CN106676557A - Metal antiseptic cleaning agent - Google Patents
Metal antiseptic cleaning agent Download PDFInfo
- Publication number
- CN106676557A CN106676557A CN201610359444.3A CN201610359444A CN106676557A CN 106676557 A CN106676557 A CN 106676557A CN 201610359444 A CN201610359444 A CN 201610359444A CN 106676557 A CN106676557 A CN 106676557A
- Authority
- CN
- China
- Prior art keywords
- metal
- cleaning agent
- corrosion
- sodium
- abluent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A metal antiseptic cleaning agent is composed of following raw materials including dodecylbenzene sulfonic acid, a corrosion inhibitor, ammonium molybdate, sodium citrate, a defoamer, sodium fluoride, a surface active agent and water. The metal antiseptic cleaning agent has the beneficial effects that the efficient cleaning agent is free of volatility, good in water solubility, high in dirt removing rate, low in corrosion speed, convenient to store and transport, safe in usage, small in toxicity, easy to operate and suitable for cleaning metal equipment of alloy steel, aluminum, copper and alloy materials of the alloy steel, the aluminum and the copper.
Description
Technical field
The present invention relates to abluent field, and in particular to anti-corrosion of metal abluent.
Background technology
At present, existing anti-corrosion of metal abluent using effect on the market is not ideal enough.
The content of the invention
The purpose of the present invention be aiming at current existing anti-corrosion of metal abluent using effect on the market it is not ideal enough it
Deficiency, and anti-corrosion of metal abluent is provided.
The present invention is made up of following raw material parts by weight of raw materials proportioning:
DBSA 65-70
Corrosion inhibiter 0.3-0.6
Sodium silicate 1-3
Ammonium molybdate 1-3
Sodium citrate 0.1-5.1
Defoamer 0.05-0.2
Sodium fluoride 0.05-0.2
Surfactant 1-2
Water 22-25.
It is made up of following raw material parts by weight of raw materials proportioning:
DBSA 68
Corrosion inhibiter 0.5
Sodium silicate 2
Ammonium molybdate 2
Sodium citrate 2
Defoamer 0.1
Sodium fluoride 0.15
Surfactant 1.5
Water 23.75.
DBSA in formula is abluent host, in cleaning process, with calcium, the magnesium compound in dirt
Generation vigorous reaction, generates solubility dodecyl benzene sulfonate.Sodium citrate can improve abluent except oxidation rust, the energy of dirt
Power.Sodium fluoride can strengthen abluent except the ability of silicate scale.Corrosion inhibiter can be to steel alloy, steel in cleaning process in formula
There is corrosion inhibition Deng metal, without spot corrosion, and there can be metallic luster after scale removal.Defoamer is mainly used for eliminating product in cleaning process
Raw foam.Surfactant can mainly reduce solution surface tension in cleaning process, cleanout fluid is easily contacted with metal,
Play a part of to increase moistening, improve the dirt-removing power of abluent.
Corrosion inhibiter is urotropine, thiourea, potassium iodide, stannous chloride or their mixture composition, according to quilt
The difference of cleaning material, may be selected different compositions as corrosion inhibiter.
Surfactant sodium dodecyl base sodium sulfonate, sodium alkyl benzene sulfonate or nonionic surfactant in this abluent,
The such as beautiful activating agent of polyoxyethylene-type nonionic table.
The content of sodium citrate is 0.1-5.1, the content of sodium fluoride for o_05-0.2 ' defoamer content for o.05-
0.2 abluent containing mentioned component, for various metal materials and various dirts have preferable cleaning performance.
Above-mentioned abluent can also it is possible to additionally incorporate water, obtain the cleanout fluid containing above-mentioned abluent.
The method have the advantages that:This efficient cleaner non-volatility, good water solubility, descaling rate is high, and corrosion rate is slow, is easy to storage
Deposit, transport, using safety, small toxicity is simple to operate, be adapted to the hardwares such as cleaning steel alloy, aluminum, copper and its alloy material.
Specific embodiment
The present invention is made up of following raw material parts by weight of raw materials proportioning:
DBSA 65-70
Corrosion inhibiter 0.3-0.6
Sodium silicate 1-3
Ammonium molybdate 1-3
Sodium citrate 0.1-5.1
Defoamer 0.05-0.2
Sodium fluoride 0.05-0.2
Surfactant 1-2
Water 22-25.
It is made up of following raw material parts by weight of raw materials proportioning:
DBSA 68
Corrosion inhibiter 0.5
Sodium silicate 2
Ammonium molybdate 2
Sodium citrate 2
Defoamer 0.1
Sodium fluoride 0.15
Surfactant 1.5
Water 23.75.
Using method:When using, at 40-60 DEG C, with dirt:Abluent=1:(1 ~ 2) consumption of abluent is estimated, will with water
Abluent is diluted to the solution of concentration 5%-10%, with dynamic rinse or static immersing, or both combine cleaning way cleaning dirt
Part.Because surface to be cleaned is very active after cleaning, can be with alkali liquor [such as o.5% -1.0%(Mass fraction)NalP04] in
With so as to pH value approximate 7.0, then film is disposably made with FeS04, the service life to prolonging blunt metal tube or container is of great benefit to.
Claims (2)
1. anti-corrosion of metal abluent, it is characterised in that it is made up of following raw material parts by weight of raw materials proportioning:
DBSA 65-70 corrosion inhibiter 0.3-0.6 sodium silicate 1-3
Ammonium molybdate 1-3 sodium citrate 0.1-5.1 defoamer 0.05-0.2
Surfactant 1-2 sodium fluoride 0.05-0.2 water 22-25.
2. anti-corrosion of metal abluent according to claim 1, it is characterised in that be made up of following raw material parts by weight of raw materials proportioning:
The sodium silicate 2 of 68 corrosion inhibiter of DBSA 0.5
The water 23.75 of 1.5 sodium fluoride of ammonium molybdate 2 sodium citrate, 2 defoamer, 0.1 surfactant 0.15.