equipment of interface bond strength test and the test method of interface bond strength Active CN106680201B (en)