CN106671535A - Waterproof roll - Google Patents
Waterproof roll Download PDFInfo
- Publication number
- CN106671535A CN106671535A CN201710140425.6A CN201710140425A CN106671535A CN 106671535 A CN106671535 A CN 106671535A CN 201710140425 A CN201710140425 A CN 201710140425A CN 106671535 A CN106671535 A CN 106671535A
- Authority
- CN
- China
- Prior art keywords
- layer
- waterproof roll
- thickness
- roll according
- corrosion protective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterproof roll, which comprises an anti-corrosion protective layer, a support layer, a color processing layer, a heat insulating layer, a self-adhering layer and a stripping layer sequentially overlapped. According to the waterproof roll provided by the invention, the anti-corrosion protective layer can play a role in corrosion prevention, the heat insulating layer can play a better role in heat protection, and the layer structures are compounded to play better roles in heat insulation, waterproofness and corrosion prevention.
Description
Technical field
The present invention relates to the technical field of waterproof material, in particular to waterproof roll.
Background technology
The reason for metal Roof seeps water has many, such as gutter underfed, structure design are unreasonable, board quality compared with
Difference, install and unreasonable etc. can all cause metal Roof to seep water.The infiltration that these anthropic factors are caused, progressively can be by people slowly
Recognize and overcome.But its most basic Reason Of Leakange, is but that metal material self-characteristic is caused, and people use metal material,
It is intended that using the advantage of metal material, but also cannot avoids or overcome its shortcoming.This point first have to from metal material this
The physical property of material is talked about, and first：Metal material has a superpower thermal conductance, that is, it has often been said that heat absorption is fast, heat transfer
Hurry up.Metal Roof so be will result under the irradiation of the sun, be rapidly heated, and suddenly encountering extreme weather or evening, temperature
Degree can fall after rise quickly again, cause roofing temperature the great temperature difference occur.Second:Metal material has good ductility, this
Extend and still can not extend in the presence of outer power, and also can automatically extend under the influence of the temperature, run into low temperature then
Can shrink.Metal material both properties just combine, and are formed expanding with heat and contract with cold for metal.
In prior art, waterproof roll insulating water-proof antiseptic property is limited.
The content of the invention
In view of this, the purpose of the embodiment of the present invention is to provide a kind of waterproof roll, and the waterproof roll has preferable
Insulating water-proof antiseptic property.
A kind of waterproof roll, including be sequentially overlapped the corrosion protective covering of setting, supporting layer, color treatments layer, thermal insulation layer, from
Adhesion coating and peel ply.
Further, the corrosion protective covering is PVDF layers.
Further, the thickness of the corrosion protective covering is 20~50 μm.
Further, the supporting layer is pet layer.
Further, the thickness of the supporting layer is 20~50 μm.
Further, the thickness of the color treatments layer is 2~5 μm.
Further, the thermal insulation layer is aluminium foil.
Further, the thickness of the thermal insulation layer is 7~100 μm.
Further, the thickness of the self-adhesive layer is 0.2~2.5mm.
Further, the thickness of the peel ply is 20~30 μm.
The waterproof roll of the present invention, corrosion protective covering can play anti-corrosion function, and thermal insulation layer can play preferable thermal resistance performance,
These Rotating fields recombination energies play preferable insulating water-proof antiseptic property.
To enable the above objects, features and advantages of the present invention to become apparent, preferred embodiment cited below particularly, and coordinate
Appended accompanying drawing, is described in detail below.
Description of the drawings
In order to be illustrated more clearly that the technical scheme of the embodiment of the present invention, below will be attached to what is used needed for embodiment
Figure is briefly described, it should be understood that, the following drawings illustrate only some embodiments of the waterproof roll of the present invention, therefore
The restriction to scope is not construed as, for those of ordinary skill in the art, in the premise for not paying creative work
Under, can be obtaining other related accompanying drawings according to these accompanying drawings.
Fig. 1 shows the structural representation of the waterproof roll that the embodiment of the present invention is provided.
Main element symbol description：
100-waterproof roll；20-corrosion protective covering；30-supporting layer；40-color treatments layer；50-thermal insulation layer；
60-self-adhesive layer；70-peel ply.
Specific embodiment
For the ease of understanding the present invention, waterproof roll is described more fully below with reference to relevant drawings.Accompanying drawing
In give the first-selected embodiment of waterproof roll.But, waterproof roll can be realized in many different forms, however it is not limited to
Embodiment described herein.On the contrary, the purpose for providing these embodiments is to make the disclosure to waterproof roll more saturating
It is thorough comprehensive.
Term used in the various embodiments of the disclosure is only used for describing the purpose of specific embodiment and not anticipating
In the various embodiments for limiting the disclosure.As used herein, singulative is intended to also including plural form, unless context is clear
Chu ground is indicated otherwise.Unless otherwise defined, all terms (including the technical term and scientific terminology) tool being otherwise used herein
There is the implication identical implication being generally understood that with the various embodiment one skilled in the art of the disclosure.The term
(term limited such as in the dictionary for generally using) is to be interpreted as to be had and the situational meaning in correlative technology field
Identical implication and will be not construed as with Utopian implication or excessively formal implication, unless in the various of the disclosure
It is clearly defined in embodiment.
In describing the invention, it is to be understood that term " longitudinal direction ", " horizontal ", " on ", D score, "front", "rear",
The orientation or position relationship of the instruction such as "left", "right", " vertical ", " level ", " top ", " bottom ", " interior ", " outward " is based on accompanying drawing institute
The orientation for showing or position relationship, are for only for ease of the description present invention and simplify description, rather than indicate or imply the dress of indication
Put or element must have specific orientation, with specific azimuth configuration and operation, therefore it is not intended that to the present invention limit
System.
In the description of this specification, reference term " one embodiment ", " some embodiments ", " example ", " specifically show
The description of example " or " some examples " etc. means to combine specific features, structure, material or spy that the embodiment or example are described
Point is contained at least one embodiment of the present invention or example.In this manual, to the schematic representation of above-mentioned term not
Necessarily refer to identical embodiment or example.And, the specific features of description, structure, material or feature can be any
One or more embodiments or example in combine in an appropriate manner.
In describing the invention, unless otherwise prescribed and limit, it should be noted that term " installation ", " connected ",
" connection " should be interpreted broadly, for example, it may be mechanically connected or electrical connection, or the connection of two element internals, can
Being to be joined directly together, it is also possible to be indirectly connected to by intermediary, for the ordinary skill in the art, can basis
Concrete condition understands the concrete meaning of above-mentioned term.
Statement (" first ", " second " etc.) used in various embodiments disclosed herein can be modified in various realities
The various element in example are applied, but corresponding element can not be limited.For example, it is presented above to be not intended to limit the element
Order and/or importance.The purpose for being only used for differentiating an element and other elements presented above.For example, first user
Device and second user device indicate different user device, although the two is all user's set.For example, without departing from the disclosure
In the case of the scope of various embodiments, the first element is referred to alternatively as the second element, and similarly, the second element is also referred to as
One element.
It should be noted that：If an element ' attach ' to another element by description, can be by the first composition unit
Part is directly connected to the second element, and " connection " the 3rd can constitute between the first element and the second element
Element.On the contrary, when an element " being directly connected to " is arrived into another element, it will be appreciated that be in the first element
And second do not have the 3rd element between element.
Additionally, this paper key elements or indefinite article " one kind " and " one " before component are to key element or the quantitative requirement of component
(i.e. occurrence number) unrestriction.Therefore " one " or " one kind " should be read as including one or at least one, and odd number
The key element or component of form also includes plural form, unless the obvious purport of the quantity refers to singulative.
Refer to Fig. 1.The waterproof roll 100 of the embodiment of the present invention includes being sequentially overlapped the corrosion protective covering 20 of setting, props up
Support layer 30, color treatments layer 40, thermal insulation layer 50, self-adhesive layer 60 and peel ply 70.
Above-mentioned " superposition is arranged " may be appreciated and refer to that multiple objects (such as thin film etc.) with Rotating fields adopt one
Fit in the stack manner on another one surface.So that A, B, C, D are sequentially overlapped setting as an example, a surface for referring to A arranges B, B
Surface arranges the surface of C, C and arranges D, i.e., according to a direction (such as from top to bottom), A, B, C, D are arranged in order.
Above-mentioned corrosion protective covering 20 can be PVDF layers, to play preferable corrosion-resistant, chemical-resistance and weather resistance.This
Place, PVDF is Kynoar.PVDF has：1st, splendid chemical-resistant characteristic；2nd, it is wear-resisting, high mechanical properties and toughness；3rd, it is resistance to
Time, uvioresistant and core ray；4th, thermostability is good and has a high dielectric strength.
In order to further improve the corrosion resistance and weatherability etc. of PVDF layers, corrosion protective covering 20 can car using modified
PVDF layers.Herein, modified PVDF is that PVDF is modified.It refers to known technology to be modified, such as Chinese patent
CN102382323A, specially：The step of method for improving Kynoar alkali corrosion resistance, is, using solution blended process by entirely
Fluoroalkyl amphipathic molecule mixes with Kynoar solution, then drying and forming-film.Comprise the following steps：It is inclined to gather to weigh quality
The perfluoroalkyl amphipathic molecule of fluorothene raw material 2%~5%, dissolves in Kynoar solution, film forming after being dried.Perfluoroalkyl
Amphipathic molecule is that perfluoro octyl sulfonic acid salt, perfluoro capryl carboxylate, perfluorinated sulfonic resin or perfluoroalkyl non-ionic surface are lived
Property agent.Solvent for use is DMF, N,N-dimethylacetamide, N- crassitudes in Kynoar solution
Ketone, dimethyl sulfoxide or Ketohexamethylene.
Or such as Chinese patent CN105435650A, specially：Raw material with Kynoar as film, the polyvinylidene fluoride
Alkene is made by the steps：1) 1~2 weight portion hexyldecanol, 0.8 weight portion hydrogen peroxide, 1.1 weight portions are put in reactor
Inorganic alkali solution, mix homogeneously, then put into 1.6 weight portion polyoxyethylene oleic acid esters, 14.5 weight portion dichlorodifluoromethane solvents,
1.8 weight portion Phenylmethanesulfonyl fluoride solution, in -6 DEG C of stirring reactions 25 minutes；2) put into again 1.3 weight portion oleoyl amino acid sodiums,
2.2 weight portion hexyldecanol solution, 59 weight portion vinylidene fluoride monomers, 1.8 weight portion methyl cyclopentanes, it is anti-in 18 DEG C of stirrings
Should, pressure drop is to terminating reaction during below 0.23MPa；3) filter, wash, be dried, obtain final product powder Kynoar.
Or such as Chinese patent CN105694307A, specially：Polyvinylidene fluoride nanometer thin-film material is according to weight portion
Raw material includes：Kynoar 20-70 parts, lithium oxide 1-5 parts, polystyrolsulfon acid 5-25 parts, Zinc Oxide 1-8 part, polypropylene
Nitrile 3-18 parts, boron oxide 1-18 parts, tellurium dioxide 1-7 parts, Zinc Oxide 1-15 part, lead oxide 1-8 parts, Barium monoxide 1-8 parts.
The referring to property of thickness of corrosion protective covering 20 be 20~50 μm, such as 20 μm, 21 μm, 25 μm, 30 μm, 35 μm,
40 μm, 45 μm, 48 μm or 50 μm etc..
Except this, corrosion protective covering 20 can also be using PTEF materials etc..
The effect of supporting layer 30 is that corrosion protective covering 20 is supported.Supporting layer 30 can be pet layer.Herein, PET is
Refer to polyethylene terephthalate, chemical formula is COC6H4COOCH2CH2O.(English：Polyethylene
Terephthalate, abbreviation PET), exchanged with glycol ester by dimethyl terephthalate (DMT) or with p-phthalic acid and ethylene glycol
Esterification first synthesizes bishydroxyethyl terephthalate, polycondensation reaction is then carried out again and is obtained.
For improve the high-low temperature resistant of supporting layer 30, stable mechanical performance, electrical insulating property excellent, anti-creep, endurance
Property, rub resistance etc. preferably, supporting layer 30 can adopt modified PET material.A kind of modified PET material can be included, its raw material bag
Containing PET resin, ultraviolet (UV) resistant agent, antioxidant, stabilizer, the consumption of the ultraviolet (UV) resistant agent be account for PET resin quality 3~
7wt%, to account for PET resin 0.8~1.2wt% of quality, the consumption of stabilizer is to account for PET resin quality to the consumption of antioxidant
2~4wt%.
Herein, antioxidant can include four [β-(3,5- di-t-butyl -4- phenyl) propanoic acid] pentaerythritol esters, three
[2.4- di-tert-butyl-phenyls] phosphite ester, 1,3,5- tri- (the 4- tert-butyl group -3- hydroxyl -2,6- dimethyl benzyls) -1,3,5- three
The instantiation such as piperazine -2,4,6- (1H, 3H, 5H)-triketone or 2,6- bis--three-level butyl -4- sylvans.
Herein, ultraviolet (UV) resistant agent can include 2,2 '-(Isosorbide-5-Nitrae-phenylene) double (4H-3,1- benzoxazinyl -4- ketone) or chlorine
For Benzotriazole Ultraviolet Stabilizer etc., except this, ultraviolet (UV) resistant agent can also be received for nano titanium oxide, nano zine oxide etc.
Rice filler.For Nano filling, in order to improve its compatibility with PET resin, can be using coupling agent to Nano filling table
Face is modified.Coupling agent can have silicone coupling agents, titanate coupling agent or aluminate coupling agent etc..Silicone coupling agents are
Refer to that there is structureMaterial, here R is hydrolyzable groups, specially halogen, alkoxyl or acetamido,
R' is the alkyl containing double bond, specially vinyl, methacryloxy or methacryloxypropyl.Can include
γ-glycidyl ether oxygen propyl trimethoxy silicane (KH560), γ-methacryloxypropyl trimethoxy silane
(KH570), γ-aminopropyl triethoxysilane (KH550) etc..Aluminate coupling agent refers to the structured (C of tool3H7O)x·Al
(OCOR)m·(OCOR1) n (OAB) y, R, R1Can be alkyl etc..Aluminate coupling agent can include SG-Al821 (distearyls
Oxygen isopropyl Aluminate), DL-411, DL-411AF, DL-411D, DL-411DF, the instantiation of Aluminate ASA.Titanate esters idol
Connection agent refers to ROO (4-n) Ti (OX-R ＇ Y) n (here, n=2,3) expression；Wherein RO- is hydrolyzable lower alkyloxy, can be with
Mineral surfaces hydroxyl reacts, so as to reach the purpose of chemical coupling；OX- can be carboxyl, alkoxyl, sulfonic group, phosphorio
Deng.Titanate coupling agent can be KR-TTS, its chemical entitled isopropyl three (different tallow phthalidyl) metatitanic acid vinegar；Or titanate esters
Coupling agent TMC-10, its chemical entitled sec.-propyl three (dioctyl phosphoric acid acyloxy) titanic acid ester；Or for titanate coupling agent
TMC-101, its Oleic acid acyloxy of chemical entitled isopropyl two (dioctyl phosphoric acid acyloxy) titanate esters etc..The modified method in surface
For example can be：Nano titanium oxide addition dehydrated alcohol is sufficiently stirred for and sonic oscillation, is then slowly added to silane coupled
Agent KH-570, is heated to 70 DEG C or so, and constant temperature flows back 2 hours, and sucking filtration, with absolute ethanol washing three times, is dried and must changed to surface
Nano titanium oxide after property.
Herein, stabilizer is also called light stabilizer, can include light stabilizer 292 (two-(N- methyl -2,2,6,6- tetra-
Methyl -4- pyridine radicals) last of the ten Heavenly stems diester and methyl-(N- methyl -2,2,6,6- tetramethyl -4- pyridine radicals last of the ten Heavenly stems diester), light stabilizer 622
(succinic acid and (4- hydroxyl -2, the polymer of 2,6,6- tetramethyl -1- piperidine alcohols)), light stabilizer 770 (double (2,2,6,6- tetra-
Methyl -4- piperidyls) sebacate), (the poly- [[6- [(1,1,3,3- tetramethyl butyl) amine] -1,3,5- tri- of light stabilizer 944
Piperazine -2,4- diyls] [(2,2,6, the 6- tetramethyl -4- piperidines) imines] dihexyls of -1,6- bis- [(2,2,6,6- tetramethyl -4- piperazines
Pyridine) imines]]]) in one or more.
Herein, the mean molecule quantity of PET resin can be 2~200,000.
Herein, the raw material of above-mentioned modified PET can also add lubricant etc..Lubricant is pentaerythritol stearate, silicone
One kind in powder, modified ethylene bis-fatty acid amides.
Supporting layer 30 is except being also the conventionally forms such as PBT for PET.In order to improve the dimensional stability of PBT, impact
Can, warpage properties and ensure its stability of strutting system, PBT material can adopt glass fibre reinforced modified, it is possible to provide a kind of modified PBT material
Material, its raw material includes 25~55wt% of PBT, 10~55wt% of acrylonitrile-butadiene-styrene copolymer, reinforcing agent：10~
30wt%, 3.0~7.0wt% of compatilizer, 0.3~0.5wt% of coupling agent, 0.1~1.0wt% of antioxidant, anti-glass emergence on the surface agent
0.3~0.7wt%.Here, compatilizer is MBS resin system styrene (S)-maleic anhydride (MA) copolymer；Reinforcing agent is glass
Fibre reinforced materials；Antioxidant includes phenolic antioxidant four [β-(3 ', 5 '-di-t-butyl -4 '-hydroxy phenyl) propanoic acid] Ji Wusi
Alcohol ester 0.05-0.5% and phosphite ester kind antioxidant (2,4 di-tert-butyl-phenyl) tris phosphite 0.05-0.5%；Anti- glass
Outer distillate medicinal water is ethylene bis stearamide.
Color treatments layer 40 is as printing layer in the present invention.Color treatments layer 40 preferably uses solvent-borne type PET ink,
Printing treatment is carried out to PET.To improve ink color inhibition, adhesive force, can be to adding ultra-violet absorption agent content about in ink
0.5% or so, firming agent 3%.
The thickness of color treatments layer 40 is 2~5 μm, for example, can be 2 μm, 2.5 μm, 3 μm, 3.5 μm, 4 μm, 4.5 μm or 5 μm
Deng.
Thermal insulation layer 50 can be aluminium foil.Aluminium foil is reflected to reach the mesh of radiating by the light to being radiated thermal insulation layer 50
's.7~100 μm of thermal insulation layer 50, such as 7 μm, 10 μm, 20 μm, 40 μm, 50 μm, 70 μm, 90 μm, 95 μm or 100 μm.
Certainly, thermal insulation layer 50 can also be the insulating moulding coating layer with preferable heat-proof quality.Can adopt as insulating moulding coating
Known form.
Thermal insulation layer 50 can also be the resin containing refractive index less than 1.52 and the filling of micropowder shape that refractive index is more than 1.60
The resin combination of agent is made (such as by extrusion moulding).Herein, resin of the refractive index less than 1.52 can include fat adoption
One kind in vinegar resinoid, acrylic resin, fluororesin, polyolefin resin fat or at least more than two kinds.Refractive index is
More than 1.60 micro- powdered filler can be titanium oxide etc..
The effect of self-adhesive layer 60 be carry out with base material to be installed it is bonding.The thickness of self-adhesive layer 60 can be 0.2~2.5mm, such as
0.2mm, 0.3mm, 0.5mm, 1.0mm, 1.5mm, 2mm, 2.2mm, 2.5mm etc..In order to improve the adhesive strength of self-adhesive layer 60, shape
Into self-adhesive layer 60 glue can comprising 25~35wt% butyl rubbers, 15~25wt% polyisobutylene, 3~7wt% butyl resins,
30~40wt% of filler, 3~7wt% of carbon black, 0.7~1.2wt% of antioxidant, 1.5~2.5wt% of ultra-violet stabilizer, stream
Flat 1.5~2.5wt% of agent.
Herein, filler is Calcium Carbonate.Antioxidant and ultra-violet stabilizer are referred to described in above-mentioned modified PET material.
Levelling agent can organosiloxane levelling agent (BYK-301) etc..
Except this, the glue of self-adhesive layer 60 can also adopt other film forming matters (such as polyurethane system), specially：Comprising
Water-borne polyurethane bond 9-16 parts, wetting agent 3-7 parts, DBSA 7-11 part, aerosol-OT salt 4-10
Part, polyisocyanate 3-10 part, TDI isocyanuric acid ester 4-7 parts, Isooctyl acrylate monomer 6-10 parts, acrylic acid 3-9 parts, azo two
Isopropyl cyanide 4-7 parts, methyl methacrylate 4-10 parts, styrene-grafted polyether polyol 8-16 part, polypropylene glycol PPG1-5 parts,
Silicone rubber 4-9 parts, polysiloxane leveling agents 3-8 parts, diluent 1-5 parts.
The effect of above-mentioned peel ply 70 is that self-adhesive layer 60 is isolated and protected, when in use, peelable stripping
Layer 70.The thickness of peel ply 70 is 20~30 μm.Peel ply 70 can be using release paper etc..
Above-mentioned waterproof roll construction when should be noted that it is following some：
1st, the lap width of coiled material is that long side is not less than 50mm, and minor face is not less than first coiled material of 100mm. to overlap joint
Place, with second coiled material to lap-joint again, it is impossible to stitch, at least staggers one meter.Between coiled material and coiled material, coiled material and enhancement layer it
Between overlap joint must be firm, it is impossible to the presence of the phenomenon of alice.
2nd, just constructed the waterproof layer for finishing, if should not at will open paste again other places. open more than secondary, will bond
Loosely, it is necessary to which brushing base treatment agent could bond.
3rd, temperature is not preferably constructed below 15 degree.Winter construction will brushing base treatment agent, early, evening construction is color
When steel tiling has dew, to stop construction.
4th, coiled material should not be firmly extruded very much at the head of a nail, certain space should be left to the head of a nail, color steel tile gap is more than 0.3MM
When to carry out consolidation process, can be constructed after process.Negative and positive angle, stake facade and plane inner corner trim, facade interior angle and exterior angle must
Extra play must be done.
5th, workmen should wear soft rubber soled shoes, the hard-caked sediment footwear for forbidding threading to follow closely.In work progress, forbid non-operation
Personnel enter scene.
The waterproof roll of the present invention can be widely used in the fields such as non-ferrous metals smelting works, steel mill, power plant.
It is above-mentioned not address part, it is adaptable to prior art.
Although more above used the term for representing structure, such as " corrosion protective covering ", " supporting layer ", " color treatments
Layer " etc., but be not precluded from using the probability of other terms.It is used for the purpose of more easily describing and explaining using these terms
The essence of the present invention；It is all contrary with spirit of the invention to be construed as any additional restriction.
The above, the only specific embodiment of the present invention, but protection scope of the present invention is not limited thereto, any
Those familiar with the art the invention discloses technical scope in, change or replacement can be readily occurred in, all should contain
Cover within protection scope of the present invention.Therefore, protection scope of the present invention described should be defined by scope of the claims.
Claims (10)
1. a kind of waterproof roll, it is characterised in that including be sequentially overlapped the corrosion protective covering of setting, supporting layer, color treatments layer,
Thermal insulation layer, self-adhesive layer and peel ply.
2. waterproof roll according to claim 1, it is characterised in that the corrosion protective covering is PVDF layers.
3. waterproof roll according to claim 1, it is characterised in that the thickness of the corrosion protective covering is 20~50 μm.
4. waterproof roll according to claim 1, it is characterised in that the supporting layer is pet layer.
5. waterproof roll according to claim 1, it is characterised in that the thickness of the supporting layer is 20~50 μm.
6. waterproof roll according to claim 1, it is characterised in that the thickness of the color treatments layer is 2~5 μm.
7. waterproof roll according to claim 1, it is characterised in that the thermal insulation layer is aluminium foil.
8. waterproof roll according to claim 1, it is characterised in that the thickness of the thermal insulation layer is 7~100 μm.
9. waterproof roll according to claim 1, it is characterised in that the thickness of the self-adhesive layer is 0.2~2.5mm.
10. waterproof roll according to claim 1, it is characterised in that the thickness of the peel ply is 20~30 μm.