CN106638067A - Durable fiber composite reinforced rope and manufacturing method thereof - Google Patents
Durable fiber composite reinforced rope and manufacturing method thereof Download PDFInfo
- Publication number
- CN106638067A CN106638067A CN201611106470.1A CN201611106470A CN106638067A CN 106638067 A CN106638067 A CN 106638067A CN 201611106470 A CN201611106470 A CN 201611106470A CN 106638067 A CN106638067 A CN 106638067A
- Authority
- CN
- China
- Prior art keywords
- strand
- fiber
- rope
- outer layer
- nylon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a durable fiber composite reinforced rope. The rope comprises a reinforced core, a medium layer and a reinforced outer layer. The reinforced core and the reinforced outer layer are both formed by winding and combining fiber folded yarns. The fiber folded yarns of the reinforced core comprise the nylon folded yarns, the carbon fiber folded yarns and the basalt folded yarns, and the ratio of the winding strand number of the nylon folded yarns to the winding strand number of the carbon fiber folded yarns to the winding strand number of the basalt folded yarns is 6:3:1; the reinforced outer layer comprises multiple sets of outer fiber bundles, and the outer fiber bundles are no less than six sets and uniformly distributed around the reinforced core; every set of outer fiber bundles comprise the glass fiber reinforced chlorinated polyvinyl chloride folded yarns and the nylon 66 folded yarns, the ratio of the winding strand number of the glass fiber reinforced chlorinated polyvinyl chloride folded yarns to the winding strand number of the nylon 66 folded yarns is (2-3):1. The fiber composite reinforced rope is fine in structure, optimized in material and good in comprehensive performance. By means of the three fibers of the reinforced core, high strength and strength at a high temperature are ensured, and the reinforced outer layer has the advantages of heat resistance, fire resistance and weather resistance while the high strength is ensured; the rope can be used in a high-load and high-temperature situation, and has a longer service life in the general environment, wherein the temperature does not exceed 1000 DEG C.
Description
Technical field
The invention belongs to Material Field, especially a kind of durable fiber composite strengthen rope.
Background technology
The plastic rope of synthetic fiber rope or fiber composite, has slowly replaced conventional metallic cable, obtains
Increasing application.Compared with metallic cable, synthetic fiber rope, fibre-reinforced plastic rope with light weight, allows length
Degree is long, will not get rusty, the characteristics of intensity is again inferior unlike cable wire.Therefore, in recent years, the rope with synthetic fibers as raw material,
Out of doors, the field such as lifting, traction, bridge is applied.
At present, synthetic fiber rope is the textile product of linear enhanced fibers material, is spun into strand, is not directly rotated
Into rope, Jing multisteps are twisted/are added sheath and form, however, intensity can also keep the fibrous raw material of suitable intensity few at 100 DEG C or so
It is again few.Secondly, in many application scenarios, the abrasion of rope is also very important Consideration.
So, the high-strength composite fibrecord of resistance to certain high temperature and certain abrasion, is the main development side of fibrecord
It is preferable cord fibers raw material, based on nylon to, the wearability of nylon and in the plastic ranking ranks forefront with heat resistance
Design a kind of rope of composite fibre, improve mechanical strength(And its mechanical strength at higher temperatures), can be somebody's turn to do for current
The technological difficulties in field provide valuable resolving ideas.
The content of the invention
For the mechanical strength of reinforcing fiber rope, and its mechanical strength being often worn out, under higher temperature, lifted
The comprehensive performance of rope and service life, the present invention provides a kind of durable fiber composite strengthen rope, to solve above-mentioned depositing
Problem.
A kind of durable fiber composite strengthen rope, including strengthen wire rope core, dielectric layer, strengthen outer layer, the enhancing wire rope core and
Strengthen outer layer to be combined by the winding of fiber strand;
The fiber strand for strengthening wire rope core includes nylon strand, carbon fiber strand, basalt fibre strand, and the line of its winding
Number of share of stock ratio is 6:3:1;
The enhancing outer layer includes some groups of outer layer fiber beams, and the outer layer fiber beam is no less than 6 groups, is uniformly distributed in strengthen rope
Around core, every group of outer layer fiber beam includes glass fiber reinforcement chliorinated polyvinyl chloride strand and nylon66 fiber strand, and glass fibre
The strand count ratio for strengthening chliorinated polyvinyl chloride strand and the winding of nylon66 fiber strand is 2 ~ 3:1.
Preferably, the dielectric layer includes adhesive, crosslinking agent and filler.Dielectric layer allows enhancing wire rope core as auxiliary
With the laminating in a certain way for strengthening outer layer, synergy is played, making the intensity of two-layer can be utilized.
Preferably, the material of the nylon strand is glass fibre reinforced nylon, glass fibre reinforced nylon and glass
In fiber reinforcement chliorinated polyvinyl chloride material, the single fiber length of glass fibre is in 3-6mm.The nylon strand of wire rope core should try
High-strength heat-resistant and intensity are put forward, doped-glass fiber is relatively inexpensive and efficient method, and the fibre length of glass fibre exists
When more than critical length, its strengthened ability is more apparent.
Preferably, also having antiaging agent in the material of the glass fiber reinforcement chliorinated polyvinyl chloride strand.As
Add antiaging agent in the material of outer layer, its weatherability and service life can be significantly improved.
Further, the antiaging agent includes hindered amine as light stabilizer and antioxidant 1010 hindered amine as light stabilizer energy
Ultraviolet opposing plastics can be absorbed and produce free radical erosion, antioxidant 1010 is a kind of efficient plastic antioxidants, both
Cooperation can effectively anti-aging.
A kind of preparation method of durable fiber composite strengthen rope, comprises the following steps:
(1), rope strand, 48 ~ 72 twists/m of the twist, carbon fiber strand, the Black Warrior are manufactured with 24 ~ 36 nylon fiber silks on rope strand machine
The per share number of fiber and the twist of rock fiber strand is identical with nylon strand;
(2), with 12 ~ 24 glass fiber reinforcement chlorinated polyvinyl chloride fibre silks rope strand, the twist 36 ~ 48 are manufactured on rope strand machine
Twist/m, the per share number of fiber and the twist of nylon66 fiber strand is identical with glass fiber reinforcement chliorinated polyvinyl chloride strand;
(3), select 12,24 or 48 strands of nylon strands, according to nylon strand, carbon fiber strand, basalt fibre strand strand count
Ratio is 6:3:1 determines after carbon fiber strand and basalt fibre strand number, and three kinds of fiber strands are manufactured on rope machine
Strengthen wire rope core, 48 ~ 60 twists/m of the twist;
(4), 3,6 or 12 strands of glass fiber reinforcement chliorinated polyvinyl chloride strands are selected, according to number of share of stock ratio:Glass fiber reinforcement chlorination
Polyvinyl chloride strand/nylon66 fiber strand=2 ~ 3:1 determining nylon66 fiber strand number, and two kinds of fiber strands are made on rope machine
One group of outer layer fiber beam is made, 36 ~ 48 twists/m of the twist makes 6 ~ 8 groups repeatedly;
(5), coat in strengthen rope wicking surface adhesive, crosslinking agent and the filler for having prepared, be heated to 120 ~ 135 DEG C, so
After choose a branch of enhancing wire rope core and 6 ~ 8 groups of outer layer fiber beams, be also heated to this temperature, the Knitted rope on rope machine, the twist 32 ~
40 twists/m, it is slowly cooled to room temperature.
Preferably, in step(3)With(4)In, per share strand by the tension regulator of rope machine control elasticity and
Subtended angle, controls tightness 60 ~ 75%, 25 ~ 45 ° of subtended angle.The magnitude relationship of the good subtended angle of elasticity is controlled to the intensity for making rope beam
The two indexs can optimize the tensile strength of rope.
Preferably, in step(5)Afterwards, by the rope for making again through drawing-off, the post processing for oiling, being dried.After locate
Reason step can to greatest extent preserve and protect performance when rope makes.
The beneficial effects of the present invention is:A kind of durable fiber composite strengthen rope of the present invention, fine structure, material is excellent
Choosing, combination property is good.Strengthen the intensity that three kinds of fibers of wire rope core ensure that under high intensity, and higher temperature, strengthen outer layer
Ensure that high intensity while having heat-resisting, fire-retardant, weather-proof characteristic concurrently, can be used for high load capacity and the high temperature less than 100 DEG C
Occasion, while also having longer service life in normal circumstances.
Description of the drawings
Fig. 1 is the cross-sectional view of the embodiment of the present invention.
1- strengthens wire rope core, and 11- nylon strands, 12- carbon fiber strands, 13- basalt fibre strands, 2- dielectric layers, 3- increases
Strong outer layer, 30- outer layer fiber beams, 31- glass fiber reinforcement chliorinated polyvinyl chloride strands, 32- nylon66 fiber strands.
Specific embodiment
A kind of durable fiber composite strengthen rope, including strengthen wire rope core 1, dielectric layer 2, strengthen outer layer 3, the enhancing wire rope core
1 is combined with outer layer 3 is strengthened by the winding of fiber strand;
The fiber strand for strengthening wire rope core 1 includes nylon strand 11, carbon fiber strand 12, basalt fibre strand 13, and its
The strand count ratio of winding is 6:3:1;
The enhancing outer layer 3 includes some groups of outer layer fiber beams 30, and the outer layer fiber beam 30 is no less than 6 groups, is uniformly distributed in
Strengthen around wire rope core 1, every group of outer layer fiber beam 30 includes glass fiber reinforcement chliorinated polyvinyl chloride strand 31 and nylon66 fiber strand
32, and glass fiber reinforcement chliorinated polyvinyl chloride strand 31 and the strand count ratio of the winding of nylon66 fiber strand 32 are 2 ~ 3:1.
Preferably, the dielectric layer 2 includes adhesive, crosslinking agent and filler.Dielectric layer 2 allows strengthen rope as auxiliary
The laminating in a certain way of core and enhancing outer layer, plays synergy, and making the intensity of two-layer can be utilized.
Preferably, the material of the nylon strand 11 is glass fibre reinforced nylon, glass fibre reinforced nylon and glass
In glass fiber reinforcement chliorinated polyvinyl chloride material, the single fiber length of glass fibre is in 3-6mm.The nylon strand 11 of wire rope core 1
High-strength heat-resistant and intensity should be tried to put forward, doped-glass fiber is relatively inexpensive and efficient method, the fiber of glass fibre
When length is more than critical length, its strengthened ability is more apparent.
Preferably, also having antiaging agent in the material of the glass fiber reinforcement chliorinated polyvinyl chloride strand 31.Make
To add antiaging agent in the material of outer layer, its weatherability and service life can be significantly improved.
Further, the antiaging agent includes hindered amine as light stabilizer and antioxidant 1010 hindered amine as light stabilizer energy
Ultraviolet opposing plastics can be absorbed and produce free radical erosion, antioxidant 1010 is a kind of efficient plastic antioxidants, both
Cooperation can effectively anti-aging.
A kind of preparation method of durable fiber composite strengthen rope, comprises the following steps:
(1), manufacture with 24 ~ 36 nylon fiber silks rope strand on rope strand machine, 48 ~ 72 twists/m of the twist is carbon fiber strand 12, profound
The per share number of fiber and the twist of the military strand of rock fiber 13 is identical with nylon strand 11;
(2), with 12 ~ 24 glass fiber reinforcement chlorinated polyvinyl chloride fibre silks rope strand, the twist 36 ~ 48 are manufactured on rope strand machine
Twist/m, the per share number of fiber and the twist of nylon66 fiber strand 32 is identical with glass fiber reinforcement chliorinated polyvinyl chloride strand 31;
(3), 12,24 or 48 strands of nylon strands 11 are selected, according to nylon strand 11, carbon fiber strand 12, basalt fibre strand 13
Strand count ratio be 6:3:1 determines after carbon fiber strand 12 and the number of basalt fibre strand 13, and three kinds of fiber strands are existed
Manufacture on rope machine strengthens wire rope core 1,48 ~ 60 twists/m of the twist;
(4), 3,6 or 12 strands of glass fiber reinforcement chliorinated polyvinyl chloride strands 31 are selected, according to number of share of stock ratio:Glass fiber reinforcement chlorine
Nylon66 fiber strand 32=2 ~ 3 of chlorinated polynvinyl chloride (CPVC) strand 31/:1 determining the number of nylon66 fiber strand 32, by two kinds of fiber strands in system
One group of outer layer fiber beam 30 is manufactured on rope machine, 36 ~ 48 twists/m of the twist makes 6 ~ 8 groups repeatedly;
(5), coat the adhesive, crosslinking agent and the filler that have prepared strengthening wire rope core 1 surface, be heated to 120 ~ 135 DEG C, so
After choose a branch of enhancing wire rope core 1 and 6 ~ 8 groups of outer layer fiber beams 30, be also heated to this temperature, the Knitted rope on rope machine, the twist
32 ~ 40 twists/m, it is slowly cooled to room temperature.
Preferably, in step(3)With(4)In, per share strand by the tension regulator of rope machine control elasticity and
Subtended angle, controls tightness 60 ~ 75%, 25 ~ 45 ° of subtended angle.The magnitude relationship of the good subtended angle of elasticity is controlled to the intensity for making rope beam
The two indexs can optimize the tensile strength of rope.
Preferably, in step(5)Afterwards, by the rope for making again through drawing-off, the post processing for oiling, being dried.After locate
Reason step can to greatest extent preserve and protect performance when rope makes.
This kind of durable fiber composite strengthen rope, fine structure, preferably, combination property is good for material.Strengthen three kinds of wire rope core
Fiber ensure that the intensity under high intensity, and higher temperature, strengthens outer layer and ensure that high intensity while having heat-resisting, resistance concurrently
Combustion, weather-proof characteristic, can be used for the occasion of high load capacity and the high temperature less than 100 DEG C, at the same in normal circumstances also have compared with
Long service life.
Above example is only to illustrate the preferred technical solution of the present invention, it is noted that general for the art
For logical technical staff, under the premise without departing from the principles of the invention, some improvement made or equivalent are accordingly to be regarded as this
The protection domain of invention, should cover in scope of the presently claimed invention.
Claims (9)
1. a kind of durable fiber composite strengthen rope, it is characterised in that including strengthening wire rope core, dielectric layer, strengthen outer layer, the increasing
Strong wire rope core and enhancing outer layer are combined by the winding of fiber strand;
The fiber strand for strengthening wire rope core includes nylon strand, carbon fiber strand, basalt fibre strand, and the line of its winding
Number of share of stock ratio is 6:3:1;
The enhancing outer layer includes some groups of outer layer fiber beams, and the outer layer fiber beam is no less than 6 groups, is uniformly distributed in strengthen rope
Around core, every group of outer layer fiber beam includes glass fiber reinforcement chliorinated polyvinyl chloride strand and nylon66 fiber strand, and glass fibre
The strand count ratio for strengthening chliorinated polyvinyl chloride strand and the winding of nylon66 fiber strand is 2 ~ 3:1.
2. a kind of durable fiber composite strengthen rope according to claim 1, it is characterised in that the dielectric layer includes glue
Glutinous agent, crosslinking agent and filler.
3. a kind of durable fiber composite strengthen rope according to claim 1, it is characterised in that the material of the nylon strand
Expect for glass fibre reinforced nylon, in the glass fibre reinforced nylon and glass fiber reinforcement chliorinated polyvinyl chloride, glass fibers
The single fiber length of dimension is in 3-6mm.
4. a kind of durable fiber composite strengthen rope according to claim 1, it is characterised in that the glass fiber reinforcement
Also there is antiaging agent in the material of chliorinated polyvinyl chloride strand.
5. a kind of durable fiber composite strengthen rope according to claim 4, it is characterised in that the antiaging agent includes
Hindered amine as light stabilizer and antioxidant 1010.
6. the preparation method of a kind of durable fiber composite strengthen rope according to any one of claim 1 ~ 5, its feature exists
In comprising the following steps:
(1), rope strand, 48 ~ 72 twists/m of the twist, carbon fiber strand, the Black Warrior are manufactured on rope strand machine with 24 ~ 36 nylon fiber silks
The per share number of fiber and the twist of rock fiber strand is identical with nylon strand;
(2), rope strand, the twist 36 ~ 48 are manufactured on rope strand machine with 12 ~ 24 glass fiber reinforcement chlorinated polyvinyl chloride fibre silks
Twist/m, the per share number of fiber and the twist of nylon66 fiber strand is identical with glass fiber reinforcement chliorinated polyvinyl chloride strand;
(3) 12,24 or 48 strands of nylon strands, are selected, according to nylon strand, carbon fiber strand, basalt fibre strand strand count
Ratio is 6:3:1 determines after carbon fiber strand and basalt fibre strand number, and three kinds of fiber strands are manufactured on rope machine
Strengthen wire rope core, 48 ~ 60 twists/m of the twist;
(4) 3,6 or 12 strands of glass fiber reinforcement chliorinated polyvinyl chloride strands, are selected, according to number of share of stock ratio:Glass fiber reinforcement chlorination
Polyvinyl chloride strand/nylon66 fiber strand=2 ~ 3:1 determining nylon66 fiber strand number, and two kinds of fiber strands are made on rope machine
One group of outer layer fiber beam is made, 36 ~ 48 twists/m of the twist makes 6 ~ 8 groups repeatedly;
(5) adhesive, crosslinking agent and the filler for having prepared, is coated in strengthen rope wicking surface, 120 ~ 135 DEG C is heated to, so
After choose a branch of enhancing wire rope core and 6 ~ 8 groups of outer layer fiber beams, be also heated to this temperature, the Knitted rope on rope machine, the twist 32 ~
40 twists/m, it is slowly cooled to room temperature.
7. a kind of preparation method of durable fiber composite strengthen rope according to claim 6, it is characterised in that the Buddhist nun
Imperial strand, carbon fiber strand, basalt fibre strand, glass fiber reinforcement chliorinated polyvinyl chloride strand, nylon66 fiber strand are in rope
During stock mechanism stock, interleaved mode is twill between fiber, and the mutual angulation of fiber is 20 ~ 45 °.
8. the preparation method of a kind of durable fiber composite strengthen rope according to claim 6, it is characterised in that in step
(3)With(4)In, per share strand controls elasticity and subtended angle by the tension regulator of rope machine, controls tightness 60 ~ 75%, subtended angle
25~45°。
9. the preparation method of a kind of durable fiber composite strengthen rope according to claim 6, it is characterised in that in step
(5)Afterwards, by the rope for making again through drawing-off, the post processing for oiling, being dried.