CN106673497A - Inorganic core material for class-A fireproof metal composite board and preparation method of inorganic core material - Google Patents
Inorganic core material for class-A fireproof metal composite board and preparation method of inorganic core material Download PDFInfo
- Publication number
- CN106673497A CN106673497A CN201611025630.XA CN201611025630A CN106673497A CN 106673497 A CN106673497 A CN 106673497A CN 201611025630 A CN201611025630 A CN 201611025630A CN 106673497 A CN106673497 A CN 106673497A
- Authority
- CN
- China
- Prior art keywords
- parts
- inorganic core
- core material
- metal composite
- blast furnace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an inorganic core material for a class-A fireproof metal composite board and a preparation method of the inorganic core material. The inorganic core material for the class-A fireproof metal composite board comprises the following components in parts by mass: 42-77 parts of magnesium hydroxide, 11-15 parts of AR glass fibers, 28-35 parts of calcium carbonate, 3-4 parts of vitrified micro bubbles, 8-15 parts of silicon powder, and 7-14 parts of blast furnace slag powder. According to the inorganic core material for the class-A fireproof metal composite board, the raw materials are reasonable in selection and compounding ratio, components mutually support and complement, requirements of class-A fireproof effects and physical properties are met, and not only are physical indexes of intensity, water resistance, weather resistance, bending resistance and the like of the core material guaranteed, but also the inorganic core material has the characteristics of being low in production cost, capable of realizing using of waste, and environmentally friendly. The technology is succinct, the quality is easy to control, and the inorganic core material has great economic benefits and favorable social benefits and is worth popularization.
Description
Technical field
The invention belongs to production of construction materials field, relate generally to a kind of inorganic core for A level fireproof metal composite plates and
Its preparation method.
Background technology
With the quickening of process of industrialization, the heavy construction in city gradually increases, but, what heavy construction was faced disappears
Anti- difficulty is also much larger compared with common building, and with the frequent generation of domestic large-sized fire accident in recent years, country builds for high level
Build propose higher and higher requirement using the fire protecting performance of material, there is many lacking in itself in the PE interlayers of traditional aluminium-plastic panel
Fall into, for example：Inflammable PE, the pole fire hazardous under the conditions of high pressure, heat release, electric discharge etc., in combustion process, flame retardant effect is not good
PE can in a large number melt drop, melt drop thing sustained combustion the intensity of a fire can be caused again constantly to expand, in burning generation a large amount of flue gases pair
Human body also toxic effect, the in addition decomposition of PE burnings can also cause the Collapse Deformation of sheet material, especially apply in airport, car
Stand, gymnasium, the decoration such as public top grade entertainment place and skyscraper when, the common aluminum plastic containing PE interlayers is subject to certain
Limit.The PE masterbatch of existing B levels fire-protection rating, simply improves its burning point, the still meeting after temperature reaches burning point
Burning, so as to initiation fire accident.Drawbacks described above causes composited aluminum and plastic decking to have serious fire risk, once there is fire
Calamity, will cause immeasurable threat to the life and property of people, so, aluminium-plastic panel cannot be expired using PE as core interlayer
The burning behavior class of sufficient national compulsory architectural fire-protection methods code requirement, people urgently find more preferable material to solve this
A little problems.
The content of the invention
It is steady that the technical problem to be solved is to provide a kind of reasonable, the obtained product quality of concise in technology
Fixed, completely unnatural, environmentally friendly inorganic core for A level fireproof metal composite plates and preparation method thereof.
The present invention is achieved through the following technical solutions：
For the inorganic core of A level fireproof metal composite plates, it is comprising component and mass fraction：42-77 parts of magnesium hydroxide, AR
11-15 parts of glass fibre, 28-35 parts of calcium carbonate, 3-4 parts of glass bead, 8-15 parts of silicon powder, ground granulated blast furnace slag 7-14
Part.
Preferably, being comprising component and mass fraction：50-65 parts of magnesium hydroxide, 12-14 parts of AR glass fibres, carbon
30-32 parts of sour calcium, 4 parts of glass bead, 10-13 parts of silicon powder, 9-12 parts of ground granulated blast furnace slag.
More preferably, it is comprising component and mass fraction：60 parts of magnesium hydroxide, 13 parts of AR glass fibres, 31 parts of calcium carbonate, glass
Change 4 parts of microballon, 12 parts of silicon powder, 11 parts of ground granulated blast furnace slag.
Preferably, the ground granulated blast furnace slag is cupro-nickel ground granulated blast furnace slag, cupro-nickel ground granulated blast furnace slag has freezing tolerance strong
The characteristics of, for frost-cracking-preventing effect when severe cold area or low skyscraper high temperature.
Based on knowledge accumulation for many years and practical experience, inventor is final to determine to take as above again through test of many times
Raw material type coordinates and corresponding proportioning, and main consideration is：First, it would be desirable to select to embody the topmost fire prevention resistance of this product
The basic material of the effect of combustion, i.e. magnesium hydroxide, magnesium hydroxide as main fire retardant, with environmental friendliness, fire-retardant, suppression cigarette and
Filling function, and decomposition temperature is high, can use under conditions of processing temperature is higher, when there is combustion case, hydrogen-oxygen
Changing magnesium can occur the decomposition reaction being dehydrated of absorbing heat, and dilute flame zone gas concentration, take away a part of combustion heat, while be dehydrated generating
Oxide the charring layer of one firm compact is formed in material surface, play a part of to stop that heat and oxygen are entered, so as to
Reduction burning velocity is reached, propagation of flame has been prevented, is reduced smokescope, and from the effect of fiery self-extinguishment；And AR glass fibres, it is
100% inorfil, is not only able to be bonded to improve service life, and bring in the erosion for being effective against high alkaloid substance at ordinary times
Power is strong, elastic modelling quantity, shock resistance, tension, bending strength is high, do not fire, freeze proof, resistance to temperature, humidity changing capability are strong, cracking resistance,
The remarkable characteristic of anti-permeability performance, the structure that especially physical modification brings strengthens ability and projects, and designability is strong, easy-formation, greatly
The big performance for improving core, it has good compatibility and powder between, can mix with other raw materials rapidly, is evenly distributed,
Uniform and irregular network distribution system is formed in powder, disperses structural stress, so as to reach the enhanced effect of cracking resistance；
Glass bead, because surface vitreous forms certain granule strength, physicochemical property is sufficiently stable, and ageing-resistant weatherability is strong, has
The anti-fiery ﹑ sound absorption qualities of excellent exhausted hot ﹑, as aglite in this product, can improve as inorganic core needed for manufacture
Slurry and easy mobility and from anti-intensity, reduce finished product shrinkage factor, improve product combination property, reduce comprehensive production cost；
Meanwhile, blast furnace iron powder is typically made steel the waste residue refinement for producing by steel mill and is formed, and has also reached twice laid, the mesh of reduces cost
's.The final employing of these raw materials and the selection of their mass fraction are all the inorganic cores according to A level fireproof metal composite plates
Performance requirement determined by lot of experiments, according to the design that principles above is carried out, the A levels fire prevention plate core that the present invention is provided
The powder of material has reached that A level flameproof effects, physical property be up to standard, environmental protection beneficial effect, and the cooperation of these ratios makes
The inorganic core of the invention is obtained while ensure that performance, manufacturing cost is minimum, if using other formulas or comparing
Example, the possible poor-performing of fireproof metal composite plate for causing product cost high or to be finally made is undesirable.
The invention also discloses the preparation method of the above-mentioned inorganic core for A level fireproof metal composite plates, comprises the steps of：
（1）Prepare raw material, in strict accordance with technological requirement raw material is purchased, incoming material must be tested strictly by quality requirement
Receive, detect do not meet quality requirement material forbid warehouse-in；
（2）Various raw materials are weighed in proportion by dispensing, must be in strict accordance with regulation during weighing；
（3）Feed intake, first, magnesium hydroxide, calcium carbonate glue and 20-40%, silicon powder, ground granulated blast furnace slag are mixed to form
Powder input mixer operating, mixer speed setting after stirring 0.5-1.5 minutes, is added surplus at 35-45 rev/min
The powder that remaining 60-80% magnesium hydroxides, calcium carbonate, silicon powder, ground granulated blast furnace slag are mixed to form, by mixer rotating speed 65- is transferred to
70 revs/min are continued to stir 0.5-1.5 minutes, finally, pour whole glass beads and AR glass fibres into mixer, while will
Mixer rotating speed is transferred to 60-80 rev/min, and altogether, in 7-9 minutes, the slurry of inorganic core needed for obtaining suppressing is simultaneously for mixing time
It is compressing.
Preferably, the glue is water base polyurethane glue.
Compared with prior art, its advantage is：The present invention is used for the original of the inorganic core of A level fireproof metal composite plates
Material selection and reasonable mixture ratio, mutually support between each composition and supply, and have reached A levels flameproof effect and physical property requirements,
While ensureing the items physical index such as intensity, water-fast, weather-proof, warping resistance of core, also with low production cost, waste profit
With the characteristics of, environmental protection, and concise in technology, quality is easily controllable, with huge economic benefit and good social benefit,
It is worthy to be popularized.
Specific embodiment
Any feature disclosed in this specification, unless specifically stated otherwise, can be equivalent or with similar purpose by other
Alternative features are replaced.I.e., unless specifically stated otherwise, each feature is an example in a series of equivalent or similar characteristics
.
Embodiment 1
For the inorganic core of A level fireproof metal composite plates, it is comprising component and mass fraction：65 parts of magnesium hydroxide, AR glass
12 parts of fiber, 28 parts of calcium carbonate, 3 parts of glass bead, 10 parts of silicon powder, 9 parts of ground granulated blast furnace slag.Preparation method, comprising following step
Suddenly：
（1）Prepare raw material, in strict accordance with technological requirement raw material is purchased, incoming material must be tested strictly by quality requirement
Receive, detect do not meet quality requirement material forbid warehouse-in；
（2）Various raw materials are weighed in proportion by dispensing, must be in strict accordance with regulation during weighing；
（3）Feed intake, first, magnesium hydroxide, calcium carbonate glue and 20-40%, silicon powder, ground granulated blast furnace slag are mixed to form
Powder input mixer operating, mixer speed setting after stirring 0.5-1.5 minutes, is added surplus at 35-45 rev/min
The powder that remaining 60-80% magnesium hydroxides, calcium carbonate, silicon powder, ground granulated blast furnace slag are mixed to form, by mixer rotating speed 65- is transferred to
70 revs/min are continued to stir 0.5-1.5 minutes, finally, pour whole glass beads and AR glass fibres into mixer, while will
Mixer rotating speed is transferred to 60-80 rev/min, and altogether, in 7-9 minutes, the slurry of inorganic core needed for obtaining suppressing is simultaneously for mixing time
It is compressing.The glue is water base polyurethane glue.
Embodiment 2
For the inorganic core of A level fireproof metal composite plates, it is comprising component and mass fraction：62 parts of magnesium hydroxide, AR glass
12 parts of fiber, 30 parts of calcium carbonate, 4 parts of glass bead, 12 parts of silicon powder, 9 parts of ground granulated blast furnace slag, preparation method and the phase of embodiment 1
Together.The ground granulated blast furnace slag is cupro-nickel ground granulated blast furnace slag.
Embodiment 3
For the inorganic core of A level fireproof metal composite plates, it is comprising component and mass fraction：60 parts of magnesium hydroxide, AR glass
13 parts of fiber, 31 parts of calcium carbonate, 4 parts of glass bead, 12 parts of silicon powder, 11 parts of ground granulated blast furnace slag, preparation method and the phase of embodiment 1
Together.
The invention is not limited in aforesaid specific embodiment.The present invention is expanded to and any in this manual disclosed
New feature or any new combination, and the arbitrary new method that discloses or the step of process or any new combination.
Claims (6)
1. the inorganic core of A level fireproof metal composite plates is used for, it is characterised in that be comprising component and mass fraction：Hydroxide
42-77 parts of magnesium, 11-15 parts of AR glass fibres, 28-35 parts of calcium carbonate, 3-4 parts of glass bead, 8-15 parts of silicon powder is high
7-14 parts of stove slag powders.
2. the inorganic core for A level fireproof metal composite plates according to claim 1, it is characterised in that comprising component
It is with mass fraction：50-65 parts of magnesium hydroxide, 12-14 parts of AR glass fibres, 30-32 parts of calcium carbonate, 4 parts of glass bead,
10-13 parts of silicon powder, 9-12 parts of ground granulated blast furnace slag.
3. the inorganic core for A level fireproof metal composite plates according to claim 2, it is characterised in that comprising component
It is with mass fraction：60 parts of magnesium hydroxide, 13 parts of AR glass fibres, 31 parts of calcium carbonate, 4 parts of glass bead, 12 parts of silicon powder is high
11 parts of stove slag powders.
4. the inorganic core for A level fireproof metal composite plates according to claim 1, it is characterised in that the blast furnace
Slag powders are cupro-nickel ground granulated blast furnace slag.
5. the preparation method of the inorganic core according to claim 1-4 any one, it is characterised in that step is included：（1）
Prepare raw material, in strict accordance with technological requirement raw material is purchased, incoming material strictly must be carried out an acceptance inspection by quality requirement, detect
Forbid warehouse-in to the material for not meeting quality requirement；（2）Various raw materials are weighed in proportion by dispensing, must during weighing
Must be in strict accordance with regulation；（3）Feed intake, first, magnesium hydroxide, calcium carbonate glue and 20-40%, silicon powder, ground granulated blast furnace slag
The powder input mixer operating being mixed to form, mixer speed setting is stirring 0.5-1.5 minutes at 35-45 rev/min
Afterwards, the powder that remaining 60-80% magnesium hydroxides, calcium carbonate, silicon powder, ground granulated blast furnace slag are mixed to form is added, by mixer
Rotating speed is transferred to 65-70 rev/min and continues to stir 0.5-1.5 minutes, finally, whole glass beads and AR glass fibres is poured into and stirred
Machine is mixed, while mixer rotating speed is transferred into 60-80 rev/min, altogether mixing time obtains inorganic needed for compacting in 7-9 minutes
The slurry of core is simultaneously compressing.
6. preparation method according to claim 5, it is characterised in that the step（1）In glue used be aqua type
Polyurethane adhesive.