CN106675136A - Coating layer used for inner side of draw-bar box shell - Google Patents
Coating layer used for inner side of draw-bar box shell Download PDFInfo
- Publication number
- CN106675136A CN106675136A CN201611223681.3A CN201611223681A CN106675136A CN 106675136 A CN106675136 A CN 106675136A CN 201611223681 A CN201611223681 A CN 201611223681A CN 106675136 A CN106675136 A CN 106675136A
- Authority
- CN
- China
- Prior art keywords
- parts
- draw
- bar box
- auxiliary agent
- box shell
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a coating layer used for the inner side of a draw-bar box shell, and relates to the technical field of draw-bar box machining and production. The coating layer is characterized by being prepared from the following materials in parts by weight: 40 parts of E saturated hydroxy polyester resin, 3 parts of triethylene glycol, 2 parts of di-12-carbon alcohol ester, 3 parts of an acrylate leveling agent, 3 parts of iso-octyl methacrylate, 4 parts of glass powder, 3 parts of benzotriazole, 4 parts of nano calcium carbonate, 3 parts of a silane coupling agent KH550, 8 parts of an anti-aging agent, 9 parts of an adjuvant and 24 parts of deionized water. The method is reasonable, convenient to operate and reasonable in proportion.
Description
Technical field
The present invention relates to draw-bar box processing technical field, and in particular to the painting that a kind of draw-bar box shell inner side uses
Layer.
Background technology
Draw-bar box refers to the luggage case with pull bar and roller.Because its is easy to use, carrying clothing etc. turns into travelling, go out and
Widely used.
Meanwhile, draw-bar box also puts a pull bar because of chest, have single tube pull bar and two-tube pulling rod point, the pipe of pull bar also has square tube
With pipe point, to facilitate during walking in tow, reduce the heavy burdens significantly.
Draw-bar box be able to can also be dragged with portable, and the wheel of our draw-bar boxes usually used is all located at chest bottom substantially
Portion, and modern have devised the draw-bar box of a neomorph, and chest has been designed to the moulding of cylinder, wheel is then whole outer
On the outside of chest, such roller design allows that this draw-bar box preferably adapts to different landform to bag, such as directly hauls
Chest just can light stair activity.
2012 it is main with cloth case, the hard casees of ABS, leather trunk, PC etc. for main material, and usability is divided into directional wheel, ten thousand
To wheel and newest detachable universal wheel draw-bar box three major types.
General suitcase, is divided by material, can be divided into two kinds of soft cloth case and hard case (hard and can be divided into ABS's
With PC etc., popular material also has pure PC for ABS or ABS+PC on the market)；Divide by construction, vertical pull bar and horizontal stroke can be divided into
Two kinds of the suitcase of formula；Divide by size, can be divided into (from small size to big size)：16 cun ', 18 cun ', 20 cun ', 22 cun ',
24 cun ', 26 cun ', 28 cun ', 30 cun ', 32 cun ' this is several！General conventional be 20 cun of three sides and add up 115CM and (remove
Britain Virgin Atlantic regulation is 105CM) can with the size boarded a plane and 28 cun of three sides and add up 158CM and fly
The international standard size that machine can be consigned freely.Domestic air mail can consign full-size for 32 cun.
The content of the invention
The technical problems to be solved by the invention be overcome existing technological deficiency provide a kind of method rationally, operation side
Just, the coating that a kind of draw-bar box shell inner side of reasonable mixture ratio uses.
The technical problems to be solved by the invention are realized using following technical scheme：
The coating that a kind of draw-bar box shell inner side uses, it is characterised in that：It is made up of the material of following weight portion,
40 parts of E saturated hydroxy polyester resins, 3 parts of triethylene glycol, 2 parts of double Lauryl Alcohol esters, 3 parts of acrylate levelling agent, first
It is 3 parts of base Isooctyl acrylate monomer, 4 parts of glass dust, 3 parts of BTA, 4 parts of nano-calcium carbonate, 3 parts of Silane coupling agent KH550, anti-
8 parts of old agent, 9 parts of auxiliary agent, 24 parts of deionized water；
The auxiliary agent is made up of the material of following weight portion,
20 parts of alkyd resin, 5 parts of dimethylbenzene, 1 part of catechol, 1 part of isooctyl thioglycolate dioctyltin, butyl acetate
5 parts, 2 parts of tributyl tin trichloride, 2 parts of aluminium nitride powder, 4 parts of mica powder；
Including following preparation process,
Auxiliary agent is put into calcining furnace 1-2 hour is calcined at 340-400 DEG C by I, is then taken out, the immersion in clear water
10-15 minutes, filter residue is filtered to obtain, then dried, then grind to form the powder of 500-600 mesh；
II is put into equipment all of material in addition to auxiliary agent, according to 700-800 revs/min of speed stirring reaction
30-36 minutes；
Material in II is put into the reactor in I and mixes with auxiliary agent by III, is heated to 65-71 DEG C, continues 25-33 points
Clock, is put into another equipment after then taking out and is disperseed 35-40 minutes at a high speed with 1800-2000 revs/min of speed；
Scattered material is put into vibrations filter and is filtered and screened by IV, the fineness of the material after filtering
≤40μm。
Beneficial effects of the present invention are：1. material cost is not high, does not have excessive financial burden, can be permanent and lasting
Production；
2. product does not have public hazards, pollution；
3. product caking property is good, good product quality.
Specific embodiment
In order that technological means, creation characteristic, reached purpose and effect that the present invention is realized are easy to understand, enter below
One step illustrates the present invention.
The coating that a kind of draw-bar box shell inner side uses, it is characterised in that：It is made up of the material of following weight portion,
40 parts of E saturated hydroxy polyester resins, 3 parts of triethylene glycol, 2 parts of double Lauryl Alcohol esters, 3 parts of acrylate levelling agent, first
It is 3 parts of base Isooctyl acrylate monomer, 4 parts of glass dust, 3 parts of BTA, 4 parts of nano-calcium carbonate, 3 parts of Silane coupling agent KH550, anti-
8 parts of old agent, 9 parts of auxiliary agent, 24 parts of deionized water；
The auxiliary agent is made up of the material of following weight portion,
20 parts of alkyd resin, 5 parts of dimethylbenzene, 1 part of catechol, 1 part of isooctyl thioglycolate dioctyltin, butyl acetate
5 parts, 2 parts of tributyl tin trichloride, 2 parts of aluminium nitride powder, 4 parts of mica powder；
Including following preparation process,
Auxiliary agent is put into calcining furnace 1-2 hour is calcined at 340-400 DEG C by I, is then taken out, the immersion in clear water
10-15 minutes, filter residue is filtered to obtain, then dried, then grind to form the powder of 500-600 mesh；
II is put into equipment all of material in addition to auxiliary agent, according to 700-800 revs/min of speed stirring reaction
30-36 minutes；
Material in II is put into the reactor in I and mixes with auxiliary agent by III, is heated to 65-71 DEG C, continues 25-33 points
Clock, is put into another equipment after then taking out and is disperseed 35-40 minutes at a high speed with 1800-2000 revs/min of speed；
Scattered material is put into vibrations filter and is filtered and screened by IV, the fineness of the material after filtering
≤40μm。
General principle of the invention and principal character and advantages of the present invention has been shown and described above.The technology of the industry
Personnel it should be appreciated that the present invention is not limited to the above embodiments, simply explanation described in above-described embodiment and specification this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appending claims and its
Equivalent thereof.
Claims (3)
1. the coating that a kind of draw-bar box shell inner side uses, it is characterised in that：It is made up of the material of following weight portion,
40 parts of E saturated hydroxy polyester resins, 3 parts of triethylene glycol, 2 parts of double Lauryl Alcohol esters, 3 parts of acrylate levelling agent, methyl-prop
3 parts of the different monooctyl ester of olefin(e) acid, 4 parts of glass dust, 3 parts of BTA, 4 parts of nano-calcium carbonate, 3 parts of Silane coupling agent KH550, age resistor
8 parts, 9 parts of auxiliary agent, 24 parts of deionized water.
2. the coating that a kind of draw-bar box shell inner side according to claim 1 uses, it is characterised in that：The auxiliary agent by with
The material of lower weight portion is made,
20 parts of alkyd resin, 5 parts of dimethylbenzene, 1 part of catechol, 1 part of isooctyl thioglycolate dioctyltin, 5 parts of butyl acetate,
2 parts of tributyl tin trichloride, 2 parts of aluminium nitride powder, 4 parts of mica powder.
3. the coating that a kind of draw-bar box shell inner side according to claim 1 uses, it is characterised in that：Including following preparation
Step,
Auxiliary agent is put into calcining furnace 1-2 hour is calcined at 340-400 DEG C by I, is then taken out, and 10-15 is soaked in clear water
Minute, filter residue is filtered to obtain, then dry, then grind to form the powder of 500-600 mesh；
II is put into equipment all of material in addition to auxiliary agent, according to 700-800 revs/min of speed stirring reaction 30-
36 minutes；
Material in II is put into the reactor in I and mixes with auxiliary agent by III, is heated to 65-71 DEG C, continues 25-33 minutes, so
It is put into another equipment after taking out afterwards and is disperseed 35-40 minutes at a high speed with 1800-2000 revs/min of speed；
Scattered material is put into vibrations filter and is filtered and screened by IV, fineness≤40 of the material after filtering
μm。