CN106674640A - Germanium energy far infrared latex product and manufacturing method thereof - Google Patents
Germanium energy far infrared latex product and manufacturing method thereof Download PDFInfo
- Publication number
- CN106674640A CN106674640A CN201611197499.5A CN201611197499A CN106674640A CN 106674640 A CN106674640 A CN 106674640A CN 201611197499 A CN201611197499 A CN 201611197499A CN 106674640 A CN106674640 A CN 106674640A
- Authority
- CN
- China
- Prior art keywords
- germanium
- far infrared
- latex product
- energy far
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a germanium energy far infrared latex product and a manufacturing method thereof. The germanium energy far infrared latex product comprises a product body made of a natural latex stock solution. Air holes are evenly distributed in the product body. Germanium powder and permanent magnetic powder are evenly mixed inside the product body. Hydrogen ions inside a human body can be taken out of the body through a germanium element, the demand for oxygen by organisms is reduced, and thus the germanium energy far infrared latex product is beneficial to health. The permanent magnetic powder is added, so that a biological static magnetic field of the earth can be simulated, the germanium energy far infrared latex product has magnetism, and a beneficial effect on the human body can be achieved under the action of the magnetic field.
Description
Technical field
The present invention relates to product technique field on bed, and in particular to a kind of germanium energy far infrared latex product and its latex
The preparation method of product.
Background technology
Existing natural emulsion bedding through stirring, are noted using environmentally friendly, the high-elastic characteristic of natural emulsion raw material
The processes such as mould, sulfuration, washing, drying, allow natural emulsion to become the high-grade bedding group material of soft comfortable, but current genuine milk
Glue is not relatively simple with other any health cares beneficial to human body, function in addition to elasticity is good, and genuine milk colloidality
Matter haggles, and old people uses cooler in winter.Natural emulsion becomes the high-grade bedding group material of soft comfortable, but current natural
Latex is not relatively simple with other any health cares beneficial to human body, function in addition to elasticity is good.
The content of the invention
For above-mentioned technical problem, the technical problem to be solved is to provide a kind of germanium energy far infrared latex system
The preparation method of product and its latex product, adds germanium powder in natural emulsion, and germanium powder is dispersed, and germanium can be in human body
Hydrion is taken out of in vitro, demand of the body to oxygen is reduced, so as to be conducive to health.Permanent magnetism magnetic powder is added, earth life is imitated
Thing magnetostatic field, by using the magnetic bedding of band, allows people when sleep, and human body is produced through the action of a magnetic field
Beneficial effect.
The technical scheme that the present invention solves above-mentioned technical problem is as follows:
A kind of germanium energy far infrared latex product, including product body made by natural emulsion stock solution, it is characterised in that institute
State product body interior and be evenly equipped with pore;The product is originally uniformly mixed with vivo germanium powder and permanent magnetism magnetic powder
Beneficial effect:Germanium powder and permanent magnetism magnetic powder are added in latex product, Ge element is a kind of very good antioxidation
Element, with anticancer, defying age, resisting hypertension, anti-inflammatory and antalgic, antioxidation and regulation immunity function.In human body, food
Decomposition carry out by oxygen, in food catabolic process, need to consume substantial amounts of oxygen, while generating water and titanium dioxide
Carbon, if human body is without sufficient oxygen, it is possible to make body give rise to diseases, and germanium can be taken the hydrion in human body out of
In vitro, demand of the body to oxygen is reduced, so as to be conducive to health.
Magnetitum cures mainly solid numbness, rheumatism, oncotic arthralgia of limbs.Inherently one huge Magnetitum of the earth, earth's magnetic field is as sunlight, sky
Gas and water point, nutrition are equally the indispensable fundamentals that life on earth body is depended on for existence.But, due to modern society's height
Building mansion stands in great numbers, the increase of various unwanted electromagnetic waves, disturbs magnetic field of the earth, while human magnetic field has also been upset, this phenomenon
Referred to as " magnetic flesh dislikes disease ".This magnetic deficiency shape shows as having a delicate constitution, fatigue, endocrine disturbance, resistance decline, muscle acid
Bitterly, neurasthenia, hypomnesis and insomnia etc..Only way is the imitative tellurian of one moderate strength of artificial setting
Magnetostatic field, by using the magnetic bedding of band, allows people when sleep, has to human body through the action of a magnetic field
The effect of benefit.
Further, the germanium powder is 4000-6000 mesh powders, and germanium powder is 1-5 with the weight ratio of the natural emulsion:
100。
Using the beneficial effect of further technical scheme:Germanium powder is nanoscale germanium powder, and surface area is easy to be evenly distributed to greatly
In natural emulsion.
Further, the permanent magnetism magnetic powder and the weight ratio of the natural emulsion are 1-3: 100, the permanent magnetism magnetic powder fineness
For 4000 mesh.
Using the beneficial effect of further technical scheme:Permanent magnetism magnetic powder fineness in 4000 mesh, be easy to greatly uniformly by surface area
In being distributed to natural emulsion.
Further, the product of stating originally also is evenly distributed with vivo vulcanizing agent, gellant, antioxidant and liquid soaps.
Using the beneficial effect of further technical scheme:Vulcanizing agent is a kind of multi-functional auxiliary agent, in natural gum, with sulfur
Huang coordinates, and can prevent recovery, improves thermostability, reduces heat, ageing-resistant.Gellant can be such that latex gradually changes uniformly
Semi-rigid solid gel and keep the additional substance of original shape, that antioxidant is prevented from latex is aging.Liquid soaps are used
In foaming.
Further, the weight ratio of the vulcanizing agent, gellant, antioxidant and liquid soaps gross weight and the natural emulsion
For 2-7: 100.
Using the beneficial effect of further technical scheme:The additive of aforementioned proportion, natural emulsion content is high, enables to
Natural rubber more preferable architectural characteristic after preparing.
As further optimization, vulcanizing agent, gellant, antioxidant and liquid soaps gross weight and the natural emulsion
Weight ratio is 5: 100.
A kind of manufacture method of germanium energy far infrared latex product, it is characterised in that in accordance with the following steps:
Step 1:Germanium powder is added in natural emulsion stock solution, vulcanizing agent, gellant, antioxidant and liquid is subsequently adding
Soap, and it is passed through air;
Step 2:The latex that step 1 is obtained persistently stirs N hours, stirs while be continually fed into air, 1 < N
< 8;
Step 3;Permanent magnetism magnetic powder is added, and is persistently stirred and is continually fed into air 6 hours, foamed;
Step 4:After the completion of foaming, latex product sizing is carried out;
Step 5:Latex product is taken out after the completion of sizing, is washed;
Step 6:Water squeezing is carried out after the completion of washing, the latex product after water squeezing is dried;
Step 7:Natural cooling after the completion of drying, obtains germanium energy far infrared latex product.
Foaming 6 hours, germanium energy far infrared latex product air entrapment is uniform.
Further, the method for latex product sizing is:The natural emulsion that step 3 foams is inserted in mould, at 100 DEG C
At a temperature of shaped.
Using the beneficial effect of further technical scheme:Fixed effect is good at a temperature of 100 DEG C.
Further, water squeezing more than 5 times after the completion of the washing.
Using the beneficial effect of further technical scheme:5 water squeezings, preferably 6 times so that latex product interior moisture content
Substantially reduce.
Specific embodiment
It is described below in conjunction with the principle and feature to the present invention, example is served only for explaining the present invention, not uses
In restriction the scope of the present invention.
Embodiment 1:
A kind of Ge element far infrared latex pillow, including latex pillow body made by natural emulsion stock solution, latex pillow sheet is internal
Portion is evenly equipped with pore;The product is originally uniformly mixed with vivo germanium powder and permanent magnetism magnetic powder.
Equally distributed germanium powder is 4000 mesh powders in product body, and germanium powder is that pure germanium unit is extracted from iron ore
Element, germanium powder is 1-5: 100 with the weight ratio of natural emulsion, elects 3: 100 as.Permanent magnetism magnetic powder fineness is in 4000 mesh, permanent-magnet magnetic
Property powder and natural emulsion weight ratio be 1-3: 100, preferably 2: 100.
Latex pillow is originally also evenly distributed with vivo vulcanizing agent, gellant, antioxidant and liquid soaps.Vulcanizing agent, gelling
The weight ratio of agent, antioxidant and liquid soaps gross weight and natural emulsion is 5: 100.
The preparation method of above-mentioned Ge element far infrared latex pillow, concretely comprises the following steps:
Step 1:Pure germanium powder is added in natural emulsion stock solution, vulcanizing agent, gellant, antioxidant and liquid is subsequently adding
Body soap, and it is passed through air;
Step 2:The natural milk gelatin of step 1 is persistently stirred into N hours, is stirred while be continually fed into air, 1 < N
< 8, N is preferably 6;
Step 3;Far infrared ceramic powder is added, and persistently stirs and be continually fed into air, foamed, foamed time is 6
Hour;
Step 4:After the completion of foaming, the natural milk gelatin that step 3 is obtained carries out latex product sizing;
Step 5:Latex product is taken out after the completion of sizing, is washed 6 times in pond;
Step 6:Water squeezing is carried out after the completion of washing, the latex product after water squeezing is put in microwave dryer by water squeezing 6 times
Row drying;
Step 7:Natural cooling after the completion of drying, obtains germanium energy far infrared latex product, to germanium energy far infrared latex
Product encapsulation and packing are processed.
Embodiment 2:
A kind of Ge element far infrared latex mattress, including natural emulsion pad body, latex mattress body interior is evenly equipped with pore;Breast
Rubber cushion is originally uniformly mixed with vivo germanium powder and permanent magnetism magnetic powder.Equally distributed germanium powder is 4000 mesh powders in product body,
Germanium powder is 1-5: 100 with the weight ratio of the natural emulsion, elects 3: 100 as.Permanent magnetism magnetic powder fineness is in 4000 mesh, permanent-magnet magnetic
Property powder and natural emulsion weight ratio be 1-3: 100, preferably 2: 100.Latex pillow is originally also evenly distributed with vivo vulcanizing agent, glue
Solidifying agent, antioxidant and liquid soaps.Vulcanizing agent, gellant, the weight of antioxidant and liquid soaps gross weight and natural emulsion
Than for 5: 100.
The preparation method of above-mentioned Ge element far infrared latex mattress, it is identical with the preparation method of Ge element far infrared latex pillow,
Except for the difference that the shaper that latex product sizing is adopted is different.The temperature shaped in shaper is 100 DEG C.
Finally, these are only presently preferred embodiments of the present invention, not to limit the present invention, all spirit in the present invention and
Within principle, any modification, equivalent substitution and improvements made etc. should be included within the scope of the present invention.
Claims (10)
1. a kind of germanium energy far infrared latex product, including product body made by natural emulsion stock solution, it is characterised in that described
Product body interior is evenly equipped with pore;The product is originally uniformly mixed with vivo germanium powder and permanent magnetism magnetic powder.
2. germanium energy far infrared latex product according to claim 1, it is characterised in that the germanium powder is 4000-6000
Mesh powder, germanium powder is 1-5: 100 with the weight ratio of the natural emulsion.
3. germanium energy far infrared latex product according to claim 1, it is characterised in that the permanent magnetism magnetic powder with it is described
The weight ratio of natural emulsion is 1-3: 100, and the permanent magnetism magnetic powder fineness is 4000 mesh.
4. germanium energy far infrared latex product according to claim 1, it is characterised in that described to state product sheet also equal in vivo
It is even to be mixed with vulcanizing agent, gellant, antioxidant and liquid soaps.
5. germanium energy far infrared latex product according to claim 4, it is characterised in that the vulcanizing agent, gellant, anti-
Oxidant and liquid soaps gross weight and the weight ratio of the natural emulsion are 2-7: 100.
6. germanium energy far infrared latex product according to claim 5, it is characterised in that the vulcanizing agent, gellant, anti-
Oxidant and liquid soaps gross weight and the weight ratio of the natural emulsion are 5: 100.
7. a kind of manufacture method of germanium energy far infrared latex product, it is characterised in that in accordance with the following steps:
Step 1:Germanium powder is added in natural emulsion stock solution, vulcanizing agent, gellant, antioxidant and Liquid Fertilizer is subsequently adding
Soap, and it is passed through air;
Step 2:The latex that step 1 is obtained persistently stirs N hours, stirs while be continually fed into air, 1 < N < 8;
Step 3;Permanent magnetism magnetic powder is added, and persistently stirs and be continually fed into air, foamed;
Step 4:After the completion of foaming, latex product sizing is carried out;
Step 5:Latex product is taken out after the completion of sizing, is washed;
Step 6:Water squeezing is carried out after the completion of washing, the latex product after water squeezing is dried;
Step 7:Natural cooling after the completion of drying, obtains germanium energy far infrared latex product.
8. the manufacture method of germanium energy far infrared latex product according to claim 7, it is characterised in that step 3 is carried out
The time of foaming is 6 hours.
9. the manufacture method of germanium energy far infrared latex product according to claim 7, it is characterised in that:Latex product is determined
The method of type is:Step 4 is that the natural emulsion that will be foamed in step 3 is inserted in mould, is carried out under 100 DEG C of temperature conditionss
Sizing.
10. the manufacture method of germanium energy far infrared latex product according to claim 7, it is characterised in that the washing
After the completion of water squeezing more than 5 times.