CN106634246A - Static-conducting rare earth modified waterborne chlorosulfonated polyethylene anticorrosive coating and preparation method thereof - Google Patents
Static-conducting rare earth modified waterborne chlorosulfonated polyethylene anticorrosive coating and preparation method thereof Download PDFInfo
- Publication number
- CN106634246A CN106634246A CN201710015697.3A CN201710015697A CN106634246A CN 106634246 A CN106634246 A CN 106634246A CN 201710015697 A CN201710015697 A CN 201710015697A CN 106634246 A CN106634246 A CN 106634246A
- Authority
- CN
- China
- Prior art keywords
- chlorosulfonated polyethylene
- parts
- coating
- static
- rare
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a static-conducting rare earth modified waterborne chlorosulfonated polyethylene anticorrosive coating and a preparation method thereof. The coating is characterized by being prepared from the following raw materials in parts by weight: 50-60 parts of chlorosulfonated polyethylene emulsion, 3-6 parts of sodium dodecyl sulfate, 2-4 parts of lanthanum oxide, 20-30 parts of nitric acid solution, 3-5 parts of talc, 6-9 parts of ammonium bicarbonate solution, 3-5 parts of titanium dioxide, 5-10 parts of static-conducting graphite, 3-6 parts of waterborne epoxy resins, 3-6 parts of polyacrylic acids and 5-10 parts of a silane coupling agent KH560. The talc is combined with the rare earth compounds, which improves the corrosion resistance, aging resistance, abrasion resistance and glossiness of the coating. The static-conducting graphite is added into the coating, so that the coating has excellent static-conducting and anti-electromagnetic interference performances, and is suitable for the coating of a variety of equipment.
Description
Technical field
The invention belongs to technical field of coatings, and in particular to a kind of rare earth modified hydrophilic chlorosulfonated polyethylene of static conductive is prevented
Rotten coating and preparation method thereof.
Background technology
Chloro-sulfonated polyethylene anti-corrosive coating is in the popularization and application eighties of 20th century.With rapidly sending out for modern industry level
Exhibition, higher, the tightened up ability for bearing environmental corrosion is proposed to anticorrosive paint.The anti-corrosive properties of the coating of conventional formulation production
Can typically be extremely difficult to require.Conventional chloro-sulfonated polyethylene anti-corrosive coating is mostly solvent type, not only causes a large amount of solvents
Waste, and solvent for use is poisonous, volatile, to environment, does not meet environmental requirement, and water paint has work
Skill cleaning, advanced technology, low emission, low energy consumption, safe and harmless advantage, therefore, research hydrophilic chlorosulfonated polyethylene anti-corrosion is applied
Material has great Social benefit and economic benefit.
Cao Hongzhang exists《Rare-earth additive modified water-soluble chloro-sulfonated polyethylene anti-corrosive coating performance study》In, using rare-earth additive
A kind of anticorrosive paint has been obtained with chlorosulfonated polyethylene, but for the anticorrosive paint as various equipment, also exist lead it is quiet
Not excellent enough the shortcoming of Electricity Functional shortcoming, antiseptic property.
The content of the invention
Thinking based on more than, the present invention is intended to provide a kind of can be excellent with the antiseptic property of static conductive, anti-electromagnetic interference
Hydrophilic chlorosulfonated polyethylene coating.
The technical problem to be solved is realized using following technical scheme:
The rare earth modified hydrophilic chlorosulfonated polyethylene anticorrosive paint of a kind of static conductive, it is characterised in that be by following weight portion
Raw material is made:
Chlorosulfonated polyethylene emulsion 50-60, dodecyl sodium sulfate 3-6, lanthana 2-4, salpeter solution 20-30, talcum powder 3-
5, ammonium bicarbonate soln 6-9, titanium dioxide 3-5, electrically conductive graphite 5-10, aqueous epoxy resins 3-6, polyacrylic acid 3-6, it is silane coupled
Agent KH560 5-10;
The solid content of the chlorosulfonated polyethylene emulsion is 30-60%;The concentration of salpeter solution is 0.5-2mol/L;Ammonium hydrogen carbonate
The concentration of solution is 1-5mol/L.
A kind of rare earth modified hydrophilic chlorosulfonated polyethylene anticorrosive paint of static conductive according to claim 1 and its system
Preparation Method, it is characterised in that be made up of following steps:
A. chlorosulfonated polyethylene emulsion, deionized water, dodecyl sodium sulfate are put in emulsifier, primary emulsion is prepared into,
Then the removed under reduced pressure organic solvent in evaporating kettle, obtains chlorosulfonated polyethylene latex;
B. add salpeter solution to be dissolved into transparence liquid lanthana, add talcum powder and ammonium bicarbonate soln, lanthanum ion and carbon
Sour hydrogen ammonium acts on forming precipitation, attaches on talcum powder, synthesizing rare-earth carbonate precursor, and Jing is filtered, washed, being dried, calcination
Afterwards, rare-earth additive is obtained;
C. by step b gained rare-earth additive and titanium dioxide, electrically conductive graphite, deionized water mixing, aqueous epoxy resins are added, is gathered
Acrylic acid, then grind on grinder, granularity is obtained<30 μm of mill base;
D. step c gained mill base is mixed with step a gained chlorosulfonated polyethylene latex, adds silane coupler KH560, adopted
Magnetic stirrer 6-10h is used, makes coating be uniformly dispersed as far as possible, obtain final product the modified hydrophilic chlorosulfonated polyethylene of rare-earth additive
Anticorrosive paint.
A kind of rare earth modified hydrophilic chlorosulfonated polyethylene anticorrosive paint of static conductive according to claim 2 and its system
Preparation Method, it is characterised in that emulsification times are 10-30min in step a.
The invention has the beneficial effects as follows:Rare-earth complex has stronger ligand complex function, big with chlorosulfonated polyethylene
Chlorosulfonyl group reaction on strand generates cross-bond, increases the degree of cross linking of molecular structure;Numerous unoccupied orbitals of rare earth ion
Unstable free radical can be caught, causes it to lose activity, be conducive to stabilization, improve corrosion resistance and resistance to ag(e)ing;This
Outward, promote free radical to produce by the variation of valence of contained rare earth ion, accelerate coating oxidation polymerization to be dried;By talcum powder with it is dilute
Earth compounds are combined, and improve wearability, the glossiness of coating;Add static conductive graphite in coating, there is coating excellent
Static conductive, anti-electromagnetic interference performance, the coating for obtaining be applied to various equipment protective coating.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.
Embodiment
The rare earth modified hydrophilic chlorosulfonated polyethylene anticorrosive paint of a kind of static conductive, it is characterised in that be by following weight
The raw material of part is made:
Chlorosulfonated polyethylene emulsion 60, dodecyl sodium sulfate 6, lanthana 4, salpeter solution 30, talcum powder 5, ammonium hydrogen carbonate is molten
Liquid 9, titanium dioxide 5, electrically conductive graphite 10, aqueous epoxy resins 6, polyacrylic acid 6, silane coupler KH560 10;
The solid content of the chlorosulfonated polyethylene emulsion is 30-60%;The concentration of salpeter solution is 0.5-2mol/L;Ammonium hydrogen carbonate
The concentration of solution is 1-5mol/L.
A kind of rare earth modified hydrophilic chlorosulfonated polyethylene anticorrosive paint of static conductive according to claim 1 and its system
Preparation Method, it is characterised in that be made up of following steps:
A. chlorosulfonated polyethylene emulsion, deionized water, dodecyl sodium sulfate are put in emulsifier, primary emulsion is prepared into,
Then the removed under reduced pressure organic solvent in evaporating kettle, obtains chlorosulfonated polyethylene latex;
B. add salpeter solution to be dissolved into transparence liquid lanthana, add talcum powder and ammonium bicarbonate soln, lanthanum ion and carbon
Sour hydrogen ammonium acts on forming precipitation, attaches on talcum powder, synthesizing rare-earth carbonate precursor, and Jing is filtered, washed, being dried, calcination
Afterwards, rare-earth additive is obtained;
C. by step b gained rare-earth additive and titanium dioxide, electrically conductive graphite, deionized water mixing, aqueous epoxy resins are added, is gathered
Acrylic acid, then grind on grinder, granularity is obtained<30 μm of mill base;
D. step c gained mill base is mixed with step a gained chlorosulfonated polyethylene latex, adds silane coupler KH560, adopted
Magnetic stirrer 6-10h is used, makes coating be uniformly dispersed as far as possible, obtain final product the modified hydrophilic chlorosulfonated polyethylene of rare-earth additive
Anticorrosive paint.
A kind of rare earth modified hydrophilic chlorosulfonated polyethylene anticorrosive paint of static conductive according to claim 2 and its system
Preparation Method, it is characterised in that emulsification times are 10-30min in step a.
The present invention technical parameter be:Acid resistance (10% H2SO4):It is >=7 days, non-foaming, do not fall off, non-corrosive;It is alkaline-resisting
Property (10% NaOH):It is >=7 days, non-foaming, do not fall off, non-corrosive.
Claims (3)
1. the rare earth modified hydrophilic chlorosulfonated polyethylene anticorrosive paint of a kind of static conductive, it is characterised in that be by following weight portion
Raw material make:
Chlorosulfonated polyethylene emulsion 50-60, dodecyl sodium sulfate 3-6, lanthana 2-4, salpeter solution 20-30, talcum powder 3-
5, ammonium bicarbonate soln 6-9, titanium dioxide 3-5, electrically conductive graphite 5-10, aqueous epoxy resins 3-6, polyacrylic acid 3-6, it is silane coupled
Agent KH560 5-10;
The solid content of the chlorosulfonated polyethylene emulsion is 30-60%;The concentration of salpeter solution is 0.5-2mol/L;Ammonium hydrogen carbonate
The concentration of solution is 1-5mol/L.
2. a kind of rare earth modified hydrophilic chlorosulfonated polyethylene anticorrosive paint of static conductive according to claim 1 and its preparation
Method, it is characterised in that be made up of following steps:
A. chlorosulfonated polyethylene emulsion, deionized water, dodecyl sodium sulfate are put in emulsifier, primary emulsion is prepared into,
Then the removed under reduced pressure organic solvent in evaporating kettle, obtains chlorosulfonated polyethylene latex;
B. add salpeter solution to be dissolved into transparence liquid lanthana, add talcum powder and ammonium bicarbonate soln, lanthanum ion and carbon
Sour hydrogen ammonium acts on forming precipitation, attaches on talcum powder, synthesizing rare-earth carbonate precursor, and Jing is filtered, washed, being dried, calcination
Afterwards, rare-earth additive is obtained;
C. by step b gained rare-earth additive and titanium dioxide, electrically conductive graphite, deionized water mixing, aqueous epoxy resins are added, is gathered
Acrylic acid, then grind on grinder, granularity is obtained<30 μm of mill base;
D. step c gained mill base is mixed with step a gained chlorosulfonated polyethylene latex, adds silane coupler KH560, adopted
Magnetic stirrer 6-10h is used, makes coating be uniformly dispersed as far as possible, obtain final product the modified hydrophilic chlorosulfonated polyethylene of rare-earth additive
Anticorrosive paint.
3. a kind of rare earth modified hydrophilic chlorosulfonated polyethylene anticorrosive paint of static conductive according to claim 2 and its preparation
Method, it is characterised in that emulsification times are 10-30min in step a.