CN106654781A - Electric brush used for dust collector motor - Google Patents
Electric brush used for dust collector motor Download PDFInfo
- Publication number
- CN106654781A CN106654781A CN201510745085.0A CN201510745085A CN106654781A CN 106654781 A CN106654781 A CN 106654781A CN 201510745085 A CN201510745085 A CN 201510745085A CN 106654781 A CN106654781 A CN 106654781A
- Authority
- CN
- China
- Prior art keywords
- brush
- electric brush
- powder
- raw mixture
- graphite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an electric brush used for a dust collector motor. The electric brush is prepared by the following method: base powder material and a binder solution are evenly mixed for preparing electric brush raw material mixture; drying and crushing are performed on the electric brush raw material mixture so that electric brush raw material mixture powder is prepared; the electric brush raw material mixture powder is added to a pressing mould to perform pressing process so as to obtain an electric brush blank; heat curing is performed on the electric brush blank so as to obtain an electric brush beginning product; and finished product processing is performed on the electric brush beginning product so as to obtain a finished electric brush, wherein the base powder material includes natural graphite, synthetic graphite, silicon carbide, polytetrafluoroethylene, carbon fiber powder, molybdenum disulfide, curing agent and polyphenyl ester resin. The electric brush used for the dust collector motor is low in resistivity, great in wear resistance, great in commutation performance, low in spark grade and great in product stability and can meet the use requirements of the efficient dust collector motor.
Description
Technical field
The present invention relates to a kind of brush used for electric engine of cleaner, more particularly to it is a kind of suitable for heavy duty detergent motor of dust collector
Brush, belongs to machine field.
Background technology
Brush is a kind of conductive component that electrical connection is formed for contacting with commutator or slip ring in motor, is electricity
The important composition part of machine.As the sliding contact body for importing and exporting electric current, its conduction, heat conduction and greasy property
Well, and with certain mechanical strength and the instinct for suppressing commutation property spark.It is widely used in various friendship directly
Stream generator, synchronous motor, storage battery dc motor, crane motor collecting ring, various electric welding machine etc., it is several
All of direct current generator and commutating machine all use brush.
With science and technology development, the species of motor and the working condition for using it is more and more diversified, thus need
There is various types of brush to meet the various requirement of motor, therefore the species of brush is also with electric machine industry
Development and it is more and more.
At present the classification method of brush has following four kinds：(1) by the soft or hard of material can be divided into soft brush,
Middle hard brush and hard brush；(2) steam turbine generator brush, steel rolling can be divided into by the use object of brush
It is brush for electromachine, traction electric machine brush, automobile and tractor brush, domestic electric appliance motor brush, electronic
Instrument brush, electric motor of automobile brush, aircrafts electric machinery brush etc.；(3) it is divided into black by the color of brush
Brush (being made with pure carbon graphite material) and color brush (being made with the metal materials such as copper and graphite)；(4)
Can be divided into electrographite brush, electrographite brush, metal-graphite brush, simple metal brush by the material difference of brush
Deng.
Motor of dust collector is generally alternating current generator, because of the needs of its applied environment, it is desirable to brush used for electric engine of cleaner
The advantages of possessing good suppression spark ability, life-span length.With issuing for the new energy-conservation instruction of European Union, household electrical appliance neck
Domain gradually tends to high efficiency, low-power, and in motor of dust collector field, heavy duty detergent motor of dust collector has become one
The trend of kind.
The concrete following points of heavy duty detergent brush used for electric engine of cleaner are required：(1) long service life and do not wear and tear
Commutator, does not make commutator the phenomenons such as cut, injustice, ablation, wire drawing occur；(2) with good commutation
Performance, motor operation spark is little, and energy loss is little；(3) it is not overheated when brush runs, not damaged, brush
Pigtail nondiscolouring, not ablation；(4) in running, one layer can quickly be formed uniformly in commutator face
Light coppery oxide-film.
However, at present general domestic brush operational efficiency is relatively low, short life, stability are poor, domestic carbon brush factory without
Method meets the use requirement of heavy duty detergent brush used for electric engine of cleaner.
The content of the invention
The invention aims to the technical problem for solving prior art presence provides a kind of used for electric engine of cleaner
Brush, brush resistance rate used for electric engine of cleaner of the invention is relatively low, anti-wear performance is good, the good, spark of commutation ability etc.
The low, product stability of level is good, can meet the use requirement of heavy duty detergent motor of dust collector.
The invention provides a kind of brush used for electric engine of cleaner, is prepared via a method which to form：
By the way that matrix powder is well mixed with binder solution, brush raw mixture is prepared；
Drying and processing is carried out to the brush raw mixture, brush raw mixture siccative is obtained；
Break process is carried out to the brush raw mixture siccative, brush raw mixture powder is obtained；
The brush raw mixture powder is added in compacting tool set, compression process is carried out to it, electricity is obtained
Brush blank；
Heat cure process is carried out to the brush blank, brush first product is obtained；
Finished product working process is carried out to the brush first product, brush finished product is obtained；
Wherein, described matrix powder includes graphite, carborundum and polytetrafluoroethylene (PTFE).
Wherein, the weight of the graphite, carborundum and polytetrafluoroethylene (PTFE) is 50-85：1-4：1-4.
Particularly, the weight of the graphite, carborundum and polytetrafluoroethylene (PTFE) is preferably 55-80：2-3：
2-3。
Especially, the weight of the graphite, carborundum and polytetrafluoroethylene (PTFE) is more preferably 60-70：
2.5：2.5.
Particularly, the graphite includes native graphite and Delanium.
Especially, the weight of the native graphite and the Delanium is 10-20：40-65.
Particularly, the weight of the native graphite and the Delanium is preferably 12-18：45-60.
Especially, the weight of the native graphite and the Delanium is more preferably 14-16：
50-55。
Particularly, the weight of the native graphite, Delanium, carborundum and polytetrafluoroethylene (PTFE) is
10-20：40-65：1-4：1-4.
Especially, the weight of the native graphite, Delanium, carborundum and polytetrafluoroethylene (PTFE) is preferred
For 12-18：45-60：2-3：2-3.
Particularly, the weight of the native graphite, Delanium, carborundum and polytetrafluoroethylene (PTFE) enters one
Step is preferably 14-16：50-55：2.5：2.5.
Wherein, the granularity of the native graphite is 100-300 mesh, and phosphorus content >=99% fixes carbon content >=60%,
Moisture≤1%, ash≤1%, volatile matter≤10%.
Especially, the granularity of the Delanium be 100-300 mesh, phosphorus content >=99%, ash≤1%, moisture
≤ 0.5%.
Particularly, the carborundum is black powder, and granularity is 200-300 mesh.Carborundum is hexagonal knot
Structure material, have the advantages that stable chemical performance Oh, thermal coefficient of expansion is little, anti-wear performance is good.
Especially, the coefficient of friction of polytetrafluoroethylene (PTFE) (PTFE) is minimum, and arc resistance is higher, with excellent
Greasy property.
Wherein, described matrix powder also includes carbon fiber powder, molybdenum bisuphide and curing agent.
Particularly, the weight of the carbon fiber powder, molybdenum bisuphide and curing agent is 1-5：1-4：0.5-3.
Especially, the weight of the carbon fiber powder, molybdenum bisuphide and curing agent is preferably 2-4：2.5-3.5：
1-2.5。
Particularly, the weight of the carbon fiber powder, molybdenum bisuphide and curing agent is more preferably
2.5-3.5：2-3：1.5-2.
Wherein, the phosphorus content of the carbon fiber powder is 90-95%.
Carbon fiber powder be by the surface treatment of high-strength high-modules carbon fibre long filament Jing special techniques, grinding, micro- examination,
Screening, high temperature drying after obtain isometric cylindrical particulate, carbon fiber under non-oxidizing atmosphere superhigh temperature resistant,
Fatigue durability is good, specific heat and electric conductivity between nonmetallic and metal between, thermal coefficient of expansion it is little and with each to different
Property, carbon fiber powder remains numerous premium properties of carbon fiber, and shape is tiny, surface is pure, specific surface
Product is big, it is easy to by resin wetted by dispersion.
Particularly, the molybdenum bisuphide is the glossiness powder of black gray expandable.
Molybdenum bisuphide has excellent greasy property, and coefficient of friction is relatively low, and commutation ability is good.
Especially, the curing agent is epoxy curing agent.
Particularly, the curing agent is preferably phenylenediamine curing agent.
Especially, affiliated curing agent is more preferably benzene dimethylamine curing agent.
Using dimethylbenzene through ammoxidation, a kind of obtained industrial chemicals of hydrogenation is mainly used as epoxy to benzene dimethylamine
The curing agent of resin, is one of optimum kind in hypotoxicity normal temperature cure agent, and both reactions with fatty amine are lived
Property and the various characteristics with aromatic amine.
Wherein, the native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon fiber powder, curing
The weight of molybdenum and curing agent is 10-20：40-65：1-4：1-4：1-5：1-4：0.5-3.
Particularly, the native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon fiber powder, two sulphur
The weight for changing molybdenum and curing agent is preferably 12-18：45-60：2-3：2-3：2-4：2.5-3.5：1-2.5.
Especially, the native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon fiber powder, two sulphur
The weight for changing molybdenum and curing agent is more preferably 14-16：50-55：2.5：2.5：2.5-3.5：2-3：
1.5-2。
Wherein, described matrix powder also includes polybenzoate resin.
Particularly, polybenzoate (PHB) resin is aromatic polyester liquid crystal polymer, by P-hydroxybenzoic acid benzene
Ester polycondensation is formed, and its molecular backbone contains to oxygen benzoyl constitutional repeating unit, and degree of crystallinity is very high, self lubricity
Good, heat endurance is high, with preferable mechanical strength and processing characteristics.
Wherein, the polybenzoate resin is fine with native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon
The weight of dimension powder, molybdenum bisuphide and curing agent is 1-5：10-20：40-65：1-4：1-4：1-5：
1-4：0.5-3.
Particularly, the polybenzoate resin and native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon
The weight of fiber powder, molybdenum bisuphide and curing agent is preferably 2-4：12-18：45-60：2-3：2-3：
2-4：2.5-3.5：1-2.5.
Especially, the polybenzoate resin and native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon
The weight of fiber powder, molybdenum bisuphide and curing agent is more preferably 2.5-3.5：14-16：50-55：
2.5：2.5：2.5-3.5：2-3：1.5-2.
Wherein, the binder solution is that the binding agent is dissolved in acetone to be obtained.
Particularly, the binding agent is the bisphenol A-type solid epoxy of intermediate molecular weight.
Especially, the binding agent and the weight of acetone are 1：2-2.5.
Wherein, the binding agent and native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon fiber powder,
The weight of molybdenum bisuphide, curing agent and polybenzoate resin is 10-30：10-20：40-65：1-4：1-4：
1-5：1-4：0.5-3：1-5.
Particularly, the binding agent and native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon fiber
The weight of powder, molybdenum bisuphide, curing agent and polybenzoate resin is preferably 15-25：12-18：45-60：
2-3：2-3：2-4：2.5-3.5：1-2.5：2-4.
Especially, the binding agent and native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon fiber
The weight of powder, molybdenum bisuphide, curing agent and polybenzoate resin is more preferably 18-22：14-16：
50-55：2.5：2.5：2.5-3.5：2-3：1.5-2：2.5-3.5.
Wherein, described to be well mixed matrix powder with binder solution, preparing brush raw mixture includes：
By native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon fiber powder, molybdenum bisuphide, polyphenyl
Ester resin and curing agent are well mixed, and matrix powder is obtained；
Binding agent is added in solvent acetone, mixed dissolution is uniform, binder solution is obtained；
Described matrix powder is well mixed with the binder solution, is uniformly spread out under room temperature condition, thickness≤
5cm, stands 2-4h, and brush raw mixture is obtained.
Wherein, drying and processing is carried out to the brush raw mixture, brush raw mixture siccative is obtained.
Particularly, the temperature of the drying and processing is 45-55 DEG C.
Especially, the time of the drying and processing is 10-14h.
Particularly, break process is carried out to the raw mixture after the drying, raw mixture powder is obtained.
Wherein, the brush raw mixture powder is added in compacting tool set using hydraulic press, it is carried out
Compression process, is obtained brush blank.
Particularly, during the compression process control brush blank bulk density.
Especially, the bulk density of the brush blank is 1.80-1.86g/cm3。
Wherein, heat cure process is carried out to the brush blank, brush first product is obtained.
Particularly, the temperature that the heat cure is processed is 220-240 DEG C.
Especially, the time that the heat cure is processed is 10-14h.
Particularly, brush blank is placed in baking oven, in 7-9h, the temperature in the baking oven is promoted to
220-240℃；Then 3-5h is kept at a temperature of 220-240 DEG C.
Wherein, finished product working process is carried out to the brush first product, obtains brush finished product.
Particularly, the finished product working process includes the brush first product is cut, refined, revolves head, milling
Groove, drill, fill out the mechanical processing steps such as line, obtaining final product.
Advantages of the present invention and Advantageous Effects are as follows：
1st, brush raw material composition of the present invention is reasonable, and scientific formulation, the brush prepared using resin glue is used
Life-span length, environmental protection, stability are high, and anti-wear performance improves more than 10%, can meet colleges and universities' type dust catcher electricity
The use requirement of machine brush.
2nd, molybdenum bisuphide is selected in brush raw material of the invention as additive so that the brush of preparation is in motor
Spark is little in running, commutation ability is good, and stability is high, anti-interference strong.
3rd, polytetrafluoroethylene (PTFE) is added in brush raw material of the invention, it is suppressed that occur machinery during brush use
Spark, grade of spark is low in brush running, and no-spark when unloaded, spark reduces at least one grade,
Extend the service life of brush.
4th, brush used for electric engine of cleaner prepared by the present invention is applied to high pressure (AC120/230V) motor of dust collector
Use.
Specific embodiment
The present invention is expanded on further with reference to specific embodiment, advantages of the present invention and feature will be with retouching
State and apparent.But these embodiments are only exemplary, do not constitute any restriction to the scope of the present invention.
It will be understood by those skilled in the art that without departing from the spirit and scope of the invention can be to skill of the present invention
The details and form of art scheme is modified or is replaced, but these modifications and replacement each fall within the protection model of the present invention
In enclosing.
Embodiment 1
1st, get the raw materials ready (part) according to following weight：
2nd, by native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon fiber powder, molybdenum bisuphide,
Polybenzoate resin and curing agent are placed in kneading pot, open the tumbler of kneading pot, are mixed under room temperature condition
Stop after 1.5h, matrix powder is obtained；Binding agent is dissolved in acetone, is uniformly mixed so as to dissolved,
Prepared binder solution；Binder solution is added in matrix powder and is stirred, is well mixed, stir 1.5h,
Material is taken out after being well mixed, is placed at room temperature, placed 2-4h and treat that acetone volatilizees so that without third in material
Ketone is remained, and brush raw mixture is obtained.
3rd, brush raw mixture is placed in baking oven first carries out drying and processing 12h at 50 DEG C, further
Acetone is removed, the raw mixture without acetone is obtained；Then break process is carried out to the material after drying, is broken
Broken material crosses 60 mesh sieves, and brush raw mixture powder, brush raw mixture powder size≤60 mesh is obtained.
4th, obtained brush raw mixture powder is placed in compacting tool set, is carried out at compacting using hydraulic press
Reason, it is 1.82-1.85g/cm that bulk density is obtained3Brush blank.
5th, brush blank is placed in baking oven, heat cure process is carried out to brush blank, will be dried first in 8h
Case temperature is increased to 230 DEG C from room temperature, and wherein heating rate is 28.75 DEG C/h；Then at a temperature of 230 DEG C
4h is kept, the brush first product after heat cure is processed is obtained；
6th, to the brush first product after curing process is cut, grinding machine, drill, fill out the machineries such as line, spot welding
Brush used for electric engine of cleaner is obtained final product after procedure of processing.
7th, according to JB/T8133.14-1999's (electric carbon product physical and chemical performance test method bulk density)
Method determines the bulk density of brush used for electric engine of cleaner；According to JB/T8133.2-1999 (electric carbon product physics
Chemical property test method resistivity) method determines the resistivity of brush used for electric engine of cleaner；Using
The Shore hardness of HS-19CTV type hardness tester machine private wipers, the results are shown in Table 1；
The wear rate of the obtained brush used for electric engine of cleaner of long duration test controller test is loaded using FNC-5 types,
Result of the test is shown in Table 2；
With reference to national standard《Electric rotating machine quota and performance (GB/T 755-2000)》The obtained dust catcher of test
High pressure resistant, the grade of spark of brush for electromachine, test result is shown in Table 3；
With reference to national standard《Electric rotating machine (except traction electric machine) determines the test method (GB/T of loss and efficiency
755.2-2003)》The efficiency of the obtained brush used for electric engine of cleaner of test, test result is shown in Table 4.
Embodiment 2
1st, get the raw materials ready (part) according to following weight：
2nd, by native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon fiber powder, molybdenum bisuphide,
Polybenzoate resin and curing agent are placed in kneading pot, open the tumbler of kneading pot, are mixed under room temperature condition
Stop after 1.5h, matrix powder is obtained；Binding agent is dissolved in acetone, is uniformly mixed so as to dissolved,
Prepared binder solution；Binder solution is added in matrix powder and is stirred, is well mixed, stir 1.5h,
Material is taken out after being well mixed, is placed at room temperature, placed 2-4h and treat that acetone volatilizees so that without third in material
Ketone is remained, and brush raw mixture is obtained.
3rd, brush raw mixture is placed in baking oven first carries out drying and processing 11h at 52 DEG C, further
Acetone is removed, the raw mixture without acetone is obtained；Then break process is carried out to the material after drying, is broken
Broken material crosses 60 mesh sieves, and brush raw mixture powder, brush raw mixture powder size≤60 mesh is obtained.
4th, obtained brush raw mixture powder is placed in compacting tool set, is carried out at compacting using hydraulic press
Reason, it is 1.84-86g/cm that bulk density is obtained3Brush blank.
5th, brush blank is placed in baking oven, heat cure process is carried out to brush blank, will first in 8.5h
Oven temperature is increased to 235 DEG C from room temperature, and wherein heating rate is 27.65 DEG C/h；Then in 235 DEG C of temperature
Lower holding 4.5h, is obtained the brush first product after heat cure is processed；
6th, to the brush first product after curing process is cut, grinding machine, drill, fill out the machineries such as line, spot welding
Brush used for electric engine of cleaner is obtained final product after procedure of processing.
7th, according to JB/T8133.14-1999's (electric carbon product physical and chemical performance test method bulk density)
Method determines the bulk density of brush used for electric engine of cleaner；According to JB/T8133.2-1999 (electric carbon product physics
Chemical property test method resistivity) method determines the resistivity of brush used for electric engine of cleaner；Using
The Shore hardness of HS-19CTV type hardness tester machine private wipers, the results are shown in Table 1；
The wear rate of the obtained brush used for electric engine of cleaner of long duration test controller test is loaded using FNC-5 types,
Result of the test is shown in Table 2；
With reference to national standard《Electric rotating machine quota and performance (GB/T 755-2000)》The obtained dust catcher of test
High pressure resistant, the grade of spark of brush for electromachine, test result is shown in Table 3；
With reference to national standard《Electric rotating machine (except traction electric machine) determines the test method (GB/T of loss and efficiency
755.2-2003)》The efficiency of the obtained brush used for electric engine of cleaner of test, test result is shown in Table 4.
Embodiment 3
1st, get the raw materials ready (part) according to following weight：
2nd, by native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon fiber powder, molybdenum bisuphide,
Polybenzoate resin and curing agent are placed in kneading pot, open the tumbler of kneading pot, are mixed under room temperature condition
Stop after 1.5h, matrix powder is obtained；Binding agent is dissolved in acetone, is uniformly mixed so as to dissolved,
Prepared binder solution；Binder solution is added in matrix powder and is stirred, is well mixed, stir 1.5h,
Material is taken out after being well mixed, is placed at room temperature, placed 2-4h and treat that acetone volatilizees so that without third in material
Ketone is remained, and brush raw mixture is obtained.
3rd, brush raw mixture is placed in baking oven first carries out drying and processing 13h at 48 DEG C, further
Acetone is removed, the raw mixture without acetone is obtained；Then break process is carried out to the material after drying, is broken
Broken material crosses 60 mesh sieves, and brush raw mixture powder, brush raw mixture powder size≤60 mesh is obtained.
4th, obtained brush raw mixture powder is placed in compacting tool set, is carried out at compacting using hydraulic press
Reason, it is 1.80-1.85g/cm that bulk density is obtained3Brush blank.
5th, brush blank is placed in baking oven, heat cure process is carried out to brush blank, will first in 7.5h
Oven temperature is increased to 225 DEG C from room temperature, and wherein heating rate is 30 DEG C/h；Then at a temperature of 225 DEG C
3.5h is kept, the brush first product after heat cure is processed is obtained；
6th, to the brush first product after curing process is cut, grinding machine, drill, fill out the machineries such as line, spot welding
Brush used for electric engine of cleaner is obtained final product after procedure of processing.
7th, according to JB/T8133.14-1999's (electric carbon product physical and chemical performance test method bulk density)
Method determines the bulk density of brush used for electric engine of cleaner；According to JB/T8133.2-1999 (electric carbon product physics
Chemical property test method resistivity) method determines the resistivity of brush used for electric engine of cleaner；Using
The Shore hardness of HS-19CTV type hardness tester machine private wipers, the results are shown in Table 1；
The wear rate of the obtained brush used for electric engine of cleaner of long duration test controller test is loaded using FNC-5 types,
Result of the test is shown in Table 2；
With reference to national standard《Electric rotating machine quota and performance (GB/T 755-2000)》The obtained dust catcher of test
High pressure resistant, the grade of spark of brush for electromachine, test result is shown in Table 3；
With reference to national standard《Electric rotating machine (except traction electric machine) determines the test method (GB/T of loss and efficiency
755.2-2003)》The efficiency of the obtained brush used for electric engine of cleaner of test, test result is shown in Table 4.
Embodiment 4
1st, get the raw materials ready (part) according to following weight：
2nd, by native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon fiber powder, molybdenum bisuphide,
Polybenzoate resin and curing agent are placed in kneading pot, open the tumbler of kneading pot, are mixed under room temperature condition
Stop after 1.5h, matrix powder is obtained；Binding agent is dissolved in acetone, is uniformly mixed so as to dissolved,
Prepared binder solution；Binder solution is added in matrix powder and is stirred, is well mixed, stir 1.5h,
Material is taken out after being well mixed, is placed at room temperature, placed 2-4h and treat that acetone volatilizees so that without third in material
Ketone is remained, and brush raw mixture is obtained.
3rd, brush raw mixture is placed in baking oven first carries out drying and processing 14h at 45 DEG C, further
Acetone is removed, the raw mixture without acetone is obtained；Then break process is carried out to the material after drying, is broken
Broken material crosses 60 mesh sieves, and brush raw mixture powder, brush raw mixture powder size≤60 mesh is obtained.
4th, obtained brush raw mixture powder is placed in compacting tool set, is carried out at compacting using hydraulic press
Reason, it is 1.83-1.85g/cm that bulk density is obtained3Brush blank.
5th, brush blank is placed in baking oven, heat cure process is carried out to brush blank, will be dried first in 6h
Case temperature is increased to 240 DEG C from room temperature, and wherein heating rate is 40 DEG C/h；Then protect at a temperature of 240 DEG C
3h is held, the brush first product after heat cure is processed is obtained；
6th, to the brush first product after curing process is cut, grinding machine, drill, fill out the machineries such as line, spot welding
Brush used for electric engine of cleaner is obtained final product after procedure of processing.
7th, according to JB/T8133.14-1999's (electric carbon product physical and chemical performance test method bulk density)
Method determines the bulk density of brush used for electric engine of cleaner；According to JB/T8133.2-1999 (electric carbon product physics
Chemical property test method resistivity) method determines the resistivity of brush used for electric engine of cleaner；Using
The Shore hardness of HS-19CTV type hardness tester machine private wipers, the results are shown in Table 1；
The wear rate of the obtained brush used for electric engine of cleaner of long duration test controller test is loaded using FNC-5 types,
Result of the test is shown in Table 2；
With reference to national standard《Electric rotating machine quota and performance (GB/T 755-2000)》The obtained dust catcher of test
High pressure resistant, the grade of spark of brush for electromachine, test result is shown in Table 3；
With reference to national standard《Electric rotating machine (except traction electric machine) determines the test method (GB/T of loss and efficiency
755.2-2003)》The efficiency of the obtained brush used for electric engine of cleaner of test, test result is shown in Table 4.
Embodiment 5
1st, get the raw materials ready (part) according to following weight：
2nd, by native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon fiber powder, molybdenum bisuphide,
Polybenzoate resin and curing agent are placed in kneading pot, open the tumbler of kneading pot, are mixed under room temperature condition
Stop after 1.5h, matrix powder is obtained；Binding agent is dissolved in acetone, is uniformly mixed so as to dissolved,
Prepared binder solution；Binder solution is added in matrix powder and is stirred, is well mixed, stir 1.5h,
Material is taken out after being well mixed, is placed at room temperature, placed 2-4h and treat that acetone volatilizees so that without third in material
Ketone is remained, and brush raw mixture is obtained.
3rd, brush raw mixture is placed in baking oven first carries out drying and processing 10h at 55 DEG C, further
Acetone is removed, the raw mixture without acetone is obtained；Then break process is carried out to the material after drying, is broken
Broken material crosses 60 mesh sieves, and brush raw mixture powder, brush raw mixture powder size≤60 mesh is obtained.
4th, obtained brush raw mixture powder is placed in compacting tool set, is carried out at compacting using hydraulic press
Reason, it is 1.84-1.86g/cm that bulk density is obtained3Brush blank.
5th, brush blank is placed in baking oven, heat cure process is carried out to brush blank, will be dried first in 4h
Case temperature is increased to 220 DEG C from room temperature, and wherein heating rate is 55 DEG C/h；Then protect at a temperature of 220 DEG C
5h is held, the brush first product after heat cure is processed is obtained；
6th, to the brush first product after curing process is cut, grinding machine, drill, fill out the machineries such as line, spot welding
Brush used for electric engine of cleaner is obtained final product after procedure of processing.
7th, according to JB/T8133.14-1999's (electric carbon product physical and chemical performance test method bulk density)
Method determines the bulk density of brush used for electric engine of cleaner；According to JB/T8133.2-1999 (electric carbon product physics
Chemical property test method resistivity) method determines the resistivity of brush used for electric engine of cleaner；Using
The Shore hardness of HS-19CTV type hardness tester machine private wipers, the results are shown in Table 1；
The wear rate of the obtained brush used for electric engine of cleaner of long duration test controller test is loaded using FNC-5 types,
Result of the test is shown in Table 2；
With reference to national standard《Electric rotating machine quota and performance (GB/T 755-2000)》The obtained dust catcher of test
High pressure resistant, the grade of spark of brush for electromachine, test result is shown in Table 3；
With reference to national standard《Electric rotating machine (except traction electric machine) determines the test method (GB/T of loss and efficiency
755.2-2003)》The efficiency of the obtained brush used for electric engine of cleaner of test, test result is shown in Table 4.
Reference examples
With commercially available motor of dust collector (P22D02, AC230V/900W) with brush as reference examples.
According to the side of JB/T8133.14-1999 (electric carbon product physical and chemical performance test method bulk density)
Method determines the bulk density of reference examples brush used for electric engine of cleaner；According to JB/T8133.2-1999 (electric carbon products
Physical and chemical performance test method resistivity) method determines the resistivity of reference examples brush used for electric engine of cleaner；
The Shore hardness of reference examples brush is tested using HS-19CTV type hardness testers machine, 1 is the results are shown in Table；
The wear rate of long duration test controller test reference examples brush used for electric engine of cleaner is loaded using FNC-5 types,
Result of the test is shown in Table 2；
With reference to national standard《Electric rotating machine quota and performance (GB/T 755-2000)》Test reference examples dust catcher
High pressure resistant, the grade of spark of brush for electromachine, test result is shown in Table 3；
With reference to national standard《Electric rotating machine (except traction electric machine) determines the test method (GB/T of loss and efficiency
755.2-2003)》The efficiency of test reference examples brush used for electric engine of cleaner, test result is shown in Table 4.
The physical and mechanical properties test result of the brush of table 1
| Performance | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Reference examples |
| Bulk density (g/cm3) | 1.60 | 1.55 | 1.57 | 1.60 | 1.58 | 1.65 |
| Shore hardness (HSD) | 24 | 24 | 25 | 24 | 23 | 23 |
| Resistivity (μ Ω m) | 520 | 650 | 600 | 450 | 400 | 400 |
| Rupture strength (MPa) | 20 | 18 | 20 | 22 | 21 | 22 |
The test result of table 1 shows：The bulk density of brush used for electric engine of cleaner prepared by the present invention is
1.55-1.60g/cm3；The resistivity 450-600 μ Ω m of brush used for electric engine of cleaner, resistivity is relatively low, is suitable for
Use in high-low pressure (AC120/230V) motor of dust collector.
The wear rate result of the test of the brush of table 2
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Reference examples | |
| Wear rate (mm/100H) | 3.26 | 3.15 | 3.37 | 3.42 | 3.20 | 2.79 |
As seen from the results in Table 2：The wear rate of the brush for electromachine of the present invention is low, and anti-wear performance is excellent, inhales with import
Dirt device brush for electromachine is compared, and abrasion resistance properties are suitable, or even wear resistance can exceed that import motor of dust collector
With the anti-wear performance of brush.
The grade of spark result of the test of the brush of table 3
From the test result of table 3：The grade of spark of the brush used for electric engine of cleaner of the present invention is low, is 11/4,
Compared with the brush used for electric engine of cleaner of common commercially available import, grade of spark reduces 1 grade, suppresses spark
Ability is good, improves safety in utilization.
The efficiency test result of the brush of table 4
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Reference examples | |
| Efficiency | 46.7% | 45.9% | 46.1% | 46.9% | 47.3% | 36.1% |
From the test result of table 4：The efficiency of the brush used for electric engine of cleaner of the present invention is compared with the reference examples import
Carbon brush is high, is a kind of energy-efficient dust collector brush for electromachine.
Claims (10)
1. a kind of brush used for electric engine of cleaner, be prepared via a method which to form including：
By the way that matrix powder is well mixed with binder solution, brush raw mixture is prepared；
Drying and processing is carried out to the brush raw mixture, brush raw mixture siccative is obtained；
Break process is carried out to the brush raw mixture siccative, brush raw mixture powder is obtained；
The brush raw mixture powder is added in compacting tool set, compression process is carried out to it, electricity is obtained
Brush blank；
Heat cure process is carried out to the brush blank, brush first product is obtained；
Finished product working process is carried out to the brush first product, brush finished product is obtained；
It is characterized in that：Described matrix powder includes graphite, carborundum and polytetrafluoroethylene (PTFE).
2. brush according to claim 1, it is characterised in that the graphite, carborundum and polytetrafluoro
The weight of ethene is 50-85：1-4：1-4.
3. brush according to claim 2, it is characterised in that the graphite includes native graphite and people
The weight for making graphite, the native graphite and the Delanium is 10-20：40-65.
4. brush according to claim 3, it is characterised in that the native graphite, Delanium,
The weight of carborundum and polytetrafluoroethylene (PTFE) is 10-20：40-65：1-4：1-4.
5. brush according to claim 3, it is characterised in that described matrix powder also includes carbon fiber
Powder, molybdenum bisuphide and curing agent.
6. brush according to claim 5, it is characterised in that the carbon fiber powder, molybdenum bisuphide and
The weight of curing agent is 1-5：1-4：0.5-3.
7. brush according to claim 6, it is characterised in that the native graphite, Delanium,
The weight of carborundum, polytetrafluoroethylene (PTFE), carbon fiber powder, molybdenum bisuphide and curing agent is 10-20：40-65：
1-4：1-4：1-5：1-4：0.5-3.
8. brush according to claim 7, it is characterised in that described matrix powder also includes polybenzoate
Resin, wherein polybenzoate resin and native graphite, Delanium, carborundum, polytetrafluoroethylene (PTFE), carbon fiber powder,
The weight of molybdenum bisuphide and curing agent is 1-5：10-20：40-65：1-4：1-4：1-5：1-4：0.5-3.
9. brush according to claim 1, it is characterised in that the temperature of the drying and processing is
15-55℃。
10. brush according to claim 1, it is characterised in that the temperature that the heat cure is processed is
220-240℃。